CN110280468A - The production method of candy color painting wheel-mounted - Google Patents

The production method of candy color painting wheel-mounted Download PDF

Info

Publication number
CN110280468A
CN110280468A CN201910676686.9A CN201910676686A CN110280468A CN 110280468 A CN110280468 A CN 110280468A CN 201910676686 A CN201910676686 A CN 201910676686A CN 110280468 A CN110280468 A CN 110280468A
Authority
CN
China
Prior art keywords
wheel
wet
paint
levelling
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910676686.9A
Other languages
Chinese (zh)
Inventor
许树刚
何芳
何国元
张伟斌
裔国宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DARE WHEEL MANUFACTURE Co Ltd
Original Assignee
DARE WHEEL MANUFACTURE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DARE WHEEL MANUFACTURE Co Ltd filed Critical DARE WHEEL MANUFACTURE Co Ltd
Priority to CN201910676686.9A priority Critical patent/CN110280468A/en
Publication of CN110280468A publication Critical patent/CN110280468A/en
Pending legal-status Critical Current

Abstract

The invention belongs to wheel application techniques field, it is related to applying the production of wheel-mounted more particularly to a kind of candy color applies the production method of wheel-mounted, include: wheel after pretreatment, into paint line spray-applied primer, 15~20 μm of film thickness, then levelling, 20~50 DEG C of temperature, 9~11min of time;The dedicated argentine paint of wet on wet method spraying, 18~23 μm of film thickness, and levelling, 20~50 DEG C of temperature, 8~10min of time;The Special colored colored varnish of selection corresponding color is sprayed on argentine paint surface with wet on wet method as needed, and 25~30 μm of film thickness, and levelling, 10~30 DEG C of temperature, 8~10min of time;Baking-curing, 190~200 DEG C of solidification temperature, 15~20min of time.Process operations of the present invention are simple, by adjusting dedicated silver paint with the wet on wet spraying of the Special colored colored varnish, the derivative candy colored appearance painting effect using different coating compositions.Using the method for the invention, it can be completely covered by wheel surface defect, and can guarantee coating adhesive force and hardness.

