CN108583125A - A kind of tap coating decoration technology - Google Patents
A kind of tap coating decoration technology Download PDFInfo
- Publication number
- CN108583125A CN108583125A CN201810372605.1A CN201810372605A CN108583125A CN 108583125 A CN108583125 A CN 108583125A CN 201810372605 A CN201810372605 A CN 201810372605A CN 108583125 A CN108583125 A CN 108583125A
- Authority
- CN
- China
- Prior art keywords
- tap
- layer
- mesh
- water
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of tap coating decoration technology, includes the following steps：(1) surface of tap blank is subjected to coarse processing, and oil removing, cleaning；(2) one layer of priming paint, solidification are sprayed in surface treated tap blank surface；(3) the coating film texture water of pre-production is needed on tap primed surface and forms grain decorating layer；(4) the grain decorating layer spray paint obtained in step (3)；(5) finishing coat surface is after sand paper grinding process, then sprays one layer of hardness and the good Transparent Nano-Coatings of wear-resisting property, and finished product is after heat treatment made.The decoration texture-rich that the present invention obtains tap is various, and environmental protection；And by the good Transparent Nano-Coatings of one layer of hardness of spraying and wear-resisting property, effective protective layer is formed, improve the hardness and wearability of light water transfer finishing coat, and the color developing effect of decorative pattern is good.
Description
Technical field
The present invention relates to bathroom decoration technique field more particularly to a kind of tap coating decoration technologies.
Background technology
Current existing tap electroplating technology is mainly the process of first copper facing, again nickel plating, last chromium plating, wherein general nickel
1-12 μm of layer thickness, 0.3-0.5 μm of layers of chrome thickness, but due to generally requiring to carry out oil removing many times, acid in water power depositing process
The process washed, and need to carry out the continuous replacement of a variety of different electrolyte, could plating solution effectively be made by the effect of electrolysis
The cation of middle metal to be plated is deposited in base metal surface, forms the coating of stable structure, therefore there are water pollutions etc.
Environmental pollution is extremely serious, and the problem that environmental protection pressure is huge, and by the decoration technology of traditional water power plating or baking vanish etc.
The decorative effect of the tap of acquisition is single, lacks the decoration of pattern, and the Material for design of tap decoration and space are limited,
The decoration technology of tap is limited by larger.
Invention content
It is an object of the invention to propose a kind of tap coating decoration technology.
For this purpose, the present invention uses following technical scheme：
A kind of tap coating decoration technology, includes the following steps：
(1) surface of tap blank is subjected to coarse processing, and oil removing, cleaning；
(2) in one layer of priming paint of surface spraying of surface treated tap blank, solidification；
(3) the coating film texture water of pre-production is needed on tap primed surface and forms grain decorating layer；
(4) the grain decorating layer spray paint obtained in step (3)；
(5) finishing coat surface is after sand paper grinding process, then sprays layer of transparent nano coating, is after heat treatment made into
Product.
The present invention proposes a kind of tap coating decoration technology, wherein tap blank to be surface-treated and be sprayed
After priming paint, then by using the mode of water coating film the decoration of the pattern of tap blank surface is carried out, effectively obtained
It is more rich and varied to obtain decorative pattern, the finer and smoother grain decorating layer of pattern；Compared to existing plating, the decoration side of baking vanish
Formula, decorative effect of the invention more enrich it is full, and by water drape over one's shoulders film coated decorative in the way of it is more environmentally-friendly, without multiple
Replace electrolyte；And since the wearability that water coating film used forms grain decorating layer is relatively low, by the texture
The surface spraying finishing coat of decorative layer and grinding process and then further one layer of hardness of spraying and the good transparent nano of wear-resisting property
Coating, to form more effective protective layer after Overheating Treatment, surface pencil hardness can reach 3-4H, and hardness is above
The tap product of other spraying classes such as baking vanish, and while the hardness and wearability for substantially increasing surface, additionally it is possible to
Promote the hair color effect of figure colour, forms preferably refraction reflection light effect, keep the color of floral designs brighter.
