CN109733105A - A kind of ceramic marble paper production method - Google Patents
A kind of ceramic marble paper production method Download PDFInfo
- Publication number
- CN109733105A CN109733105A CN201910050888.2A CN201910050888A CN109733105A CN 109733105 A CN109733105 A CN 109733105A CN 201910050888 A CN201910050888 A CN 201910050888A CN 109733105 A CN109733105 A CN 109733105A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- paraffin
- marble paper
- paper production
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic marble paper production methods, comprising the following steps: makes the metal otter board of different coloured patterns respectively；Paraffin is dissolved into print after liquid by heating metal otter board forms release layer on a pet film；Paraffin ceramic paint is made in ceramic paint and heating paraffin dissolution stirring, and the paraffin ceramic paint of different colours is printed on formation pattern color layer on the release layer；Protective layer is printed in the pattern color layer surface.The ceramic marble paper that ceramic marble paper production method of the invention obtains is transferred on ceramics and after decoration firing, have many advantages, such as that surface hardness height, long service life, appearance are smoothly bright, resulting ceramic flower face three-dimensional sense is strong, color is beautiful, and has the function of self-cleaning, antiacid corrosivity and the erosion of anti-detergent and antibacterial etc..
Description
Technical field
The present invention relates to the technical fields of decoration, and in particular to a kind of ceramic marble paper production method.
Background technique
Marble paper is sticked on porcelain blank surface, so that porcelain is formed various colourful patterns by barbecue, is porcelain table
A kind of universal application method is decorated in face, is widely used in household china and is display in the production of decorative ceramics.The print of traditional ceramics marble paper
Brush method is first, then in pattern and color printed thereon windrow, to have a disadvantage in that in film paper printed thereon pattern and color:
After film paper is attached on ceramic body, many colors can disappear in sintering procedure, and the ceramic three-dimensional sense burnt out is poor,
Color is not beautiful enough, and printing cost is high.And existing ceramic marble paper generally uses inorganic pigment to print, decoration firing
It there is a problem that self-cleaning property is poor, acidresistant property is poor, appearance is unsmooth bright afterwards.
Summary of the invention
In order to overcome the shortcomings in the prior art, the object of the present invention is to provide a kind of ceramic marble paper production method, production
Ceramic marble paper has the function of self-cleaning, antiacid corrosion and aggressivity and antibacterial etc., makes resulting ceramic flower face three-dimensional sense
By force, color is beautiful.
In order to solve the above-mentioned technical problems, the present invention provides a kind of ceramic marble paper production methods, comprising the following steps:
S1, the metal otter board for making different coloured patterns respectively；
Paraffin is dissolved into print after liquid and forms release layer on a pet film by S2, heating metal otter board；
S3, paraffin ceramic paint is made in ceramic paint and heating paraffin dissolution stirring, by the paraffin ceramic paint of different colours
It is printed on formation pattern color layer on the release layer；
S4, protective layer is printed in the pattern color layer surface.
Preferably, the ceramic paint is by feldspar powder, quartz, polyacrylic resin, shellsol T and nanometer
Inorganic pigment granules mix.
Wherein, the feldspar powder, quartz, polyacrylic resin, shellsol T and nano inorganic granules of pigments
Between mass ratio be 2:3:1:1:0.01~0.03.
In a preferred embodiment of the invention, in step s 2, the electric current for 80A~110A being loaded on metal otter board makes metal
The wire mesh temperature of web plate maintains is printed between 45~75 DEG C.
In a preferred embodiment of the invention, in step s3, ceramic paint and paraffin are added with the ratio of 1:1.5~2
Paraffin ceramic paint is made in heat of solution stirring.
Compared with prior art, the beneficial effects of the present invention are: the ceramics that ceramic marble paper production method of the invention obtains
Marble paper is transferred on ceramics and after decoration firing, has many advantages, such as that surface hardness height, long service life, appearance are smoothly bright, gained
Ceramic flower face three-dimensional sense it is strong, color is beautiful, and has that self-cleaning, antiacid corrosivity and anti-detergent corrode and antibacterial
Etc. functions.
Detailed description of the invention
It, below will be to required in embodiment or description of the prior art in order to illustrate more clearly of technical solution of the present invention
The attached drawing used is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, right
For those of ordinary skill in the art, without creative efforts, it can also be obtained according to these attached drawings
Its attached drawing.
Fig. 1 is the flow chart of ceramic marble paper production method provided in an embodiment of the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art under the premise of not making the creative labor it is obtained it is all its
His embodiment, shall fall within the protection scope of the present invention.
As shown in Figure 1, ceramic marble paper production method of the present invention the following steps are included:
Embodiment 1
One, the metal otter board of different coloured patterns is made respectively；
Two, paraffin is dissolved into print after liquid by heating metal otter board forms release layer on a pet film, loads on metal otter board
The electric current of 100A maintains the wire mesh temperature of metal otter board to be printed between 60 DEG C；
Three, paraffin ceramic paint is made in ceramic paint and heating paraffin dissolution stirring, by the paraffin ceramic paint of different colours
Be printed on the release layer formation pattern color layer, wherein the ceramic paint by feldspar powder, quartz, polyacrylic resin,
Shellsol T and nano inorganic granules of pigments mix, first that feldspar powder, quartz and aromatic hydrocarbon mixture is molten
Agent is uniformly mixed, and is then mixed again with polyacrylic resin and nano inorganic granules of pigments.The feldspar powder, quartz, polypropylene
Mass ratio between acid resin, shellsol T and nano inorganic granules of pigments is 2:3:1:1:0.02.Ceramic paint
Dissolve by heating stirring with the ratio of 1:2 with paraffin and paraffin ceramic paint is made；
Four, protective layer is printed in the pattern color layer surface, obtains ceramic marble paper, ceramic marble paper is attached on ceramic body and is passed through
It crosses 1250-1300 DEG C of high temperature decoration firing and obtains finished product ceramic.
