CN109705732A - A kind of children's wooden toy blue paste and production method - Google Patents
A kind of children's wooden toy blue paste and production method Download PDFInfo
- Publication number
- CN109705732A CN109705732A CN201811454493.0A CN201811454493A CN109705732A CN 109705732 A CN109705732 A CN 109705732A CN 201811454493 A CN201811454493 A CN 201811454493A CN 109705732 A CN109705732 A CN 109705732A
- Authority
- CN
- China
- Prior art keywords
- parts
- edible
- children
- low
- wooden toy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of children's wooden toy blue paste and production methods, including using brilliant blue pigment, it is the composition weight proportion of the coating are as follows: 1 part to 2 parts of brilliant blue pigment, 5 parts to 10 parts edible gelatins, 2 parts to 5 parts of low-ester pectin, 0.5 part to 2 parts of edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water, wherein 1 part to 2 parts of brilliant blue pigment, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water form mill base group, 5 parts to 10 parts edible gelatins and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, it is sufficiently mixed for two groups when use.A kind of children's wooden toy blue paste that the production method of this use invention obtains, with high safety, after being coated on children's wooden toy, the toy even if children bite when playing, health hazard will not be brought to the person of biting, ensured the healthy growth of children, and both ensure that after being painted on wooden toy color it is bright-coloured and also keep wooden toy much cleaner and safe.
Description
Technical field
The present invention relates to a kind of production technology of coating, especially a kind of children's wooden toy blue paste and producer
Method.
Background technique
In existing toy coating, it is especially used for the toy for children coating of woodwork, used coating to be substantially third
Olefin(e) acid class coating, as disclosed in 200910193125.X " acrylic emulsion of water-borne toy coating ", disclosed in 200910038289.5
" a kind of low volatility, quick-drying aqueous toy coating and its manufacturing method ", although acrylic coating is compared to poly- ammonia
Esters coating toxicity is low, but as being used for toy for children, children when playing often biting in toy posting port, institute
With for children and unsafe, as the coating of articles for children, it is not only that it should be without harmful volatility object
Matter, also answering entrance is also to have safety.
For the wooden toy of children, the purpose of coating is to give various colors abundant, rather than extends wooden toy
The problem of holding time, thus how to obtain it is a kind of can be given on woodwork color abundant without to child skin,
It is the toy for children paint development matter of utmost importance to be considered that entrance, which all brings the coating of harm, at present almost without such a true
Really it is suitable for the safety dope of children's wooden toy.
Summary of the invention
One kind is provided and is had a safety feature the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art, and can be obtained
Bright colors and being suitble to are attached to a kind of children's wooden toy blue paste and production method of woodwork.
To achieve the goals above, a kind of children's wooden toy blue paste designed by the present invention, including using bright
Cyanine is the composition weight proportion of the coating are as follows: 0.5 part to 1.0 parts of brilliant blue pigment, 5 parts to 10 parts edible gelatins,
2 parts to 5 parts of low-ester pectin, 0.5 part to 2 parts of edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water,
Wherein 0.5 part to 1.0 parts of brilliant blue pigment, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water group
At mill base group, 5 parts to 10 parts edible gelatins and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, two when use
Group is sufficiently mixed.
In order to further be incorporated in pigment on wood fibre, and in the presence of calcium ion there is preferably solidification to make
With, the wear-resisting property and color saturation of coating are improved, keeps color more bright-coloured beautiful, a kind of children's wooden toy blue
Coating is the cornstarch being additionally provided in every 100 parts of above-mentioned components no more than 2 parts.
The present invention provides a kind of production method of children's wooden toy blue paste, is first by 2 parts to 5 parts of low ester fruit
Glue is wet with edible ethanol, for standard, then under high velocity agitation the dosage of edible ethanol is all wet with reaching low-ester pectin
Low-ester pectin after will be wet is dissolved in 50 parts of water, and 0.5 part to 2 parts of edible grade sodium chloride and 0.5 is added after being uniformly dissolved
The brilliant blue pigment of part to 1.0 parts continues to stir all to be sufficiently solubilized to edible grade sodium chloride and brilliant blue pigment that mill base group is made；Separately
5 parts to 10 parts edible gelatins are dissolved by heating, gelatin solution is made in 50 parts of water, heating and temperature control is at 60 DEG C hereinafter, bright
1 part to 10 parts food grade calcium carbonate is added in sol solution and carries out that composition film forming promotion group is sufficiently stirred.When needing coating, by mill base
Group and film forming promotion group mix and are stirred well to uniformly and adjust pH value to 6.5 with reagent grade hydrochloric acid.
