CN109648961A - A kind of grinding tempered glass functional carpet and preparation method thereof - Google Patents
A kind of grinding tempered glass functional carpet and preparation method thereof Download PDFInfo
- Publication number
- CN109648961A CN109648961A CN201910033388.8A CN201910033388A CN109648961A CN 109648961 A CN109648961 A CN 109648961A CN 201910033388 A CN201910033388 A CN 201910033388A CN 109648961 A CN109648961 A CN 109648961A
- Authority
- CN
- China
- Prior art keywords
- grinding
- preparation
- tempered glass
- carpet
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of grinding tempered glass functional carpets and preparation method thereof, include the following steps: S1: villus is woven on base fabric and base blanket is made by the preparation of base blanket；S2: the carpet surface of base blanket uses antistatic agent coating processing；S3: base blanket back face coats latex and grid yarn network cloth is pasted；S4: by the base blanket and grid yarn network cloth drying machine drying finished product after coating latex；A kind of functional carpet of grinding tempered glass, which is made, using above-mentioned preparation method has mechanical property good, and villus withdrawal force is high, and backing peel strength is high, and during grinding tempered glass, milling time is long, is not easy hair loss, backing advantage not easily to fall off.
Description
Technical field
The present invention relates to high-performance fiber preparation technical fields, and in particular to a kind of functional carpet of grinding tempered glass
And preparation method thereof.
Background technique
Carpet is using natural fiber or chemical synthetic fiber class as raw material, and the one kind to process from strand is plated in object；Electronics produces
Product display is a kind of pair of very high tempered glass of flatness requirement with tempered glass, and grinding is the water using load grounds travel
It is carried out in solution, it is high to the carrier media of carrying grinding amidin, and carpet is as a kind of object with water suction, water-holding capacity
Matter can be used as the carrier of carrying grinding amidin, grind on the abrasive disk of glass grinder to tempered glass.
But the carpet pile withdrawal force routinely produced is low, and the peel strength of backing is low, can not reach the requirement of grinding tempered glass, because
This needs to develop a kind of functional carpet that can grind tempered glass.
Summary of the invention
It is of the invention the purpose of the present invention is to provide a kind of grinding tempered glass functional carpet and preparation method thereof
Carpet mechanical property is good, and villus withdrawal force is high, and backing peel strength is high, is not easy hair loss, backing during grinding tempered glass
It is not easily to fall off.
In order to solve the above technical problems, the invention adopts the following technical scheme:
A kind of grinding tempered glass preparation method of functional carpet, includes the following steps:
S1: villus is woven on base fabric and base blanket is made by the preparation of base blanket；
S2: the carpet surface of base blanket uses antistatic agent coating processing；
S3: base blanket back face coats latex and grid yarn network cloth is pasted；
S4: by the base blanket and grid yarn network cloth drying machine drying finished product after coating latex.
Preferably, base fabric is polypropylene base fabric in S1 step, and the grammes per square metre of the polypropylene base fabric is 105g/m2, using gram
The biggish 105g/m of weight2Polypropylene base fabric, threads per unit length of backing is big, makes villus and base fabric stable connection, improves tuft withdrawal force.
Preferably, villus is twisted by polypropylene silk thread in S1 step and simultaneously tufting is made, and the height of naps is 14mm-
23mm。
Preferably, antistatic agent and water is taken to dilute in S2 step by weight 1:20, the antistatic agent solution after dilution adds
The lauryl sodium sulfate that add weight part is 0.2% is evenly applied to the carpet surface of base blanket after foamed machine foaming processing.
Preferably, latex is mixed simultaneously with heavy calcium carbonate by weight 1:1.5 by low temperature water proof type latex in S3 step
The bleeding agent that parts by weight are 0.2% is added to be made.
Preferably, the fineness of heavy calcium carbonate is 600 mesh, is easy to be precipitated when grinding when heavy calcium carbonate is too thin, too
Fineness can be used for the heavy calcium carbonate of 600 mesh to glass is scratched when thick, grind calcium powder in glass process and be not easy to be precipitated, keep away
Exempt from the yields that glass is improved to glass scratch.
