CN107779008A - A kind of high surface hardness PCM color painted steel strips - Google Patents

A kind of high surface hardness PCM color painted steel strips Download PDF

Info

Publication number
CN107779008A
CN107779008A CN201711173303.3A CN201711173303A CN107779008A CN 107779008 A CN107779008 A CN 107779008A CN 201711173303 A CN201711173303 A CN 201711173303A CN 107779008 A CN107779008 A CN 107779008A
Authority
CN
China
Prior art keywords
coating
substrate
paint layer
topcoat paint
steel strips
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711173303.3A
Other languages
Chinese (zh)
Inventor
赵东明
黄雄白
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xingheyuan Composite Materials Co Ltd
Original Assignee
Suzhou Xingheyuan Composite Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Xingheyuan Composite Materials Co Ltd filed Critical Suzhou Xingheyuan Composite Materials Co Ltd
Priority to CN201711173303.3A priority Critical patent/CN107779008A/en
Publication of CN107779008A publication Critical patent/CN107779008A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of high surface hardness PCM color painted steel strips; including substrate; the upper surface of the substrate is coated with coating; and the upper surface of upper coating scribbles topcoat paint layer; the outer surface of the topcoat paint layer is equipped with diaphragm; the lower surface of the substrate scribbles lower coating, and the low side of lower coating scribbles epoxy back of the body enamelled coating.Invention passes through surface preparation by scribbling coating and topcoat paint layer on substrate, painting is coated, it is made through overbaking and cooling, make steel plate that there is lightweight, high rigidity performance attractive in appearance and good, can directly it process again, amino resins, epoxy resin and heat fixation acrylic coat reticulate structure in topcoat paint layer, have good hardness and luster performance, good toughness, hardness is big after curable polyester resin.

