CN106239679A - A kind of manufacture method of solid wood skirting modelled after an antique - Google Patents
A kind of manufacture method of solid wood skirting modelled after an antique Download PDFInfo
- Publication number
- CN106239679A CN106239679A CN201610791311.3A CN201610791311A CN106239679A CN 106239679 A CN106239679 A CN 106239679A CN 201610791311 A CN201610791311 A CN 201610791311A CN 106239679 A CN106239679 A CN 106239679A
- Authority
- CN
- China
- Prior art keywords
- skirting
- paint
- antique
- modelled
- sheet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the manufacture method of a kind of solid wood skirting modelled after an antique, the method comprises the steps: (1) saw lumber and is dried: fast growing wood makes sheet material, and the drying mode combined by air dry and kiln drying by sheet material moisture control 8～12%；(2) sawn timber and finger: prepared sheet material is processed through multiple blade saw, automatic comb and finger joint machine, obtains the skirting size of specification；(3) milling molding: by four side moulder simultaneous manufacturing, surface mills out a stress slow release groove, and the back side is provided with symmetric function groove；(4) embossing modelled after an antique: extrude grain pattern in skirting surface roll；(5) surface processes: the semi-finished product skirting prepared after step (4), after opposite sex sanding paint finish process covered with paint, lacquer, colour wash, etc. by priming paint, obtains solid wood skirting finished product.Use that processing cost of the present invention is low, skirting good stability and three-dimensional attractive in appearance.
Description
Technical field
The invention belongs to decorative building material technical field, be specifically related to the manufacture method of a kind of solid wood skirting modelled after an antique.
Background technology
Fast growing wood Eucalyptus, Lignum seu Ramulus Cunninghamiae Lanceolatae etc. typically all can produce substantial amounts of discarded reel after rotary-cut at present, because of such reel profit
Big by difficulty, and quality is uneven causes poor stability, therefore such discarded reel seldom can carry out the utilization of high value again,
Thus result in the substantial amounts of waste of timber.
In Home Fashion & Design Shanghai, Wood skirting line is widely used in building decoration, furniture finishing etc., and it includes density board
Skirting, plywood skirting and solid wood skirting, and the production Technology of density board skirting, plywood skirting is more
Simply, and free formaldehyde be easier to release.Solid wood skirting in the market, its appearance and modeling is simple and the most single, does not has
Third dimension, and decorative pattern and color cannot be unified in skirting surface.The making of solid wood skirting modelled after an antique, for fast growing wood and discarded
The lifting of reel application in wood products and timber added value has appreciable impact.People's trial pulverized limestone adds Calx etc.
Slow setting water makes the method that the construction material such as compound, putty is attached to wood surface, thus improves fast growing wood skirting
Surface property, although serve certain effect, but Coating technology is complex, affects the safety of user with healthy, simultaneously
Also result in problem of environmental pollution.
Meanwhile, make solid wood skirting currently with the discarded reel after fast growing wood Eucalyptus, Lignum seu Ramulus Cunninghamiae Lanceolatae rotary-cut, and realize playing
Low cost, the good and three-dimensional technology attractive in appearance of product stability that payment to a porter produces yet there are no report.
Summary of the invention
For above-mentioned technical problem, the present invention provides a kind of and utilizes the discarded reel after the rotary-cuts such as fast growing wood Eucalyptus, Lignum seu Ramulus Cunninghamiae Lanceolatae
Make solid wood skirting, and realize that processing cost is low, skirting good stability and three-dimensional solid wood skirting system modelled after an antique attractive in appearance
Make method,
For achieving the above object, the present invention adopts the following technical scheme that
The manufacture method of a kind of solid wood skirting modelled after an antique, it is characterised in that the method comprises the steps:
(1) saw lumber and being dried: fast growing wood is made sheet material, and the drying mode combined by air dry and kiln drying is by sheet material
Moisture control is 8～12%；
(2) sawn timber and finger: prepared sheet material is processed through multiple blade saw, automatic comb and finger joint machine, obtains the skirt of specification
Linear dimension；
(3) milling molding: by four side moulder simultaneous manufacturing, surface mills out a stress slow release groove, and the back side is provided with symmetry
The function groove of property；
(4) embossing modelled after an antique: extrude grain pattern in skirting surface roll；
(5) surface processes: the semi-finished product skirting prepared after step (4) covers with paint, lacquer, colour wash, etc. opposite sex sanding paint through priming paint
After facing processes, obtain solid wood skirting finished product.
