CN109648258A - A kind of stainless steel vacuum cup surface lacquer technique - Google Patents
A kind of stainless steel vacuum cup surface lacquer technique Download PDFInfo
- Publication number
- CN109648258A CN109648258A CN201811478628.7A CN201811478628A CN109648258A CN 109648258 A CN109648258 A CN 109648258A CN 201811478628 A CN201811478628 A CN 201811478628A CN 109648258 A CN109648258 A CN 109648258A
- Authority
- CN
- China
- Prior art keywords
- vacuum cup
- stainless steel
- priming paint
- polishing
- steel vacuum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to stainless steel products manufacture fields, specifically disclose a kind of stainless steel vacuum cup surface lacquer technique.Comprise the steps of: that 1, vacuum cup carries out the polishing of surface of revolution polishing machine；2, one layer of priming paint is first sprayed after polishing, after drying, then sprays the priming paint of one layer of addition curing agent；3, grain pattern is applied to using non-woven fabrics the product surface for having sprayed priming paint, then goes out lines with tap water；4, surface water drops are dried up with spray gun again；5, it is dried, topcoating after drying, finishing coat uses acrylic resin as base-material while joined bronzing varnish.The present invention provides a kind of easy to operate, and bond effect is good, and surface tinted multiplicity, the surface lacquer technique of the stainless steel vacuum cup of pattern beauty, the present invention goes out lines with tap water, then carries out spray paint, so that pattern flows naturally.
Description
Technical field
The present invention relates to stainless steel products manufacture fields, are specifically related to a kind of stainless steel vacuum cup surface lacquer technique.
Background technique
Stainless steel (Stainless Steel) is the abbreviation of stainless acid resistant steel, the weak corrosive medium such as resistance to air, steam, water
Or the steel grade with rustless property is known as stainless steel.Stainless steel refers to that the weak corrosive medium such as resistance to air, steam, water and acid, alkali, salt etc. are changed
Learn the steel of erosion dielectric corrosion, also known as stainless acid resistant steel.In practical application, often the steel by resistance to weak corrosive medium corrosion is known as not
Become rusty steel, and the steel that resistant to chemical media corrodes is known as acid resisting steel.Due to difference of the two in chemical component, the former is not necessarily resistance to
Chemical mediator corrosion, and the latter then generally has rustless property.The corrosion resistance of stainless steel depends on alloying element contained in steel.
For existing stainless steel since nickel price is unprecedented soaring, stainless steel price also has very big amount of increase in recent years.Using stainless
Steel is raw material, causes the raw material cost of material to produce household appliances to steeply rise, is difficult to correspondingly increase so as to cause finished product price,
And existing stainless steel surface processing technique can only accomplish the stainless steel true qualities or polished, coating of wire drawing, frosted finish effect
The pitch-dark expensive black titanium obtained, surface effect seem single, and the optional tone of client is restricted.Conventionally employed stainless steel
After heat preservation cup formation of the material for raw material production, carries out polishing technology and handle to smooth, bright product.This kind of finished product is stainless steel
Primary colors, vision is as bright as a sixpence, but the continuous improvement with people to vacuum cup appearance requirement, and the change of aesthetic conceptions is this stainless
Steel primary colors has been not suitable with the needs of situation.And then one layer of coating of spraying on common vacuum cup is derived, both beauty met
The characteristic of different crowd, and cup can be made to become bright soft.
Summary of the invention
The technical problem to be solved in the present invention is that the relatively simple defect of stainless steel surface for the prior art provides one
The surface lacquer technique of kind stainless steel vacuum cup.
The technical solution adopted by the present invention are as follows: provide a kind of easy to operate, bond effect is good, surface tinted multiplicity, pattern
The surface lacquer technique of beautiful stainless steel vacuum cup, specifically comprises the following steps:
1, first vacuum cup is polished, polishing selection revolving speed 35 000-40000rpm surface of revolution polishing machine into
Row polishing；
2, one layer of priming paint is first sprayed after polishing, after drying, then sprays the priming paint of one layer of addition curing agent；
3, designed desired grain pattern is uniformly applied to using non-woven fabrics the product surface for having sprayed priming paint, then
Lines is gone out with tap water；
It 4, with spray gun pressure is again 0.4-0.8MPa, the direction along vacuum cup bottle bottom dries up surface water drops；
5, it is dried, is carrying out topcoating after drying, finishing coat uses acrylic resin as base-material while joined bronze
Paint.
Preferably, it first can be used to remove polishing scratch with abrasive pastes and buff in step 1, then with viscous felt and diamond abrasive
Cream is polished.
Preferably, in step 2 ratio of priming paint and curing agent be 50:1-3, priming paint use acrylic resin and epoxy resin for
Base-material.
Preferably, non-woven fabrics is 2 layers in step 3, and smearing direction is tap water hydraulic 0.15-0.3MPa punching from top to bottom
Lines out.
Preferably, in step 5 topcoat with a thickness of 1.5-3mm.
