CN106481052A - Plane multi-layer solid wood composite floor modelled after an antique and its manufacture method - Google Patents
Plane multi-layer solid wood composite floor modelled after an antique and its manufacture method Download PDFInfo
- Publication number
- CN106481052A CN106481052A CN201611175553.6A CN201611175553A CN106481052A CN 106481052 A CN106481052 A CN 106481052A CN 201611175553 A CN201611175553 A CN 201611175553A CN 106481052 A CN106481052 A CN 106481052A
- Authority
- CN
- China
- Prior art keywords
- layer
- antique
- solid wood
- paint
- wood composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plane multi-layer solid wood composite floor modelled after an antique, belong to decoration material field, including multi-layer substrate layer, decoration veneer layer and skin of paint, described multi-layer substrate layer is with the crisscross plywood overlaying of fast growing wood veneer, the vertical and horizontal both sides of described plywood are respectively provided with tenon and the groove of adaptation, it is the thick natural famous and precious decoration veneer layer of 0.6 2.0mm that described plywood upper surface posts a layer thickness, described decoration veneer layer upper roller scribbles the UV solidification skin of paint of layer of transparent, described decoration veneer layer surface is provided perpendicular to the band of floor length direction arrangement, described band is the sand trace that the depth that manual amendment chromatography are processed after mechanical grinding is 0.1 0.2mm.The invention also discloses a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique.There is plate face antique effect enrich, solid layer feeling is strong, environmental protection, with low cost, the advantage of suitable mechanization production, when disposing furniture, do not need the soft feet of additional pads.
Description
Technical field
The present invention relates to solid wooden floor board, the multi-layer solid wood composite floor modelled after an antique particularly to a kind of plane and its manufacturer
Method, belongs to decoration material field.
Background technology
In recent years, on market, the building and ornament materials of style modelled after an antique are increasingly pursued, and floor is modelled after an antique in the market
Effect is also perfect not to the utmost.
The style modelled after an antique of ancient imitation floor board currently on the market mainly by mechanical external force or is manually made in floor surface
Rough effect, during use, laying furniture needs to pad soft feet, in-convenience in use.Therefore, develop a kind of plane
The multi-layer solid wood composite floor modelled after an antique of type can retain solution while style modelled after an antique to be laid needs during furniture to pad soft feet
Problem, may also adapt to mechanization production.
Content of the invention
The defect existing for prior art, it is an object of the invention to disclose a kind of plane multi-layer solid wood modelled after an antique to be combined ground
Plate, including multi-layer substrate layer, decoration veneer layer and skin of paint, described multi-layer substrate layer is with certain thickness fast growing wood veneer
The crisscross plywood overlaying, the vertical and horizontal both sides of described plywood are respectively provided with tenon and the groove of adaptation,
Described plywood upper surface posts one layer of natural famous and precious decoration veneer layer, and the thickness of described decoration veneer layer is 0.6-2.0mm, special
Not, described decoration veneer layer surface is provided perpendicular to the band of floor length direction arrangement, and described band is with machinery
Polishing, manual repair, again chromatography process form.