It further illustrates, the coating film texture water is needed on tap primed surface and includes the following steps：
A, designed decoration connection with production of structures is transferred into coating film at water；
B, water transfer coating film is cut as required, is laid on the constant temperature water surface, water temperature control is in 25 ± 5 DEG C, pH value
It is neutral；
C, activator is sprayed；
D, by water transfer operation, coating film texture is transferred to tap primed surface, line is formed after washing, drying
Manage decorative layer；
C. use air pressure spray gun in the apertures 0.8-1.2mm in grain decorating layer surface spray paint.
According to the design of coating film texture, existing plating can be formed using aforesaid way, the decorating method of baking vanish can not
The various decorative patterns such as stone pattern, the wood grain produced, to enrich, can make and the matched the whole series in bathroom cabinet face with dicoration
Decorative product, the advantages of increasing Material for design and the space of designer, and energy conservation and environmental protection；And utilize finishing coat and water transfer printing film
Intrinsic bonding force makes finishing coat generate high adhesion force with water transfer printing film, to be formed by curing one layer of hard protection film layer, effectively
It prevents water coating film layer to be destroyed, improves the stability of decoration flower lamina.
The Transparent Nano-Coatings that the surface of the grain decorating layer formed simultaneously in water coating further coats, with finishing coat knot
Close and not only increase the hardness and wearability on surface, grain decorating layer is prevented to be destroyed, but also can be penetrated by finishing coat to
In grain decorating layer, promotes the color development of the figure colour of grain decorating layer, form refraction reflection light effect evenly, make
Decorative pattern is finer and smoother.
It is molten to avoid the too low substrate layer that can make water transfer printing film paper of water temperature by controlling water temperature in the range of 20-30 DEG C
Solution property declines；And water temperature over-high can then damage the picture and text layer of film paper, and decorative pattern is caused to deform；And after the completion of water transfers
It is washed, washes out remaining film, keep the spraying of finishing coat more uniform.
Further illustrate, the activator be by benezene material, lipid material, alcohols material and white spirit mixed configuration and
At.Wherein, the benezene material includes benzene, dimethylbenzene, and the lipid material includes n-butyl acetate, ethyl acetate, the alcohol
Substance includes isopropanol, ethyl alcohol, propyl alcohol, and the white spirit is petroleum ether or n-hexane, passes through the surface spraying work in film paper
Agent can dissolve rapidly and destroy the polyvinyl alcohol in water transfer printing film paper, but not destroy decorative pattern figure layer, make decorative pattern figure layer in water
In free state, to reach better transferring effect.
It further illustrates, the priming paint and finishing coat are oiliness or waterborne polyurethane resin, and fineness is -400 mesh of 200 mesh.
It is sprayed using the priming paint and finishing coat of certain fineness, to prevent from blocking spray gun, keeps spraying more uniform, adhesive force is good.Pass through
Certain thickness priming paint is sprayed to increase the adhesive force of water transfer printing film and tap blank, and increases tap blank surface and puts down
Whole degree covers tiny flaw, ensures product surface smooth；The finishing coat plays the role of being effectively protected to water transfer printing film.
It further illustrates, the time of the washing is 2-5min, and the temperature of drying is 80-100 DEG C, drying time 30-
60min。
It further illustrates, through sand paper grinding process, sand paper used is 600-1000 mesh on the finishing coat surface.Utilize physics
Polishing mode increases the surface roughness of the finishing coat, to improve the adhesive force between finishing coat and Transparent Nano-Coatings, improves
The phenomenon that stability of interlayer structure, anti-delamination.
It further illustrates, coarse processing described in step (1) is using -800 mesh of 220 mesh sand milling or/and 120 mesh -400
Mesh sandblasting is handled.The sand material is corundum sand material, high pressure draught can be made to carry brown corundum abrasive secretly to the fire hose by sandblasting
The surface of head blank carries out coarse processing, to improve the adhesive force between priming paint and tap blank；And before spray-applied primer
Drifting dust can be carried out, makes to avoid greasy dirt dust etc. from causing the influence of priming paint adhesive force except cleaning by oil removing dedusting.
It further illustrates, the Transparent Nano-Coatings material is silicon-aluminum sol class nano paint, and fineness is 200 mesh -400
Mesh is sprayed using the apertures 1.0-1.2mm air pressure spray gun, through 80 DEG C of heat treatment 30-60min.
