CN109618945A - 一种宠物用砂及其制备方法 - Google Patents
一种宠物用砂及其制备方法 Download PDFInfo
- Publication number
- CN109618945A CN109618945A CN201811570019.4A CN201811570019A CN109618945A CN 109618945 A CN109618945 A CN 109618945A CN 201811570019 A CN201811570019 A CN 201811570019A CN 109618945 A CN109618945 A CN 109618945A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- sodium
- pet
- illite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及宠物用品领域,尤其涉及一种宠物用砂及其制备方法。本发明的宠物用砂包括以下重量份的组分:44~55份伊利石功能粉体;3~8份硅藻土;30~40份钠化膨润土;5~12份水;所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。其制备方法为:将44~55份伊利石功能粉体,3~8份硅藻土,30~40份钠化膨润土和5~12份水混合均匀,然后经过造粒及烘干处理,得到宠物用砂。本发明的宠物用砂具有团结性、吸水性,除臭性的。还具有激发空气负离子,吸附室内甲醛及异味,发射远红外线,抗菌防霉等作用。
Description
技术领域
本发明涉及宠物用品领域,尤其涉及一种宠物用砂及其制备方法。
背景技术
随着社会的发展,饲养宠物的人越来越多,且宠物大部分与主人处于同样的室内环境中,随着宠物饲养的普及和人们对环境质量日益重视,健康、环保意识的增强,对于如何能更好地解决饲养过程中宠物排泄物造成的环境污染问题,人们提出了更高的要求,对宠物用砂也有了新的要求。
传统宠物用砂主要有膨润土猫砂,水晶猫砂,植物猫砂等等,其中膨润土具有成本低廉、吸水团结的优点,但其易产生粉尘、除臭效果不理想,废弃物投入土壤里,致使土壤板结;水晶猫砂具有无粉尘的优点,但其不结团,吸水性低不能很好的吸收宠物尿液,不吸味等缺点;植物猫砂,虽然较为环保,但其主要成分为植物纤维素,有木质气味宠物不喜欢使用、造粒时有机粘合剂的加入会释放甲醛。具有吸水性吸味性差、成本较高、质地松散等缺点。以上传统宠物用砂易使宠物患上呼吸道及泌尿系统的疾病。且影响宠物及人的居住环境。
发明内容
本发明要解决的技术问题是:提供一种宠物用砂及其制备方法,所述宠物用砂不仅吸水性、除臭性、团结性好,净化室内环境;而且使用后可直接在土壤中掩埋是极好的土壤改良剂和肥料。
本发明公开了一种宠物用砂,包括以下重量份的组分:
44~55份伊利石功能粉体;
3~8份硅藻土;
30~40份钠化膨润土;
5~12份水;
所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。
优选地,所述伊利石功能粉体的制备方法为:
将天然伊利石矿物经过破碎及粉磨处理,得到粉体;
所述粉体在300~500℃的条件下活化,将含有镧系稀土元素的溶液附着在所述活化后的粉体上,得到伊利石功能粉体。
优选地,所述粉体的粒径分布D97为40μm~500μm。
优选地,所述天然伊利石矿物中的伊利石质量百分含量大于等于20%。
优选地,所述硅藻土中二氧化硅的质量百分含量大于等于60%。
优选地,所述钠化膨润土中蒙脱石的质量百分含量大于等于60%。
优选地,所述钠化膨润土的制备方法为:
将膨润土矿石经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入钠化剂搅拌均匀,钠化48~72小时。
优选地,所述钠化剂为碳酸钠、氯化钠和氧化钠中的一种或多种。
优选地,所述钠化剂的质量为膨润土粉质量的0.1~0.3%。
本发明还公开了一种宠物用砂的制备方法,包括以下步骤:
将44~55份伊利石功能粉体,3~8份硅藻土,30~40份钠化膨润土和5~12份水混合均匀,然后经过造粒及烘干处理,得到宠物用砂;所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。