Further, the drying mode that described in step (1), air dry and kiln drying combine, first use air dry mode by sheet material
Moisture control, to 41～52%, then uses kiln drying mode again by described sheet material moisture control to 8～12%.
Further, described timber is discarded reel after fast-growing Eucalyptus, Lignum seu Ramulus Cunninghamiae Lanceolatae or rotary-cut.
Further, in described step (3), the surface stress well width described in milling formative stage is 0.1～2cm, the degree of depth
It is 0.2～0.5cm；The width of back side symmetry groove is 0.5～2cm, and the degree of depth is 0.1～0.5cm, uses under this parameter, becomes
Template is the most attractive in appearance and stability best, and meanwhile, described skirting upper side edge is set as stair-stepping arcuate structure, and lower side is
Button-shaped structure, it is simple to install；
Further, the embossed technology modelled after an antique described in described step (4), roll-in carries out dyestuff covering with paint to running roller simultaneously,
The rag degree of depth 1～5mm of running roller, pressure limit is 1～10MPa, and transmission speed is 5～20m/s, at this roll-in speed and pressure
Under, and combine the structures such as described stress groove, the balance of upper and lower whole plate stress is effectively ensured, significantly improves the stability of plate.
Further, described dyestuff is aqueous color essence, aqueous color paste, ink etc..
Further, it is to first pass through priming paint to cover with paint, lacquer, colour wash, etc. that surface described in described step (5) processes, and quantity for spray is 100～200g/
m2, then it is dried cured, then use the abrasive band of Heterotype sander 280～320 mesh, surface and dual-side are carried out sand
Light, last finish paint top finishing, and through the infrared levelling that excess temperature is 30～90 DEG C, 3～9m length, naturally dry；By above-mentioned
The stage covered with paint, lacquer, colour wash, etc. by the priming paint that surface processes, and effectively prevents enamelled coating from ftractureing, and uses the careful grinding in abrasive band of 280～320 mesh, improves paint film
Adhesive force；Make paint film reach preferably richness and vividness and improve the antiseptic power in plate face, increase lacquer painting stability.
Further, described priming paint is UV paint, and described finish paint is PU paint.
The present invention having the beneficial effects that compared to existing technology:
The solid wood skirting modelled after an antique that the present invention makes, Technology is consummate, overcomes wood-based plate skirting, wood-plastic board skirt
The shortcoming that the changeablenesss such as line, mechanical strength are low, surface after the paint finishing PROCESS FOR TREATMENT in " PU face at the bottom of UV ", have antibacterial,
The advantage such as moistureproof, non-foaming, roll-in rag processing procedure also improves the mechanical property of solid wood skirting, reduces its cracking and becomes
Shape.Use water color ink, UV and PU to paint equal health environment-friendly, Technology can not only be optimized, more can improve product glossiness,
Wearability and hardness of paint film.Functional groove is set at skirting surface configuration stress slow release groove and the back side, improves skirt
Line stabilization, reduces the deformation in producing and using.Solid wood skirting modelled after an antique can be greatly improved fast growing wood and discarded rotary-cut wood
The solid wood value of core, the not only beautifying and decorating indoor global design of its antique effect and protection body of wall, and there is production
Low cost, functional and practical, the advantage of good stability, high-efficiency environment friendly.
With reference to national forestry industry standard LY/T1987-2011 " Wood skirting line ", solid wood skirting modelled after an antique is carried out physics and chemistry
Performance evaluation, finger face dipping and stripping length is respectively less than 1/3, and paint film adhesion is preferable, and burst size of methanal reaches E0 level.
