CN109594348A - A kind of preparation process of fire retardant protective clothing dedicated functionality lining - Google Patents
A kind of preparation process of fire retardant protective clothing dedicated functionality lining Download PDFInfo
- Publication number
- CN109594348A CN109594348A CN201811293895.7A CN201811293895A CN109594348A CN 109594348 A CN109594348 A CN 109594348A CN 201811293895 A CN201811293895 A CN 201811293895A CN 109594348 A CN109594348 A CN 109594348A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- fire retardant
- drying
- lining
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention proposes a kind of preparation processes of fire retardant protective clothing dedicated functionality lining, successively the following steps are included: base fabric weaving, the pre-treatment of overflow pine formula, pad drying and processing, flame-proof treatment, hot melt adhesive layer processing, bake and bank up with earth processing, winding inspection processing, it is formed through, weft yarn using 90% cotton and the blended 20S weaving yarns of 10% aramid fiber, make product that there is excellent flame protection performance, good heat-insulation effect by PROBAN technique again.Fire retardant is added in rubber powder formula and is formed, and there is the colloid progress double-dot coating of flame retardant effect to form, product flame retardant effect is lasting, drapability is good, resistance to dry, washing, it can be widely applied to require in the clothing making of flame retarding function, change because its flame retardant property stabilization will not be with washing times, therefore pole is suitable for the production of all kinds of protective clothings.
Description
[technical field]
The present invention relates to the field of fabric, especially a kind of preparation process of fire retardant protective clothing dedicated functionality lining.
[background technique]
With the development of economy and the raising of living standards of the people.The demand of people's flame retardant textiles is more urgent.According to
Fire investigation interpretation of result accounts for the 20% of fire incident because textile does not have fire caused by flame retardant property is ignited and spreads
More than.In terms of reducing fire hazard, flame retardant textiles have apparent superiority.When flame-retardant textile allows to have longer escape
Between, lacking for heat ratio end flame-retardant textile that when burning discharges can be such that loss caused by fire greatly reduces.Therefore, how to reduce
The release of toxic gas, reduces the loss of people's lives and properties, has caused the whole mankind's when textile combustion risk and burning
Concern and attention.In addition, the work clothes of some special industries, if the war door of fireman takes, work, Welder, electricity before copper and iron factory
The industries such as work, coal mine and the work clothes of oilfield worker, these industries have strict requirements to fire-retardant.Because a little, exploitation flame-retardant textile
For ensuring that the person and property safety, reduction fire are imperative, in the vehicles, public building decoration, home and office intranets
Fire safety problem on have attracted more and more attention from people, the market demand of inflaming retarding fabric is huge.And the flame-resistant garment of compatibility therewith
The research of adhesive lining is in preparation process that is extremely urgent, therefore proposing a kind of fire retardant protective clothing dedicated functionality lining.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, propose what a kind of fire retardant protective clothing dedicated functionality served as a contrast
Preparation process, warp, weft yarn are formed using 90% cotton and the blended 20S weaving yarns of 10% aramid fiber, then make product by PROBAN technique
With excellent flame protection performance, good heat-insulation effect.
To achieve the above object, the invention proposes a kind of preparation processes of fire retardant protective clothing dedicated functionality lining, including
Following steps:
A: base fabric weaving: forming base fabric through plain weave in tricot machine for warp thread, weft yarn, warp thread, weft yarn be all made of cotton,
Aramid fiber is blended；
B: overflow pine formula pre-treatment: preliminary drying preshrunk processing is carried out to base fabric, then under the control of high temperature and pressure overflow machine
The preshrunk setting treatment that relaxes is carried out to base fabric, wind pressure is 40~45HZ, and temperature is 40~45 DEG C, and ambient humidity is 30~40%；
C: pad drying and processing: second dipping and rolling processing carried out to base fabric using CATIONIC SOFTNER, then by base fabric with 7%~
8% overfeeding speed enters three segmented drying chambers and completes drying, and the temperature of the drying chamber is followed successively by 60~70 DEG C, 80~90
DEG C, 100~120 DEG C；
D: flame-proof treatment: base fabric is handled using PROBAN flame retarding process；
E: hot melt adhesive layer processing: silicone oil neutral emulsion and polyester amide hot melt adhesive are carried out by double-dot coating using cylinder and formed
Base fabric is sent into drying chamber after cooling, is mixed with fire retardant in polyester amide hot melt adhesive by hot melt adhesive layer；
F: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100
DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 120~140 DEG C, and drying time is 4~5 minutes, third drying chamber
Temperature be 170~180 DEG C, drying time be 2~3 minutes；
G: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding,
And it carries out the qualified product of quality, appearance to be packaged as finished product.