It is sprayed under pressure using the silicon-aluminum sol class nano paint of the modification of certain fineness, prevents from blocking
Spray gun, spraying is more uniform, and after 80 DEG C are heat-treated 30-60min, makes silicon-aluminum sol class nano coating and grain decorating layer
Between adhesive force it is more preferable.
It further illustrates, the thickness of the priming paint is 20-35 μm.
Beneficial effects of the present invention：The pattern flower of tap blank surface is carried out by using the mode of water coating film
The decoration of line, acquisition decorative pattern is more rich and varied, the finer and smoother grain decorating layer of pattern, the decorative effect of tap
It is more abundant full, and by water drape over one's shoulders film coated decorative in the way of it is more environmentally-friendly；And also pass through the table in the grain decorating layer
Face spray paint and grinding process and then further one layer of hardness of spraying and the good Transparent Nano-Coatings of wear-resisting property, pass through
More effective protective layer is formed after heat treatment, surface pencil hardness can reach 3-4H, and hardness is above baking vanish etc., and other are sprayed
The tap product for applying class, while the hardness and wearability for substantially increasing surface, additionally it is possible to promote the hair of figure colour
Color effect forms preferably refraction reflection light effect, keeps the color of floral designs brighter.
Specific implementation mode
The technical solution further illustrated the present invention below by specific implementation mode.
A kind of tap coating decoration technology of dark fund patterns of embodiment 1-, includes the following steps：
(1) by tap blank in sand-blasting machine, 220 mesh sanded treatments is carried out to the surface of tap blank, wine is used in combination
Essence or Environment protection cleaning liquid or Environment protection cleaning liquid add ultrasonic cleaning oil removing, dry；
(2) in one layer of priming paint of surface spraying of surface treated tap blank, the priming paint is that water transfer is special
PU priming paint is used in combination 200 mesh filter screens to filter；Using the hand-held air pressure spray gun hand spray tap in the apertures 1.2mm, basecoat paint
Thickness is 20 μm, makes its solidification from dry；
(3)a:Configure that required activator is for use according to the ratio, by the Portoro being pre-designed decoration connection with production of structures Cheng Shuizhuan
Coating film is printed, and is cut as required, thermostatic water bath surface is laid in, water temperature is 20 DEG C, keeps PH values to be in neutrality, and spray work
Agent；
b:By the tap blank profile that need to be transferred gradually close to water transfer printing film, free pattern decoration layer can be in hydraulic pressure
It is slowly transferred to faucet surface under effect, needs the shape uniform rotation tap according to tap, junction is avoided to be overlapped
Excessive picture and text layer can cause decorative pattern overlapping chaotic；The tap blank after transfer is hung over into tunnel type water drenching again and rinses line, rinses 5
Minute, enter tunnel-type drying furnace later and carry out 80-100 DEG C of drying time 60min, forms grain decorating layer；
C. use air pressure spray gun in the apertures 1.2mm in the surface spraying finishing coat of tap blank, from dry or 80 DEG C of bakings
60min；The finishing coat is aqueous class finishing coat, and 200 mesh filter screens is used in combination to filter.
(4) after the finishing coat for using 600-1000 mesh sand paper polishing tap blank surface, using the apertures 1.2mm air pressure spray gun
One layer of silicon-aluminum sol class nano paint of spraying is carried out, the silicon-aluminum sol class nano paint is filtered with 200 mesh filter screens, by the fire hose
Head blank is sent into after oven toast the processing of dry 60min at 80 DEG C and obtains the tap for draping over one's shoulders film coated decorative with dark fund pattern water
1, its surface pencil hardness is 3H after tested；And the dress of its dark fund decorative pattern can not be then obtained by existing plating or baking varnish method
Adorn effect.
