CN104530790A - Formula for acrylic composite coating - Google Patents
Formula for acrylic composite coating Download PDFInfo
- Publication number
- CN104530790A CN104530790A CN201510029341.6A CN201510029341A CN104530790A CN 104530790 A CN104530790 A CN 104530790A CN 201510029341 A CN201510029341 A CN 201510029341A CN 104530790 A CN104530790 A CN 104530790A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite coating
- acrylic composite
- formula
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula for an acrylic composite coating. The acrylic composite coating is prepared from the following raw materials in parts by mass: 30-35 parts of an acrylic emulsion, 30-35 parts of heavy calcium carbonate, 5-8 parts of sierozem, 5-10 parts of butyl acrylate, 2-3 parts of polyvinyl alcohol, 1-2 parts of a thickener, 1-2 parts of a defoamer, 1-2 parts of titanium dioxide, 1-2 parts of a titanate coupling agent, 5-10 parts of deionized water and 1-2 parts of propylene glycol. The acrylic composite coating disclosed by the invention has good adhesion, high tinting strength and excellent impact resistance and can be used for coloring and coating metals, plastic, hard fiberboards, plywood and other materials.
Description
Technical field
The present invention relates to chemical field, be specifically related to a kind of vinylformic acid composite coating.
Background technology
Acrylic emulsion coatings commercially available is at present a lot, but tolerance and scrub performance are generally, especially scrub performance, and in the process of cleaning, the change of color or quality can occur coatingsurface, brings inconvenience therefore to the cleaning on surface.
Summary of the invention
Goal of the invention: the object of the invention is, in order to solve deficiency of the prior art, to provide a kind of paint film adhesion good, strong coloring force, the vinylformic acid composite coating that impact strength is outstanding.
Technical scheme: a kind of vinylformic acid composite coating formula of the present invention, comprise the following raw material of proportion by weight: ACRYLIC EMULSION 30-35 part, coarse whiting 30-35 part, grey calcium 5-8 part, butyl acrylate 5-10 part, polyvinyl alcohol 2-3 part, thickening material 1-2 part, defoamer 1-2 part, titanium dioxide 1-2 part, titanate coupling agent 1-2 part, deionized water 5-10 part, propylene glycol 1-2 part.
Beneficial effect: vinylformic acid composite coating paint film adhesion of the present invention is good, strong coloring force, and impact strength is outstanding, can be used for the coloring and coating of the materials such as metal, plastics, hardboard, glued board.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of vinylformic acid composite coating formula, comprise the following raw material of proportion by weight: ACRYLIC EMULSION 33 parts, coarse whiting 32 parts, grey calcium 8 parts, butyl acrylate 7 parts, polyvinyl alcohol 3 parts, thickening material 2 parts, defoamer 1 part, titanium dioxide 1 part, titanate coupling agent 2 parts, deionized water 9 parts, propylene glycol 2 parts.
Embodiment 2
A kind of vinylformic acid composite coating formula, comprise the following raw material of proportion by weight: ACRYLIC EMULSION 30 parts, coarse whiting 35 parts, grey calcium 8 parts, butyl acrylate 8 parts, polyvinyl alcohol 3 parts, thickening material 2 parts, defoamer 1 part, titanium dioxide 2 parts, titanate coupling agent 1 part, deionized water 8 parts, propylene glycol 2 parts.
Embodiment 3
A kind of vinylformic acid composite coating formula, comprise the following raw material of proportion by weight: ACRYLIC EMULSION 35 parts, coarse whiting 30 parts, grey calcium 5 parts, butyl acrylate 7 parts, polyvinyl alcohol 3 parts, thickening material 2 parts, defoamer 2 parts, titanium dioxide 2 parts, titanate coupling agent 2 parts, deionized water 10 parts, propylene glycol 2 parts.
Claims (2)
1. a vinylformic acid composite coating formula, it is characterized in that: the following raw material comprising proportion by weight: ACRYLIC EMULSION 30-35 part, coarse whiting 30-35 part, grey calcium 5-8 part, butyl acrylate 5-10 part, polyvinyl alcohol 2-3 part, thickening material 1-2 part, defoamer 1-2 part, titanium dioxide 1-2 part, titanate coupling agent 1-2 part, deionized water 5-10 part, propylene glycol 1-2 part.
2. a kind of vinylformic acid composite coating formula according to claim 1, it is characterized in that: the following raw material comprising proportion by weight: ACRYLIC EMULSION 35 parts, coarse whiting 30 parts, grey calcium 5 parts, butyl acrylate 7 parts, polyvinyl alcohol 3 parts, thickening material 2 parts, defoamer 2 parts, titanium dioxide 2 parts, titanate coupling agent 2 parts, deionized water 10 parts, propylene glycol 2 parts.