Specifically, described multi-layer substrate layer is with the crisscross gluing overlaying of certain thickness fast growing wood veneer
Plate, sticks agent bonding, glue-spread 140-160 g/m using modified urea-formaldehyde resin glue during overlaying2, with the pressure precompressed of 12MPa
30min makes glue precuring, after the completion of precompressed under the conditions of 12-14MPa, temperature 115-125 DEG C hot pressing 200s, by overlay
Workpiece is placed in 25 DEG C of temperature, the balance cylinder balance 48h of air moisture content 6-13%, then uses 50# belt sanding wood on sander
Epidermis face forms sand trace, and in 0.1-0.2mm, it is vertical, so that feedstock direction is split into the length direction after lath to sand trace depth with floor
Afterwards with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；Tongue and groove production line is passed through on the vertical and horizontal both sides of plywood respectively
Output tenon and groove；Subsequently manual amendment, makes sanding trace more equalize with the imperfect place of instrument finishing machine device sanding, protects simultaneously
Card plate face is smooth, facilitates subsequent handling to produce；Black water coating is covered with paint, lacquer, colour wash, etc., in coating, the volume ratio according to 15-20% adds during chromatography
Enter the permeance property that water strengthens water paint, described black water coating is the black color of PPG aqueous priming paint+10% mass parts
Essence, the sponge roller coating with hardness for 15-20 °, coating weight is 15-20 g/m2, spontaneously dry 24h after infrared drying；Subsequently
Carry out sanding process it is therefore an objective to the mill base of plate face is removed, be retained in the mill base in sand trace groove, form band, strengthen plate face and stand
Body-sensing and stereovision；The last UV solidification skin of paint transparent in decoration veneer layer surface spraying, described transparent UV solidified oil
Enamelled coating roller coat 4-8 time in the way of multiple roller coat, the total coating weight of control is 140-150 g/m2, coating process instantaneous solidification, be in
Transparence obtains final product plane multi-layer solid wood composite floor modelled after an antique.
The beneficial effects of the present invention is：Provide a kind of plane multi-layer solid wood composite floor modelled after an antique, there is plate face modelled after an antique
Effect is enriched, and solid layer feeling is strong, environmental protection, with low cost, the advantage of suitable mechanization production, does not need when disposing furniture
The soft feet of additional pads.
Brief description
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, embodiment will be described below
In required use accompanying drawing be briefly described it should be apparent that, drawings in the following description be only the present invention some
Embodiment, for those of ordinary skill in the art, on the premise of not paying creative work, can also be attached according to these
Figure and related text description obtain other similar or equivalent technical schemes.In the accompanying drawings：
Fig. 1 is the perspective view of plane disclosed by the invention multi-layer solid wood composite floor modelled after an antique.
Specific embodiment
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, the present invention is now with reference to showing
The accompanying drawing going out the embodiment of the present invention is described more fully hereinafter.However, the present invention can be embodied simultaneously with a lot of multi-forms
And should not be construed as being limited to specific embodiment set forth herein.On the contrary, these embodiments are supplied to people in the art
Member understands technical scheme.
Embodiment 1
Referring to the drawings 1, disclose a kind of embodiment of plane multi-layer solid wood composite floor modelled after an antique, including multi-layer substrate layer 1, decoration
Veneer layer 2 and skin of paint 3, described multi-layer substrate layer is with the crisscross glue overlaying of certain thickness fast growing wood veneer
Plywood, described plywood is respectively provided with tenon 4 and the groove 5 of adaptation, described plywood upper surface patch on vertical and horizontal both sides
There is one layer of birch decoration veneer layer, the thickness of described decoration veneer layer is 0.6mm, especially, described decoration veneer layer surface sets
It is equipped with the band 6 perpendicular to floor length direction arrangement, described band is with mechanical grinding, manual repair, again chromatography process
Form, band depth 0.1mm.In decoration veneer after forming band, the transparent UV solidification paint of roller coat, is obtained flat after solidification
Face multi-layer solid wood composite floor modelled after an antique.
Embodiment 2
Referring to the drawings 1, disclose a kind of embodiment of plane multi-layer solid wood composite floor modelled after an antique, including multi-layer substrate layer 1, decoration
Veneer layer 2 and skin of paint 3, described multi-layer substrate layer is with the crisscross glue overlaying of certain thickness fast growing wood veneer
Plywood, described plywood is respectively provided with tenon 4 and the groove 5 of adaptation, described plywood upper surface patch on vertical and horizontal both sides
There is one layer of Xylosmae japonici decoration veneer layer, the thickness of described decoration veneer layer is 1.0mm, especially, described decoration veneer layer surface sets
It is equipped with the band 6 perpendicular to floor length direction arrangement, described band is with mechanical grinding, manual repair, again chromatography process
Form, band depth 0.15mm.In decoration veneer after forming band, the transparent UV solidification paint of roller coat, is obtained flat after solidification
Face multi-layer solid wood composite floor modelled after an antique.