Here, brilliant blue light resistance, heat resistance, acid resistance, salt tolerance and microbial resistance are fine；Pectin plays pigment herein
The dispersion and stabilization of emulsification, pigment after dissolving in gelatin, further stable pigment plays the role of protecting color, brilliant blue sodium chloride
Pigment is with good stability in the environment existing for pectin, keeps bright in color distinctness without fugitive color；Food grade carbonic acid
The addition of calcium can control opacity needed for wood materials according to the adjusting of additional amount, and calcium ion also promotes low ester fruit
The film forming of glue, pectin film can play antibacterial and bacteriostasis, form antibiotic layer in wood surface, make the much cleaner safety of wooden toy；
Using reagent grade hydrochloric acid adjusting coating pH value, guarantor's colour circle border of brilliant blue pigment both ensure that.
When needing that cornstarch is added, it is the cornstarch being added in every 100 parts of above-mentioned components no more than 2 parts, first will
Cornstarch is completely dissolved under high velocity agitation in 50 parts of water, is added the low-ester pectin with edible ethanol after wet, is worked as jade
Rice starch and low-ester pectin be added in stirring again after being completely dissolved 0.5 part to 2 parts edible grade sodium chloride and 1 part to 2 parts
Mill base group is made in brilliant blue pigment, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, guarantees coating
Product quality.
A kind of children's wooden toy blue paste that the production method of this use invention obtains, it is all former using food-grade
Material has high safety, and after being coated on children's wooden toy, the toy even if children bite when playing will not be gnawed
The person of stinging brings health hazard, has ensured the healthy growth of children, here, low-ester pectin, cornstarch and edible gelatin are in this hair
In the composition of bright offer all have film forming, and have respective effect, both ensure that after being painted on wooden toy color
It is bright-coloured, also make wooden toy much cleaner and safe.
Specific embodiment
Below with reference to embodiment, the present invention is further described.
Embodiment 1:
A kind of children's wooden toy blue paste that this implementation column provides, including brilliant blue pigment is used, it is the coating
Form weight proportion are as follows: 0.5 part of brilliant blue pigment, 5 parts of edible gelatins, 5 parts of low-ester pectin, 0.5 part of edible grade sodium chloride, 1 part
Food grade calcium carbonate and 100 parts of water, wherein 0.5 part of brilliant blue pigment, 5 parts of low-ester pectin and 0.5 part of edible grade sodium chloride and
50 parts of water form mill base groups, 5 parts of edible gelatins and 1 part of food grade calcium carbonate and 50 parts of water composition film forming promotion groups, two when use
Group is sufficiently mixed.
It is first by 5 parts of low-ester pectin the present embodiment provides a kind of production method of children's wooden toy blue paste
Wet with edible ethanol, the dosage of edible ethanol is all wet with reaching low-ester pectin as standard, then under high velocity agitation will
Low-ester pectin after wet is dissolved in 50 parts of water, and 0.5 part of edible grade sodium chloride and 0.5 part of sapphirine are added after being uniformly dissolved
Element continues to stir all to be sufficiently solubilized to edible grade sodium chloride and brilliant blue pigment that mill base group is made；Separately 5 parts of edible gelatins are heated
It is dissolved in 50 parts of water and gelatin solution is made, heating and temperature control is at 60 DEG C hereinafter, 1 part of food grade carbon is added in gelatin solution
Sour calcium simultaneously carries out that composition film forming promotion group is sufficiently stirred.When needing coating, mill base group and film forming promotion group are mixed and be sufficiently stirred
To uniformly and with reagent grade hydrochloric acid adjusting pH value to 6.5.
A kind of children's wooden toy blue paste that the present embodiment obtains, by naturally dry after being painted on wooden toy
Translucent beautiful blue is presented after film forming in dry film forming.
Embodiment 2:
A kind of children's wooden toy blue paste that this implementation column provides, including brilliant blue pigment is used, it is the coating
Form weight proportion are as follows: 1 part of brilliant blue pigment, 10 parts of edible gelatins, 2 parts of low-ester pectins, 2 parts of edible grade sodium chloride, 10 parts
Food grade calcium carbonate and 100 parts of water, wherein 2 parts of brilliant blue pigment, 2 parts of low-ester pectins and 2 parts of edible grade sodium chloride and 50
Part water forms mill base group, 10 parts of edible gelatins and 10 parts of food grade calcium carbonate and 50 parts of water composition film forming promotion groups, two when use
Group is sufficiently mixed.