Preferably, the PROBAN flame retarding process in the step d is handled base fabric using polyphosphoric acid chemical assistant.
Preferably, the non-ionic resistance of 7-8% is added in the polyester amide hot melt adhesive in the step e in process of production
Fire agent.
Preferably, the mesh number of cylinder is CP40 in the step e, the aperture of cylinder is 0.30-0.33mm, the thickness of cylinder
Degree is 0.16-0.18mm.
Preferably, being passed through in the step a, weft yarn is formed using 90% cotton and the blended 20S weaving yarns of 10% aramid fiber.
Beneficial effects of the present invention: the present invention proposes a kind of preparation process of fire retardant protective clothing dedicated functionality lining, warp, latitude
Yarn is formed using 90% cotton and the blended 20S weaving yarns of 10% aramid fiber, then makes product with excellent fire-retardant by PROBAN technique
Protective performance, good heat-insulation effect.Fire retardant is added in rubber powder formula and is formed, and there is the colloid of flame retardant effect to carry out double-dot coating
It forms.Product flame retardant effect is lasting, and drapability is good, and resistance to dry, washing can be widely applied to the clothing making for requiring flame retarding function
In, change because its flame retardant property stabilization will not be with washing times, therefore pole is suitable for the production of all kinds of protective clothings.
Feature and advantage of the invention will be described in detail by embodiment.
[specific embodiment]
A kind of preparation process of fire retardant protective clothing dedicated functionality lining of the present invention, comprising the following steps:
A: base fabric weaving: warp thread, weft yarn are formed into base fabric through plain weave in tricot machine, warp, weft yarn use 90% cotton
It is formed with the blended 20S of 10% aramid fiber；
B: overflow pine formula pre-treatment: preliminary drying preshrunk processing is carried out to base fabric, then under the control of high temperature and pressure overflow machine
The preshrunk setting treatment that relaxes is carried out to base fabric, wind pressure is 40~45HZ, and temperature is 40~45 DEG C, and ambient humidity is 30~40%；
C: pad drying and processing: second dipping and rolling processing carried out to base fabric using CATIONIC SOFTNER, then by base fabric with 7%~
8% overfeeding speed enters three segmented drying chambers and completes drying, and the temperature of the drying chamber is followed successively by 60~70 DEG C, 80~90
DEG C, 100~120 DEG C；
D: flame-proof treatment: base fabric is handled using PROBAN flame retarding process；
E: hot melt adhesive layer processing: silicone oil neutral emulsion and polyester amide hot melt adhesive are carried out by double-dot coating using cylinder and formed
Base fabric is sent into drying chamber after cooling, the non-ionic fire retardant of 7-8% is mixed in polyester amide hot melt adhesive by hot melt adhesive layer；
F: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100
DEG C, drying time is 5~7 minutes, and the temperature of the second drying chamber is 120~140 DEG C, and drying time is 4~5 minutes, third drying chamber
Temperature be 170~180 DEG C, drying time be 2~3 minutes；
G: winding inspection processing: base fabric being wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding,
And it carries out the qualified product of quality, appearance to be packaged as finished product.
PROBAN flame retarding process in the step d is handled base fabric using polyphosphoric acid chemical assistant.The step e
The mesh number of middle cylinder is CP40, and the aperture of cylinder is 0.30-0.33mm, cylinder with a thickness of 0.16-0.18mm.The step a
Middle weaving yarns form.
Technical performance index:
1, peel strength: before washing >=15N/5 × 10cm washing after >=12N/5 × 10cm；
2, xeothermic size changing rate: through to -1.5~+0.4% broadwise -1.0~+0.4%；
3, size changing rate is washed: through to -1.5~+0.4% broadwise -1.5~+0.4%；
4, solid carbon dioxide washes cosmetic variation: 4 grades；
5, free formaldehyde :≤75ppm is discharged；
6, limit oxygen index (LOI): >=28.