Embodiment 3
Referring to the drawings 1, disclose a kind of embodiment of plane multi-layer solid wood composite floor modelled after an antique, including multi-layer substrate layer 1, decoration
Veneer layer 2 and skin of paint 3, described multi-layer substrate layer is with the crisscross glue overlaying of certain thickness fast growing wood veneer
Plywood, described plywood is respectively provided with tenon 4 and the groove 5 of adaptation, described plywood upper surface patch on vertical and horizontal both sides
There is one layer of Xylosmae japonici decoration veneer layer, the thickness of described decoration veneer layer is 1.5mm, especially, described decoration veneer layer surface sets
It is equipped with the band 6 perpendicular to floor length direction arrangement, described band is with mechanical grinding, manual repair, again chromatography process
Form, band depth 0.2mm.In decoration veneer after forming band, the transparent UV solidification paint of roller coat, is obtained flat after solidification
Face multi-layer solid wood composite floor modelled after an antique.
Embodiment 4
Referring to the drawings 1, disclose a kind of embodiment of plane multi-layer solid wood composite floor modelled after an antique, including multi-layer substrate layer 1, decoration
Veneer layer 2 and skin of paint 3, described multi-layer substrate layer is with the crisscross glue overlaying of certain thickness fast growing wood veneer
Plywood, described plywood is respectively provided with tenon 4 and the groove 5 of adaptation, described plywood upper surface patch on vertical and horizontal both sides
There is one layer of Xylosmae japonici decoration veneer layer, the thickness of described decoration veneer layer is 2.0mm, especially, described decoration veneer layer surface sets
It is equipped with the band 6 perpendicular to floor length direction arrangement, described band is with mechanical grinding, manual repair, again chromatography process
Form, band depth 0.18mm.In decoration veneer after forming band, the transparent UV solidification paint of roller coat, is obtained flat after solidification
Face multi-layer solid wood composite floor modelled after an antique.
Embodiment 5
Present embodiment discloses a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique, multi-layer substrate layer is with necessarily thick
The crisscross plywood overlaying of fast growing wood veneer of degree, sticks agent bonding using modified urea-formaldehyde resin glue during overlaying,
Glue-spread 140 g/m2, glue precuring is made with the pressure precompressed 30min of 12MPa, in 12MPa after the completion of precompressed, 115 DEG C of temperature
Under the conditions of hot pressing 200s, the workpiece overlaying is placed at 21 DEG C of temperature, balance cylinder the balance 48h, Ran Hou of relative humidity 38%
50# belt sanding veneer surface is used to form sand trace on sander, sand trace depth is split into lath on 0.1mm, feedstock direction and floor
Rear length direction is vertical, then with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；The vertical and horizontal two of plywood
Tenon and groove are outputed by tongue and groove production line respectively in side；Subsequently manual amendment, is made with the imperfect place of instrument finishing machine device sanding
Sanding trace more equalizes, and ensures that plate face is smooth simultaneously, facilitates subsequent handling to produce；Black water coating, coating is covered with paint, lacquer, colour wash, etc. during chromatography
According to 15% volume ratio add water strengthen water paint permeance property, described black water coating is PPG aqueous priming paint
The black color essence of+10% mass parts, the sponge roller coating being 15 with hardness, coating weight is 15g/m2, naturally do after infrared drying
Dry 24h；Subsequently carry out sanding process it is therefore an objective to the mill base of plate face is removed, stay the mill base in sand trace groove, formed horizontal
Stricture of vagina, strengthens plate face third dimension and stereovision；The last UV solidification skin of paint transparent in decoration veneer layer surface spraying, described is saturating
Bright UV solidification skin of paint roller coat 4 times in the way of multiple roller coat, the total coating weight of control is 140 g/m2, coating process moment is admittedly
Change, transparent shape obtains final product plane multi-layer solid wood composite floor modelled after an antique.