A kind of tap coating decoration technology of rose auroras of embodiment 2-, includes the following steps：
(1) by tap blank in sand-blasting machine, 400 mesh blasting treatments is carried out to the surface of tap blank, wine is used in combination
Essence or Environment protection cleaning liquid or Environment protection cleaning liquid add ultrasonic cleaning oil removing, dry；
(2) in one layer of priming paint of surface spraying of surface treated tap blank, the priming paint is that water transfer is special
PU priming paint is used in combination 400 mesh filter screens to filter；Using the hand-held air pressure spray gun hand spray tap in the apertures 1.0mm, basecoat paint
Thickness is 35 μm, makes its solidification from dry；
(3)a:Configure that required activator is for use according to the ratio, by the rose aurora being pre-designed decoration connection with production of structures Cheng Shuizhuan
Coating film is printed, and is cut as required, thermostatic water bath surface is laid in, water temperature is 30 DEG C, keeps PH values to be in neutrality, and spray work
Agent；
b:By the tap blank profile that need to be transferred gradually close to water transfer printing film, free pattern decoration layer can be in hydraulic pressure
It is slowly transferred to faucet surface under effect, needs the shape uniform rotation tap according to tap, junction is avoided to be overlapped
Excessive picture and text layer can cause decorative pattern overlapping chaotic；The tap blank after transfer is hung over into tunnel type water drenching again and rinses line, rinses 2
Minute, enter tunnel-type drying furnace later and carry out 80-100 DEG C of drying time 30min, forms grain decorating layer；
C. use air pressure spray gun in the apertures 0.8mm in the surface spraying finishing coat of tap blank, from dry or 80 DEG C of bakings
30min；The finishing coat is aqueous class finishing coat, and 400 mesh filter screens is used in combination to filter.
(4) after the finishing coat for using 600-1000 mesh sand paper polishing tap blank surface, using the apertures 1.0mm air pressure spray gun
One layer of silicon-aluminum sol class nano paint of spraying is carried out, the silicon-aluminum sol class nano paint is filtered with 400 mesh filter screens, by the fire hose
Head blank is sent into after oven toast the heat treatment of dry 30min at 80 DEG C and obtains the fire hose for draping over one's shoulders film coated decorative with rose aurora water
Head, its surface pencil hardness is 3.8H after tested；And the topaz parmelia saxatilis can not then be obtained by existing plating or baking varnish method
The decorative effect of line.
A kind of tap coating decoration technology of bluish white patterns of embodiment 3-, includes the following steps：
(1) by tap blank in sand-blasting machine, 120 mesh blasting treatments is carried out to the surface of tap blank, wine is used in combination
Essence or Environment protection cleaning liquid or Environment protection cleaning liquid add ultrasonic cleaning oil removing, dry；
(2) in one layer of priming paint of surface spraying of surface treated tap blank, the priming paint is that water transfer is special
PU priming paint is used in combination 300 mesh filter screens to filter；Tap, the thickness of basecoat paint are sprayed using the air pressure spray gun in the apertures 1.1mm automatically
It is 30 μm, makes its solidification from dry；
(3)a:The bluish white flower decoration connection with production of structures Cheng Shuizhuan that required activator is for use, will be pre-designed is configured according to the ratio
Coating film is printed, and is cut as required, thermostatic water bath surface is laid in, water temperature is 25 DEG C, keeps PH values to be in neutrality, and spray work
Agent；
b:By the tap blank profile that need to be transferred gradually close to water transfer printing film, free pattern decoration layer can be in hydraulic pressure
It is slowly transferred to faucet surface under effect, needs the shape uniform rotation tap according to tap, junction is avoided to be overlapped
Excessive picture and text layer can cause decorative pattern overlapping chaotic；The tap blank after transfer is hung over into tunnel type water drenching again and rinses line, rinses 3
Minute, enter tunnel-type drying furnace later and carry out 80-100 DEG C of drying time 45min, forms grain decorating layer；
C. use air pressure spray gun in the apertures 1.1mm in the surface spraying finishing coat of tap blank, from dry or 80 DEG C of bakings
45min；The finishing coat is aqueous class finishing coat, and 300 mesh filter screens is used in combination to filter.
(4) after the finishing coat for using 600-1000 mesh sand paper polishing tap blank surface, using the apertures 1.1mm air pressure spray gun
One layer of silicon-aluminum sol class nano paint of spraying is carried out, the silicon-aluminum sol class nano paint is filtered with 300 mesh filter screens, by the fire hose
Head blank is sent into after oven toast the processing of dry 45min at 80 DEG C and obtains the fire hose for draping over one's shoulders film coated decorative with bluish white pattern water
Head, its surface pencil hardness is 4H after tested；And the bluish white decorative pattern can not then be obtained by existing plating or baking varnish method
Decorative effect.
