CN109602108A - A kind of viscous lining method of sewing of collar bottom wool fabric - Google Patents
A kind of viscous lining method of sewing of collar bottom wool fabric Download PDFInfo
- Publication number
- CN109602108A CN109602108A CN201910074486.6A CN201910074486A CN109602108A CN 109602108 A CN109602108 A CN 109602108A CN 201910074486 A CN201910074486 A CN 201910074486A CN 109602108 A CN109602108 A CN 109602108A
- Authority
- CN
- China
- Prior art keywords
- sewing
- viscous lining
- viscous
- base fabric
- collar bottom
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of viscous lining method of sewing of collar bottom wool fabric, include the following steps: S1: carrying out the preparation of viscous lining, base fabric manufacture, S2: baking processing is carried out to the base fabric that step S1 is obtained, S3: the sewing of viscous lining and collar bottom wool fabric is carried out, S4: collar bottom wool fabric is rotated into 180 degree by axis of the first sewing connection on the basis of above-mentioned steps at this time, it is steady to the side ironing of Nian Chen lower layer that part then will be stitched with flatiron, S5: first viscous lining layer is fixed on collar bottom wool fabric with flat-seam gimmick on the basis of step S4, the viscous lining method of sewing step of the collar bottom wool fabric is clear, time and its efficiency of raising of manual person can greatly be saved by operating, the independent production of viscous lining can ensure the high-quality of viscous lining simultaneously, to facilitate subsequent processing.
Description
Technical field
The present invention relates to garment technology field more particularly to a kind of viscous lining method of sewing of collar bottom wool fabric.
Background technique
Viscous lining is a kind of lining for being coated with hot melt adhesive, is that fabrics makes one of commonly used auxiliary material.Viscous laying-in crosses heating
Pressing is attached to the back side of cloth, can be embodied by adding viscous lining when cloth needs to express well-pressed, thickness, or
Cloth is too soft smooth when being difficult to operate, and adding viscous lining can make cloth become well-behaved along obedient, often needs in clothes processing
It to sew to collar bottom wool fabric and viscous lining, traditional bind is too complicated, and the clothing that sewing finishes easily occurs
The case where taking out stitches.
Summary of the invention
The invention proposes a kind of viscous lining method of sewing of collar bottom wool fabric, to solve the problems mentioned in the above background technology.
The invention proposes a kind of viscous lining method of sewing of collar bottom wool fabric, include the following steps:
S1: carrying out the preparation of viscous lining, and base fabric manufacture, will using 50D low elastic polyester filament as weft yarn using 50D low elastic polyester filament as warp thread
Warp thread and weft yarn form base fabric after air-jet loom weaving, then preliminary drying preshrunk processing are carried out to base fabric, then in high temperature and pressure
The preshrunk setting treatment that relaxes is carried out to base fabric under the control of overflow machine, carries out padding processing again after being disposed, by padding
Resin liquid arranges base fabric using the technique of second dipping and rolling；
S2: carrying out baking processing to the base fabric that step S1 is obtained, baking finish after by base fabric with the speed of 20~35m/min into
Enter hot melt adhesive coating step, wherein hot melt adhesive coating step is that polyurethane and polyesteramide system are carried out two point painting using cylinder
Layer, the primer layer using polyurethane as hot melt adhesive, polyesteramide form hot melt adhesive layer, Zhi Houzai as the face glue-line of hot melt adhesive
Secondary to bake base fabric, baking carries out final inspection packing and handles to obtain viscous lining after finishing；
S3: carrying out the sewing of viscous lining and collar bottom wool fabric, determines seam part in viscous lining, distance glues lining edge 0.5cm and draws first line, is
First sewing connection, then glue lining edge 1.2cm in distance and draw first line, it is the second sewing connection, then with sewing machine along second
Sewing connection is sewed, and viscous lining is peeled off from cloth edge to the second sewing connection, is divided into viscous lining layer and Nian Chen lower layer, at this time will
Viscous lining layer is aligned with the edge of collar bottom wool fabric, is sutured along the first sewing connection with sewing machine, while will be under the viscous lining of suture
0.2cm is reduced in the edge of layer, so that seam part generation is ladder-like；
S4: rotating 180 degree by axis of the first sewing connection for collar bottom wool fabric on the basis of above-mentioned steps at this time, will then be stitched with flatiron
It is part steady to the side ironing of Nian Chen lower layer, viscous lining layer is folded to the side of stripping and then and pushes down the first sewing connection, with pressing
The ironing that struggles against is smooth；
Viscous lining layer: being first fixed on collar bottom wool fabric on the basis of step S4 with flat-seam gimmick by S5, followed by dark behaviour's needle
Gimmick sew up by hand to viscous lining layer and viscous lining layer, and the elasticity of needle gage and suture, Bu Yaolu are kept during sewing
Machine suture out finally removes the line of flat-seam.
