CN109605530A - A kind of process of surface treatment of outdoor desk-chair - Google Patents
A kind of process of surface treatment of outdoor desk-chair Download PDFInfo
- Publication number
- CN109605530A CN109605530A CN201811616462.0A CN201811616462A CN109605530A CN 109605530 A CN109605530 A CN 109605530A CN 201811616462 A CN201811616462 A CN 201811616462A CN 109605530 A CN109605530 A CN 109605530A
- Authority
- CN
- China
- Prior art keywords
- surface treatment
- hot pressing
- parts
- chair according
- outdoor desk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of process of surface treatment of outdoor desk-chair, it is related to furniture manufacturing field, for solving the problems, such as the advantages of outdoor furniture cannot have both metal material and wooden material, the following steps are included: being pre-processed to the piece surface of the tables and chairs of metal material, pretreatment includes polishing, sanding, phosphatization, and in the external coating aqueous priming paint of part；It is applied to after sawdust, additive and binder are uniformly mixed by weight 6:2:2 on the piece surface of tables and chairs；The part is placed into hot pressing die and carries out hot pressing；The surface of part is post-processed, present invention process is simple, and it is easy to operate, it is low in cost, the hardness and strength of metal material are had both, but also with the sense of touch and appearance of wooden material, good combination property is easy to maintenance and low in cost, is conducive to environmental protection.
Description
Technical field
The present invention relates to technical field of furniture manufacturing more particularly to a kind of process of surface treatment of outdoor desk-chair.
Background technique
Nowadays, people are when buying furniture, therefore, deep by wide because wood furniture has the wood grain appearance of nature gracefulness
The favor of big buyer.Wood furniture is influenced by material, can have following problems in use: limited strength is not suitable for ground
It shakes prone areas to use, so that wood furniture use scope is restricted；It needs to expend a large amount of timber in manufacturing process, wastes
Resource, does not utilize environmental protection.
In addition to wood furniture, on the market there are also sale metal furniture, metal furniture can overcome the above-mentioned of wood furniture to lack
Point.But also cannot achieve using the prior art and process the wood grain pattern of texture on metal furniture surface, generally all
It is to spray the pattern without texture on metal furniture surface by the way of spray painting, pattern is inflexible, influences the use effect of metal furniture
Fruit, and then affect the popularization and use of metal furniture.
Summary of the invention
The purpose of the present invention is to solve outdoor furnitures existing in the prior art cannot have both metal material and wooden
The problem of the advantages of material, and a kind of process of surface treatment of the outdoor desk-chair proposed.
A kind of process of surface treatment of outdoor desk-chair, comprising the following steps:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
(3) part is placed into hot pressing die and carries out hot pressing；
(4) surface of part is post-processed.
Preferably, after sawdust is crushed by pulverizer in the step (2), screening granularity is 20~60 mesh, and is utilized micro-
Wave dries it, so that the moisture content of sawdust is within 5/1000ths.
Preferably, in the step (2) additive by weight by 60~80 parts of stalk powder, plastic powders 30~40
Part, 5~10 parts of metal powder and 0.5~2 part of coloring agent composition, the granularity of the stalk powder, plastic powders and metal powder
For 20~60 mesh.
Preferably, the plastic powders select one of polyvinyl chloride, polyethylene and polypropylene thermoplastics or more
Kind.
Preferably, binder uses epoxy adhesive in the step (2).
Preferably, the temperature range of hot pressing is 150 to 300 degrees Celsius in the step (3), and pressing pressure is 3~5MPa,
Hot pressing time is 20~60 minutes.
Preferably, post-processing includes to piece surface deburring, polishing, coloring, coats protective paint simultaneously in the step (4)
It dries.
Preferably, the mode of the coloring includes hand drawing, water transfer and roller printing and dyeing.
Preferably, the protective paint uses one of Wood protecting agent GH-A, aqueous woodware paint, wood wax oil, anti-decaying paint
Or it is a variety of.
The beneficial effects of the present invention are:
1, it in the present invention, uses metal material for substrate, the outside of substrate is provided with layer of wood, on the one hand can make
Outdoor furniture has stronger hardness, firmer, and on the other hand, the surface of furniture has wooden sense of touch and wooden outer
It sees, the class of furniture is improved, suitable for different customer demands.
2, in the present invention, simple process is easy to operate, low in cost, using hot pressing by layer of wood in conjunction with metallic substrates,
So that layer of wood is stronger in conjunction with metallic substrates, the quality of furniture entirety is improved.
3, in the present invention, layer of wood uses the layer of wood of sawdust, additive and adhesive as outer layer, when outside layer of wood
When the damages such as collide with, scratch occurs in surface, it can use wood dust and common glue repaired, easy to maintenance, maintenance cost
It is cheap.
