CN109735711A - 一种混凝土中钚的浸取方法 - Google Patents
一种混凝土中钚的浸取方法 Download PDFInfo
- Publication number
- CN109735711A CN109735711A CN201811611125.2A CN201811611125A CN109735711A CN 109735711 A CN109735711 A CN 109735711A CN 201811611125 A CN201811611125 A CN 201811611125A CN 109735711 A CN109735711 A CN 109735711A
- Authority
- CN
- China
- Prior art keywords
- plutonium
- concrete
- leaching method
- centrifuge tube
- concrete according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种混凝土中钚的浸取方法,包括以下步骤:S1:钚污染混凝土经破碎﹑研磨﹑筛分仪筛分为200um‑125um的试样;S2:称取200um‑125um的试样5.0g于50mL塑料离心管中,加入4.5mol/L HNO3—5%H2O2溶液25mL,取出,离心分相,残渣留存在离心管中;S3:用20mL4.5mol/L HNO3—5%H2O2洗涤离心管中的残渣,再次离心分相。
Description
技术领域
核设施退役治理技术领域,具体涉及一种混凝土中钚的浸取方法。
背景技术
对于α残留废物——混凝土中富集回收钚的文献国内外鲜有报道,仅有的可用于指导钚回收的文献均为典型的高放废液分离流程及核燃料后处理工艺流程中钚的萃取分离,萃取分离对象为液体,对于固体混凝土中钚的回收未见报道,对于钚回收工艺研究,钚的萃取分离可引用高放废液分离流程及核燃料后处理工艺流程中钚的萃取分离方法,但怎么使混凝土中的钚转移至水相中是首要解决的技术难点。
发明内容
本发明的目的在于:为解决混凝土中钚转移至水相中的技术难点,本专利寻找一种残留废物——混凝土样品预处理方法,使混凝土中90%以上的钚转移至水相中。
本发明的技术方案如下:一种混凝土中钚的浸取方法,包括以下步骤:
S1:钚污染混凝土经破碎﹑研磨﹑筛分仪筛分为200um-125um的试样;
S2:称取200um-125um的试样5.0g于50mL塑料离心管中,加入4.5mol/L HNO3—5%H2O2溶液25mL,取出,离心分相,残渣留存在离心管中;
S3:用20mL4.5mol/L HNO3—5%H2O2洗涤离心管中的残渣,再次离心分相。
所述S1中,钚污染混凝土经JC5颚式破碎机破碎。
所述S1中,钚污染混凝土经BM4行星式球磨机研磨。
所述S2中,上清液转移至50mL容量瓶中。
所述S3中,上清液合并入步骤2的50mL塑料瓶中,稀释至刻度,摇匀备用。
所述S2中,于水浴锅中70℃下加热浸取3h,取出。
所述S2中,取出,冷却至室温后离心分相。
本发明的显著效果在于:采用本方法浸取α残留废物——混凝土中钚,90%以上的钚转移至水相中,解决了钚回收工艺研究中混凝土样品预处理过程。
具体实施方式
一种混凝土中钚的浸取方法,包括以下步骤:
S1:钚污染混凝土经JC5颚式破碎机破碎﹑BM4行星式球磨机研磨﹑筛分仪筛分为200um-125um的试样;
S2:称取200um-125um的试样5.0g于50mL塑料离心管中,加入4.5mol/L HNO3—5%H2O2溶液25mL,于水浴锅中70℃下加热浸取3h,取出,冷却至室温后离心分相,上清液转移至50mL容量瓶中;而残渣留存在离心管中
S3:用20mL4.5mol/L HNO3—5%H2O2洗涤离心管中的残渣,再次离心分相,上清液合并入步骤2的50mL塑料瓶中,稀释至刻度,摇匀备用。
Claims (7)
1.一种混凝土中钚的浸取方法,其特征在于:包括以下步骤:
S1:钚污染混凝土经破碎﹑研磨﹑筛分仪筛分为200um-125um的试样;
S2:称取200um-125um的试样5.0g于50mL塑料离心管中,加入4.5mol/L HNO3—5%H2O2溶液25mL,取出,离心分相,残渣留存在离心管中;
S3:用20mL4.5mol/L HNO3—5%H2O2洗涤离心管中的残渣,再次离心分相。
2.根据权利要求1所述的一种混凝土中钚的浸取方法,其特征在于:所述S1中,钚污染混凝土经JC5颚式破碎机破碎。
3.根据权利要求1所述的一种混凝土中钚的浸取方法,其特征在于:所述S1中,钚污染混凝土经BM4行星式球磨机研磨。
4.根据权利要求1所述的一种混凝土中钚的浸取方法,其特征在于:所述S2中,上清液转移至50mL容量瓶中。
5.根据权利要求1所述的一种混凝土中钚的浸取方法,其特征在于:所述S3中,上清液合并入步骤2的50mL塑料瓶中,稀释至刻度,摇匀备用。
6.根据权利要求1所述的一种混凝土中钚的浸取方法,其特征在于:所述S2中,于水浴锅中70℃下加热浸取3h,取出。
7.根据权利要求6所述的一种混凝土中钚的浸取方法,其特征在于:所述S2中,取出,冷却至室温后离心分相。