Description

The production method of candy color painting wheel-mounted
Technical field
The invention belongs to wheel application techniques field, it is related to applying the production more particularly to a kind of candy color coating of wheel-mounted The production method of wheel.
Background technique
Currently, due to pursuing the universal of personalized theory, many clients all pursues automotive wheel with metal sense, thick and heavy satisfy The all especially strong visual effect of full sense, aerial perspective.In existing coating process, the sprayed on material of automotive hub paint is mainly The metallic paint of various colors or pure plain color paint, metallic paint flash of light, metal sense is strong, but lacks thick and heavy satiety, and color is dull;Plain color Qi Yanli is colorful, but lacks flash of light sense, does not have metal sense.
Candy color coating is sprayed from colourful transparent paint by different combinations using the aluminium paint of special allotment, is reached and is changed The effect of kind appearance obtains final products appearance and glistens metal sense, thick and heavy satiety, aerial perspective all especially by force, visually gives People is with fresh and new candy colour sensation.This appearance had not only remained the flash effect of metallic paint, but also had thick and heavy, full Texture, and be colourful effect, aerial perspective is very strong, similar with the candy of riot of color, therefore is called candy Color.Candy color, which applies wheel-mounted, has the unexistent appearance of conventional paint wheel, and production technology is not limited by color, can basis Customer requirement carries out any combination.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is disclose a kind of life of candy color painting wheel-mounted Production method.
A kind of candy color applies the production method of wheel-mounted, includes the following steps:
A, wheel after pretreatment, into paint line spray-applied primer, 15~20 μm of film thickness, then levelling, temperature 20~50 DEG C, 9~11min of time;
B, the dedicated argentine paint of wet on wet method spraying, 18~23 μm of film thickness, and levelling, 20~50 DEG C of temperature, the time 8~ 10min;
C, the Special colored colored varnish of selection corresponding color is sprayed on argentine paint surface with wet on wet method as needed, 25~30 μm of film thickness, and levelling, 10~30 DEG C of temperature, 8~10min of time;
D, baking-curing, 190~200 DEG C of solidification temperature, 15~20min of time.
In the more excellent disclosed example of the present invention, enter paint line spray-applied primer described in step A, 18 μm of film thickness, then levelling, temperature 35 DEG C, time 10min.
In the more excellent disclosed example of the present invention, the composition of dedicated argentine paint described in step B is by mass percentage are as follows: acrylic acid Resin 35~40%, acetylbutyrylcellulose 10~15%, amino resins 10~15%, epoxy resin 3~5%, aluminium powder 5~ 10%, fourth rouge 5~10%, regulator 5~0%.
In the more excellent disclosed example of the present invention, the dedicated argentine paint of wet on wet method spraying described in step B, 20 μm of film thickness, cocurrent It is flat, 35 DEG C of temperature, time 9min.
In the more excellent disclosed example of the present invention, the composition of the Special colored colored varnish described in step C is by mass percentage are as follows: acrylic acid Resin 50~60%, amino resins 20~30%, epoxy resin 3~6%, pigment 3~8%, regulator 10~15%.
In the more excellent disclosed example of the present invention, select the Special colored colored varnish of corresponding color with wet described in step C as needed Wet spray is touched on argentine paint surface, 28 μm of film thickness, and levelling, 20 DEG C of temperature, time 9min.
In the more excellent disclosed example of the present invention, 195 DEG C of solidification temperature described in step D, time 18min.
Not every silver paint combines the effect that can be obtained by candy color with colourful transparent paint, passes through step B and step Silver-colored paint+colourful transparent paint of two kinds of dedicated preparations is applied to produce in mature technique, obtains candy color effect by C.
Explanation of technical terms:
It is wet on wet: paint spraying three apply: priming paint+colored paint+colored varnish, it is wet on wet be relative to it is dry touch it is wet for;
It is dry touch it is wet: the priming paint-levelling-solidification-colored paint-levelling-colored varnish-levelling-solidification (usually said three spray three is roasting);
It is wet on wet: the priming paint-levelling-colored paint-levelling-colored varnish-levelling-solidification (three usually said sprays one are roasting).
The advantage and disadvantage list of the various paint of 1 coating of table
For spray-applied primer of the present invention to cover the defect of hub surface, levelling keeps primed surface flat and smooth, and wheel has good Good appearance;Wet on wet method sprays dedicated argentine paint on priming paint, and the metallic paint of only this dedicated silver color can just have sugar The effect of fruit color, the metallic paint of other colors are not up to the appearance of candy color, also pass through levelling after the spraying of argentine paint, Allow metallic paint smooth surface;With levelling is also passed through after the spraying of the Special colored colored varnish, make colourful transparent paint surface flat It is whole smooth;Spraying colourful transparent paint is required according to color, wheel surface paint is solidified, makes to paint complete glue chain, it is fixed Color.
Beneficial effect
Process operations of the present invention are simple, by adjusting dedicated silver paint and the wet on wet spraying of the Special colored colored varnish, utilize Different coating compositions and derivative candy colored appearance painting effect.Using the method for the invention, wheel table can be completely covered by Planar defect, and can guarantee coating adhesive force and hardness.
Specific embodiment
The following describes the present invention in detail with reference to examples, so that those skilled in the art more fully understand this hair It is bright, but the invention is not limited to following embodiments.
Unless otherwise defined, term (including scientific and technical terminology) used herein above should be construed as having as belonging to the present invention The identical meaning that those skilled in the art are commonly understood by.It will also be understood that term used herein above should be explained To have the meaning consistent with their meanings in the content of this specification and the relevant technologies, and should not be with idealization Or excessive form is explained, unless expressly so limiting here.
Embodiment 1
A kind of candy color applies the production method of wheel-mounted (product type DW1177), includes the following steps:
1, wheel spray-applied primer, film thickness are 16 μm;
2, priming paint levelling, technique are 80 DEG C of temperature, time 9min;
3, spraying argentine paint film thickness is 19 μm, and levelling, and levelling technique is 80 DEG C of temperature, time 8min;
4, requiring spraying colourful transparent paint film thickness according to color is 25 μm, and levelling, and levelling technique is 10 DEG C of temperature, the time 8min;
5, wheel surface is painted and carries out glue connection solidification, solidification temperature is 190 DEG C, duration 20min.
Embodiment 2
A kind of candy color applies the production method of wheel-mounted (product type DW1180), includes the following steps:
1, wheel spray-applied primer film thickness be 20 μm, wheel surface defect can be completely covered by, but can guarantee coating adhesive force and Hardness;
2, priming paint levelling, technique are 120 DEG C of temperature, time 11min;
3, spraying argentine paint film thickness is 23 μm, and levelling, and levelling technique is 120 DEG C of temperature, time 8min;
4, requiring spraying colourful transparent paint film thickness according to color is 30 μm, and levelling, and levelling technique is 20 DEG C of temperature, the time 10min;
5, wheel surface is painted and carries out glue connection solidification, solidification temperature is 190 DEG C, duration 15min.
Embodiment 3
A kind of candy color applies the production method of wheel-mounted (product type DW1575), includes the following steps:
1, wheel spray-applied primer film thickness be 19 μm, wheel surface defect can be completely covered by, but can guarantee coating adhesive force and Hardness;
2, priming paint levelling, technique are 135 DEG C of temperature, time 11min;
3, spraying argentine paint film thickness is 20 μm, and levelling, and levelling technique is 135 DEG C of temperature, time 9min;
4, requiring spraying colourful transparent paint film thickness according to color is 28 μm, and levelling, and levelling technique is 20 DEG C of temperature, the time 10min;
5, wheel surface is painted and carries out glue connection solidification, solidification temperature is 190 DEG C, duration 20min.
The wheel of above-described embodiment institute coating, test result is as follows:
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair Equivalent structure or equivalent flow shift made by bright specification is applied directly or indirectly in other relevant technical fields, Similarly it is included within the scope of the present invention.

