CN111117441A - Water-based high-performance super-boiling-resistant vacuum cup paint - Google Patents
Water-based high-performance super-boiling-resistant vacuum cup paint Download PDFInfo
- Publication number
- CN111117441A CN111117441A CN201911405475.8A CN201911405475A CN111117441A CN 111117441 A CN111117441 A CN 111117441A CN 201911405475 A CN201911405475 A CN 201911405475A CN 111117441 A CN111117441 A CN 111117441A
- Authority
- CN
- China
- Prior art keywords
- amino resin
- percent
- water
- methylated melamine
- ethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based high-performance super-boiling-resistant vacuum cup paint which is prepared from the following raw materials, by weight, 40-50% of epoxy modified acrylic resin, 40-8% of amino resin A6, 2-2% of amino resin B1, 3-4% of propenyl ethylene glycol diether PM, 1-3% of butyl cellosolve/ethylene glycol butyl ether BCS, 0.2-0.3% of wetting agent, 0.05-0.1% of defoaming agent, 1-2% of sealing curing agent and the balance of water; wherein the amino resin A is 40-50% methylated melamine, and the amino resin B is fully methylated melamine. The invention has the beneficial effects that: epoxy modified acrylic resin with higher polarity is selected, and the epoxy group provides excellent wet adhesion. The amino resin in the formula is prepared by matching partial methylated melamine with 1-2 parts of fully methylated melamine, so that a paint film has high hardness and high toughness.
Description
Technical Field
The invention relates to the field of coatings, and mainly relates to a water-based high-performance super-boiling-resistant vacuum cup paint.
Background
The vacuum cup is made of stainless steel, has larger surface energy and higher surface hardness, and is difficult to wet and adhere. It is required to develop a water-based vacuum cup paint with excellent adhesion and super-good boiling resistance.
Disclosure of Invention
The invention aims to overcome the defects in the prior art and provide the water-based high-performance super-boiling-resistant vacuum cup paint.
The object of the present invention is achieved by the following technical means. The water-based high-performance super-boiling-resistant vacuum cup paint is prepared from the following raw materials, by weight, 40-50% of epoxy modified acrylic resin, 40-8% of amino resin A6, 1-2% of amino resin B, 3-4% of propenyl ethylene glycol diether PM, 1-3% of butyl cellosolve/ethylene glycol butyl ether BCS, 0.2-0.3% of wetting agent, 0.05-0.1% of defoaming agent, 1-2% of sealing curing agent and the balance of water; wherein the amino resin A is 40-50% methylated melamine, and the amino resin B is fully methylated melamine.
Preferably, the raw materials are prepared according to the following weight percentage, 40 percent of epoxy modified acrylic resin, 6 percent of amino resin A, 1 percent of amino resin B, 3 percent of propenyl ethylene glycol diether PM, 2 percent of butyl cellosolve/ethylene glycol butyl ether BCS, 0.2 percent of wetting agent, 0.08 percent of defoaming agent, 1 percent of closed curing agent and the balance of water; wherein the amino resin A is 45 percent methylated melamine, and the amino resin B is fully methylated melamine.
Preferably, the defoaming agent is an organic silicon type defoaming agent, and the wetting agent is a silanol nonionic surfactant.
The invention has the beneficial effects that: epoxy modified acrylic resin with higher polarity is selected, and the epoxy group provides excellent wet adhesion. The amino resin in the formula is prepared by matching partial methylated melamine with 1-2 parts of fully methylated melamine, so that a paint film has high hardness and high toughness.
Detailed Description
The present invention will be described in detail with reference to the following examples:
the invention discloses a water-based high-performance super-boiling-resistant vacuum cup paint which is prepared from the following raw materials, by weight, 40-50% of epoxy modified acrylic resin, 40-8% of amino resin A6, 2-2% of amino resin B1, 1-3% of propenyl ethylene glycol diether PM3, 1-3% of butyl cellosolve/ethylene glycol monobutyl ether BCS, 0.2-0.3% of wetting agent, 0.05-0.1% of defoaming agent, 1-2% of sealing curing agent and the balance of water; wherein the amino resin A is 40-50% methylated melamine, and the amino resin B is fully methylated melamine.
Example 1: the invention discloses a water-based high-toughness high-sealing baking varnish, which is prepared from the following raw materials in percentage by weight, 40% of epoxy modified acrylic resin, 40% of amino resin A6%, 1% of amino resin B, 3% of propenyl ethylene glycol diether PM, 2% of butyl cellosolve/ethylene glycol monobutyl ether BCS, 0.2% of wetting agent, 0.08% of defoaming agent, 1% of sealing curing agent and the balance of water; wherein the amino resin A is 45 percent methylated melamine, and the amino resin B is fully methylated melamine. The defoaming agent is an organic silicon type defoaming agent, and the wetting agent is silanol nonionic surfactant, GSK-588/582/585 and the like.
Example 2: the raw materials comprise, by weight, 50% of waterborne acrylic resin, 21% of waterborne polyester resin, 15% of amino resin, 3% of propenyl ethylene glycol diether PM 4%, 0.3% of butyl cellosolve/ethylene glycol monobutyl ether BCS, 0.1% of a wetting agent, and the balance of water. The defoaming agent is an organic silicon type defoaming agent, and the wetting agent is silanol nonionic surfactant, GSK-588/582/585 and the like.
Example 3: the raw materials are prepared according to the following weight percentage, 50 percent of epoxy modified acrylic resin, 8 percent of amino resin A, 2 percent of amino resin B, 3 percent of propenyl ethylene glycol diether PM4 percent, 3 percent of butyl cellosolve/ethylene glycol butyl ether BCS, 0.3 percent of wetting agent, 0.1 percent of defoaming agent, 2 percent of closed curing agent and the balance of water; wherein the amino resin A is 40-50% methylated melamine, and the amino resin B is fully methylated melamine.
Wherein the wetting agent is silanol nonionic surfactant, GSK-588/582/585, etc.
It should be understood that equivalent substitutions and changes to the technical solution and the inventive concept of the present invention should be made by those skilled in the art to the protection scope of the appended claims.
Claims (3)
1. The utility model provides a water-based high performance surpasses boiling water thermos cup lacquer which characterized in that: the raw materials are prepared according to the following weight percentage, 40-50% of epoxy modified acrylic resin, 6-8% of amino resin A, 1-2% of amino resin B, 3-4% of propenyl ethylene glycol diether PM, 1-3% of butyl cellosolve/ethylene glycol monobutyl ether BCS, 0.2-0.3% of wetting agent, 0.05-0.1% of defoaming agent, 1-2% of sealing curing agent and the balance of water; wherein the amino resin A is 40-50% methylated melamine, and the amino resin B is fully methylated melamine.
2. The aqueous high-performance super-boiling-resistant thermos cup paint of claim 1, characterized in that: the raw materials are prepared according to the following weight percentage, 40 percent of epoxy modified acrylic resin, 6 percent of amino resin A, 1 percent of amino resin B, 3 percent of propenyl ethylene glycol diether PM, 2 percent of butyl cellosolve/ethylene glycol monobutyl ether BCS, 0.2 percent of wetting agent, 0.08 percent of defoaming agent, 1 percent of closed curing agent and the balance of water; wherein the amino resin A is 45 percent methylated melamine, and the amino resin B is fully methylated melamine.
3. The aqueous high-performance super-boiling-resistant thermos cup paint of claim 1 or 2, characterized in that: the defoaming agent is an organic silicon type defoaming agent, and the wetting agent is a silanol nonionic surfactant.