CN109706463A - A kind of metal surface cleaning liquid and preparation method thereof - Google Patents
A kind of metal surface cleaning liquid and preparation method thereof Download PDFInfo
- Publication number
- CN109706463A CN109706463A CN201910183434.2A CN201910183434A CN109706463A CN 109706463 A CN109706463 A CN 109706463A CN 201910183434 A CN201910183434 A CN 201910183434A CN 109706463 A CN109706463 A CN 109706463A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal surface
- cleaning liquid
- surface cleaning
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal surface cleaning liquids, it is characterised in that it includes the raw material of following parts by weight: 5~10 parts of frosting powder, 0.25~0.5 part of catalyst, thickener 1~3,0.3~0.5 part of disinfectant, 1~3 part of solubilizer, 2~5 parts of chelating agent, 2~5 parts of preservative, 0.5~0.8 part of antirust agent, 10~20 parts of surfactant, 300~450 parts of distilled water.The present invention passes through addition frosting powder, there can be preferable rubbing action to metallic surface during cleaning, to effectively remove the remaining residue in metal surface, cleaning is very clean thorough, by adding antirust agent, the rust staining that metal surface can be cleaned improves the finish of metal surface；Meanwhile preparation process of the present invention is simple, rationally, economic benefit is very good.
Description
Technical field
The present invention relates to cleaning solution technical fields more particularly to a kind of metal surface cleaning liquid and preparation method thereof.
Background technique
When machining is with the maintenance and repair of mechanical equipment, automobile etc., diesel oil, coal Water Oil Or Gas is mostly used to clean greatly
Liquid cleans part.This not only waste of energy, and there is potential insecurity factors, it is careless slightly, then it may lead to fire.
In recent years, a kind of novel metal cleaner is gradually widely used, it being capable of diesel oil substitute, kerosene and vapour well
Oil cleans part, and cheap, and use is safe, be well suited for mechanized cleaning operation.It can be washed for metal, and
Rust staining is not had, here it is so-called metal cleaners.
But existing metal cleaner can only clear up the greasy dirt of metal surface, and to the residue of metal surface, rust staining
There is no good cleaning effect, cause to need to clean repeatedly in actual washing and cleaning operation, operation is very troublesome, therefore we mention
A kind of metal surface cleaning liquid and preparation method thereof out.
Summary of the invention
The one kind for having a difficult cleaning of problem of residue, rust staining the purpose of the present invention is to solve metal surface, and proposing
Metal surface cleaning liquid.
To achieve the goals above, present invention employs following technical solutions:
A kind of metal surface cleaning liquid, which is characterized in that the raw material including following parts by weight: 5~10 parts of frosting powder, catalysis
0.25~0.5 part of agent, thickener 1~3,0.3~0.5 part of disinfectant, 1~3 part of solubilizer, 2~5 parts of chelating agent, preservative 2~
5 parts, 0.5~0.8 part of antirust agent, 10~20 parts of surfactant, 300~450 parts of distilled water；
The frosting powder is one of aluminium oxide, silicon stone, and the catalyst is iron chloride, and the thickener is that sodium base is swollen
Moisten one of soil, organobentonite, diatomite, the disinfectant is one of hydrogen peroxide, copper sulphate, and the solubilizer is
One of propylene glycol, glycerine, the chelating agent are one of ethylenediamine tetra-acetic acid, disodium EDTA, institute
Stating preservative is one of benzoic acid, sodium benzoate, sorbic acid, potassium sorbate, calcium propionate, and the antirust agent is phosphoric acid, pine
One of perfume, the surfactant are one of sodium n-alkylbenzenesulfonate, fatty alcohol-ether sodium sulfate.
Preferably, 5 parts of the aluminium oxide, 0.25 part of iron chloride, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, propylene glycol 1
Part, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, 0.5 part of phosphoric acid, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
Preferably, 8 parts of the aluminium oxide, 0.25 part of iron chloride, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, propylene glycol 1
Part, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, 0.5 part of phosphoric acid, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
Preferably, 10 parts of the aluminium oxide, 0.25 part of iron chloride, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, propylene glycol 1
Part, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, 0.5 part of phosphoric acid, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
Preferably, 5 parts of the aluminium oxide, 0.25 part of iron chloride, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, propylene glycol 1
Part, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, 0.8 part of phosphoric acid, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
The invention also provides a kind of preparation methods of metal surface cleaning liquid, comprising the following steps:
S1: taking 1/3 distilled water, be added in agitator tank, surfactant is added in agitator tank, stirring and dissolving；
S2: catalyst, thickener, solubilizer, chelating agent, preservative, disinfectant, antirust are successively added into agitator tank
Constantly remaining 2/3 distilled water is added during addition for agent, frosting powder, it is every add a kind of ingredient before be both needed to face
The ingredient of addition is completely dissolved；
S3: the pH value of mixed liquor is detected after all the components are completely dissolved in tank to be mixed, and will by addition regulator
It mixes molten pH and is adjusted to neutrality to get metal surface cleaning liquid, by metal surface cleaning liquid bottling, sealing, wherein adjusting
Agent is citric acid or ammonium hydroxide.