Detailed description of the invention
The following stated is only some embodiments of the present invention, is not defined the scope of the present invention.
Embodiment 1
A kind of manufacture method of solid wood skirting modelled after an antique
(1) it is dried: after rotary-cut, discarded reel is combined mode by air dry and kiln drying, by sheet material moisture control 10%
Left and right；
(2) sawn timber and finger: dried reel, through multiple blade saw, plate joggling apparatus, automatic comb and finger joint machine, makes sheet material,
And saw the skirting size of specification processed；
(3) milling molding: the surface stress well width described in milling formative stage is 0.1cm, the degree of depth is 0.3cm；The back side
The width of symmetry groove is 1cm, and the degree of depth is 0.1cm.Described skirting upper side edge is set as the stair-stepping arcuate structure of two-layer, often
One layer of step-thickness is the 1/2 of skirting thickness.
(4) embossing modelled after an antique: roll-in carries out dyestuff covering with paint to running roller simultaneously, rag degree of depth 1mm of running roller, pressure is 1MPa,
Transmission speed is 5m/s,
(5) surface processes: it is to first pass through priming paint to cover with paint, lacquer, colour wash, etc. that surface processes, and quantity for spray is 100g/m2, then carry out UV dry solidification
Process, then use the abrasive band of Heterotype sander 300 mesh, surface and dual-side are carried out sanding, last PU finish paint top finishing,
And be 30 DEG C, the infrared levelling of 3m through excess temperature, naturally dry.
Through test, in embodiment 1, after rotary-cut, discarded reel is processed into solid wood skirting, and superficial makings highlights, and has
The strongest third dimension.Compared to the solid wood skirting of unslotted, surface configuration stress slow release groove, the back side are provided with functional recessed
The solid wood skirting product modelled after an antique of groove, processing characteristics is more excellent, is difficult to craze and transfiguration, and stability improves more apparent, wherein angularity
Reducing about 23%, after heating, width and thickness direction size changing rate reduce by 16%, about 30% respectively.Surface is coated with through paint
After decorations process, having good moisture effect, and antibacterial, health environment-friendly, the glossiness of product is more uniform, and dipping and stripping, paint film are hard
Degree and wearability all can reach industry standard, and burst size of methanal reaches E0 level.
Embodiment 2
The method of discarded reel system solid wood modelled after an antique skirting after rotary-cut:
(1) it is dried: after rotary-cut, discarded reel is combined mode by air dry and kiln drying, by sheet material moisture control 10%
Left and right；
(2) sawn timber and finger: dried reel, through multiple blade saw, plate joggling apparatus, automatic comb and finger joint machine, makes sheet material,
And saw the skirting size of specification processed；
(3) milling molding: milling molding phase table face stress well width is 0.6cm, and the degree of depth is 0.2cm；Back side symmetry
The width of function groove is 0.5cm, and the degree of depth is 0.2cm；Each layer of step-thickness of upper side is the 1/2 of skirting thickness.
(4) embossing modelled after an antique:, rag degree of depth 2mm of running roller, roll-in carries out water color ink covering with paint to running roller simultaneously, running roller
Rag degree of depth 4mm, pressure limit is 6MPa, and transmission speed is 12m/s.
(5) surface processes: first passing through UV priming paint and cover with paint, lacquer, colour wash, etc., quantity for spray is 130g/m2, then carries out UV dry solidification process, so
The abrasive band of rear employing Heterotype sander 280 mesh, carries out sanding, last PU finish paint top finishing, and passes through surface and dual-side
Temperature is 40 DEG C, the infrared levelling of 6m length, naturally dries.