Embodiment 2
One, the metal otter board of different coloured patterns is made respectively；
Two, paraffin is dissolved into print after liquid by heating metal otter board forms release layer on a pet film, loads on metal otter board
The electric current of 80A maintains the wire mesh temperature of metal otter board to be printed between 75 DEG C；
Three, paraffin ceramic paint is made in ceramic paint and heating paraffin dissolution stirring, by the paraffin ceramic paint of different colours
Be printed on the release layer formation pattern color layer, wherein the ceramic paint by feldspar powder, quartz, polyacrylic resin,
Shellsol T and nano inorganic granules of pigments mix, first that feldspar powder, quartz and aromatic hydrocarbon mixture is molten
Agent is uniformly mixed, and is then mixed again with polyacrylic resin and nano inorganic granules of pigments.The feldspar powder, quartz, polypropylene
Mass ratio between acid resin, shellsol T and nano inorganic granules of pigments is 2:3:1:1:0.01.Ceramic paint
Dissolve by heating stirring with the ratio of 1:1.7 with paraffin and paraffin ceramic paint is made；
Four, protective layer is printed in the pattern color layer surface, obtains ceramic marble paper, ceramic marble paper is attached on ceramic body and is passed through
It crosses 1250-1300 DEG C of high temperature decoration firing and obtains finished product ceramic.
Embodiment 3
One, the metal otter board of different coloured patterns is made respectively；
Two, paraffin is dissolved into print after liquid by heating metal otter board forms release layer on a pet film, loads on metal otter board
The electric current of 110A maintains the wire mesh temperature of metal otter board to be printed between 45 DEG C；
Three, paraffin ceramic paint is made in ceramic paint and heating paraffin dissolution stirring, by the paraffin ceramic paint of different colours
Be printed on the release layer formation pattern color layer, wherein the ceramic paint by feldspar powder, quartz, polyacrylic resin,
Shellsol T and nano inorganic granules of pigments mix, first that feldspar powder, quartz and aromatic hydrocarbon mixture is molten
Agent is uniformly mixed, and is then mixed again with polyacrylic resin and nano inorganic granules of pigments.The feldspar powder, quartz, polypropylene
Mass ratio between acid resin, shellsol T and nano inorganic granules of pigments is 2:3:1:1:0.03.Ceramic paint
Dissolve by heating stirring with the ratio of 1:1.5 with paraffin and paraffin ceramic paint is made；
Four, protective layer is printed in the pattern color layer surface, obtains ceramic marble paper, ceramic marble paper is attached on ceramic body and is passed through
It crosses 1250-1300 DEG C of high temperature decoration firing and obtains finished product ceramic.
The ceramic marble paper that ceramic marble paper production method of the invention obtains is transferred on ceramics and after decoration firing, has surface
The advantages that hardness height, long service life, appearance are smoothly bright, resulting ceramic flower face three-dimensional sense is strong, and color is beautiful, and has
There are self-cleaning, antiacid corrosivity and the functions such as the erosion of anti-detergent and antibacterial.
Above disclosed be only several preferred embodiments of the invention, cannot limit the present invention's certainly with this
Interest field, therefore equivalent changes made in accordance with the claims of the present invention, are still within the scope of the present invention.
Claims (5)
1. a kind of ceramic marble paper production method, it is characterised in that: the following steps are included:
S1, the metal otter board for making different coloured patterns respectively；
Paraffin is dissolved into print after liquid and forms release layer on a pet film by S2, heating metal otter board；
S3, paraffin ceramic paint is made in ceramic paint and heating paraffin dissolution stirring, by the paraffin ceramic paint of different colours
It is printed on formation pattern color layer on the release layer；
S4, protective layer is printed in the pattern color layer surface.
2. ceramic marble paper production method according to claim 1, it is characterised in that: the ceramic paint is by feldspar powder, stone
English, polyacrylic resin, shellsol T and nano inorganic granules of pigments mix.
3. ceramic marble paper production method according to claim 2, it is characterised in that: the feldspar powder, quartz, polypropylene
Mass ratio between acid resin, shellsol T and nano inorganic granules of pigments is 2:3:1:1:0.01~0.03.
4. ceramic marble paper production method according to claim 1, it is characterised in that: in step s 2, on metal otter board
The electric current of load 80A~110A maintains the wire mesh temperature of metal otter board to be printed between 45~75 DEG C.
5. ceramic marble paper production method according to claim 1, it is characterised in that: in step s3, ceramic paint and stone
Wax dissolve by heating stirring with the ratio of 1:1.5~2 is made paraffin ceramic paint.