CN109735231A - A kind of children's wooden toy encrimson and production method - Google Patents
A kind of children's wooden toy encrimson and production method Download PDFInfo
- Publication number
- CN109735231A CN109735231A CN201811453400.2A CN201811453400A CN109735231A CN 109735231 A CN109735231 A CN 109735231A CN 201811453400 A CN201811453400 A CN 201811453400A CN 109735231 A CN109735231 A CN 109735231A
- Authority
- CN
- China
- Prior art keywords
- parts
- edible
- children
- low
- wooden toy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of children's wooden toy encrimson and production methods, including using shellac red acid, it is the composition weight proportion of the coating are as follows: 1 part to 2 parts of shellac red acid, 5 parts to 10 parts edible gelatins, 2 parts to 5 parts of low-ester pectin, 0.5 part to 2 parts of edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water, wherein 1 part to 2 parts of shellac red acid, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water form mill base group, 5 parts to 10 parts edible gelatins and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, it is sufficiently mixed for two groups when use.A kind of children's wooden toy encrimson that the production method of this use invention obtains, with high safety, after being coated on children's wooden toy, the toy even if children bite when playing, health hazard will not be brought to the person of biting, ensured the healthy growth of children, and both ensure that after being painted on wooden toy color it is bright-coloured and also keep wooden toy much cleaner and safe.
Description
Technical field
The present invention relates to a kind of production technology of coating, especially a kind of children's wooden toy encrimson and producer
Method.
Background technique
In existing toy coating, it is especially used for the toy for children coating of woodwork, used coating to be substantially third
Olefin(e) acid class coating, as disclosed in 200910193125.X " acrylic emulsion of water-borne toy coating ", disclosed in 200910038289.5
" a kind of low volatility, quick-drying aqueous toy coating and its manufacturing method ", although acrylic coating is compared to poly- ammonia
Esters coating toxicity is low, but as being used for toy for children, children when playing often biting in toy posting port, institute
With for children and unsafe, as the coating of articles for children, it is not only that it should be without harmful volatility object
Matter, also answering entrance is also to have safety.
For the wooden toy of children, the purpose of coating is to give various colors abundant, rather than extends wooden toy
The problem of holding time, thus how to obtain it is a kind of can be given on woodwork color abundant without to child skin,
It is the toy for children paint development matter of utmost importance to be considered that entrance, which all brings the coating of harm, at present almost without such a true
Really it is suitable for the safety dope of children's wooden toy.
Summary of the invention
One kind is provided and is had a safety feature the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art, and can be obtained
Bright colors and being suitble to are attached to a kind of children's wooden toy encrimson and production method of woodwork.
To achieve the goals above, a kind of children's wooden toy encrimson designed by the present invention, including use worm
Glue red acid is the composition weight proportion of the coating are as follows: 1 part to 2 parts of shellac red acid, 5 parts to 10 parts edible gelatins, 2 parts
To 5 parts of low-ester pectins, 0.5 part to 2 parts of edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water,
In 1 part to 2 parts of shellac red acid, 2 parts to 5 parts of low-ester pectin and 0.5 part to 2 parts edible grade sodium chloride and water form mill base
Group, 5 parts to 10 parts edible gelatins and 1 part to 10 parts food grade calcium carbonate and water composition film forming promotion group, when use two groups it is abundant
Mixing.
In order to further be incorporated in pigment on wood fibre, and in the presence of calcium ion there is preferably solidification to make
With, the wear-resisting property and color saturation of coating are improved, keeps color more bright-coloured beautiful, a kind of children's wooden toy red
Coating is the cornstarch being additionally provided in every 100 parts of above-mentioned components no more than 2 parts.
The present invention provides a kind of production method of children's wooden toy encrimson, is first by 2 parts to 5 parts of low ester fruit
Glue is wet with edible ethanol, for standard, then under high velocity agitation the dosage of edible ethanol is all wet with reaching low-ester pectin
Will it is wet after low-ester pectin be dissolved in 50 parts of water, be added after being uniformly dissolved 0.5 part to 2 parts edible grade sodium chloride and 1 part
To 2 parts of shellac red acid, continue to stir all to be sufficiently solubilized to edible grade sodium chloride and shellac red acid that mill base group is made;Separately by 5
Part dissolves by heating to 10 parts of edible gelatins and gelatin solution is made in 50 parts of water, and heating and temperature control is at 60 DEG C hereinafter, again bright
1 part to 10 parts food grade calcium carbonate is added in sol solution and carries out that composition film forming promotion group is sufficiently stirred;When needing coating, by mill base
Group and film forming promotion group are mixed and are stirred well to uniformly, and adjust pH value to 7.0 with calcium hydroxide saturated aqueous solution.