It is preferred: to pad the mixed liquor that resin liquid is organic siloxane polymer and water in step S1, pad pressure first
Power is 1~2kg/cm2, the air in base fabric is mainly rolled, and make to pad resin liquid and penetrate into base fabric in advance, second pads pressure
Power is 3~4kg/cm2, make to pad resin liquid and be uniformly distributed in base fabric, and squeeze and pad resin liquid except scrim surfaces.
Preferred: stoving temperature is 50~60 DEG C in the first time of step S2 bakes, and baking time is 3~5 minutes, is dried
Roasting to the moisture content of base fabric is 8~12%, and stoving temperature is 170~180 DEG C in second of baking, and the processing time is 5~8
Minute.
It is preferred: to need to be stained with adhesive lining item on the inside of the Nian Chen lower layer of stripping in step s3, prevent from deforming.
It is preferred: to need to carry out taking-up activities to viscous lining before step S2 carries out final inspection packing.
It is preferred: taking-up activities be specially embryo cloth carry out ultraviolet lamp inspection, after allowing by treated product with 150 meters/
It is batched, batching speed is 45m/min.
Preferred: the temperature for padding resin liquid is 25 DEG C, and padding resin liquid is organic siloxane polymer and water according to 1:
The mixed liquor that 25 ratio mixes.
A kind of viscous lining method of sewing of collar bottom wool fabric proposed by the present invention, beneficial effect are: the viscous lining method of sewing of the collar bottom wool fabric
Step is clear, and the time of manual person can greatly be saved and improve its efficiency by operating, while the viscous independent production energy served as a contrast
Enough ensure the high-quality of viscous lining, to facilitate subsequent processing.
Specific embodiment
It is next combined with specific embodiments below that the present invention will be further described.
Embodiment 1
The invention proposes a kind of viscous lining method of sewing of collar bottom wool fabric, include the following steps:
S1: carrying out the preparation of viscous lining, and base fabric manufacture, will using 50D low elastic polyester filament as weft yarn using 50D low elastic polyester filament as warp thread
Warp thread and weft yarn form base fabric after air-jet loom weaving, then preliminary drying preshrunk processing are carried out to base fabric, then in high temperature and pressure
The preshrunk setting treatment that relaxes is carried out to base fabric under the control of overflow machine, carries out padding processing again after being disposed, by padding
Resin liquid arranges base fabric using the technique of second dipping and rolling；
S2: carrying out baking processing to the base fabric that step S1 is obtained, and bakes and base fabric is entered heat with the speed of 20m/min after finishing
Melten gel coating step, wherein hot melt adhesive coating step is that polyurethane and polyesteramide system are carried out double-dot coating using cylinder,
Primer layer using polyurethane as hot melt adhesive, polyesteramide form hot melt adhesive layer as the face glue-line of hot melt adhesive, later again
Base fabric is baked, baking carries out final inspection packing and handles to obtain viscous lining after finishing；
S3: carrying out the sewing of viscous lining and collar bottom wool fabric, determines seam part in viscous lining, distance glues lining edge 0.5cm and draws first line, is
First sewing connection, then glue lining edge 1.2cm in distance and draw first line, it is the second sewing connection, then with sewing machine along second
Sewing connection is sewed, and viscous lining is peeled off from cloth edge to the second sewing connection, is divided into viscous lining layer and Nian Chen lower layer, at this time will
Viscous lining layer is aligned with the edge of collar bottom wool fabric, is sutured along the first sewing connection with sewing machine, while will be under the viscous lining of suture
0.2cm is reduced in the edge of layer, so that seam part generation is ladder-like；
S4: rotating 180 degree by axis of the first sewing connection for collar bottom wool fabric on the basis of above-mentioned steps at this time, will then be stitched with flatiron
It is part steady to the side ironing of Nian Chen lower layer, viscous lining layer is folded to the side of stripping and then and pushes down the first sewing connection, with pressing
The ironing that struggles against is smooth；
Viscous lining layer: being first fixed on collar bottom wool fabric on the basis of step S4 with flat-seam gimmick by S5, followed by dark behaviour's needle
Gimmick sew up by hand to viscous lining layer and viscous lining layer, and the elasticity of needle gage and suture, Bu Yaolu are kept during sewing
Machine suture out finally removes the line of flat-seam.