It is first to use 2 parts of low-ester pectins the present embodiment provides a kind of production method of children's wooden toy blue paste
Edible ethanol is wet, and the dosage of edible ethanol is all wet with reaching low-ester pectin as standard, then under high velocity agitation will be wet
Low-ester pectin after profit is dissolved in 50 parts of water, and 2 parts of edible grade sodium chloride and 1 part of brilliant blue pigment are added after being uniformly dissolved,
Continue to stir all to be sufficiently solubilized to edible grade sodium chloride and brilliant blue pigment that mill base group is made；It is separately that 10 parts of edible gelatin heating are molten
Gelatin solution is made in solution in 50 parts of water, and heating and temperature control is at 60 DEG C hereinafter, 10 parts of food grade carbon are added in gelatin solution
Sour calcium simultaneously carries out that composition film forming promotion group is sufficiently stirred.When needing coating, mill base group and film forming promotion group are mixed and be sufficiently stirred
To uniformly and with reagent grade hydrochloric acid adjusting pH value to 6.5.
A kind of children's wooden toy blue paste that the present embodiment obtains, by naturally dry after being painted on wooden toy
Opaque beautiful blue is presented after film forming in dry film forming.
Embodiment 3:
A kind of children's wooden toy blue paste that this implementation column provides is implemented at every 100 parts on the basis of embodiment 1
2 parts of cornstarch is added in component described in example 1.It is the jade that 2 parts are added in every 100 parts of above-mentioned components when cornstarch is added
Cornstarch is first completely dissolved in 50 parts of water by rice starch under high velocity agitation, is added low after wet with edible ethanol
Ester pectin, be added in stirring again after cornstarch and low-ester pectin are completely dissolved 0.5 part edible grade sodium chloride and 0.5 part
Mill base group is made in brilliant blue pigment, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, guarantees coating
Product quality.
Embodiment 4:
A kind of children's wooden toy blue paste that this implementation column provides is implemented on the basis of embodiment 2 at every 100 parts
0.5 part of cornstarch is added in component described in example 2.It is that 0.5 part is added in every 100 parts of above-mentioned components when cornstarch is added
Cornstarch, first cornstarch is completely dissolved under high velocity agitation in 50 parts of water, add with edible ethanol it is wet after
Low-ester pectin, be added in stirring again after cornstarch and low-ester pectin are completely dissolved 2 parts edible grade sodium chloride and 1 part
Brilliant blue pigment mill base group is made, this successive addition sequence guarantees to apply to facilitate the dispersion and dissolution of low-ester pectin in water
The product quality of material.
Claims (4)
1. a kind of children's wooden toy blue paste, including use brilliant blue pigment, it is characterised in that the composition weight of the coating
Amount proportion are as follows: 0.5 part to 1.0 parts of brilliant blue pigment, 5 parts to 10 parts edible gelatins, 2 parts to 5 parts of low-ester pectin, 0.5 part to 2
The edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water of part, wherein 0.5 part to 1.0 parts of brilliant blue pigment,
2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water form mill base group, 5 parts to 10 parts edible gelatins
With 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, it is sufficiently mixed for two groups when use.
2. a kind of children's wooden toy blue paste according to claim 1, it is characterized in that in every 100 parts of above-mentioned components
In be additionally provided with cornstarch no more than 2 parts.
3. a kind of a kind of production method of children's wooden toy blue paste according to claim 1, it is characterized in that first
2 parts to 5 parts of low-ester pectin is moistened with edible ethanol, the dosage of edible ethanol is all wet with reaching low-ester pectin as mark
Standard, the low-ester pectin after then moistening under high velocity agitation are dissolved in 50 parts of water, and 0.5 part to 2 parts is added after being uniformly dissolved
Edible grade sodium chloride and 0.5 part to 1.0 parts of brilliant blue pigment, continue stirring and all filled to edible grade sodium chloride and brilliant blue pigment
Divide dissolution that mill base group is made；Separately 5 parts to 10 parts edible gelatins are dissolved by heating, gelatin solution, heating temperature is made in 50 parts of water
Control is at 60 DEG C hereinafter, 1 part to 10 parts food grade calcium carbonate is added in gelatin solution again and carries out that composition film forming is sufficiently stirred
Promotion group；When needing coating, mill base group and film forming promotion group are mixed and is stirred well to uniformly and adjusts PH with reagent grade hydrochloric acid
It is worth to 6.5.
4. the production method of a kind of children's wooden toy blue paste according to claim 3, it is characterized in that every 100
It is additionally provided with the cornstarch no more than 2 parts in the above-mentioned component of part, cornstarch is first completely dissolved in 50 parts under high velocity agitation
In water, the low-ester pectin with edible ethanol after wet is added, is being stirred again after cornstarch and low-ester pectin are completely dissolved
Mill base group is made in 0.5 part to 2 parts of edible grade sodium chloride of middle addition and 0.5 part to 1.0 parts of brilliant blue pigment.