4, in the present invention, layer of wood uses the layer of wood of sawdust, additive and adhesive as outer layer, not only can be as wood
Material is equally sawed, digs, punches and is painted, and high mechanical strength, and water imbibition is smaller than timber, and dimensional stability is better than timber, is also had
There is anti-flammability, comprehensive performance is more preferable.
5, in the present invention, the use scope of metal furniture is greatly expanded, and can substitute wood furniture in more areas, in turn
Reduce the demand to the forest reserves, is conducive to environmental protection.
To sum up, present invention process is simple, easy to operate, low in cost, has both the hardness and strength of metal material, but also with
The sense of touch and appearance of wooden material, good combination property is easy to maintenance and low in cost, is conducive to environmental protection.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
A kind of process of surface treatment of outdoor desk-chair, comprising the following steps:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
It polishes and carries out smooth treatment for the surface to metal parts, guarantee the flatness of metal piece surface, with after an action of the bowels
Continue the wooden outside for being placed on metal parts；
Sanding is a kind of common surfacing process, metal parts surface can be made smooth, while increasing the strong of surface
Degree；
Phosphatization is the process of a kind of chemistry and electrochemical reaction formation phosphate chemical conversion film, can be mentioned to metal parts
For protection, while playing the role of etch-proof；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
The thickness of smearing determines that in general, the thickness of smearing is needed according to the layer of wood thickness of parts to be processed needs
Bigger than design thickness 5 to 30mm；
(3) part is placed into hot pressing die and carries out hot pressing；
(4) surface of part is post-processed.
Further, after sawdust is crushed by pulverizer in the step (2), screening granularity is 20~60 mesh, and is utilized
Microwave dries it, so that the moisture content of sawdust within 5/1000ths, guarantees the degree of drying of sawdust, it is subsequent in order to prevent
In heat pressing process, layer of wood bubble, reduces the pit of layer of wood, guarantees the flatness of layer of wood caused by moisture evaporates.
Further, in the step (2) additive by weight by 60~80 parts of stalk powder, plastic powders 30~40
Part, 5~10 parts of metal powder and 0.5~2 part of coloring agent composition, the granularity of the stalk powder, plastic powders and metal powder
For 20~60 mesh, stalk can be used in heat pressing process using rice straw, straw, sorghum stalk and cornstalk etc., plastic powders, will
Each ingredient is merged in additive, improves the intensity of layer of wood entirety, and coloring agent guarantees wood for dyeing to layer of wood
The beauty of matter layer.
Further, the plastic powders select one of polyvinyl chloride, polyethylene and polypropylene thermoplastics or
It is a variety of.
Further, binder uses epoxy adhesive in the step (2).
Further, in the step (3) hot pressing temperature range be 150 to 300 degrees Celsius, pressing pressure be 3~
5MPa, hot pressing time are 20~60 minutes.
Further, post-processing includes to piece surface deburring, polishing, coloring, coating protective paint in the step (4)
And it dries.
Further, the mode of the coloring includes that hand drawing, water transfer and roller are printed and dyed, can be to wooden layer surface
Beautified.
Further, the protective paint is using one in Wood protecting agent GH-A, aqueous woodware paint, wood wax oil, anti-decaying paint
Kind is a variety of.
Embodiment 1:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
After sawdust is crushed by pulverizer, screening granularity is 20 mesh, and is dried using microwave to it, so that sawdust is aqueous
Rate is within 5/1000ths, and additive is by weight by 60 parts of stalk powder, 30 parts of plastic powders, 5 parts of metal powder and dyeing
0.5 part of agent composition, the granularity of the stalk powder, plastic powders and metal powder are 20 mesh, and binder is viscous using epoxy resin
Tie agent.
(3) part is placed into hot pressing die and carries out hot pressing；
The temperature range of hot pressing is 150 degrees Celsius, pressing pressure 3MPa, and hot pressing time is 20 minutes.
(4) surface of part is post-processed.
Embodiment 2:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
After sawdust is crushed by pulverizer, screening granularity is 30 mesh, and is dried using microwave to it, so that sawdust is aqueous
Rate is within 5/1000ths, and additive is by weight by 70 parts of stalk powder, 35 parts of plastic powders, 7 parts of metal powder and dyeing
1 part of agent composition, the granularity of the stalk powder, plastic powders and metal powder are 40 mesh, and binder is bonded using epoxy resin
Agent.
(3) part is placed into hot pressing die and carries out hot pressing；
The temperature range of hot pressing is 230 degrees Celsius, pressing pressure 4MPa, and hot pressing time is 40 minutes.
(4) surface of part is post-processed.
Embodiment 3:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
After sawdust is crushed by pulverizer, screening granularity is 60 mesh, and is dried using microwave to it, so that sawdust is aqueous
Rate is within 5/1000ths, and additive is by weight by 80 parts of stalk powder, 40 parts of plastic powders, 10 parts of metal powder and dyeing
2 parts of agent compositions, the granularity of the stalk powder, plastic powders and metal powder are 60 mesh, and binder is bonded using epoxy resin
Agent.
