CN105176284A - Water-based glaze-imitation paint and preparing method thereof - Google Patents
Water-based glaze-imitation paint and preparing method thereof Download PDFInfo
- Publication number
- CN105176284A CN105176284A CN201510604604.1A CN201510604604A CN105176284A CN 105176284 A CN105176284 A CN 105176284A CN 201510604604 A CN201510604604 A CN 201510604604A CN 105176284 A CN105176284 A CN 105176284A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- material component
- resistance
- based glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based glaze-imitation paint and a preparing method thereof. The material components A of the water-based glaze-imitation paint include, by weight, 90 parts of butyl acrylate, 45 parts of methyl methacrylate, 1.3 parts of ammonium persulfate, 2.2 parts of polyethylene glycol octylphenol ether, 1.1 parts of crylic acid-methacrylic acid copolymer ammonium salt and 210 parts of water. The material components B of the water-based glaze-imitation paint include, by weight, 80 parts of water emulsion film forming matter, 7.5 parts of rutile titanium dioxide, 0.8 part of sodium hexametaphosphate, 6.2 parts of butyl cellosolve and 61 parts of water. The water-based glaze-imitation paint is suitable for decoration of an inner wall, an outer wall and roof tile surfaces of a building and has the advantages of being flat and smooth in surface, high in glossiness, high in adhesive force, high in water resistance, aging resistance, acid-base resistance, scouring resistance and pollution resistance, capable of resisting temperature over 100 DEG C and quite low in cost.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of water soluble imitation glaze coating being applicable to build inner, external wall and roof tiling decoration, have surfacing smooth, glossiness is high, the characteristic of strong adhesion, has the positively effects such as water-fast, ageing-resistant, acid and alkali-resistance, washability, stain resistance are strong.
Background technology
Coating is coated in protected or decorated body surface; and the continuous film of firm attachment can be formed with coated article, normally based on resin or oil or emulsion, add or do not add pigment, filler; add corresponding additive, with organic solvent or the formulated thick liquid of water." coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms adhere well, has some strength, continuous print solid film.The film common name film of such formation, also known as paint film or coating." coating (paint), our usual said paint is one wherein.Refer to coat body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins instead of vegetables oil, therefore is called coating.Coating non-liquid, powder coating is the large class of coating variety one.Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.The classification of the Chemicals of passing through according to the modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.Effect mainly contains 4 points: protection, decoration, covers up defect and other special roles of product, the value of improving product.Large is in early days main material mainly with vegetables oil, therefore has the title of paint.Show the large portion of synthetic resins or all instead of vegetables oil, therefore being called coating.
Summary of the invention
The object of the present invention is to provide a kind of water soluble imitation glaze coating being applicable to build inner, external wall and roof tiling decoration, there is surfacing smooth, glossiness is high, the characteristic of strong adhesion, has the positively effects such as water-fast, ageing-resistant, acid and alkali-resistance, washability, stain resistance are strong.
Water soluble imitation glaze coating of the present invention is combined by material component A and material component B.
Present invention employs such technical scheme: in described water soluble imitation glaze coating, the material of material component A and weight proportion are respectively: butyl acrylate 90 parts, methyl methacrylate 45 parts, ammonium persulphate 1.3 parts, Triton X-100 2.2 parts, acrylic acid-methacrylic acid multipolymer ammonium salt 1.1 parts, 210 parts, water.
The material of material component B and weight proportion be respectively: water-latex type film forming matter 80 parts, Rutile type Titanium Dioxide 7.5 parts, Sodium hexametaphosphate 99 0.8 part, butyl glycol ether 6.2 parts, 61 parts, water.
The present invention is applicable in building inner, external wall and roof tiling decoration.
It is smooth that this product has surfacing, and glossiness is high, the characteristic of strong adhesion; There is the positively effects such as water-fast, ageing-resistant, acid and alkali-resistance, washability, stain resistance are strong, the high temperature of more than 100 DEG C can be resisted; Cost is lower.
Embodiment
Water soluble imitation glaze coating of the present invention is combined by material component A and material component B.
Present invention employs such technical scheme: in described water soluble imitation glaze coating, the material of material component A and weight proportion are respectively: butyl acrylate 90 parts, methyl methacrylate 45 parts, ammonium persulphate 1.3 parts, Triton X-100 2.2 parts, acrylic acid-methacrylic acid multipolymer ammonium salt 1.1 parts, 210 parts, water.
The material of material component B and weight proportion be respectively: water-latex type film forming matter 80 parts, Rutile type Titanium Dioxide 7.5 parts, Sodium hexametaphosphate 99 0.8 part, butyl glycol ether 6.2 parts, 61 parts, water.
Its preparation method is following steps:
Step one), monomer is made emulsion, at 75 DEG C of temperature, add initiator solution, temperature risen to 95 DEG C, keep 0.5h stopped reaction, obtain material component A;
Step 2), by step one) the material component A that obtains after material component B fully mixes, in high speed dispersor, disperse about 10min;
Step 3), in step 2) material that obtains grinds about 1.5h in skin grinder, with 160 order filter-cloth filterings, finished product.
Claims (2)
1. a water soluble imitation glaze coating, it is characterized in that, material and weight proportion respectively: the material of material component A and weight proportion respectively: butyl acrylate 90 parts, methyl methacrylate 45 parts, ammonium persulphate 1.3 parts, Triton X-100 2.2 parts, acrylic acid-methacrylic acid multipolymer ammonium salt 1.1 parts, 210 parts, water.The material of material component B and weight proportion be respectively: water-latex type film forming matter 80 parts, Rutile type Titanium Dioxide 7.5 parts, Sodium hexametaphosphate 99 0.8 part, butyl glycol ether 6.2 parts, 61 parts, water.
2. according to water soluble imitation glaze coating according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), monomer is made emulsion, at 75 DEG C of temperature, add initiator solution, temperature is risen to 95 DEG C, keep 0.5h stopped reaction, obtain material component A;
Step 2), by step one) the material component A that obtains after material component B fully mixes, in high speed dispersor, disperse about 10min;
Step 3), in step 2) material that obtains grinds about 1.5h in skin grinder, with 160 order filter-cloth filterings, finished product.