CN109747305A - 一种石材工艺品的制作方法 - Google Patents
一种石材工艺品的制作方法 Download PDFInfo
- Publication number
- CN109747305A CN109747305A CN201711080958.6A CN201711080958A CN109747305A CN 109747305 A CN109747305 A CN 109747305A CN 201711080958 A CN201711080958 A CN 201711080958A CN 109747305 A CN109747305 A CN 109747305A
- Authority
- CN
- China
- Prior art keywords
- stone
- production method
- corrosion
- stone material
- inhibiting coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种石材工艺品的制作方法，包括以下步骤：步骤一、选取质地坚硬的花岗石按照需求切割成长方体、球体或其它形状；步骤二、将切割好的石材放入石灰水中浸泡3h‑5h；步骤三、清洗后，自然干燥；步骤四、根据需求进行雕刻，雕刻过程中控制表面粗糙度1‑1.6；步骤五、对雕刻好的石材进行打磨；步骤六、清洗打磨后的石材，在石材表面涂刷防腐涂层，防腐涂层厚度为1mm‑3mm；步骤七、在120℃‑150℃的温度下干燥3h‑5h。本发明制作工艺简单快捷，工艺条件容易控制。
Description
技术领域
本发明属于工艺品领域，具体涉及一种石材工艺品的制作方法。
背景技术
随着经济社会的发展，人们对生活的要求更高了，在满足物质需求的同时对精神生活的追求越来越多。工艺品以其自身独特的艺术形式越来越受到人们的青睐。现有技术中，制作工艺品的材料通常是采用陶瓷、石膏材料或高分子材料，制作工艺比较复杂，如高分子材料制备的工艺品，需要对材料进行加热、成型、后整理等工序，而且这种工艺品抗老化能力低，容易对环境和人体造成伤害。
发明内容
本发明所要解决的技术问题便是针对上述现有技术的不足，提供一种石材工艺品的制作方法，制作工艺简单快捷，工艺条件容易控制。
本发明所采用的技术方案是：一种石材工艺品的制作方法，包括以下步骤：
步骤一、选取质地坚硬的花岗石按照需求切割成长方体、球体或其它形状；
步骤二、将切割好的石材放入石灰水中浸泡3h-5h；
步骤三、清洗后，自然干燥；
步骤四、根据需求进行雕刻，雕刻过程中控制表面粗糙度1-1.6；
步骤五、对雕刻好的石材进行打磨；
步骤六、清洗打磨后的石材，在石材表面涂刷防腐涂层，防腐涂层厚度为1mm-3mm；
步骤七、在120℃-150℃的温度下干燥3h-5h。
其中一个实施例中，步骤二中，浸泡时间为3h。
其中一个实施例中，步骤四中，表面粗糙度为1.6。
其中一个实施例中，步骤六中，防腐涂层厚度为3mm。
其中一个实施例中，步骤七中，干燥温度为150℃，干燥时间为5h。
本发明的有益效果在于：该方法以石头为主要原料组分，所需的原材料来源广泛，制作工艺简单快捷，工艺条件容易控制，该方法制备出来的石材工艺品形式多样，质量稳定，能够满足人们对工艺品的需求。
具体实施方式
下面将结合具体实施例对本发明作进一步详细说明。
一种石材工艺品的制作方法，包括以下步骤：
步骤一、选取质地坚硬的花岗石按照需求切割成长方体、球体或其它形状；
步骤二、将切割好的石材放入石灰水中浸泡3h-5h；
步骤三、清洗后，自然干燥；
步骤四、根据需求进行雕刻，雕刻过程中控制表面粗糙度1-1.6；
步骤五、对雕刻好的石材进行打磨；
步骤六、清洗打磨后的石材，在石材表面涂刷防腐涂层，防腐涂层厚度为1mm-3mm；
步骤七、在120℃-150℃的温度下干燥3h-5h。
本实施例中，步骤二中，浸泡时间为3h。
本实施例中，步骤四中，表面粗糙度为1.6。
本实施例中，步骤六中，防腐涂层厚度为3mm。
本实施例中，步骤七中，干燥温度为150℃，干燥时间为5h。
本发明的有益效果在于：该方法以石头为主要原料组分，所需的原材料来源广泛，制作工艺简单快捷，工艺条件容易控制，该方法制备出来的石材工艺品形式多样，质量稳定，能够满足人们对工艺品的需求。
以上所述实施例仅表达了本发明的具体实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。
Claims (5)
1.一种石材工艺品的制作方法，其特征在于：包括以下步骤：
步骤一、选取质地坚硬的花岗石按照需求切割成长方体、球体或其它形状；
步骤二、将切割好的石材放入石灰水中浸泡3h-5h；
步骤三、清洗后，自然干燥；
步骤四、根据需求进行雕刻，雕刻过程中控制表面粗糙度1-1.6；
步骤五、对雕刻好的石材进行打磨；
步骤六、清洗打磨后的石材，在石材表面涂刷防腐涂层，防腐涂层厚度为1mm-3mm；
步骤七、在120℃-150℃的温度下干燥3h-5h。
2.根据权利要求1所述的一种石材工艺品的制作方法，其特征在于：步骤二中，浸泡时间为3h。
3.根据权利要求1所述的一种石材工艺品的制作方法，其特征在于：步骤四中，表面粗糙度为1.6。
4.根据权利要求1所述的一种石材工艺品的制作方法，其特征在于：步骤六中，防腐涂层厚度为3mm。
5.根据权利要求1所述的一种石材工艺品的制作方法，其特征在于：步骤七中，干燥温度为150℃，干燥时间为5h。