Preferably, bleeding agent is fatty alcohol polyoxyethylene ether.
Preferably, the resin added of latex is 600-800g/m in S3 step2。
Preferably, it is 155 DEG C that drying temperature is controlled in S4 step, and drying time 8-10min makes the cross-linking reaction of latex
It is sufficiently complete, it is tightly combined base blanket with grid yarn network cloth, improves the backing peel strength and tuft withdrawal force of carpet.
The functional carpet of a kind of grinding tempered glass, according to a kind of grinding tempering glass of above-mentioned preparation method preparation arrived
The functional carpet of glass.
Compared with prior art, the beneficial effects of the present invention are:
1, carpet mechanical property of the invention is good, and villus withdrawal force is high, and backing peel strength is high, in grinding tempered glass process
In, milling time is long, is not easy hair loss, and backing is not easily to fall off.
2, carpet backing waterproof of the invention, intensity is high, will not be taken off in grinding glass process using carpet of the invention
Hard particulate matter is fallen, glass will not be scratched, the yields of glass is high.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1
A kind of grinding tempered glass preparation method of functional carpet, includes the following steps:
S1: polypropylene silk thread is twisted and simultaneously the obtained height of tufting is 14mm villus, uses grammes per square metre for 105g/m by the preparation of base blanket2's
Polypropylene is base fabric, villus is woven on base fabric, base blanket is made；
S2: the carpet surface of base blanket uses antistatic agent coating processing, and taking antistatic agent, (antistatic agent selects grace Guo Tuona company
TANASTAT PH) and water diluted by weight 1:20, the dodecane that antistatic agent solution after dilution addition parts by weight are 0.2%
Base sodium sulphate is evenly applied to the carpet surface of base blanket after foamed machine foaming processing.
S3: low temperature water proof type latex is taken to mix and add by weight 1:1.5 with the heavy calcium carbonate that fineness is 600 mesh
Coating latex is made in the fatty alcohol polyoxyethylene ether that parts by weight are 0.2%, and latex obtained is pressed 600 g/m2Resin added apply
It is overlying on base blanket back face and is pasted on grid yarn network cloth.
S4: the grid yarn network cloth that will be pasted with base blanket is sent into drying machine drying, and control drying temperature is 155 DEG C, when drying
Between be 8min.Finished product is cut after drying.
It is a kind of to use a kind of functional carpet of grinding tempered glass, performance made from the above method as follows: backing stripping
From intensity 75N, tuft withdrawal force 28N, grinding glass (such as: mobile phone terminal surface glass) using the time is 10 days, and glass yields is
92%。
Embodiment 2
A kind of grinding tempered glass preparation method of functional carpet, includes the following steps:
S1: polypropylene silk thread is twisted and simultaneously the obtained height of tufting is 16mm villus, uses grammes per square metre for 105g/m by the preparation of base blanket2's
Polypropylene is base fabric, villus is woven on base fabric, base blanket is made；
S2: the carpet surface of base blanket uses antistatic agent coating processing, and taking antistatic agent, (antistatic agent selects grace Guo Tuona company
TANASTAT PH) and water diluted by weight 1:20, the dodecane that antistatic agent solution after dilution addition parts by weight are 0.2%
Base sodium sulphate is evenly applied to the carpet surface of base blanket after foamed machine foaming processing.
S3: low temperature water proof type latex is taken to mix and add by weight 1:1.5 with the heavy calcium carbonate that fineness is 600 mesh
Coating latex is made in the fatty alcohol polyoxyethylene ether that parts by weight are 0.2%, and latex obtained is pressed 700 g/m2Resin added apply
It is overlying on base blanket back face and is pasted on grid yarn network cloth.
S4: the grid yarn network cloth that will be pasted with base blanket is sent into drying machine drying, and control drying temperature is 155 DEG C, when drying
Between be 9min.Finished product is cut after drying.