Through test, in embodiment 2, after rotary-cut, discarded reel is processed into solid wood skirting, and superficial makings highlights, and has
The strongest third dimension.Compared to the solid wood skirting of unslotted, surface configuration stress slow release groove, the back side are provided with functional recessed
The solid wood skirting product modelled after an antique of groove, processing characteristics is more excellent, is difficult to craze and transfiguration, and stability improves more apparent, wherein angularity
Reducing about 25%, after heating, width and thickness direction size changing rate reduce by 17%, about 31% respectively.Surface is coated with through paint
After decorations process, having good moisture effect, and antibacterial, health environment-friendly, the glossiness of product is more uniform, and dipping and stripping, paint film are hard
Degree and wearability all can reach industry standard, and burst size of methanal reaches E0 level.
Embodiment 3
The method of fast-growing path eucalyptus globulus Wooden pseudo-classic solid wood skirting:
(1) saw lumber and being dried: specification square bar made by fast-growing path Eucalyptus saw, then combined mode by air dry and kiln drying,
By sheet material moisture control about 10%；
(2) sawn timber and finger: dried square bar through multiple blade saw, automatic comb, finger joint machine and, plate joggling apparatus, make sheet material,
And the skirting size of prepared specification；
(3) milling molding: milling molding phase table face stress well width is 0.5cm, and the degree of depth is 0.3cm；Back side symmetry
The width of function groove is 0.6cm, and the degree of depth is 0.3cm；Each layer of step-thickness of upper side is the 1/2 of skirting thickness.
(4) embossing modelled after an antique:, rag degree of depth 1mm of running roller, roll-in carries out water color ink covering with paint to running roller simultaneously, running roller
Rag degree of depth 4mm, pressure limit is 6MPa, and transmission speed is 12m/s.
(5) surface processes: first passing through UV priming paint and cover with paint, lacquer, colour wash, etc., quantity for spray is 150g/m2, then carries out UV dry solidification process, so
The abrasive band of rear employing Heterotype sander 320 mesh, carries out sanding, last PU finish paint top finishing, and passes through surface and dual-side
Temperature is 45 DEG C, the infrared levelling of 8m length, naturally dries.
Through test, in embodiment 3, fast-growing path Eucalyptus is processed into solid wood skirting, and superficial makings highlights, and product is lived
Joint is the warmest, great aesthetic feeling and third dimension.Compared to the solid wood skirting of unslotted, surface configuration stress slow release
Groove, the back side are provided with the solid wood skirting product modelled after an antique of functional groove, and processing characteristics is more excellent, is difficult to craze and transfiguration, stability
Improving more apparent, wherein angularity reduces about 18%, after heating width and thickness direction size changing rate reduce by 27% respectively,
About 42%., after paint finishing processes, there are good moisture effect, and antibacterial, health environment-friendly in surface, and the glossiness of product is relatively
Uniformly, hardness of paint film and wearability all can reach industry standard, and burst size of methanal reaches E0 level.
Embodiment 4
A kind of manufacture method of solid wood skirting modelled after an antique
(1) it is dried: after rotary-cut, discarded reel is combined mode by air dry and kiln drying, by sheet material moisture control 10%
Left and right；
(2) sawn timber and finger: dried reel, through multiple blade saw, plate joggling apparatus, automatic comb and finger joint machine, makes sheet material,
And saw the skirting size of specification processed；
(3) milling molding: the surface stress well width described in milling formative stage is 2cm, the degree of depth is 0.5cm；The back side pair
The width of property groove is called 2cm, and the degree of depth is 0.5cm.Described skirting upper side edge is set as the stair-stepping arcuate structure of two-layer, each
Layer step-thickness is the 1/2 of skirting thickness.
(4) embossing modelled after an antique: roll-in carries out dyestuff covering with paint to running roller simultaneously, rag degree of depth 5mm of running roller, pressure is 10MPa,
Transmission speed is 20m/s,
(5) surface processes: it is to first pass through priming paint to cover with paint, lacquer, colour wash, etc. that surface processes, and quantity for spray is 200g/m2, then carry out UV dry solidification
Process, then use the abrasive band of Heterotype sander 320 mesh, surface and dual-side are carried out sanding, last PU finish paint top finishing,
And be 90 DEG C, the infrared levelling of 9m through excess temperature, naturally dry.