Here, shellac red acid has the tone of natural red plant, and it is very stable in the environment for having light and heat, it shows just
Normal red;Pectin plays the dispersion and stabilization of the emulsification after pigment dissolves in gelatin, pigment herein, and sodium chloride is further
Stablize pigment to play the role of protecting color, shellac red acid is with good stability in the environment existing for pectin, keeps bright in color
Distinctness is without fugitive color;The addition of food grade calcium carbonate can control covering needed for wood materials according to the adjusting of additional amount
Degree, and calcium ion also promotes the film forming of low-ester pectin, and pectin film can play antibacterial and bacteriostasis, form antibacterial in wood surface
Layer, makes the much cleaner safety of wooden toy;Using calcium hydroxide aqueous solution adjusting coating pH value, it both ensure that shellac red acid to red
Guarantor's colour circle border, while it have certain sterilization, insecticidal action, can kill some fungies colonized on wood materials,
Bacterium and pest.
When needing that cornstarch is added, it is the cornstarch being added in every 100 parts of above-mentioned components no more than 2 parts, first will
Cornstarch is completely dissolved under high velocity agitation in 50 parts of water, is added the low-ester pectin with edible ethanol after wet, is worked as jade
Rice starch and low-ester pectin be added in stirring again after being completely dissolved 0.5 part to 2 parts edible grade sodium chloride and 1 part to 2 parts
Mill base group is made in shellac red acid, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, guarantees coating
Product quality.
A kind of children's wooden toy encrimson that the production method of this use invention obtains, it is all former using food-grade
Material has high safety, and after being coated on children's wooden toy, the toy even if children bite when playing will not be gnawed
The person of stinging brings health hazard, has ensured the healthy growth of children, here, low-ester pectin, cornstarch and edible gelatin are in this hair
In the composition of bright offer all have film forming, and have respective effect, both ensure that after being painted on wooden toy color
It is bright-coloured, also make wooden toy much cleaner and safe.
Specific embodiment
Below with reference to embodiment, the present invention is further described.
Embodiment 1:
A kind of children's wooden toy encrimson that this implementation column provides, including shellac red acid is used, it is the coating
Form weight proportion are as follows: 1 part of shellac red acid, 5 parts of edible gelatins, 5 parts of low-ester pectin, 0.5 part of edible grade sodium chloride, 1 portion of food
With grade calcium carbonate and 100 parts of water, wherein 1 part of shellac red acid, 5 parts of low-ester pectin and 0.5 part of edible grade sodium chloride and 50 parts
Water forms mill base group, 5 parts of edible gelatins and 1 part of food grade calcium carbonate and 50 parts of water composition film forming promotion groups, fills for two groups when use
Divide mixing.
It is first by 5 parts of low-ester pectin the present embodiment provides a kind of production method of children's wooden toy encrimson
Wet with edible ethanol, the dosage of edible ethanol is all wet with reaching low-ester pectin as standard, then under high velocity agitation will
Low-ester pectin after wet is dissolved in 50 parts of water, and 0.5 part of edible grade sodium chloride and 1 part of shellac red acid are added after being uniformly dissolved,
Continue to stir all to be sufficiently solubilized to edible grade sodium chloride and shellac red acid that mill base group is made;It is separately that 5 parts of edible gelatin heating are molten
Gelatin solution is made in solution in 50 parts of water, and heating and temperature control is at 60 DEG C hereinafter, 1 part of food grade carbon is added in gelatin solution again
Sour calcium simultaneously carries out that composition film forming promotion group is sufficiently stirred;When needing coating, mill base group and film forming promotion group are mixed and be sufficiently stirred
PH value is adjusted to 7.0 to uniform, and with calcium hydroxide saturated aqueous solution.
A kind of children's wooden toy encrimson that the present embodiment obtains, by naturally dry after being painted on wooden toy
Translucent beautiful red is presented after film forming in dry film forming.
Embodiment 2:
A kind of children's wooden toy encrimson that this implementation column provides, including shellac red acid is used, it is the coating
Form weight proportion are as follows: 2 parts of shellac red acid, 10 parts of edible gelatins, 2 parts of low-ester pectins, 2 parts of edible grade sodium chloride, 10 parts
Food grade calcium carbonate and 100 parts of water, wherein 2 parts of shellac red acid, 2 parts of low-ester pectins and 2 parts of edible grade sodium chloride and 50
Part water forms mill base group, 10 parts of edible gelatins and 10 parts of food grade calcium carbonate and 50 parts of water composition film forming promotion groups, two when use
Group is sufficiently mixed.