It is a kind of to use a kind of functional carpet of grinding tempered glass, performance made from the above method as follows: backing stripping
From intensity 80N, tuft withdrawal force 30N, grind glass (such as: mobile phone terminal surface glass) is 13 days using the time, glass yields
91.5%。
Embodiment 3
A kind of grinding tempered glass preparation method of functional carpet, includes the following steps:
S1: polypropylene silk thread is twisted and simultaneously the obtained height of tufting is 23mm villus, uses grammes per square metre for 105g/m by the preparation of base blanket2's
Polypropylene is base fabric, villus is woven on base fabric, base blanket is made；
S2: the carpet surface of base blanket uses antistatic agent coating processing, and taking antistatic agent, (antistatic agent selects grace Guo Tuona company
TANASTAT PH) and water diluted by weight 1:20, the dodecane that antistatic agent solution after dilution addition parts by weight are 0.2%
Base sodium sulphate is evenly applied to the carpet surface of base blanket after foamed machine foaming processing.
S3: low temperature water proof type latex is taken to mix and add by weight 1:1.5 with the heavy calcium carbonate that fineness is 600 mesh
Coating latex is made in the fatty alcohol polyoxyethylene ether that parts by weight are 0.2%, and latex obtained is pressed 800 g/m2Resin added apply
It is overlying on base blanket back face and is pasted on grid yarn network cloth.
S4: the grid yarn network cloth that will be pasted with base blanket is sent into drying machine drying, and control drying temperature is 155 DEG C, when drying
Between be 10min.Finished product is cut after drying.
It is a kind of to use a kind of functional carpet of grinding tempered glass, performance made from the above method as follows: backing stripping
From intensity 85N, tuft withdrawal force 32N, grinding glass (such as: mobile phone terminal surface glass) using the time is 17 days, glass yields
91.8%。
Although reference be made herein to invention has been described for multiple explanatory embodiments of the invention, however, it is to be understood that
Those skilled in the art can be designed that a lot of other modification and implementations, these modifications and implementations will fall in this Shen
It please be within disclosed scope and spirit.It more specifically, within the scope of the present disclosure and claims, can be to master
The building block and/or layout for inscribing composite configuration carry out a variety of variations and modifications.In addition to what is carried out to building block and/or layout
Outside modification and improvement, to those skilled in the art, other purposes also be will be apparent.
Claims (10)
1. a kind of grinding tempered glass preparation method of functional carpet, characterized by the following steps: S1: base blanket
Villus is woven on base fabric using tufting machine and base blanket is made by preparation；S2: the carpet surface of base blanket uses antistatic agent coating processing；
S3: base blanket back face coats latex and grid yarn network cloth is pasted；S4: base blanket and grid yarn network cloth drying machine after coating latex
Dry finished product.
2. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 1, it is characterised in that: institute
Stating base fabric in S1 step is polypropylene base fabric, and the grammes per square metre of the polypropylene base fabric is 105g/m2。
3. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 1, it is characterised in that: institute
State in S1 step villus twisted by polypropylene silk thread and and tufting be made, the height of naps is 14mm-23mm.
4. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 1, it is characterised in that: institute
It states and antistatic agent and water is taken to dilute in S2 step by weight 1:20, the antistatic agent solution addition parts by weight after dilution are 0.2%
Lauryl sodium sulfate, the carpet surface of base blanket is evenly applied to after foamed machine foaming processing.
5. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 1, it is characterised in that: institute
It states latex in S3 step and is mixed with heavy calcium carbonate by weight 1:1.5 by low temperature water proof type latex and add parts by weight and be
0.2% bleeding agent is made.
6. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 5, it is characterised in that: institute
The fineness for stating heavy calcium carbonate is 600 mesh.
7. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 5, it is characterised in that: institute
Stating bleeding agent is fatty alcohol polyoxyethylene ether.
8. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 1, it is characterised in that: institute
The resin added for stating latex in S3 step is 600-800g/m2。
9. a kind of preparation method of the functional carpet of grinding tempered glass according to claim 1, it is characterised in that: institute
Stating and controlling drying temperature in S4 step is 155 DEG C, drying time 8-10min.
10. a kind of grinding tempered glass that any one preparation method is prepared according to claim 1~9 is with functionally
Blanket.