Compared with prior art, the beneficial effects of the present invention are:
The present invention can have preferable friction to make metallic surface by addition frosting powder during cleaning
With to effectively remove the remaining residue in metal surface, cleaning is very clean thorough, by adding antirust agent, can clean
The rust staining of metal surface improves the finish of metal surface；Meanwhile preparation process of the present invention is simple, rationally, economic benefit is non-
Chang Hao.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.
Embodiment one:
A kind of metal surface cleaning liquid proposed by the present invention, the raw material including following parts by weight: 5 parts of frosting powder, catalyst
0.25 part, 1 part of thickener, 0.3 part of disinfectant, 1 part of solubilizer, 2 parts of chelating agent, 2 parts of preservative, 0.5 part of antirust agent, surface is living
10 parts of agent, 400 parts of distilled water of property.
Frosting powder is aluminium oxide, and catalyst is iron chloride, and thickener is sodium bentonite, and disinfectant is hydrogen peroxide, solubilising
Agent is propylene glycol, and chelating agent is ethylenediamine tetra-acetic acid, and preservative is benzoic acid, and antirust agent is phosphoric acid, and surfactant is straight chain
Sodium alkyl benzene sulfonate.
Preparation method, comprising the following steps:
S1: taking 1/3 distilled water, be added in agitator tank, surfactant is added in agitator tank, stirring and dissolving；
S2: catalyst, thickener, solubilizer, chelating agent, preservative, disinfectant, antirust are successively added into agitator tank
Constantly remaining 2/3 distilled water is added during addition for agent, frosting powder, it is every add a kind of ingredient before be both needed to face
The ingredient of addition is completely dissolved；
S3: the pH value of mixed liquor is detected after all the components are completely dissolved in tank to be mixed, and will by addition regulator
It mixes molten pH and is adjusted to neutrality to get metal surface cleaning liquid, by metal surface cleaning liquid bottling, sealing, wherein adjusting
Agent is citric acid or ammonium hydroxide.
Embodiment two:
A kind of metal surface cleaning liquid proposed by the present invention, the raw material including following parts by weight: 8 parts of frosting powder, catalyst
0.25 part, 1 part of thickener, 0.3 part of disinfectant, 1 part of solubilizer, 2 parts of chelating agent, 2 parts of preservative, 0.5 part of antirust agent, surface is living
10 parts of agent, 400 parts of distilled water of property.
Frosting powder is aluminium oxide, and catalyst is iron chloride, and thickener is sodium bentonite, and disinfectant is hydrogen peroxide, solubilising
Agent is propylene glycol, and chelating agent is ethylenediamine tetra-acetic acid, and preservative is benzoic acid, and antirust agent is phosphoric acid, and surfactant is straight chain
Sodium alkyl benzene sulfonate.
Preparation method, comprising the following steps:
S1: taking 1/3 distilled water, be added in agitator tank, surfactant is added in agitator tank, stirring and dissolving；
S2: catalyst, thickener, solubilizer, chelating agent, preservative, disinfectant, antirust are successively added into agitator tank
Constantly remaining 2/3 distilled water is added during addition for agent, frosting powder, it is every add a kind of ingredient before be both needed to face
The ingredient of addition is completely dissolved；
S3: the pH value of mixed liquor is detected after all the components are completely dissolved in tank to be mixed, and will by addition regulator
It mixes molten pH and is adjusted to neutrality to get metal surface cleaning liquid, by metal surface cleaning liquid bottling, sealing, wherein adjusting
Agent is citric acid or ammonium hydroxide.
Embodiment three:
A kind of metal surface cleaning liquid proposed by the present invention, the raw material including following parts by weight: 10 parts of frosting powder, catalyst
0.25 part, 1 part of thickener, 0.3 part of disinfectant, 1 part of solubilizer, 2 parts of chelating agent, 2 parts of preservative, 0.5 part of antirust agent, surface is living
10 parts of agent, 400 parts of distilled water of property.
Frosting powder is aluminium oxide, and catalyst is iron chloride, and thickener is sodium bentonite, and disinfectant is hydrogen peroxide, solubilising
Agent is propylene glycol, and chelating agent is ethylenediamine tetra-acetic acid, and preservative is benzoic acid, and antirust agent is phosphoric acid, and surfactant is straight chain
Sodium alkyl benzene sulfonate.
Preparation method, comprising the following steps:
S1: taking 1/3 distilled water, be added in agitator tank, surfactant is added in agitator tank, stirring and dissolving；
S2: catalyst, thickener, solubilizer, chelating agent, preservative, disinfectant, antirust are successively added into agitator tank
Constantly remaining 2/3 distilled water is added during addition for agent, frosting powder, it is every add a kind of ingredient before be both needed to face
The ingredient of addition is completely dissolved；
S3: the pH value of mixed liquor is detected after all the components are completely dissolved in tank to be mixed, and will by addition regulator
It mixes molten pH and is adjusted to neutrality to get metal surface cleaning liquid, by metal surface cleaning liquid bottling, sealing, wherein adjusting
Agent is citric acid or ammonium hydroxide.