Through test, in embodiment 4, after rotary-cut, discarded reel is processed into solid wood skirting, and superficial makings highlights, and has
The strongest third dimension.Compared to the solid wood skirting of unslotted, surface configuration stress slow release groove, the back side are provided with functional recessed
The solid wood skirting product modelled after an antique of groove, processing characteristics is more excellent, is difficult to craze and transfiguration, and stability improves more apparent, wherein angularity
Reducing about 22%, after heating, width and thickness direction size changing rate reduce by 15%, about 29% respectively.Surface is coated with through paint
After decorations process, having good moisture effect, and antibacterial, health environment-friendly, the glossiness of product is more uniform, and dipping and stripping, paint film are hard
Degree and wearability all can reach industry standard, and burst size of methanal reaches E0 level.
Described above is only explanation of the invention so that those of ordinary skill in the art's can completely implements we
Case, but be not limitation of the present invention, those skilled in the art can be as required to this reality after reading this specification
Executing example and make the amendment not having creative contribution, these are all the most creative amendments.But as long as the right in the present invention
All protected by Patent Law in claimed range.
Claims (8)
1. the manufacture method of a solid wood skirting modelled after an antique, it is characterised in that the method comprises the steps:
(1) saw lumber and being dried: fast growing wood is made sheet material, and the drying mode combined by air dry and kiln drying is aqueous by sheet material
Rate controls 8～12%；
(2) sawn timber and finger: prepared sheet material is processed through multiple blade saw, automatic comb and finger joint machine, obtains the skirting chi of specification
Very little；
(3) milling molding: by four side moulder simultaneous manufacturing, surface mills out a stress slow release groove, and the back side is provided with symmetric
Function groove；
(4) embossing modelled after an antique: extrude grain pattern in skirting surface roll；
(5) surface processes: the semi-finished product skirting prepared after step (4) covers with paint, lacquer, colour wash, etc. opposite sex sanding paint finish through priming paint
After process, obtain solid wood skirting finished product.
The manufacture method of a kind of solid wood skirting modelled after an antique the most according to claim 1, it is characterised in that described step (1)
In described air dry and the drying mode that combines of kiln drying, first use air dry mode by sheet material moisture control to 41～52%,
Then use kiln drying mode again by described sheet material moisture control to 8～12%.
Method the most according to claim 1, it is characterised in that described timber is useless after fast-growing Eucalyptus, Lignum seu Ramulus Cunninghamiae Lanceolatae or rotary-cut
Abandon reel.
Method the most according to claim 1, it is characterised in that surface described in milling formative stage in described step (3)
Stress well width is 0.1～2cm, and the degree of depth is 0.2～0.5cm；The width of back side symmetry groove is 0.5～2cm, and the degree of depth is
0.1～0.5cm；Meanwhile, described skirting upper side edge is set as stair-stepping arcuate structure, and lower side is button-shaped structure, it is simple to
Install.
Method the most according to claim 1, it is characterised in that the embossed technology modelled after an antique described in described step (4), roll-in
Running roller is carried out dyestuff covering with paint simultaneously, the rag degree of depth 1～5mm of running roller, pressure limit is 1～10MPa, transmission speed be 5～
20m/s。
Method the most according to claim 5, it is characterised in that described dyestuff is aqueous color essence, aqueous color paste, ink
Deng.
Method the most according to claim 1, it is characterised in that it is to first pass through the end that surface described in described step (5) processes
Paint is covered with paint, lacquer, colour wash, etc., and quantity for spray is 100～200g/m2, then it is dried cured, then use Heterotype sander 280～320 purpose
Abrasive band, carries out sanding to surface and dual-side, last finish paint top finishing, and through excess temperature be the red of 30～90 DEG C, 3～9m length
Outer levelling, dries naturally.
Method the most according to claim 7, it is characterised in that priming paint is UV paint, finish paint is PU paint.