Embodiment 6
Present embodiment discloses a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique, multi-layer substrate layer is with necessarily thick
The crisscross plywood overlaying of fast growing wood veneer of degree, sticks agent bonding using modified urea-formaldehyde resin glue during overlaying,
Glue-spread 150 g/m2, glue precuring is made with the pressure precompressed 30min of 12MPa, in 13MPa after the completion of precompressed, 120 DEG C of temperature
Under the conditions of hot pressing 200s, the workpiece overlaying is placed at 20 DEG C of temperature, balance cylinder the balance 48h, Ran Hou of relative humidity 43%
50# belt sanding veneer surface is used to form sand trace on sander, sand trace depth is split into lath on 0.15mm, feedstock direction and floor
Rear length direction is vertical, then with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；The vertical and horizontal two of plywood
Tenon and groove are outputed by tongue and groove production line respectively in side；Subsequently manual amendment, is made with the imperfect place of instrument finishing machine device sanding
Sanding trace more equalizes, and ensures that plate face is smooth simultaneously, facilitates subsequent handling to produce；Black water coating, coating is covered with paint, lacquer, colour wash, etc. during chromatography
According to 18% volume ratio add water strengthen water paint permeance property, described black water coating is PPG aqueous priming paint
The black color essence of+10% mass parts, the sponge roller coating being 18 ° with hardness, coating weight is 18g/m2, natural after infrared drying
24h is dried；Subsequently carry out sanding process it is therefore an objective to the mill base of plate face is removed, stay the mill base in sand trace groove, formed horizontal
Stricture of vagina, strengthens plate face third dimension and stereovision；The last UV solidification skin of paint transparent in decoration veneer layer surface spraying, described is saturating
Bright UV solidification skin of paint roller coat 6 times in the way of multiple roller coat, the total coating weight of control is 145 g/m2, coating process moment is admittedly
Change, transparent shape obtains final product plane multi-layer solid wood composite floor modelled after an antique.
Embodiment 7
Present embodiment discloses a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique, multi-layer substrate layer is with necessarily thick
The crisscross plywood overlaying of fast growing wood veneer of degree, sticks agent bonding using modified urea-formaldehyde resin glue during overlaying,
Glue-spread 160 g/m2, glue precuring is made with the pressure precompressed 30min of 12MPa, in 14MPa after the completion of precompressed, 125 DEG C of temperature
Under the conditions of hot pressing 200s, the workpiece overlaying is placed at 23 DEG C of temperature, balance cylinder the balance 48h, Ran Hou of relative humidity 48%
50# belt sanding veneer surface is used to form sand trace on sander, sand trace depth is split into lath on 0.2mm, feedstock direction and floor
Rear length direction is vertical, then with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；The vertical and horizontal two of plywood
Tenon and groove are outputed by tongue and groove production line respectively in side；Subsequently manual amendment, is made with the imperfect place of instrument finishing machine device sanding
Sanding trace more equalizes, and ensures that plate face is smooth simultaneously, facilitates subsequent handling to produce；Black water coating, coating is covered with paint, lacquer, colour wash, etc. during chromatography
According to 20% volume ratio add water strengthen water paint permeance property, described black water coating is PPG aqueous priming paint
The black color essence of+10% mass parts, the sponge roller coating being 20 ° with hardness, coating weight is 20 g/m2, natural after infrared drying
24h is dried；Subsequently carry out sanding process it is therefore an objective to the mill base of plate face is removed, stay the mill base in sand trace groove, formed horizontal
Stricture of vagina, strengthens plate face third dimension and stereovision；The last UV solidification skin of paint transparent in decoration veneer layer surface spraying, described is saturating
Bright UV solidification skin of paint roller coat 8 times in the way of multiple roller coat, the total coating weight of control is 150 g/m2, coating process moment is admittedly
Change, transparent shape obtains final product plane multi-layer solid wood composite floor modelled after an antique.