与现有技术相比,本发明的宠物用砂包括以下重量份的组分:44~55份伊利石功能粉体;3~8份硅藻土;30~40份钠化膨润土;5~12份水;所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。在本发明中,伊利石功能粉体具有除味、杀菌、释放远红外线、激发负氧离子、吸附甲醛等性能,而且其具有高吸水性及粘结性。将所述伊利石功能粉体与硅藻土、钠化膨润土和水混合后,利用各组分的配合作用,可形成具有团结性、吸水性,除臭性的宠物用砂。本发明制备的宠物用砂无色无味,还具有激发空气负离子,吸附室内甲醛及异味,发射远红外线,抗菌防霉等作用。使用后的宠物用砂,可以直接在突然中掩埋,可作为土塘的改良剂和肥料,减少宠物呼吸道及泌尿系统等疾病的患病几率。既为宠物营造了理想的排泄环境,又对室内环境产生一定的净化功能。
具体实施方式
为了进一步理解本发明,下面结合实施例对本发明优选实施方案进行描述,但是应当理解,这些描述只是为进一步说明本发明的特征和优点,而不是对本发明的限制。
本发明的实施例公开了一种宠物用砂,包括以下重量份的组分:
44~55份伊利石功能粉体;
3~8份硅藻土;
30~40份钠化膨润土;
5~12份水;
所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。
伊利石是一种富钾的2∶1型层间缺失的二八面体硅酸盐云母类粘土矿物,属于两个硅氧四面体夹一个铝氧八面体(即T-O-T)结构,层间有水及阳离子。
本发明选用伊利石作为主要组分,并且通过处理,获得了适合用于宠物用砂的伊利石功能粉体。本发明所述的伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。进一步优选地,所述伊利石功能粉体的制备方法为:
将天然伊利石矿物经过破碎及粉磨处理,得到粉体;
所述粉体在300~500℃的条件下活化,将含有镧系稀土元素的溶液附着在所述活化后的粉体上,得到伊利石功能粉体。
在所述伊利石粉体的制备方法中,以天然伊利石矿物为原料,首先经过破碎及粉磨处理,得到粉体。优选地,所述粉体的粒径分布D97为40μm~500μm。
优选地,所述天然伊利石矿物中的伊利石质量百分含量大于等于20%。
得到所述粉体后,将所述粉体在300~500℃的条件下活化,优选地,在410~~500℃的条件下活化;然后,将含有镧系稀土元素的溶液附着在活化后的粉体上,得到伊利石功能粉体。含有镧系稀土元素的溶液附着在活化后的粉体的表面或者内部。
优选地,含有镧系稀土元素的溶液通过使用喷淋、或者喷雾的方法附着于活化后的粉体上。所述镧系稀土元素为选自镧、铈、镨、钕、钐、铕、钆、铽、镝、钬、铒、铥、镱、镥中的一种或多种。所述镧系稀土元素的质量为伊利石功能粉体质量的0.05%~0.1%。
经过高温活化,在不破坏伊利石晶体结构的情况下,去除了层间的水及阳离子,增加了其吸水性和吸附性。层间阳离子的交换可激发空气负离子的产生,且可以负载铈、镧、镨等功能离子而具备杀菌、释放远红外线的作用,并具有一定的粘结性。
在本发明中,包括44~55份伊利石功能粉体,优选地,包括45~52份伊利石功能粉体。
在本发明中,包括3~8份硅藻土,优选地包括4~7份硅藻土。优选地,所述硅藻土中二氧化硅的质量百分含量大于等于60%。
在本发明中,包括30~40份钠化膨润土,优选地,包括35~40份钠化膨润土。优选地,所述钠化膨润土中蒙脱石的质量百分含量大于等于60%。
所述钠化膨润土的制备方法优选为:
将膨润土矿石经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入钠化剂搅拌均匀,钠化48~72小时。
优选地,所述钠化剂为碳酸钠、氯化钠和氧化钠中的一种或多种。所述钠化剂的质量优选为膨润土粉质量的0.1~0.3%。
在本发明中,还包括5~12份水。优选地,包括6~10份水。
本发明的实施例还公开了一种宠物用砂的制备方法,包括以下步骤:
将44~55份伊利石功能粉体,3~8份硅藻土,30~40份钠化膨润土和5~12份水混合均匀,然后经过造粒及烘干处理,得到宠物用砂。
本发明选用的组分及其用量在上述技术方案中已经进行了描述。在此不再赘述。
按照本发明,将伊利石功能粉体、硅藻土、钠化膨润土和水混合均匀,然后经过造粒及烘干处理,得到宠物用砂。