(3) part is placed into hot pressing die and carries out hot pressing；
The temperature range of hot pressing is 300 degrees Celsius, pressing pressure 5MPa, and hot pressing time is 60 minutes.
(4) surface of part is post-processed.
Embodiment 4:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
After sawdust is crushed by pulverizer, screening granularity is 30 mesh, and is dried using microwave to it, so that sawdust is aqueous
Rate is within 5/1000ths, and additive is by weight by 70 parts of stalk powder, 30 parts of plastic powders, 7 parts of metal powder and dyeing
1 part of agent composition, the granularity of the stalk powder, plastic powders and metal powder are 30 mesh, and binder is bonded using epoxy resin
Agent.
(3) part is placed into hot pressing die and carries out hot pressing；
The temperature range of hot pressing is 200 degrees Celsius, pressing pressure 4MPa, and hot pressing time is 30 minutes.
(4) surface of part is post-processed.
Embodiment 5:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
After sawdust is crushed by pulverizer, screening granularity is 50 mesh, and is dried using microwave to it, so that sawdust is aqueous
Rate is within 5/1000ths, and additive is by weight by 65 parts of stalk powder, 36 parts of plastic powders, 8 parts of metal powder and dyeing
1 part of agent composition, the granularity of the stalk powder, plastic powders and metal powder are 40 mesh, and binder is bonded using epoxy resin
Agent.
(3) part is placed into hot pressing die and carries out hot pressing；
The temperature range of hot pressing is 250 degrees Celsius, pressing pressure 4MPa, and hot pressing time is 35 minutes.
(4) surface of part is post-processed.
Embodiment 6:
(1) piece surface of the tables and chairs of metal material is pre-processed, is pre-processed including polishing, sanding, phosphatization, and
The external coating aqueous priming paint of part；
(2) parts list of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On face；
After sawdust is crushed by pulverizer, screening granularity is 40 mesh, and is dried using microwave to it, so that sawdust is aqueous
Rate is within 5/1000ths, and additive is by weight by 75 parts of stalk powder, 35 parts of plastic powders, 8 parts of metal powder and dyeing
1 part of agent composition, the granularity of the stalk powder, plastic powders and metal powder are 50 mesh, and binder is bonded using epoxy resin
Agent.
(3) part is placed into hot pressing die and carries out hot pressing；
The temperature range of hot pressing is 250 degrees Celsius, pressing pressure 4MPa, and hot pressing time is 50 minutes.
(4) surface of part is post-processed.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of process of surface treatment of outdoor desk-chair, which comprises the following steps:
(1) piece surface of the tables and chairs of metal material is pre-processed, pretreatment includes polishing, sanding, phosphatization, and in part
External coating aqueous priming paint；
(2) piece surface of tables and chairs is applied to after being uniformly mixed sawdust, additive and binder by weight 6:2:2
On；
(3) part is placed into hot pressing die and carries out hot pressing；
(4) surface of part is post-processed.
2. a kind of process of surface treatment of outdoor desk-chair according to claim 1, which is characterized in that in the step (2)
After sawdust is crushed by pulverizer, screening granularity is 20~60 mesh, and is dried using microwave to it, so that the moisture content of sawdust exists
Within 5/1000ths.
3. a kind of process of surface treatment of outdoor desk-chair according to claim 1, which is characterized in that in the step (2)
Additive is by weight by 60~80 parts of stalk powder, 30~40 parts of plastic powders, 5~10 parts of metal powder and coloring agent 0.5
~2 parts of compositions, the granularity of the stalk powder, plastic powders and metal powder are 20~60 mesh.
4. a kind of process of surface treatment of outdoor desk-chair according to claim 3, which is characterized in that the plastic powders choosing
With one of polyvinyl chloride, polyethylene and polypropylene thermoplastics or a variety of.
5. a kind of process of surface treatment of outdoor desk-chair according to claim 1, which is characterized in that in the step (2)
Binder uses epoxy adhesive.
6. a kind of process of surface treatment of outdoor desk-chair according to claim 1, which is characterized in that in the step (3)
The temperature range of hot pressing is 150 to 300 degrees Celsius, and pressing pressure is 3~5MPa, and hot pressing time is 20~60 minutes.
7. a kind of process of surface treatment of outdoor desk-chair according to claim 1, which is characterized in that in the step (4)
Post-processing includes to piece surface deburring, polishing, coloring, coating protective paint and drying.
8. a kind of process of surface treatment of outdoor desk-chair according to claim 7, which is characterized in that the mode of the coloring
Including hand drawing, water transfer and roller printing and dyeing.
9. a kind of process of surface treatment of outdoor desk-chair according to claim 7, which is characterized in that the protective paint uses
One of Wood protecting agent GH-A, aqueous woodware paint, wood wax oil, anti-decaying paint are a variety of.