Embodiment 8
Present embodiment discloses a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique, multi-layer substrate layer is with necessarily thick
The crisscross plywood overlaying of fast growing wood veneer of degree, sticks agent bonding using modified urea-formaldehyde resin glue during overlaying,
Glue-spread 155 g/m2, glue precuring is made with the pressure precompressed 30min of 12MPa, in 12MPa after the completion of precompressed, 118 DEG C of temperature
Under the conditions of hot pressing 200s, the workpiece overlaying is placed at 25 DEG C of temperature, balance cylinder the balance 48h, Ran Hou of relative humidity 45%
50# belt sanding veneer surface is used to form sand trace on sander, sand trace depth is split into lath on 0.18mm, feedstock direction and floor
Rear length direction is vertical, then with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；The vertical and horizontal two of plywood
Tenon and groove are outputed by tongue and groove production line respectively in side；Subsequently manual amendment, is made with the imperfect place of instrument finishing machine device sanding
Sanding trace more equalizes, and ensures that plate face is smooth simultaneously, facilitates subsequent handling to produce；Black water coating, coating is covered with paint, lacquer, colour wash, etc. during chromatography
According to 17% volume ratio add water strengthen water paint permeance property, described black water coating is PPG aqueous priming paint
The black color essence of+10% mass parts, the sponge roller coating being 20 with hardness, coating weight is 20 g/m2, natural after infrared drying
24h is dried；Subsequently carry out sanding process it is therefore an objective to the mill base of plate face is removed, stay the mill base in sand trace groove, formed horizontal
Stricture of vagina, strengthens plate face third dimension and stereovision；The last UV solidification skin of paint transparent in decoration veneer layer surface spraying, described is saturating
Bright UV solidification skin of paint roller coat 6 times in the way of multiple roller coat, the total coating weight of control is 145 g/m2, coating process moment is admittedly
Change, transparent shape obtains final product plane multi-layer solid wood composite floor modelled after an antique.
Embodiment 9
Present embodiment discloses a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique, multi-layer substrate layer is with necessarily thick
The crisscross plywood overlaying of fast growing wood veneer of degree, sticks agent bonding using modified urea-formaldehyde resin glue during overlaying,
Glue-spread 145 g/m2, glue precuring is made with the pressure precompressed 30min of 12MPa, in 13MPa after the completion of precompressed, 115 DEG C of temperature
Under the conditions of hot pressing 200s, the workpiece overlaying is placed at 25 DEG C of temperature, balance cylinder the balance 48h, Ran Hou of relative humidity 40%
50# belt sanding veneer surface is used to form sand trace on sander, sand trace depth is split into lath on 0.16mm, feedstock direction and floor
Rear length direction is vertical, then with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；The vertical and horizontal two of plywood
Tenon and groove are outputed by tongue and groove production line respectively in side；Subsequently manual amendment, is made with the imperfect place of instrument finishing machine device sanding
Sanding trace more equalizes, and ensures that plate face is smooth simultaneously, facilitates subsequent handling to produce；Black water coating, coating is covered with paint, lacquer, colour wash, etc. during chromatography
According to 18% volume ratio add water strengthen water paint permeance property, described black water coating is PPG aqueous priming paint
The black color essence of+10% mass parts, the sponge roller coating being 15 with hardness, coating weight is 17g/m2, naturally do after infrared drying
Dry 24h；Subsequently carry out sanding process it is therefore an objective to the mill base of plate face is removed, stay the mill base in sand trace groove, formed horizontal
Stricture of vagina, strengthens plate face third dimension and stereovision；The last UV solidification skin of paint transparent in decoration veneer layer surface spraying, described is saturating
Bright UV solidification skin of paint roller coat 8 times in the way of multiple roller coat, the total coating weight of control is 150 g/m2, coating process moment is admittedly
Change, transparent shape obtains final product plane multi-layer solid wood composite floor modelled after an antique.
