CN109705731A - A kind of children's wooden toy green coating and production method - Google Patents
A kind of children's wooden toy green coating and production method Download PDFInfo
- Publication number
- CN109705731A CN109705731A CN201811454491.1A CN201811454491A CN109705731A CN 109705731 A CN109705731 A CN 109705731A CN 201811454491 A CN201811454491 A CN 201811454491A CN 109705731 A CN109705731 A CN 109705731A
- Authority
- CN
- China
- Prior art keywords
- parts
- edible
- children
- low
- wooden toy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of children's wooden toy green coating and production methods, including using sodium copper chlorophyllin, it is the composition weight proportion of the coating are as follows: 1 part to 2 parts of sodium copper chlorophyllin, 5 parts to 10 parts edible gelatins, 2 parts to 5 parts of low-ester pectin, 0.5 part to 2 parts of edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water, wherein 1 part to 2 parts of sodium copper chlorophyllin, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water form mill base group, 5 parts to 10 parts edible gelatins and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, it is sufficiently mixed for two groups when use.A kind of children's wooden toy green coating that the production method of this use invention obtains, with high safety, after being coated on children's wooden toy, the toy even if children bite when playing, health hazard will not be brought to the person of biting, ensured the healthy growth of children, and both ensure that after being painted on wooden toy color it is bright-coloured and also keep wooden toy much cleaner and safe.
Description
Technical field
The present invention relates to a kind of production technology of coating, especially a kind of children's wooden toy green coating and producer
Method.
Background technique
In existing toy coating, it is especially used for the toy for children coating of woodwork, used coating to be substantially third
Olefin(e) acid class coating, as disclosed in 200910193125.X " acrylic emulsion of water-borne toy coating ", disclosed in 200910038289.5
" a kind of low volatility, quick-drying aqueous toy coating and its manufacturing method ", although acrylic coating is compared to poly- ammonia
Esters coating toxicity is low, but as being used for toy for children, children when playing often biting in toy posting port, institute
With for children and unsafe, as the coating of articles for children, it is not only that it should be without harmful volatility object
Matter, also answering entrance is also to have safety.
For the wooden toy of children, the purpose of coating is to give various colors abundant, rather than extends wooden toy
The problem of holding time, thus how to obtain it is a kind of can be given on woodwork color abundant without to child skin,
It is the toy for children paint development matter of utmost importance to be considered that entrance, which all brings the coating of harm, at present almost without such a true
Really it is suitable for the safety dope of children's wooden toy.
Summary of the invention
One kind is provided and is had a safety feature the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art, and can be obtained
Bright colors and being suitble to are attached to a kind of children's wooden toy green coating and production method of woodwork.
To achieve the goals above, a kind of children's wooden toy green coating designed by the present invention, including use leaf
Green element copper sodium, is the composition weight proportion of the coating are as follows: 1 part to 2 parts of sodium copper chlorophyllin, 5 parts to 10 parts it is edible
Gelatin, 2 parts to 5 parts of low-ester pectin, 0.5 part to 2 parts of edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts
Water, wherein 1 part to 2 parts of sodium copper chlorophyllin, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride
Mill base group, 5 parts to 10 parts edible gelatins and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group are formed with water, is made
Two groups of used time are sufficiently mixed.
In order to further be incorporated in pigment on wood fibre, and in the presence of calcium ion there is preferably solidification to make
With, the wear-resisting property and color saturation of coating are improved, keeps color more bright-coloured beautiful, a kind of children's wooden toy green
Coating is the cornstarch being additionally provided in every 100 parts of above-mentioned components no more than 2 parts.
The present invention provides a kind of production method of children's wooden toy green coating, is first by 2 parts to 5 parts of low ester fruit
Glue is wet with edible ethanol, for standard, then under high velocity agitation the dosage of edible ethanol is all wet with reaching low-ester pectin
Will it is wet after low-ester pectin be dissolved in 50 parts of water, be added after being uniformly dissolved 0.5 part to 2 parts edible grade sodium chloride and 1 part
To 2 parts of sodium copper chlorophyllin, continue to stir all to be sufficiently solubilized to edible grade sodium chloride and sodium copper chlorophyllin that mill base is made
Group；5 parts to 10 parts edible gelatins heating for dissolving is separately made gelatin solution in 50 parts of water, heating and temperature control 60 DEG C with
Under, it is added and 1 part to 10 parts food grade calcium carbonate and is sufficiently stirred in gelatin solution, and with calcium hydroxide saturated aqueous solution
PH value is adjusted to 8.0 to 9.0 composition film forming promotion groups.When needing coating, mill base group and film forming promotion group are mixed and be sufficiently stirred
To uniform.