优选地,经过造粒后形成粒径为3~8mm的颗粒,以便于宠物使用。所述烘干的温度优选为50~100℃,以保证伊利石功能粉体与其他组分更好的粘合,并保证功能成分不失效。
本发明制备的宠物用砂,具有以下优点:
1、团结性、吸水性、除臭性好;
2、颗粒强度高不易碎;
3、均为无机非金属材料,绿色健康、无色无味;
4、减少宠物呼吸道及泌尿系统疾病的发生几率;
5、还具有激发空气负离子、吸附室内甲醛及异味、发射远红外线、抗菌防霉的功能性;
6、用后的砂可直接作为农肥使用,避免了二次污染。
为了进一步理解本发明,下面结合实施例对本发明提供的一种宠物用砂及其制备方法进行详细说明,本发明的保护范围不受以下实施例的限制。
实施例1
将天然伊利石矿物其矿物组成伊利石含量37.8%,破碎、粉磨、分级至D97=56μm,于300℃活化2小时。
分别配置800ml浓度为10mg/ml的含稀土元素钪、钇、镧、铈、镨和钕的溶液,400ml浓度为10mg/ml的含稀土元素钐、铕和钆的溶液,以及100ml浓度为10mg/ml的含稀土元素铽的溶液。
向活化后的伊利石粉体中喷淋上述溶液,搅拌,使稀土元素包覆在伊利石粉体表面,得到伊利石功能粉体。
将膨润土矿石(蒙脱石含量为68%)经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入碳化钠搅拌均匀,钠化48小时,得到钠化膨润土;所述碳化钠的质量为膨润土粉质量的0.1%。
取伊利石功能粉体50份,硅藻土(SiO2含量为65.3%)5份,钠化膨润土38份,水7份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机50℃烘干制得宠物用砂。
实施例2
将天然伊利石矿物其矿物组成伊利石含量35%,破碎、粉磨、分级至D97=100μm,于350℃活化1.5小时。
配置400ml浓度为10mg/ml的含稀土元素钐、铕和钆的溶液。
向活化后的伊利石粉体中喷淋上述溶液,搅拌,使稀土元素包覆在伊利石粉体表面,得到伊利石功能粉体。
将膨润土矿石(蒙脱石含量为60%)经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入氯化钠搅拌均匀,钠化55小时,得到钠化膨润土;所述碳化钠的质量为膨润土粉质量的0.2%。
取伊利石功能粉体45份,硅藻土(SiO2含量为60.2%)8份,钠化膨润土40份,水12份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机烘干制得宠物用砂。
实施例3
将天然伊利石矿物其矿物组成伊利石含量46%,破碎、粉磨、分级至D97=300μm,于500℃活化1小时。
配置400ml浓度为10mg/ml的含稀土元素钪、钇、镧、铈、镨、钕、钐、铕和钆的溶液。
向活化后的伊利石粉体中喷淋上述溶液,搅拌,使稀土元素包覆在伊利石粉体表面,得到伊利石功能粉体。
将膨润土矿石(蒙脱石含量为68%)经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入碳化钠搅拌均匀,钠化52小时,得到钠化膨润土;所述碳化钠的质量为膨润土粉质量的0.25%。
取伊利石功能粉体55份,硅藻土(SiO2含量为65.3%)3份,钠化膨润土36份,水6份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机烘干制得宠物用砂。
实施例4
将天然伊利石矿物其矿物组成伊利石含量46%,破碎、粉磨、分级至D97=300μm,于410℃活化1小时。
配置400ml浓度为10mg/ml的含稀土元素钪、钇、镧、铈、镨、钕、钐、铕和钆的溶液。
向活化后的伊利石粉体中喷淋上述溶液,搅拌,使稀土元素包覆在伊利石粉体表面,得到伊利石功能粉体。
将膨润土矿石(蒙脱石含量为68%)经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入碳化钠、氧化钠搅拌均匀,钠化60小时,得到钠化膨润土;所述碳化钠和氧化钠的总质量为膨润土粉质量的0.3%。
取伊利石功能粉体48份,硅藻土(SiO2含量为65.3%)4份,钠化膨润土39份,水10份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机烘干制得宠物用砂。
实施例5