Description

A kind of high surface hardness PCM color painted steel strips
Technical field
The present invention relates to ornament materials processing technique field, more particularly to a kind of high surface hardness PCM color painted steel strips.
Background technology
High surface hardness polyester coating is a kind of using rapid automatized production line balance mode, is coated on continuous metal On thin plate (thin plate passes through derusting, oil removing, cleaning, passivation and surface treatment before coating), the film forming after hot setting, reach A kind of professional coating of certain machinery and physical property.Pre-coated coil product after application is widely used in building, household electrical appliances, collection Each field such as vanning, automobile making, cooker.User have purchased pre-coated coil product, i.e., after color painted steel strip, can directly add Work is into variously-shaped.Product need not application again, the production technology of sheet metal parts is enormously simplify, when reducing application Coating loss, reduce the pollution to environment.Color painted steel strip is of wide application, now largely in field of household appliances Middle use, the appearance requirement of household electrical appliances color steel is high, and paint film T is curved to require 0~1T, and has preferable antiseptic property, while also The environmental protection instruction for meeting European Union requires.
It is applied to the Coil Coating Products of household electrical appliances in the market, in order to meet the requirement of aftershaping and various complicated processing shapes, Generally excellent performance is required at the curved aspects of T, it is desirable to can reach 0~1T, but such a Coil Coating Products, in terms of case hardness Relatively low, usually F~H, during punch forming, surface and contacting dies easily cause surface tear, reduce qualification rate, The problem of easily wiping scuffing is also faced in later stage household electrical appliances final assembly reduces final qualification rate, existing color steel hardness It is low, have a strong impact on the service life of subsequent product.
The content of the invention
It is contemplated that at least solves one of technical problem in correlation technique to a certain extent.Therefore, the present invention One purpose is to propose a kind of high surface hardness PCM color painted steel strips, the present invention by scribbled on substrate coating and Topcoat paint layer passes through surface preparation, and painting is coated, through overbaking and cooling and be made, make steel plate have lightweight, it is attractive in appearance and Good high rigidity performance, can directly be processed again, in topcoat paint layer amino resins, epoxy resin and heat fixation acrylic coat into Network structure, has good hardness and a luster performance, good toughness, and hardness is big after curable polyester resin.
A kind of high surface hardness PCM color painted steel strips according to embodiments of the present invention, including substrate, the substrate it is upper Surface smear has upper coating, and the upper surface of upper coating scribbles topcoat paint layer, and the outer surface of the topcoat paint layer is equipped with Diaphragm, the lower surface of the substrate scribbles lower coating, and the low side of lower coating scribbles epoxy back of the body enamelled coating.
In other embodiments of the present invention, the upper coating is thermosetting acrylic coat.
In other embodiments of the present invention, amino resins and epoxy resin, amino are also added with the upper coating Resin, epoxy resin and heat fixation acrylic coat reticulate structure.
In other embodiments of the present invention, the weight/mass percentage composition of the composition of the topcoat paint dope layer is:Tree Fat 50~70%, pigment 2~6%, solvent 20~30%, auxiliary agent 2~5%;Wherein, for resin to there is polyester resin, pigment is sulphur Hydrochlorate and the phenol mountain valley with clumps of trees and bamboo are blue, and solvent is dimethylbenzene and aromatic hydrocarbons intermixture, and auxiliary agent is organobentonite.
In other embodiments of the present invention, silica is added with the epoxy back of the body enamelled coating.
A kind of preparation method of high surface hardness PCM color painted steel strips, is comprised the following steps that:
S1:Pretreatment, alkali cleaning degreasing, the greasy dirt and impurity of cleaning base plate, ensure plate face cleaning, for the later stage work of japanning Skill makees basis, after degreasing, is cleaned using clear water, ensures that no raffinate is retained;
S2:Dry for the first time, cleaning uses drying oven to carry out drying operation to substrate after finishing, and makees for first time rendering Prepare;
S3:Rendering, applied in the upper surface of substrate and spread coating, the thickness of upper coating is 25-45um, in the lower surface of bottom plate Lower coating is coated with, the thickness of lower coating is 20-35um, by changing the speed of service and the direction of application roll opposing webs, control Coating layer thickness processed;
S4:Secondary drying, after rendering is completed, solidification and stoving process are completed into drying oven, temperature control is 160 DEG C -300 DEG C, hardening time 15-30s;
S5:Essence painting, finish paint essence painting is carried out on upper coating after secondary drying, carry out smearing finish paint painting by smart painting machine The bed of material and epoxy back of the body enamelled coating, in 15-30um, the thickness of epoxy back of the body enamelled coating is 10-25um for the thickness control of topcoat paint layer;
S6:Drying, essence are entered in drying oven after applying and dried again;
S7:Wind cooling temperature lowering, using wind cooling temperature lowering, temperature control is below 40 DEG C;
S8:Pad pasting, after cooling, pad pasting is embossed in the upper surface of topcoat paint layer, pastes layer protecting film;
S9:Wind kink:The winding of color steel coil of strip edging is ensured according to the winding signal of electronic probe, reaches outgoing It is required that.
Beneficial effect in the present invention:The present invention is pre- by surface by scribbling coating and topcoat paint layer on substrate Processing, painting are coated, and are made through overbaking and cooling, steel plate is had lightweight, high rigidity performance attractive in appearance and good, again may be used Directly process, amino resins, epoxy resin and heat fixation acrylic coat reticulate structure in topcoat paint layer, have hard well Degree and luster performance, good toughness, hardness is big after curable polyester resin, by adding pigment and auxiliary agent, makes coating surface scattered equal Even, color is beautiful, good luster, can provide high surface hardness, improves qualification rate of the product during whole production and use, carries High yield quality, silica is heat-resist, and chemical stability is good and cheap, and brushing performance is good, phenol mountain valley with clumps of trees and bamboo indigo plant Stability Analysis of Structures, With excellent acidproof, alkaline-resisting, light resistance, tinting strength, tinting power is fabulous, bright-colored.