The invention has the benefit that
The present invention provides a kind of easy to operate, and bond effect is good, surface tinted multiplicity, the stainless steel vacuum cup of pattern beauty
Surface lacquer technique, the prior art can only generally paint ejection pure color, cannot make pattern, the present invention is using non-woven fabrics band
The pattern of lines is uniformly applied to the product surface for having sprayed priming paint, then goes out lines with tap water, then carry out spray paint, makes
Pattern is obtained to flow naturally.
Specific embodiment
Embodiment 1
1, first vacuum cup being polished, surface of revolution polishing machine of the polishing selection revolving speed in 35 000rpm is polished,
It first can be used to remove polishing scratch with abrasive pastes and buff, then be polished with viscous felt and diamond abrasive cream；
2, one layer of priming paint is first sprayed after polishing, after drying, then sprays the priming paint of one layer of addition curing agent, priming paint and curing agent
Ratio be 50:1, priming paint uses acrylic resin and epoxy resin for base-material；
3, using 1 layer of non-woven fabrics, designed desired grain pattern is uniformly applied to from top to bottom and has sprayed priming paint
Then product surface goes out lines with tap water hydraulic 0.15MPa；
It 4, with spray gun pressure is again 0.4MPa, the direction along vacuum cup bottle bottom dries up surface water drops；
5, it is dried, is carrying out topcoating after drying, finishing coat uses acrylic resin as base-material while joined bronze
Paint, top coat layer is with a thickness of 1.5mm.
Embodiment 2
1, first vacuum cup is polished, surface of revolution polishing machine of the polishing selection revolving speed in 40000rpm is polished；
2, one layer of priming paint is first sprayed after polishing, after drying, then sprays the priming paint of one layer of addition curing agent, priming paint and curing agent
Ratio be 50:3, priming paint uses acrylic resin and epoxy resin for base-material；
3, designed desired grain pattern is uniformly applied to from left to right using 4 layers of non-woven fabrics the production for having sprayed priming paint
Then lines is gone out with tap water 0.3MPa in product surface；
It 4, with spray gun pressure is again 0.8MPa, the direction along vacuum cup bottle bottom dries up surface water drops；
5, it is dried, is carrying out topcoating after drying, finishing coat uses acrylic resin as base-material while joined bronze
Paint, top coat layer is with a thickness of 3mm.
Embodiment 3
1, first vacuum cup is polished, surface of revolution polishing machine of the polishing selection revolving speed in 35 000rpm is polished；
2, one layer of priming paint is first sprayed after polishing, after drying, then sprays the priming paint of one layer of addition curing agent, priming paint and curing agent
Ratio be 25:1, priming paint uses acrylic resin and epoxy resin for base-material；
3, designed desired grain pattern is uniformly applied to from top to bottom using 2 layers of non-woven fabrics the production for having sprayed priming paint
Then lines is gone out with tap water 0.22MPa in product surface；
It 4, with spray gun pressure is again 0.6MPa, the direction along vacuum cup bottle bottom dries up surface water drops；
5, it is dried, is carrying out topcoating after drying, finishing coat uses acrylic resin as base-material while joined bronze
Paint, topcoat is with a thickness of 2.5mm.
Embodiment described above only expresses several better embodiments of the invention, and the description thereof is more specific and detailed,
But it cannot be understood as limitations on the scope of the patent of the present invention.It should be pointed out that for the ordinary skill of this field
For personnel, without departing from the inventive concept of the premise, several modifications and improvements are made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (5)
1. a kind of stainless steel vacuum cup surface lacquer technique, which is characterized in that the method includes the steps of:
1, first vacuum cup is polished, surface of revolution polishing machine of the polishing selection revolving speed in 35 000-40000rpm is thrown
Light；
2, one layer of priming paint is first sprayed after polishing, after drying, then sprays the priming paint of one layer of addition curing agent；
3, designed desired grain pattern is uniformly applied to using non-woven fabrics the product surface for having sprayed priming paint, then with certainly
Water goes out lines；
It 4, with spray gun pressure is again 0.4-0.8MPa, the direction along vacuum cup bottle bottom dries up surface water drops；
5, it is dried, is carrying out topcoating after drying, finishing coat uses acrylic resin as base-material while joined bronzing varnish.
2. a kind of stainless steel vacuum cup surface lacquer technique according to claim 1, which is characterized in that in the step 1
It first can be used to remove polishing scratch with abrasive pastes and buff, then be polished with viscous felt and diamond abrasive cream.
3. a kind of stainless steel vacuum cup surface lacquer technique according to claim 1, which is characterized in that in the step 2
The ratio of priming paint and curing agent is 50:1-3, and priming paint uses acrylic resin and epoxy resin for base-material.
4. a kind of stainless steel vacuum cup surface lacquer technique according to claim 1, which is characterized in that in the step 3
Non-woven fabrics is 2 layers, and smearing direction is from top to bottom that tap water hydraulic 0.15-0.3MPa goes out lines.
5. a kind of stainless steel vacuum cup surface lacquer technique according to claim 1, which is characterized in that in the step 5
Topcoat is with a thickness of 1.5-3mm.