The mixed liquor that resin liquid is organic siloxane polymer and water is padded in step S1, it is 1kg/ that first, which pads pressure,
cm2, the air in base fabric is mainly rolled, and make to pad resin liquid and penetrate into base fabric in advance, it is 3kg/cm that second, which pads pressure,2,
Make to pad resin liquid and be uniformly distributed in base fabric, and squeezes and pad resin liquid except scrim surfaces.
Stoving temperature is 50 DEG C in the first time of step S2 bakes, and baking time is 3 minutes, is baked aqueous to base fabric
Rate is 8%, and stoving temperature is 170 DEG C in second of baking, and the processing time is 5 minutes.
It needs to be stained with adhesive lining item on the inside of the Nian Chen lower layer of stripping in step s3, prevents from deforming.
It needs to carry out taking-up activities to viscous lining before step S2 carries out final inspection packing.
Taking-up activities be specially embryo cloth carry out ultraviolet lamp inspection, after allowing by treated product with 150 meters/roll up
It takes, batching speed is 45m/min.
The temperature for padding resin liquid is 25 DEG C, and padding resin liquid is the ratio of organic siloxane polymer and water according to 1:25
The mixed liquor mixed.
Embodiment 2
The invention proposes a kind of viscous lining method of sewing of collar bottom wool fabric, include the following steps:
S1: carrying out the preparation of viscous lining, and base fabric manufacture, will using 50D low elastic polyester filament as weft yarn using 50D low elastic polyester filament as warp thread
Warp thread and weft yarn form base fabric after air-jet loom weaving, then preliminary drying preshrunk processing are carried out to base fabric, then in high temperature and pressure
The preshrunk setting treatment that relaxes is carried out to base fabric under the control of overflow machine, carries out padding processing again after being disposed, by padding
Resin liquid arranges base fabric using the technique of second dipping and rolling；
S2: carrying out baking processing to the base fabric that step S1 is obtained, and bakes and base fabric is entered heat with the speed of 35m/min after finishing
Melten gel coating step, wherein hot melt adhesive coating step is that polyurethane and polyesteramide system are carried out double-dot coating using cylinder,
Primer layer using polyurethane as hot melt adhesive, polyesteramide form hot melt adhesive layer as the face glue-line of hot melt adhesive, later again
Base fabric is baked, baking carries out final inspection packing and handles to obtain viscous lining after finishing；
S3: carrying out the sewing of viscous lining and collar bottom wool fabric, determines seam part in viscous lining, distance glues lining edge 0.5cm and draws first line, is
First sewing connection, then glue lining edge 1.2cm in distance and draw first line, it is the second sewing connection, then with sewing machine along second
Sewing connection is sewed, and viscous lining is peeled off from cloth edge to the second sewing connection, is divided into viscous lining layer and Nian Chen lower layer, at this time will
Viscous lining layer is aligned with the edge of collar bottom wool fabric, is sutured along the first sewing connection with sewing machine, while will be under the viscous lining of suture
0.2cm is reduced in the edge of layer, so that seam part generation is ladder-like；
S4: rotating 180 degree by axis of the first sewing connection for collar bottom wool fabric on the basis of above-mentioned steps at this time, will then be stitched with flatiron
It is part steady to the side ironing of Nian Chen lower layer, viscous lining layer is folded to the side of stripping and then and pushes down the first sewing connection, with pressing
The ironing that struggles against is smooth；
Viscous lining layer: being first fixed on collar bottom wool fabric on the basis of step S4 with flat-seam gimmick by S5, followed by dark behaviour's needle
Gimmick sew up by hand to viscous lining layer and viscous lining layer, and the elasticity of needle gage and suture, Bu Yaolu are kept during sewing
Machine suture out finally removes the line of flat-seam.
The mixed liquor that resin liquid is organic siloxane polymer and water is padded in step S1, it is 2kg/ that first, which pads pressure,
cm2, the air in base fabric is mainly rolled, and make to pad resin liquid and penetrate into base fabric in advance, it is 4kg/cm that second, which pads pressure,2,
Make to pad resin liquid and be uniformly distributed in base fabric, and squeezes and pad resin liquid except scrim surfaces.