Here, sodium copper chlorophyllin has the tone of natural green plant, in the solid state and the environment of pH value 8 to 9
There is down preferable stability；Pectin plays the dispersion and stabilization of the emulsification after pigment dissolves in gelatin, pigment, chlorine herein
Changing sodium, further stable pigment plays the role of protecting color, and sodium copper chlorophyllin has good stabilization in the environment existing for pectin
Property, keep bright in color distinctness without fugitive color；The addition of food grade calcium carbonate can be controlled according to the adjusting of additional amount to wooden
Opacity needed for material, and calcium ion also promotes the film forming of low-ester pectin, and pectin film can play antibacterial and bacteriostasis, in wood
Material surface forms antibiotic layer, makes the much cleaner safety of wooden toy；Using calcium hydroxide aqueous solution adjusting coating pH value, both ensure that
Guarantor's colour circle border of sodium copper chlorophyllin, while it has certain sterilization, insecticidal action, can kill and colonize on wood materials
Some fungies, bacterium and pest.
When needing that cornstarch is added, it is the cornstarch being added in every 100 parts of above-mentioned components no more than 2 parts, first will
Cornstarch is completely dissolved under high velocity agitation in 50 parts of water, is added the low-ester pectin with edible ethanol after wet, is worked as jade
Rice starch and low-ester pectin be added in stirring again after being completely dissolved 0.5 part to 2 parts edible grade sodium chloride and 1 part to 2 parts
Mill base group is made in sodium copper chlorophyllin, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, guarantees
The product quality of coating.
A kind of children's wooden toy green coating that the production method of this use invention obtains, it is all former using food-grade
Material has high safety, and after being coated on children's wooden toy, the toy even if children bite when playing will not be gnawed
The person of stinging brings health hazard, has ensured the healthy growth of children, here, low-ester pectin, cornstarch and edible gelatin are in this hair
In the composition of bright offer all have film forming, and have respective effect, both ensure that after being painted on wooden toy color
It is bright-coloured, also make wooden toy much cleaner and safe.
Specific embodiment
Below with reference to embodiment, the present invention is further described.
Embodiment 1:
A kind of children's wooden toy green coating that this implementation column provides, including sodium copper chlorophyllin is used, it is the painting
The composition weight proportion of material are as follows: 1 part of sodium copper chlorophyllin, 5 parts of edible gelatins, 5 parts of low-ester pectin, 0.5 part of food grade chlorination
Sodium, 1 part of food grade calcium carbonate and 100 parts of water, wherein 1 part of sodium copper chlorophyllin, 5 parts of low-ester pectin and 0.5 part of food grade
Sodium chloride and 50 parts of water form mill base group, 5 parts of edible gelatins and 1 part of food grade calcium carbonate and 50 parts of water composition film forming promotion groups,
It is sufficiently mixed for two groups when use.
It is first by 5 parts of low-ester pectin the present embodiment provides a kind of production method of children's wooden toy green coating
Wet with edible ethanol, the dosage of edible ethanol is all wet with reaching low-ester pectin as standard, then under high velocity agitation will
Low-ester pectin after wet is dissolved in 50 parts of water, and 0.5 part of edible grade sodium chloride and 1 part of chlorophyll copper sodium are added after being uniformly dissolved
Salt continues to stir all to be sufficiently solubilized to edible grade sodium chloride and sodium copper chlorophyllin that mill base group is made；Separately by 5 parts of edible gelatins
It dissolves by heating and gelatin solution is made in 50 parts of water, heating and temperature control is eaten at 60 DEG C hereinafter, 1 part is added in gelatin solution
Grade calcium carbonate is simultaneously sufficiently stirred, and adjusts pH value to 8.0 composition film forming promotion groups with calcium hydroxide saturated aqueous solution.It needs to apply
When dress, mill base group and film forming promotion group are mixed and are stirred well to uniformly.
A kind of children's wooden toy green coating that the present embodiment obtains, by naturally dry after being painted on wooden toy
Translucent beautiful green is presented after film forming in dry film forming.
Embodiment 2:
A kind of children's wooden toy green coating that this implementation column provides, including sodium copper chlorophyllin is used, it is the painting
The composition weight proportion of material are as follows: 2 parts of sodium copper chlorophyllin, 10 parts of edible gelatins, 2 parts of low-ester pectins, 2 parts of food grade chlorination
Sodium, 10 parts of food grade calcium carbonate and 100 parts of water, wherein 2 parts of sodium copper chlorophyllin, 2 parts of low-ester pectins and 2 parts of food grade
Sodium chloride and 50 parts of water form mill base group, 10 parts of edible gelatins and 10 parts of food grade calcium carbonate and 50 parts of water composition film forming promote
Group is sufficiently mixed for two groups when use.
