CN1097199A - 醇溶型可剥离被膜剂 - Google Patents
醇溶型可剥离被膜剂 Download PDFInfo
- Publication number
- CN1097199A CN1097199A CN 93111340 CN93111340A CN1097199A CN 1097199 A CN1097199 A CN 1097199A CN 93111340 CN93111340 CN 93111340 CN 93111340 A CN93111340 A CN 93111340A CN 1097199 A CN1097199 A CN 1097199A
- Authority
- CN
- China
- Prior art keywords
- nylon
- alcohol
- dirt
- copolymer
- stripper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明关于一种醇溶型可剥离被膜剂,由醇溶性
共聚尼龙、溶剂醇和剥离剂组成,对各种材质均有良
好的附着力,被膜形成迅速、干燥快,成膜耐油、耐水、
耐候、耐温,可剥离性能好,清除油污垢简单彻底,可
有效地解决排气扇,抽油烟机及室内、厨房卫生设施
的油污垢清除难题,保护设备设施不受油污垢的污染
和侵蚀。
Description
本发明属日用化工领域,为一种能够防油防污的醇溶型可剥离被膜剂。
目前厨房用排气扇、抽油烟机及其它卫生设施油污垢形成快,清除困难,给使用带来很大不便,目前还没有很好的方法来解决,虽然有各种防油、防污产品,但产品涂覆后,不能剥离,还不能有效地解决问题,吉林科学出版社出版的郭延福编修订版《实用化工产品工艺手册》第462页记载了一种溶剂型可剥塑料,具有可剥离的特性,配方是聚苯乙烯树脂100份,邻苯二甲酸二丁酯40份,石油磺酸钡5-10份,变压器油2份,二苯胺0.5份,磷酸三苯酯2份,油溶性颜料适量。但基料聚苯乙烯树脂脆性大、耐候、耐热性能低。溶剂采用4号过氯乙烯稀释剂含有80%的甲苯,而甲苯有毒,因而这种溶剂型可剥塑料不适合作厨房排气扇、抽油烟机及室内卫生设施的被膜剂。
本发明的目的在于克服现有技术的不足,而提供一种性能优良的防油防污醇溶型可剥离被膜剂。
本发明的目的是通过如下方式来实现的:
醇溶型可剥离被膜剂,包括成膜物、溶剂,特征在于还包括剥离剂,成膜物为醇溶性共聚尼龙,溶剂为醇。
以重量百分数计,醇溶性共聚尼龙为5-25%,溶剂醇为74-94.9%,剥离剂为0.08-0.12%,各组分的百分数之和应为100%。
上所述的剥离剂为十二醇或聚醚改性聚硅氧烷。
上所述的醇为乙醇,共聚尼龙可以是尼龙6、尼龙66的共聚物,也可以是尼龙6、尼龙66、尼龙1010的共聚物,也可以是尼龙6、尼龙66、尼龙1010及含有苯的酰胺共聚物。最佳为尼龙6、尼龙66、尼龙1010的共聚物。含有苯的酰胺为间苯二甲酰巴二胺(MXD)。
溶剂采用食用级乙醇,本发明所述被膜剂可以应用于室内卫生设施如厨房排气扇,抽油烟机等。
醇溶性共聚尼龙属树脂材料,半透明、无味、无毒,其作为成膜材料,成膜性能好,成膜耐油、耐水、耐温(150℃)、耐侯。十二醇或聚醚改性聚硅氧烷作为剥离剂,剥离性能好,本发明集各种成份的优良性能于一体,性能好,效果明显。
性能试验:
将本发明分别涂布于塑料片(10×10cm)、铝质板片(10×10cm)、釉面砖(15×15cm)、玻璃(10×10cm)表面,试验性能如下:
1、耐水:在20℃的水中浸泡100小时,被膜附着良好,不发粘和试验前一样。
2、耐侯:用人工老化机试验150小时,被膜无发脆现象,和试验前一样。
3、耐油、耐温:将150℃的食用油以一定数量涂布一定的面积,在80℃的恒温箱中放30日,被膜未因与油接触和油温而变软或硬化、发粘、发脆、和试验前一样。
本发明的优点:
1、本发明组成材料少,制作工艺简单,对各种材质均有良好的附着力,如材质为塑料、玻璃、釉面砖、铝质等。
2、被膜形成迅速、干燥快,成膜耐油、耐水、耐酸碱、耐侯、耐温(150℃)性能好。
3、清除油污垢时可将被膜与油污垢一次连续剥下,可剥离性能好。清除油污垢简单彻底,省工、省力,使用方便。
4、本发明产品无毒、半透明、微有醇味,可以有效地解决排气扇、抽油烟机及室内、厨房卫生设施的油污垢清除难题,保护设备、设施不受油污垢的污染和侵蚀。
实施例一:
醇溶性共聚尼龙20%、乙醇79.9%、十二醇或聚醚改性聚硅氧烷0.1%。
制作工艺:将乙醇加入带有搅拌器的夹层反应釜中,开动搅拌器,夹层使用热水或蒸汽加温,向反应釜中加入醇溶性共聚尼龙,物料温度控制在35℃左右,反应全溶解后再添加剥离剂至全溶为止。
实施例二:
醇溶性共聚尼龙5%,乙醇94.9%
十二醇或聚醚改性聚硅氧烷0.1%
工艺如实施例一:
实施例三:
醇溶性共聚尼龙25%,乙醇74.92%
十二醇或聚醚改性聚硅氧烷0.08%
实施例四:
醇溶性共聚尼龙14.88% 乙醇85%
十二醇或聚醚改性聚硅氧烷0.12%
实施例1-4所述的溶性共聚尼龙为尼龙6、尼龙66、尼龙1010共聚物。
将本发明的产品涂布于塑料排气扇的扇叶与框架,被膜形成后使用一个月或更长时间,将被膜与油污垢一次连续剥下,清垢简单彻底。膜厚为10-30μm。
将本发明产品涂布于抽油烟机各部位,性能效果同上。
本发明产品可以喷涂也可以刷涂。
Claims (5)
1、一种醇溶型可剥离被膜剂,包括成膜物、溶剂,其特征在于还包括剥离剂,成膜物为醇溶性共聚尼龙,溶剂为醇。
2、根据权利要求1所述的被膜剂,特征在于以重量百分数计,醇溶性共聚尼龙为5-25%,溶剂醇为74-94.9%,剥离剂为0.08-0.12%。
3、根据权利要求1、2所述的被膜剂,特征在于所述剥离剂为十二醇或聚醚改性聚硅氧烷。
4、根据权利要求1所述的被膜剂,特征在于所述醇为乙醇,共聚尼龙可以是尼龙6、尼龙66的共聚物,也可以是尼龙6、尼龙66、尼龙1010的共聚物,也可以是尼龙6、尼龙66、尼龙1010及含有苯的酰胺共聚物。
5、根据权利要求4所述的被膜剂,特征在于所述共聚尼龙以尼龙6、尼龙66、尼龙1010的共聚物最佳。