Stoving temperature is 60 DEG C in the first time of step S2 bakes, and baking time is 5 minutes, is baked aqueous to base fabric
Rate is 12%, and stoving temperature is 180 DEG C in second of baking, and the processing time is 8 minutes.
It needs to be stained with adhesive lining item on the inside of the Nian Chen lower layer of stripping in step s3, prevents from deforming.
It needs to carry out taking-up activities to viscous lining before step S2 carries out final inspection packing.
Taking-up activities be specially embryo cloth carry out ultraviolet lamp inspection, after allowing by treated product with 150 meters/roll up
It takes, batching speed is 45m/min.
The temperature for padding resin liquid is 25 DEG C, and padding resin liquid is the ratio of organic siloxane polymer and water according to 1:25
The mixed liquor mixed.
Embodiment 3
The invention proposes a kind of viscous lining method of sewing of collar bottom wool fabric, include the following steps:
S1: carrying out the preparation of viscous lining, and base fabric manufacture, will using 50D low elastic polyester filament as weft yarn using 50D low elastic polyester filament as warp thread
Warp thread and weft yarn form base fabric after air-jet loom weaving, then preliminary drying preshrunk processing are carried out to base fabric, then in high temperature and pressure
The preshrunk setting treatment that relaxes is carried out to base fabric under the control of overflow machine, carries out padding processing again after being disposed, by padding
Resin liquid arranges base fabric using the technique of second dipping and rolling；
S2: carrying out baking processing to the base fabric that step S1 is obtained, and bakes and base fabric is entered heat with the speed of 25m/min after finishing
Melten gel coating step, wherein hot melt adhesive coating step is that polyurethane and polyesteramide system are carried out double-dot coating using cylinder,
Primer layer using polyurethane as hot melt adhesive, polyesteramide form hot melt adhesive layer as the face glue-line of hot melt adhesive, later again
Base fabric is baked, baking carries out final inspection packing and handles to obtain viscous lining after finishing；
S3: carrying out the sewing of viscous lining and collar bottom wool fabric, determines seam part in viscous lining, distance glues lining edge 0.5cm and draws first line, is
First sewing connection, then glue lining edge 1.2cm in distance and draw first line, it is the second sewing connection, then with sewing machine along second
Sewing connection is sewed, and viscous lining is peeled off from cloth edge to the second sewing connection, is divided into viscous lining layer and Nian Chen lower layer, at this time will
Viscous lining layer is aligned with the edge of collar bottom wool fabric, is sutured along the first sewing connection with sewing machine, while will be under the viscous lining of suture
0.2cm is reduced in the edge of layer, so that seam part generation is ladder-like；
S4: rotating 180 degree by axis of the first sewing connection for collar bottom wool fabric on the basis of above-mentioned steps at this time, will then be stitched with flatiron
It is part steady to the side ironing of Nian Chen lower layer, viscous lining layer is folded to the side of stripping and then and pushes down the first sewing connection, with pressing
The ironing that struggles against is smooth；
Viscous lining layer: being first fixed on collar bottom wool fabric on the basis of step S4 with flat-seam gimmick by S5, followed by dark behaviour's needle
Gimmick sew up by hand to viscous lining layer and viscous lining layer, and the elasticity of needle gage and suture, Bu Yaolu are kept during sewing
Machine suture out finally removes the line of flat-seam.
The mixed liquor that resin liquid is organic siloxane polymer and water is padded in step S1, padding pressure first is
1.5kg/cm2, the air in base fabric is mainly rolled, and make to pad resin liquid and penetrate into base fabric in advance, second pads pressure and is
3.5kg/cm2, make to pad resin liquid and be uniformly distributed in base fabric, and squeeze and pad resin liquid except scrim surfaces.
Stoving temperature is 55 DEG C in the first time of step S2 bakes, and baking time is 4 minutes, is baked aqueous to base fabric
Rate is 10%, and stoving temperature is 175 DEG C in second of baking, and the processing time is 6 minutes.
It needs to be stained with adhesive lining item on the inside of the Nian Chen lower layer of stripping in step s3, prevents from deforming.
It needs to carry out taking-up activities to viscous lining before step S2 carries out final inspection packing.
Taking-up activities be specially embryo cloth carry out ultraviolet lamp inspection, after allowing by treated product with 150 meters/roll up
It takes, batching speed is 45m/min.