Brief description of the drawings
Accompanying drawing is used for providing a further understanding of the present invention, and a part for constitution instruction, the reality with the present invention Apply example to be used to explain the present invention together, be not construed as limiting the invention.In the accompanying drawings:
Fig. 1 is structural representation proposed by the present invention.
In figure:1 diaphragm, 2 topcoat paint layers, coating, 4 substrates, 5 times coatings, 6 epoxies back of the body enamelled coating on 3.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.
Reference picture 1, embodiment 1
A kind of high surface hardness PCM color painted steel strips, including substrate 4, the upper surface of the substrate 4 are coated with coating 3, and the upper surface of upper coating 3 scribbles topcoat paint layer 2, the outer surface of the topcoat paint layer 2 is equipped with diaphragm 1, described The lower surface of substrate 4 scribbles lower coating 5, and the low side of lower coating 5 scribbles epoxy back of the body enamelled coating 6.
The upper coating 3 is thermosetting acrylic coat, and amino resins and epoxy resin are also added with the upper coating 3, Amino resins, epoxy resin and heat fixation acrylic coat reticulate structure, the quality hundred of the composition of the topcoat paint dope layer Point content is:Resin 50%, pigment 2%, solvent 20%, auxiliary agent 2%, wherein, for resin to there is polyester resin, pigment is sulfate Blue with the phenol mountain valley with clumps of trees and bamboo, solvent is dimethylbenzene and aromatic hydrocarbons intermixture, and auxiliary agent is organobentonite, is added with the epoxy back of the body enamelled coating 6 Silica.
A kind of preparation method of high surface hardness PCM color painted steel strips, is comprised the following steps that:
S1:Pretreatment, alkali cleaning degreasing, the greasy dirt and impurity of cleaning base plate 4, ensure plate face cleaning, for the later stage of japanning Technique makees basis, after degreasing, is cleaned using clear water, ensures that no raffinate is retained;
S2:Dry for the first time, cleaning uses drying oven to carry out drying operation to substrate 4 after finishing, and is first time rendering Prepare;
S3:Rendering, applied in the upper surface of substrate 4 and spread coating 3, the thickness of upper coating 3 is 25um, in the lower surface of bottom plate Lower coating 5 is coated with, the thickness of lower coating 5 is 20um, by changing the speed of service and the direction of application roll opposing webs, control Coating layer thickness;
S4:Secondary drying, after rendering is completed, solidification and stoving process are completed into drying oven, temperature control is 160 DEG C, hardening time 15s;
S5:Essence is applied, and carrying out finish paint essence on upper coating 3 after secondary drying is applied, and smearing finish paint is carried out by smart painting machine Dope layer 2 and epoxy back of the body enamelled coating 6, in 15um, the thickness of epoxy back of the body enamelled coating 6 is 10um for the thickness control of topcoat paint layer 2;
S6:Drying, essence are entered in drying oven after applying and dried again;
S7:Wind cooling temperature lowering, using wind cooling temperature lowering, temperature control is below 40 DEG C;
S8:Pad pasting, after cooling, pad pasting is embossed in the upper surface of topcoat paint layer 2, pastes layer protecting film 1;
S9:Wind kink:The winding of color steel coil of strip edging is ensured according to the winding signal of electronic probe, reaches outgoing It is required that.
Embodiment 2
A kind of high surface hardness PCM color painted steel strips, including substrate 4, the upper surface of the substrate 4 are coated with coating 3, and the upper surface of upper coating 3 scribbles topcoat paint layer 2, the outer surface of the topcoat paint layer 2 is equipped with diaphragm 1, described The lower surface of substrate 4 scribbles lower coating 5, and the low side of lower coating 5 scribbles epoxy back of the body enamelled coating 6.
Method and step is with embodiment 1, different technological parameters:
Resin 70%, pigment 6%, solvent 30%, auxiliary agent 5%.
The thickness of upper coating 3 is 45um, and the thickness of lower coating 5 is 35um.
Secondary drying temperature control is at 300 DEG C, hardening time 30s.
For the thickness control of topcoat paint layer 2 in 30um, the thickness of epoxy back of the body enamelled coating 6 is 25um.
Embodiment 3
A kind of high surface hardness PCM color painted steel strips, including substrate 4, the upper surface of the substrate 4 are coated with coating 3, and the upper surface of upper coating 3 scribbles topcoat paint layer 2, the outer surface of the topcoat paint layer 2 is equipped with diaphragm 1, described The lower surface of substrate 4 scribbles lower coating 5, and the low side of lower coating 5 scribbles epoxy back of the body enamelled coating 6.
Method and step is with embodiment 1, different technological parameters:
Resin 60%, pigment 4%, solvent 25%, auxiliary agent 3.5%.
The thickness of upper coating 3 is 35um, and the thickness of lower coating 5 is 30um.
Secondary drying temperature control is at 200 DEG C, hardening time 25s.
For the thickness control of topcoat paint layer 2 in 25um, the thickness of epoxy back of the body enamelled coating 6 is 20um.
Embodiment 4
A kind of high surface hardness PCM color painted steel strips, including substrate 4, the upper surface of the substrate 4 are coated with coating 3, and the upper surface of upper coating 3 scribbles topcoat paint layer 2, the outer surface of the topcoat paint layer 2 is equipped with diaphragm 1, described The lower surface of substrate 4 scribbles lower coating 5, and the low side of lower coating 5 scribbles epoxy back of the body enamelled coating 6.
Method and step is with embodiment 1, different technological parameters:
Resin 65%, pigment 4.5%, solvent 22%, auxiliary agent 4%.
The thickness of upper coating 3 is 30um, and the thickness of lower coating 5 is 25um.
Secondary drying temperature control is at 250 DEG C, hardening time 20s.
For the thickness control of topcoat paint layer 2 in 20um, the thickness of epoxy back of the body enamelled coating 6 is 15um.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show The description of example " or " some examples " etc. means specific features, structure, material or the spy for combining the embodiment or example description Point is contained at least one embodiment or example of the present invention.In this manual, to the schematic representation of above-mentioned term not Necessarily refer to identical embodiment or example.Moreover, specific features, structure, material or the feature of description can be any One or more embodiments or example in combine in an appropriate manner.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto, Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.