It is first to use 2 parts of low-ester pectins the present embodiment provides a kind of production method of children's wooden toy encrimson
Edible ethanol is wet, and the dosage of edible ethanol is all wet with reaching low-ester pectin as standard, then under high velocity agitation will be wet
Low-ester pectin after profit is dissolved in 50 parts of water, and 2 parts of edible grade sodium chloride and 2 parts of shellac red acid are added after being uniformly dissolved,
Continue to stir all to be sufficiently solubilized to edible grade sodium chloride and shellac red acid that mill base group is made;It is separately that 10 parts of edible gelatin heating are molten
Gelatin solution is made in solution in 50 parts of water, and heating and temperature control is at 60 DEG C hereinafter, 10 parts of food grade carbon are added in gelatin solution
Sour calcium simultaneously carries out that composition film forming promotion group is sufficiently stirred.When needing coating, mill base group and film forming promotion group are mixed and be sufficiently stirred
To uniformly and with calcium hydroxide saturated aqueous solution adjustment pH value to 7.0.
A kind of children's wooden toy encrimson that the present embodiment obtains, by naturally dry after being painted on wooden toy
Opaque beautiful red is presented after film forming in dry film forming.
Embodiment 3:
A kind of children's wooden toy encrimson that this implementation column provides is implemented at every 100 parts on the basis of embodiment 1
2 parts of cornstarch is added in component described in example 1.It is the jade that 2 parts are added in every 100 parts of above-mentioned components when cornstarch is added
Cornstarch is first completely dissolved in 50 parts of water by rice starch under high velocity agitation, is added low after wet with edible ethanol
0.5 part of edible grade sodium chloride and 1 portion of worm is added in ester pectin in stirring again after cornstarch and low-ester pectin are completely dissolved
Mill base group is made in glue red acid, this successive addition sequence, to facilitate the dispersion and dissolution of low-ester pectin in water, guarantees coating
Product quality.
Embodiment 4:
A kind of children's wooden toy encrimson that this implementation column provides is implemented on the basis of embodiment 2 at every 100 parts
0.5 part of cornstarch is added in component described in example 2.It is that 0.5 part is added in every 100 parts of above-mentioned components when cornstarch is added
Cornstarch, first cornstarch is completely dissolved under high velocity agitation in 50 parts of water, add with edible ethanol it is wet after
Low-ester pectin, be added in stirring again after cornstarch and low-ester pectin are completely dissolved 2 parts edible grade sodium chloride and 2 parts
Shellac red acid mill base group is made, this successive addition sequence guarantees to apply to facilitate the dispersion and dissolution of low-ester pectin in water
The product quality of material.
Claims (4)
1. a kind of children's wooden toy encrimson, including use shellac red acid, it is characterised in that the composition weight of the coating
Amount proportion are as follows: 1 part to 2 parts of shellac red acid, 5 parts to 10 parts edible gelatins, 2 parts to 5 parts of low-ester pectin, 0.5 part to 2 parts
Edible grade sodium chloride, 1 part to 10 parts food grade calcium carbonate and 100 parts of water, wherein 1 part to 2 parts of shellac red acid, 2 parts to 5 parts
Low-ester pectin and 0.5 part to 2 parts of edible grade sodium chloride and water form mill base group, 5 parts to 10 parts edible gelatins and 1 part to 10
Part food grade calcium carbonate and water composition film forming promotion group are sufficiently mixed for two groups when use.
2. a kind of children's wooden toy encrimson according to claim 1, it is characterized in that in every 100 parts of above-mentioned components
In be additionally provided with cornstarch no more than 2 parts.
3. a kind of a kind of production method of children's wooden toy encrimson according to claim 1, it is characterized in that first
2 parts to 5 parts of low-ester pectin is moistened with edible ethanol, the dosage of edible ethanol is all wet with reaching low-ester pectin as mark
Standard, the low-ester pectin after then moistening under high velocity agitation are dissolved in 50 parts of water, and 0.5 part to 2 parts is added after being uniformly dissolved
Edible grade sodium chloride and 1 part to 2 parts of shellac red acid, continue stirring to edible grade sodium chloride and shellac red acid all by sufficiently molten
Mill base group is made in solution;Separately 5 parts to 10 parts edible gelatins are dissolved by heating, gelatin solution, heating and temperature control is made in 50 parts of water
At 60 DEG C hereinafter, 1 part to 10 parts food grade calcium carbonate is added in gelatin solution again and carries out that composition film forming promotion is sufficiently stirred
Group;When needing coating, mill base group and film forming promotion group mixs and be stirred well to it is uniform, and with calcium hydroxide saturated aqueous solution tune
Whole pH value is to 7.0.
4. the production method of a kind of children's wooden toy encrimson according to claim 3, it is characterized in that every 100
It is additionally provided with the cornstarch no more than 2 parts in the above-mentioned component of part, cornstarch is first completely dissolved in 50 parts under high velocity agitation
In water, the low-ester pectin with edible ethanol after wet is added, is being stirred again after cornstarch and low-ester pectin are completely dissolved
Mill base group is made in 0.5 part to 2 parts of edible grade sodium chloride of middle addition and 1 part to 2 parts of shellac red acid.