Claims (7)

1. the production method that a kind of candy color applies wheel-mounted, which comprises the steps of:
A. wheel after pretreatment, into paint line spray-applied primer, 15~20 μm of film thickness, then levelling, 20~50 DEG C of temperature, 9~11min of time;
B. the dedicated argentine paint of wet on wet method spraying, 18~23 μm of film thickness, and levelling, 20~50 DEG C of temperature, the time 8~ 10min;
C. the Special colored colored varnish of selection corresponding color is sprayed on argentine paint surface, film with wet on wet method as needed It is 25~30 μm thick, and levelling, 10~30 DEG C of temperature, 8~10min of time;
D. baking-curing, 190~200 DEG C of solidification temperature, 15~20min of time.
2. candy color applies the production method of wheel-mounted according to claim 1, it is characterised in that: enter coating described in step A Wire spraying priming paint, 18 μm of film thickness, then levelling, 35 DEG C of temperature, time 10min.
3. candy color applies the production method of wheel-mounted according to claim 1, it is characterised in that: dedicated silver color described in step B The composition of metallic paint is by mass percentage are as follows: acrylic resin 35~40%, acetylbutyrylcellulose 10~15%, amino resins 10 ~15%, epoxy resin 3~5%, aluminium powder 5~10%, fourth rouge 5~10%, regulator 5~0%.
4. candy color applies the production method of wheel-mounted according to claim 1, it is characterised in that: wet on wet method described in step B Spray dedicated argentine paint, 20 μm of film thickness, and levelling, 35 DEG C of temperature, time 9min.
5. candy color applies the production method of wheel-mounted according to claim 1, it is characterised in that: Special colored described in step C The composition of the colored varnish is by mass percentage are as follows: acrylic resin 50~60%, amino resins 20~30%, epoxy resin 3~6%, face Material 3~8%, regulator 10~15%.
6. candy color applies the production method of wheel-mounted according to claim 1, it is characterised in that: described in step C as needed The Special colored colored varnish of corresponding color is selected to be sprayed on argentine paint surface with wet on wet method, 28 μm of film thickness, and levelling, temperature 20 DEG C of degree, time 9min.
7. candy color applies the production method of wheel-mounted according to claim 1, it is characterised in that: solidification temperature described in step D 195 DEG C, time 18min.
CN201910676686.9A 2019-07-25 2019-07-25 The production method of candy color painting wheel-mounted Pending CN110280468A (en)