Unless otherwise defined, term used herein above（Comprise scientific and technical terminology）Should be construed to have as belonging to the present invention
The same meaning that those skilled in the art are commonly understood by.It will also be understood that term used herein above should be explained
For having the consistent meaning of the meaning in the content of this specification and correlation technique with them, and should be not idealize
Or excessive form explanation, unless expressly so limited here.
Although here of the present invention is described with reference to the specific aspect of the present invention, feature and exemplary embodiment, should
When being understood by, the purposes of the present invention does not therefore suffer from limiting, but extend and cover numerous other changes, modification with
And alternate embodiment, as implied giving those skilled in the art in the invention based on disclosure herein.Correspondingly, all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvement done etc., should be included in the guarantor of the present invention
Within the scope of shield.
Claims (7)
1. a kind of plane multi-layer solid wood composite floor modelled after an antique, including multi-layer substrate layer, decoration veneer layer and skin of paint, described multilamellar
Substrate layer is with the crisscross plywood overlaying of fast growing wood veneer, described plywood upper surface post one layer natural famous and precious
Decoration veneer layer, described decoration veneer layer upper roller scribble layer of transparent UV solidification skin of paint it is characterised in that：Described decoration
The setting of veneer layer surface is perpendicular to the band of floor length direction arrangement.
2. plane according to claim 1 multi-layer solid wood composite floor modelled after an antique it is characterised in that：Described band is through machine
After tool polishing, the depth of manual amendment chromatography process is the sand trace of 0.1-0.2mm.
3. plane according to claim 1 multi-layer solid wood composite floor modelled after an antique it is characterised in that：Described natural famous and precious dress
Decorations veneer layer is the birch that thickness is 0.6-2.0mm.
4. plane according to claim 1 multi-layer solid wood composite floor modelled after an antique it is characterised in that：Described plywood vertical
To the tenon and the groove that are respectively provided with adaptation with horizontal both sides.
5. a kind of manufacture method of plane multi-layer solid wood composite floor modelled after an antique, comprises the following steps：
A) overlay, sticking agent with modified urea-formaldehyde resin glue makes decoration veneer layer glued with multi-layer substrate layer, and glue-spread is 140-
160g/m2, under 12MPa pressure, precompressed 30min makes glue precuring, then in pressure 12-14MPa, temperature 115-125 DEG C
Under the conditions of hot pressing 200s；
B) health preserving, in temperature 20-25 DEG C, the balance cylinder balance 48h of relative humidity 38% 45%；
C) polish, decoration veneer surface formation depth is polished for the thick sand trace of 0.1-0.2mm on sander with 50# abrasive band, enters
It is vertical that material direction is split into the length direction after lath with floor；
D) sawing sheet, with multiple blade saw sawing sheet and back side sanding is determined thickness and made plain plate；
E) molding, outputs tenon and groove by tongue and groove production line respectively on the vertical and horizontal both sides of plywood；
F) repair, manually use instrument finishing machine device sanding to decorate the imperfect place of veneer surface, so that sanding trace is equalized, plate face is smooth；
Water paint is coated on decoration veneer surface with the sponge roller for 15-20 ° for the hardness by g) chromatography, and coating weight is 15-
20g/m2, carry out sanding process through infrared drying and after spontaneously drying 24h, the mill base of plate face removed, retain in sand trace groove
Mill base forms band；
H) roller coat, in the decoration veneer after forming band, the transparent UV solidification paint of roller coat, is obtained plane modelled after an antique many after solidification
Layer solid wooden compound floor.
6. plane according to claim 5 multi-layer solid wood composite floor modelled after an antique manufacture method it is characterised in that：Described
Water paint is the black color essence composition adding 10% mass parts in PPG aqueous priming paint, and it is dilute to add water according to the volume ratio of 15-20%
Release the permeance property strengthening water paint.
7. plane according to claim 5 multi-layer solid wood composite floor modelled after an antique manufacture method it is characterised in that：Described
Roller coat is roller coat 4-8 time in the way of multiple roller coat, and controls total coating weight that UV solidification is painted to be 140-150 g/m2.