Example IV:
A kind of metal surface cleaning liquid proposed by the present invention, the raw material including following parts by weight: 5 parts of frosting powder, catalyst
0.25 part, 1 part of thickener, 0.3 part of disinfectant, 1 part of solubilizer, 2 parts of chelating agent, 2 parts of preservative, 0.8 part of antirust agent, surface is living
10 parts of agent, 400 parts of distilled water of property.
Frosting powder is aluminium oxide, and catalyst is iron chloride, and thickener is sodium bentonite, and disinfectant is hydrogen peroxide, solubilising
Agent is propylene glycol, and chelating agent is ethylenediamine tetra-acetic acid, and preservative is benzoic acid, and antirust agent is phosphoric acid, and surfactant is straight chain
Sodium alkyl benzene sulfonate.
Preparation method, comprising the following steps:
S1: taking 1/3 distilled water, be added in agitator tank, surfactant is added in agitator tank, stirring and dissolving；
S2: catalyst, thickener, solubilizer, chelating agent, preservative, disinfectant, antirust are successively added into agitator tank
Constantly remaining 2/3 distilled water is added during addition for agent, frosting powder, it is every add a kind of ingredient before be both needed to face
The ingredient of addition is completely dissolved；
S3: the pH value of mixed liquor is detected after all the components are completely dissolved in tank to be mixed, and will by addition regulator
It mixes molten pH and is adjusted to neutrality to get metal surface cleaning liquid, by metal surface cleaning liquid bottling, sealing, wherein adjusting
Agent is citric acid or ammonium hydroxide.
The present invention can have preferable friction to make metallic surface by addition frosting powder during cleaning
With to effectively remove the remaining residue in metal surface, cleaning is very clean thorough, by adding antirust agent, can clean
The rust staining of metal surface improves the finish of metal surface；Meanwhile preparation process of the present invention is simple, rationally, economic benefit is non-
Chang Hao.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of metal surface cleaning liquid, which is characterized in that the raw material including following parts by weight: 5~10 parts of frosting powder, catalyst
0.25~0.5 part, thickener 1~3,0.3~0.5 part of disinfectant, 1~3 part of solubilizer, 2~5 parts of chelating agent, preservative 2~5
Part, 0.5~0.8 part of antirust agent, 10~20 parts of surfactant, 300~450 parts of distilled water；
The frosting powder is one of aluminium oxide, silicon stone, and the catalyst is iron chloride, and the thickener is Na-bentonite
One of soil, organobentonite, diatomite, the disinfectant are one of hydrogen peroxide, copper sulphate, and the solubilizer is third
One of glycol, glycerine, the chelating agent be one of ethylenediamine tetra-acetic acid, disodium EDTA, it is described
Preservative is one of benzoic acid, sodium benzoate, sorbic acid, potassium sorbate, calcium propionate, and the antirust agent is phosphoric acid, rosin
One of water, the surfactant are one of sodium n-alkylbenzenesulfonate, fatty alcohol-ether sodium sulfate.
2. a kind of metal surface cleaning liquid according to claim 1, which is characterized in that 5 parts of the aluminium oxide, iron chloride
0.25 part, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, 1 part of propylene glycol, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, phosphoric acid 0.5
Part, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
3. a kind of metal surface cleaning liquid according to claim 2, which is characterized in that 8 parts of the aluminium oxide, iron chloride
0.25 part, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, 1 part of propylene glycol, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, phosphoric acid 0.5
Part, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
4. a kind of metal surface cleaning liquid according to claim 2, which is characterized in that 10 parts of the aluminium oxide, iron chloride
0.25 part, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, 1 part of propylene glycol, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, phosphoric acid 0.5
Part, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
5. a kind of metal surface cleaning liquid according to claim 2, which is characterized in that 5 parts of the aluminium oxide, iron chloride
0.25 part, 1 part of sodium bentonite, 0.3 part of hydrogen peroxide, 1 part of propylene glycol, 2 parts of ethylenediamine tetra-acetic acid, 2 parts of benzoic acid, phosphoric acid 0.8
Part, 10 parts of sodium n-alkylbenzenesulfonate, 400 parts of distilled water.
6. a kind of preparation method of metal surface cleaning liquid according to any one of claims 1 to 5, which is characterized in that
The following steps are included:
S1: taking 1/3 distilled water, be added in agitator tank, surfactant is added in agitator tank, stirring and dissolving；
S2: catalyst, thickener, solubilizer, chelating agent, preservative, disinfectant, antirust agent, mill are successively added into agitator tank
Constantly remaining 2/3 distilled water is added during addition for emery dust, it is every add a kind of ingredient before be both needed to face addition
Ingredient is completely dissolved；
S3: the pH value of mixed liquor is detected after all the components are completely dissolved in tank to be mixed, and will be mixed by addition regulator
Molten pH is adjusted to neutrality to get metal surface cleaning liquid, and by metal surface cleaning liquid bottling, sealing, wherein regulator is
Citric acid or ammonium hydroxide.