A kind of preparation process of fire retardant protective clothing dedicated functionality lining of the present invention, base fabric use 90% cotton using warp, weft yarn
It is formed with the blended 20S weaving yarns of 10% aramid fiber, not only improve the spinnability of raw material and improves the wearability of fabric.Due to cotton
Fiber is inflammable, carries out flame-proof treatment to blended fabric, the cotton fiber ingredient in blended fabric is made to have provided anti-flammability.Using two kinds
Fiber it is blended made of flame retardant base cloth, so that two kinds of fibers is had complementary advantages, to meet the requirement to flame-retardant textile；
Using PROBAN flame retarding process, base fabric is handled using polyphosphoric acid chemical assistant and PROBAN flame retarding process,
Accelerate the carbonization of fabric heat, form separation layer, fabric will stop burning immediately, reach self-extinguishment, make afterflame and glow when
Between it is extremely short and have flame retardant property.The cloth handled through Proban is soft, free from extraneous odour, the flame retardant property with durability,
The cloth handled through Proban is soft, free from extraneous odour；This water-soluble flame retardant easily penetrates into fibrous inside, by ammonia cure
Become high molecular polymer after learning reaction, forms permanent cross-links, make it have the flame retardant property of durability, and this flame retardant property
It is not reduced with increasing for washing times.This flame-proof treatment simultaneously does not change the primary characteristic of fabric fibre, thus
Maintain original performance of fabric；
Using polyester amide hot melt adhesive, the advantages of it has accumulated polyester hot-melt adhesive and polyamide hot.It passes through polyester
It is prepared with monomer of polyamide macromolecular chain exchange reaction, which can stablize, and be not easily decomposed in preservation.It is high-elastic when room temperature
State, heat fusing is in viscous state after heating, and adhesion strength with higher, viscosity is low when heating melting, operation easy to process, poly-
The non-ionic fire retardant of 7-8% is added in esteramides hot melt adhesive production process, heat resistance is good, and does not influence the transparent of product
Property, flame retardant effect is excellent, the colloid of flame retardant effect is formed, so that the flame retardant effect and garment material of lining cloth more match.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention
Scheme all belong to the scope of protection of the present invention.
Claims (5)
1. a kind of preparation process of fire retardant protective clothing dedicated functionality lining, it is characterised in that: the following steps are included:
A: base fabric weaving: warp thread, weft yarn are formed into base fabric through plain weave in tricot machine, warp thread, weft yarn are all made of cotton, aramid fiber
It is blended；
B: overflow pine formula pre-treatment: preliminary drying preshrunk processing is carried out to base fabric, then to base under the control of high temperature and pressure overflow machine
Cloth carries out the preshrunk setting treatment that relaxes, and wind pressure is 40~45HZ, and temperature is 40~45 DEG C, and ambient humidity is 30~40%；
C: it pads drying and processing: second dipping and rolling processing being carried out to base fabric using CATIONIC SOFTNER, then by base fabric with 7%~8%
Overfeeding speed enter three segmented drying chambers and complete drying, the temperature of the drying chamber be followed successively by 60~70 DEG C, 80~90 DEG C,
100~120 DEG C；
D: flame-proof treatment: base fabric is handled using PROBAN flame retarding process；
E: hot melt adhesive layer processing: silicone oil neutral emulsion and polyester amide hot melt adhesive are carried out by double-dot coating using cylinder and form hot melt
Base fabric is sent into drying chamber after cooling, is mixed with fire retardant in polyester amide hot melt adhesive by glue-line；
F: it bakes and banks up with earth processing: base fabric being completed into drying by three segmented drying chambers, the temperature of the first drying chamber is 80~100 DEG C, is dried
The dry time is 5~7 minutes, and the temperature of the second drying chamber is 120~140 DEG C, and drying time is 4~5 minutes, the temperature of third drying chamber
It is 170~180 DEG C, drying time is 2~3 minutes；
G: winding inspection processing: base fabric is wound after trimming meter is long, carries out artificial final inspection to the yardage roll after winding, and will
The qualified product of quality, appearance carries out being packaged as finished product.
2. a kind of preparation process of fire retardant protective clothing dedicated functionality lining as described in claim 1, it is characterised in that: the step
PROBAN flame retarding process in rapid d is handled base fabric using polyphosphoric acid chemical assistant.
3. a kind of preparation process of fire retardant protective clothing dedicated functionality lining as described in claim 1, it is characterised in that: the step
The non-ionic fire retardant of 7-8% is added in polyester amide hot melt adhesive in rapid e in process of production.
4. a kind of preparation process of fire retardant protective clothing dedicated functionality lining as described in claim 1, it is characterised in that: the step
The mesh number of cylinder is CP40 in rapid e, and the aperture of cylinder is 0.30-0.33mm, cylinder with a thickness of 0.16-0.18mm.
5. a kind of preparation process of fire retardant protective clothing dedicated functionality lining as described in claim 1, it is characterised in that: the step
It is passed through in rapid a, weft yarn is formed using 90% cotton and the blended 20S yarn of 10% aramid fiber.