The temperature for padding resin liquid is 25 DEG C, and padding resin liquid is the ratio of organic siloxane polymer and water according to 1:25
The mixed liquor mixed.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of viscous lining method of sewing of collar bottom wool fabric, which comprises the following steps:
S1: carrying out the preparation of viscous lining, and base fabric manufacture, will using 50D low elastic polyester filament as weft yarn using 50D low elastic polyester filament as warp thread
Warp thread and weft yarn form base fabric after air-jet loom weaving, then preliminary drying preshrunk processing are carried out to base fabric, then in high temperature and pressure
The preshrunk setting treatment that relaxes is carried out to base fabric under the control of overflow machine, carries out padding processing again after being disposed, by padding
Resin liquid arranges base fabric using the technique of second dipping and rolling；
S2: carrying out baking processing to the base fabric that step S1 is obtained, baking finish after by base fabric with the speed of 20~35m/min into
Enter hot melt adhesive coating step, wherein hot melt adhesive coating step is that polyurethane and polyesteramide system are carried out two point painting using cylinder
Layer, the primer layer using polyurethane as hot melt adhesive, polyesteramide form hot melt adhesive layer, Zhi Houzai as the face glue-line of hot melt adhesive
Secondary to bake base fabric, baking carries out final inspection packing and handles to obtain viscous lining after finishing；
S3: carrying out the sewing of viscous lining and collar bottom wool fabric, determines seam part in viscous lining, distance glues lining edge 0.5cm and draws first line, is
First sewing connection, then glue lining edge 1.2cm in distance and draw first line, it is the second sewing connection, then with sewing machine along second
Sewing connection is sewed, and viscous lining is peeled off from cloth edge to the second sewing connection, is divided into viscous lining layer and Nian Chen lower layer, at this time will
Viscous lining layer is aligned with the edge of collar bottom wool fabric, is sutured along the first sewing connection with sewing machine, while will be under the viscous lining of suture
0.2cm is reduced in the edge of layer, so that seam part generation is ladder-like；
S4: rotating 180 degree by axis of the first sewing connection for collar bottom wool fabric on the basis of above-mentioned steps at this time, will then be stitched with flatiron
It is part steady to the side ironing of Nian Chen lower layer, viscous lining layer is folded to the side of stripping and then and pushes down the first sewing connection, with pressing
The ironing that struggles against is smooth；
Viscous lining layer: being first fixed on collar bottom wool fabric on the basis of step S4 with flat-seam gimmick by S5, followed by dark behaviour's needle
Gimmick sew up by hand to viscous lining layer and viscous lining layer, and the elasticity of needle gage and suture, Bu Yaolu are kept during sewing
Machine suture out finally removes the line of flat-seam.
2. a kind of viscous lining method of sewing of collar bottom wool fabric according to claim 1, it is characterised in that: pad resin liquid in step S1
For the mixed liquor of organic siloxane polymer and water, it is 1~2kg/cm that first, which pads pressure,2, mainly roll the sky in base fabric
Gas, and make to pad resin liquid and penetrate into base fabric in advance, it is 3~4kg/cm that second, which pads pressure,2, make to pad resin liquid and uniformly divide
It is distributed in base fabric, and squeezes and pad resin liquid except scrim surfaces.
3. a kind of viscous lining method of sewing of collar bottom wool fabric according to claim 1, it is characterised in that: dried in the first time of step S2
Stoving temperature is 50~60 DEG C in roasting, and baking time is 3~5 minutes, and baking to the moisture content of base fabric is 8~12%, the
Stoving temperature is 170~180 DEG C in secondary baking, and the processing time is 5~8 minutes.
4. a kind of viscous lining method of sewing of collar bottom wool fabric according to claim 1, it is characterised in that: need shelling in step s3
It is stained with adhesive lining item on the inside of the Nian Chen lower layer opened, prevents from deforming.
5. a kind of viscous lining method of sewing of collar bottom wool fabric according to claim 1, it is characterised in that: carry out final inspection in step S2 and beat
It needs to carry out taking-up activities to viscous lining before packet.
6. a kind of viscous lining method of sewing of collar bottom wool fabric according to claim 5, it is characterised in that: taking-up activities are specially embryo cloth
Carry out ultraviolet lamp inspection, after allowing by treated product with 150 meters/batch, batch speed as 45m/min.
7. a kind of viscous lining method of sewing of collar bottom wool fabric according to claim 2, it is characterised in that: the temperature for padding resin liquid is
25 DEG C, padding resin liquid is the mixed liquor that organic siloxane polymer and water are mixed according to the ratio of 1:25.