Claims (5)

  1. A kind of 1. high surface hardness PCM color painted steel strips, it is characterised in that:
    Including substrate, the upper surface of the substrate is coated with coating, and the upper surface of upper coating scribbles topcoat paint layer, described The outer surface of topcoat paint layer is equipped with diaphragm, and the lower surface of the substrate scribbles lower coating, and the low side of lower coating scribbles Epoxy carries on the back enamelled coating.
  2. A kind of 2. high surface hardness PCM color painted steel strips according to claim 1, it is characterised in that:The upper coating For thermosetting acrylic coat.
  3. A kind of 3. high surface hardness PCM color painted steel strips according to claim 2, it is characterised in that:The upper coating In be also added with amino resins and epoxy resin, amino resins, epoxy resin and heat fixation acrylic coat reticulate structure.
  4. A kind of 4. high surface hardness PCM color painted steel strips according to claim 1, it is characterised in that:The finish paint applies The weight/mass percentage composition of the composition of the bed of material is:Resin 50~70%, pigment 2~6%, solvent 20~30%, auxiliary agent 2~5%;Its In, resin is has polyester resin, and pigment is that sulfate and the phenol mountain valley with clumps of trees and bamboo are blue, and solvent is dimethylbenzene and aromatic hydrocarbons intermixture, and auxiliary agent is to have Machine bentonite.
  5. A kind of 5. high surface hardness PCM color painted steel strips according to claim 1, it is characterised in that:The epoxy back of the body Silica is added with enamelled coating.
    A kind of preparation method of high surface hardness PCM color painted steel strips, is comprised the following steps that:
    S1:Pretreatment, alkali cleaning degreasing, the greasy dirt and impurity of cleaning base plate, ensure plate face cleaning, make for the late stage process of japanning Basis, after degreasing, cleaned using clear water, ensure that no raffinate is retained;
    S2:Dry for the first time, cleaning uses drying oven to carry out drying operation to substrate after finishing, and is that first time rendering is valid It is standby;
    S3:Rendering, applied in the upper surface of substrate and spread coating, the thickness of upper coating is 25-45umm, is applied in the lower surface of bottom plate Lower coating is wiped with, the thickness of lower coating is 20-35umm, by changing the speed of service and the direction of application roll opposing webs, control Coating layer thickness;
    S4:Secondary drying, rendering complete after, into drying oven complete solidification and stoving process, temperature control 160 DEG C- 300 DEG C, hardening time 15-30s;
    S5:Essence applies, and carrying out finish paint essence on upper coating after secondary drying applies, and carries out smearing topcoat paint layer by smart painting machine Enamelled coating is carried on the back with epoxy, and in 15-30umm, the thickness of epoxy back of the body enamelled coating is 10-25umm for the thickness control of topcoat paint layer;
    S6:Drying, essence are entered in drying oven after applying and dried again;
    S7:Wind cooling temperature lowering, using wind cooling temperature lowering, temperature control is below 40 DEG C;
    S8:Pad pasting, after cooling, pad pasting is embossed in the upper surface of topcoat paint layer, pastes layer protecting film;
    S9:Wind kink:The winding of color steel coil of strip edging is ensured according to the winding signal of electronic probe, reaching outgoing will Ask.
CN201711173303.3A 2017-11-22 2017-11-22 A kind of high surface hardness PCM color painted steel strips Pending CN107779008A (en)