Comparative example 1- is taken based on the tap decoration technology that the dark fund pattern water of embodiment 1 drapes over one's shoulders film coated decorative
The finishing coat of tap blank surface of being polished using 600-1000 mesh sand paper in the step that disappears (4), directly carries out spraying silicon-aluminum sol
Class nano paint, remaining preparation process and experiment parameter condition are same as Example 1, and obtaining, there is dark fund pattern water to drape over one's shoulders
The tap 2 of film coated decorative, the pencil hardness on its surface is 2.1H after tested.
Comparative example 2- is taken based on the tap decoration technology that the dark fund pattern water of embodiment 1 drapes over one's shoulders film coated decorative
The finishing coat of tap blank surface of being polished using 600-1000 mesh sand paper in the step that disappears (4), and silicon-aluminum sol class is not sprayed
Nano paint, remaining preparation process and experiment parameter condition are same as Example 1, and obtaining, there is dark fund pattern water to drape over one's shoulders
The tap 3 of film coated decorative, the pencil hardness on its surface is 1.5H after tested, and its decorative pattern color is compared with Example 1, should
Color is more obscure.
It can thus be seen that more rich and varied, the line that can not only obtain pattern in the way of water coating decoration
The finer and smoother decorative effect of reason, and by the surface spraying silicon-aluminum sol class nano paint in the finishing coat after polishing,
More effective protective layer can be formed, surface pencil hardness can reach 3-4H, and in the hardness that improves surface and wear-resisting
While property, additionally it is possible to promote the hair color effect of figure colour, keep the color of floral designs brighter.
The technical principle of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's
Principle, and it cannot be construed to limiting the scope of the invention in any way.Based on the explanation herein, the technology of this field
Personnel would not require any inventive effort the other specific implementation modes that can associate the present invention, these modes are fallen within
Within protection scope of the present invention.
Claims (9)
1. a kind of tap coating decoration technology, it is characterised in that：Include the following steps：
(1) surface of tap blank is subjected to coarse processing, and oil removing, cleaning；
(2) in one layer of priming paint of surface spraying of surface treated tap blank, solidification；
(3) the coating film texture water of pre-production is needed on tap primed surface and forms grain decorating layer；
(4) the grain decorating layer spray paint obtained in step (3)；
(5) finishing coat surface is after sand paper grinding process, then sprays layer of transparent nano coating, and finished product is after heat treatment made.
2. a kind of tap coating decoration technology according to claim 1, it is characterised in that：The coating film texture water turns
Tap primed surface is printed on to include the following steps：
A, designed decoration connection with production of structures is transferred into coating film at water；
B, water transfer coating film is cut as required, is laid on the constant temperature water surface, water temperature is controlled at 25 ± 5 DEG C, and pH value is in neutrality；
C, activator is sprayed；
D, by water transfer operation, coating film texture is transferred to tap primed surface, forms texture dress after washing, drying
Adorn layer；
C. use air pressure spray gun in the apertures 0.8-1.2mm in grain decorating layer surface spray paint.
3. a kind of tap coating decoration technology according to claim 2, it is characterised in that：The activator is by benzene class
Substance, lipid material, alcohols material and white spirit mixed configuration form.
4. a kind of tap coating decoration technology according to claim 2, it is characterised in that：The priming paint and finishing coat are oil
Property or waterborne polyurethane resin, fineness be -400 mesh of 200 mesh.
5. a kind of tap coating decoration technology according to claim 2, it is characterised in that：The time of the washing is 2-
The temperature of 5min, drying are 80-100 DEG C, drying time 30-60min.
6. a kind of tap coating decoration technology according to claim 2, it is characterised in that：The finishing coat surface is through sand paper
Grinding process, sand paper used are 600-1000 mesh.
7. a kind of tap coating decoration technology according to claim 1, it is characterised in that：It is coarse described in step (1)
Processing is to be handled using -800 mesh of 220 mesh sand milling or/and -400 mesh sandblasting of 120 mesh.
8. a kind of tap coating decoration technology according to claim 1, it is characterised in that：The Transparent Nano-Coatings material
Matter is silicon-aluminum sol class nano paint, and fineness is -400 mesh of 200 mesh, is sprayed using the apertures 1.0-1.2mm air pressure spray gun, is passed through
80 DEG C of heat treatment 30-60min.
9. a kind of tap coating decoration technology according to claim 1, it is characterised in that：The thickness of the priming paint is
20-35μm。