It is first to use 2 parts of low-ester pectins the present embodiment provides a kind of production method of children's wooden toy green coating
Edible ethanol is wet, and the dosage of edible ethanol is all wet with reaching low-ester pectin as standard, then under high velocity agitation will be wet
Low-ester pectin after profit is dissolved in 50 parts of water, and 2 parts of edible grade sodium chloride and 2 parts of chlorophyll copper sodium are added after being uniformly dissolved
Salt continues to stir all to be sufficiently solubilized to edible grade sodium chloride and sodium copper chlorophyllin that mill base group is made；Separately 10 parts are eaten bright
Gelatin solution is made in glue heating for dissolving in 50 parts of water, and heating and temperature control is at 60 DEG C hereinafter, 10 parts are added in gelatin solution
Food grade calcium carbonate is simultaneously sufficiently stirred, and adjusts pH value to 9.0 composition film forming promotion groups with calcium hydroxide saturated aqueous solution.
When needing coating, mill base group and film forming promotion group are mixed and are stirred well to uniformly.
A kind of children's wooden toy green coating that the present embodiment obtains, by naturally dry after being painted on wooden toy
Opaque beautiful green is presented after film forming in dry film forming.
Embodiment 3:
A kind of children's wooden toy green coating that this implementation column provides is implemented at every 100 parts on the basis of embodiment 1
2 parts of cornstarch is added in component described in example 1.It is the jade that 2 parts are added in every 100 parts of above-mentioned components when cornstarch is added
Cornstarch is first completely dissolved in 50 parts of water by rice starch under high velocity agitation, is added low after wet with edible ethanol
0.5 part of edible grade sodium chloride and 1 part of leaf is added in ester pectin in stirring again after cornstarch and low-ester pectin are completely dissolved
Mill base group is made in green element copper sodium, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, guarantees to apply
The product quality of material.
Embodiment 4:
A kind of children's wooden toy green coating that this implementation column provides is implemented on the basis of embodiment 2 at every 100 parts
0.5 part of cornstarch is added in component described in example 2.It is that 0.5 part is added in every 100 parts of above-mentioned components when cornstarch is added
Cornstarch, first cornstarch is completely dissolved under high velocity agitation in 50 parts of water, add with edible ethanol it is wet after
Low-ester pectin, be added in stirring again after cornstarch and low-ester pectin are completely dissolved 2 parts edible grade sodium chloride and 2 parts
Sodium copper chlorophyllin mill base group is made, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, protect
Demonstrate,prove the product quality of coating.
Claims (4)
1. a kind of children's wooden toy green coating, including use sodium copper chlorophyllin, it is characterised in that the group of the coating
At weight proportion are as follows: 1 part to 2 parts of sodium copper chlorophyllin, 5 parts to 10 parts edible gelatins, 2 parts to 5 parts of low-ester pectins, 0.5
The edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water of part to 2 parts, wherein 1 part to 2 parts of copper chlorophyll
Sodium salt, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water form mill base group, and 5 parts to 10 parts edible
Gelatin and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, are sufficiently mixed for two groups when use.
2. a kind of children's wooden toy green coating according to claim 1, it is characterized in that in every 100 parts of above-mentioned components
In be additionally provided with cornstarch no more than 2 parts.
3. a kind of a kind of production method of children's wooden toy green coating according to claim 1, it is characterized in that first
2 parts to 5 parts of low-ester pectin is moistened with edible ethanol, the dosage of edible ethanol is all wet with reaching low-ester pectin as mark
Standard, the low-ester pectin after then moistening under high velocity agitation are dissolved in 50 parts of water, and 0.5 part to 2 parts is added after being uniformly dissolved
Edible grade sodium chloride and 1 part to 2 parts of sodium copper chlorophyllin, continue stirring to edible grade sodium chloride and sodium copper chlorophyllin all
It is sufficiently solubilized and mill base group is made；Separately 5 parts to 10 parts edible gelatins are dissolved by heating, gelatin solution is made in 50 parts of water, heated
Temperature control 1 part to 10 parts food grade calcium carbonate and is sufficiently stirred at 60 DEG C hereinafter, being added in gelatin solution again, is used in combination
Calcium hydroxide saturated aqueous solution adjusts pH value to 8.0 to 9.0 composition film forming promotion groups；When needing coating, mill base group and film forming are promoted
Into group mixing and it is stirred well to uniformly.
4. the production method of a kind of children's wooden toy green coating according to claim 3, it is characterized in that every 100
It is additionally provided with the cornstarch no more than 2 parts in the above-mentioned component of part, cornstarch is first completely dissolved in 50 parts under high velocity agitation
In water, the low-ester pectin with edible ethanol after wet is added, is being stirred again after cornstarch and low-ester pectin are completely dissolved
Mill base group is made in 0.5 part to 2 parts of edible grade sodium chloride of middle addition and 1 part to 2 parts of sodium copper chlorophyllin.