CN109575712A - A kind of polyvinyl chloride composition metal antirust paint and preparation method thereof - Google Patents
A kind of polyvinyl chloride composition metal antirust paint and preparation method thereof Download PDFInfo
- Publication number
- CN109575712A CN109575712A CN201710905627.5A CN201710905627A CN109575712A CN 109575712 A CN109575712 A CN 109575712A CN 201710905627 A CN201710905627 A CN 201710905627A CN 109575712 A CN109575712 A CN 109575712A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- preparation
- composition metal
- antirust paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polyvinyl chloride composition metal antirust paints and preparation method thereof, it is prepared from the following raw materials in parts by weight: 8-10 parts of hydroxyethyl cellulose, 20-40 parts of chliorinated polyvinyl chloride, 25-50 parts of terpene resin, 10-25 parts of monoxone, 2-10 parts of reptazin zinc, 5-20 parts of polyvinyl alcohol, 7-9 parts of butyl stearate, 10-30 parts of toluene, 35-40 parts of deionized water, 2-5 parts of coalescing agent, 10-20 parts of industrial naptha, 1-2 parts of adhesive, it is 4-6 parts of talcum powder, 1-5 parts and coalescing agent 2-5 parts of type aluminium powder slurries not floating.Color of paint of the present invention is bright, paint layer is smooth, and colour fixation is strong, be exposed to air or it is submerged in water when, rust-proof effect is good.
Description
Technical field
The present invention relates to antirust paint technical field more particularly to a kind of polyvinyl chloride composition metal antirust paint and its preparation sides
Method.
Background technique
Existing antirust paint is varied, and the present invention is directed to existing antirust paint, improves.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the compound gold of a kind of polyvinyl chloride proposed
Belong to antirust paint and preparation method thereof.
To achieve the goals above, present invention employs following technical solutions:
A kind of polyvinyl chloride composition metal antirust paint and preparation method thereof, is prepared from the following raw materials in parts by weight: hydroxyl second
8-10 parts of base cellulose, 20-40 parts of chliorinated polyvinyl chloride, 25-50 parts of terpene resin, 10-25 parts of monoxone, reptazin zinc
2-10 parts, 5-20 parts of polyvinyl alcohol, 7-9 parts of butyl stearate, 10-30 parts of toluene, 35-40 parts of deionized water, coalescing agent 2-
5 parts, 10-20 parts of industrial naptha, 1-2 parts of adhesive, 4-6 parts of talcum powder, do not float 1-5 parts of type aluminium powder slurries and coalescing agent 2-5
Part.
The beneficial effects of the present invention are: color of paint is bright, paint layer is smooth, colour fixation is strong, is exposed to air or leaching
When not in water, rust-proof effect is good.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.
A kind of polyvinyl chloride composition metal antirust paint and preparation method thereof, is prepared from the following raw materials in parts by weight: hydroxyl second
8-10 parts of base cellulose, 20-40 parts of chliorinated polyvinyl chloride, 25-50 parts of terpene resin, 10-25 parts of monoxone, reptazin zinc
2-10 parts, 5-20 parts of polyvinyl alcohol, 7-9 parts of butyl stearate, 10-30 parts of toluene, 35-40 parts of deionized water, coalescing agent 2-
5 parts, 10-20 parts of industrial naptha, 1-2 parts of adhesive, 4-6 parts of talcum powder, do not float 1-5 parts of type aluminium powder slurries and coalescing agent 2-5
Part.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (1)
1. a kind of polyvinyl chloride composition metal antirust paint and preparation method thereof, it is characterised in that:
It is prepared from the following raw materials in parts by weight:
8-10 parts of hydroxyethyl cellulose, 20-40 parts of chliorinated polyvinyl chloride, 25-50 parts of terpene resin, 10-25 parts of monoxone, pentachloro-
2-10 parts of benzenethiol zinc, 5-20 parts of polyvinyl alcohol, 7-9 parts of butyl stearate, 10-30 parts of toluene, 35-40 parts of deionized water, at
2-5 parts of film auxiliary agent, 10-20 parts of industrial naptha, 1-2 parts of adhesive, 4-6 parts of talcum powder, do not float 1-5 parts of type aluminium powder slurries and film forming
2-5 parts of auxiliary agent.