将天然伊利石矿物其矿物组成伊利石含量46%,破碎、粉磨、分级至D97=300μm,于450℃活化1小时。
配置400ml浓度为10mg/ml的含稀土元素钪、钇、镧、铈、镨、钕、钐、铕和钆的溶液。
向活化后的伊利石粉体中喷淋上述溶液,搅拌,使稀土元素包覆在伊利石粉体表面,得到伊利石功能粉体。
将膨润土矿石(蒙脱石含量为68%)经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入氧化钠搅拌均匀,钠化60小时,得到钠化膨润土;所述碳化钠的质量为膨润土粉质量的0.28%。
取伊利石功能粉体52份,硅藻土(SiO2含量为65.3%)6份,钠化膨润土37份,水8份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机烘干制得宠物用砂。
比较例1
取天然伊利石矿石粉52份,硅藻土(SiO2含量为65.3%)6份,膨润土(蒙脱石含量68%)37份,水8份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机烘干制砂体。
比较例2
将天然伊利石矿物其矿物组成伊利石含量46%,破碎、粉磨、分级至D97=300μm,于450℃活化1小时。
配置400ml浓度为10mg/ml的含稀土元素钪、钇、镧、铈、镨、钕、钐、铕和钆的溶液。
向活化后的伊利石粉体中喷淋上述溶液,搅拌,使稀土元素包覆在伊利石粉体表面,得到伊利石功能粉体。
取伊利石功能粉体52份,硅藻土(SiO2含量为65.3%)6份,水8份,于高速搅拌机中充分搅拌均匀,入圆盘造粒机中造粒,颗粒直径5mm。于烘干机烘干制得砂体。
对实施例制备的宠物用砂进行测试,测试方法详见表1
表1
测试结果,详见表2
表2
市售产品1以膨润土为主成分。
市售产品2以木质植物粉末为主成分。
以上实施例的说明只是用于帮助理解本发明的方法及其核心思想。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以对本发明进行若干改进和修饰,这些改进和修饰也落入本发明权利要求的保护范围内。
对所公开的实施例的上述说明,使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的,本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下,在其它实施例中实现。因此,本发明将不会被限制于本文所示的这些实施例,而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种宠物用砂,包括以下重量份的组分:
44~55份伊利石功能粉体;
3~8份硅藻土;
30~40份钠化膨润土;
5~12份水;
所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。
2.根据权利要求1所述的宠物用砂,其特征在于,所述伊利石功能粉体的制备方法为:
将天然伊利石矿物经过破碎及粉磨处理,得到粉体;
所述粉体在300~500℃的条件下活化,将含有镧系稀土元素的溶液附着在所述活化后的粉体上,得到伊利石功能粉体。
3.根据权利要求2所述的宠物用砂,其特征在于,所述粉体的粒径分布D97为40μm~500μm。
4.根据权利要求1所述的宠物用砂,其特征在于,所述天然伊利石矿物中的伊利石质量百分含量大于等于20%。
5.根据权利要求1所述的宠物用砂,其特征在于,所述硅藻土中二氧化硅的质量百分含量大于等于60%。
6.根据权利要求1所述的宠物用砂,其特征在于,所述钠化膨润土中蒙脱石的质量百分含量大于等于60%。
7.根据权利要求1所述的宠物用砂,其特征在于,所述钠化膨润土的制备方法为:
将膨润土矿石经过破碎及粉磨,得到膨润土粉;
在所述膨润土粉中加入钠化剂搅拌均匀,钠化48~72小时。
8.根据权利要求7所述的宠物用砂,其特征在于,所述钠化剂为碳酸钠、氯化钠和氧化钠中的一种或多种。
9.根据权利要求7所述的宠物用砂,其特征在于,所述钠化剂的质量为膨润土粉质量的0.1~0.3%。
10.一种宠物用砂的制备方法,包括以下步骤:
将44~55份伊利石功能粉体,3~8份硅藻土,30~40份钠化膨润土和5~12份水混合均匀,然后经过造粒及烘干处理,得到宠物用砂;
所述伊利石功能粉体由天然伊利石矿物依次经过破碎、高温活化及改性处理得到。