CN105585915A - White priming paint used for wood furniture - Google Patents
White priming paint used for wood furniture Download PDFInfo
- Publication number
- CN105585915A CN105585915A CN201410561320.4A CN201410561320A CN105585915A CN 105585915 A CN105585915 A CN 105585915A CN 201410561320 A CN201410561320 A CN 201410561320A CN 105585915 A CN105585915 A CN 105585915A
- Authority
- CN
- China
- Prior art keywords
- priming paint
- titanium dioxide
- white primer
- wood furniture
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a white priming paint used for wood furniture. The white priming paint comprises the following components by weight percentage: 38-41% of an aqueous acrylic acid emulsion, 53-56% of a filling material, 1.7% of an auxiliary agent, 4% of a film forming auxiliary agent, and 0.3% of a thickening agent. The filling material is composed of 4.5-5.5% of titanium dioxide, 38.5-40% of heavy calcium and 9-10.5% of powdered steatile with weight percentage in the white priming paint raw material. The white priming paint has excellent polishing property and filling property; has advantages of high hardness and good sealing performance, can effectively seal tannic acid in timber, can solve the problems of wood swelling and fiberboard swelling, can simplify the construction operation, saves coating cost; and employs an acrylic acid emulsion with low cost, wherein titanium dioxide, powdered steatile and heavy calcium can be the filling materials with a proper ratio, and cost of the white priming paint is reduced under prerequisite that the priming paint performance is not influenced, and cost of the white priming paint is lower than that of the other priming paints.
Description
Technical field
The present invention relates to furniture lacquer technical field, particularly, relate to a kind of white primer for wood furniture.
Background technology
Along with the day by day raising of people to environmental protection and healthy requirement, and constantly the improving and strengthen of environmental regulation both at home and abroad, water-borne wood coating is more and more subject to everybody attention. Water-borne wood coating is the class coating taking water as decentralized medium, have do not fire, nontoxic, free from environmental pollution, save the advantage such as the energy, market prospects are wide.
In real production process, aqueous wooden ware white primer will have good workability, and high, the easy polishing of hardness, fillibility are good, but the white primer that often meets these conditions generally adopts titanium dioxide as filler, and its price is all higher.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of white primer for wood furniture, and it carries out suitable proportioning as filler using titanium dioxide, talcum powder and coarse whiting, suitably reduces the cost of white primer under the prerequisite that does not affect primer performance.
The present invention addresses the above problem adopted technical scheme:
For the white primer of wood furniture, by weight percentage, comprise following component: aqueous acrylic emulsion 38-41%, filler 53-56%, auxiliary agent 1.7%, coalescents 4%, thickener 0.3%, described filler is made up of titanium dioxide, coarse whiting, talcum powder, and the percentage by weight that three accounts for white primer raw material is respectively: titanium dioxide 4.5-5.5%, coarse whiting 38.5-40%, talcum powder 9-10.5%.
As a further improvement on the present invention, described auxiliary agent is one or more combination in defoamer, dispersant, wetting agent, antimildew disinfectant.
Further, described aqueous acrylic emulsion is selected the metal corsslinking type emulsion with acrylic compounds nucleocapsid structure, predetermined vitrification point.
Further, described titanium dioxide, coarse whiting, talcum powder are all selected 1200 object powders.
Further, the described white primer for wood furniture by weight percentage, comprises following component: aqueous acrylic emulsion 39%, titanium dioxide 5%, coarse whiting 40%, talcum powder 10%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1.2%, wetting agent 0.2%, antimildew disinfectant 0.1%.
Further, the described white primer for wood furniture by weight percentage, by weight percentage, comprise following component: aqueous acrylic emulsion 40%, titanium dioxide 5%, coarse whiting 39%, talcum powder 10%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, antimildew disinfectant 0.3%.
Further, the described white primer for wood furniture by weight percentage, by weight percentage, comprise following component: aqueous acrylic emulsion 40%, titanium dioxide 5%, coarse whiting 39.5%, talcum powder 9.5%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, antimildew disinfectant 0.3%.
The invention has the beneficial effects as follows:
1, white primer of the present invention has excellent grinability and fillibility;
2, white primer of the present invention has the advantages such as hardness is high, closure is good, can effectively seal the tannic acid in timber, and solves the problem that solid wood is swollen and fiberboard is swollen, and can simplify working procedure, saves painting cost;
3, the lower acrylic emulsion of employing price of white primer of the present invention, titanium dioxide, talcum powder and coarse whiting are carried out to suitable proportioning as filler, the cost that further reduces white primer under the prerequisite that does not affect primer performance, therefore the cost of white primer of the present invention is also low more than other priming paint.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is done to detailed description further, but embodiments of the present invention are not limited to this.
Embodiment 1:
For the white primer of wood furniture, by weight percentage, comprise following component: aqueous acrylic emulsion 38-41%, filler 53-56%, auxiliary agent 1.7%, coalescents 4%, thickener 0.3%, described filler is made up of titanium dioxide, coarse whiting, talcum powder, and the percentage by weight that three accounts for white primer raw material is respectively: titanium dioxide 4.5-5.5%, coarse whiting 38.5-40%, talcum powder 9-10.5%. White primer formula for wood furniture provided by the invention, carries out suitable proportioning as filler using titanium dioxide, talcum powder and coarse whiting, suitably reduces the cost of white primer under the prerequisite that does not affect primer performance.
In the present embodiment, described auxiliary agent is one or more combination in defoamer, dispersant, wetting agent, antimildew disinfectant; Described aqueous acrylic emulsion is selected the metal corsslinking type emulsion with acrylic compounds nucleocapsid structure, predetermined vitrification point; Described titanium dioxide, coarse whiting, talcum powder are all selected 1200 object powders.
Embodiment 2:
The difference of the present embodiment and embodiment 1 is:
For the white primer of wood furniture, by weight percentage, comprise following component: aqueous acrylic emulsion 39%, titanium dioxide 5%, coarse whiting 40%, talcum powder 10%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1.2%, wetting agent 0.2%, antimildew disinfectant 0.1%.
Its preparation method is for weighing aqueous acrylic emulsion, titanium dioxide, coarse whiting, talcum powder, coalescents, defoamer, dispersant, wetting agent to join successively in beaker by formula quantity, under the condition that is 2000r/min at rotating speed, stir 30min, then add antimildew disinfectant, thickener, stir.
Embodiment 3:
The difference of the present embodiment and embodiment 2 is: for the white primer of wood furniture, by weight percentage, comprise following component: aqueous acrylic emulsion 40%, titanium dioxide 5%, coarse whiting 39%, talcum powder 10%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, antimildew disinfectant 0.3%.
Embodiment 4:
The difference of the present embodiment and embodiment 2 is: for the white primer of wood furniture, by weight percentage, comprise following component: aqueous acrylic emulsion 40%, titanium dioxide 5%, coarse whiting 39.5%, talcum powder 9.5%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, antimildew disinfectant 0.3%.
Priming paint is used for increasing the adhesive force of coating and timber, so priming paint will be got well the wetting and permeability of timber. The relative finish paint of priming paint, cheap, in ensureing that film has enough richness, can reduce painting cost. Therefore the present invention selects acrylic emulsion that price is lower to reduce costs, and its hardness of film is higher, can increase the hardness of finish paint. In addition, white primer of the present invention can also close the tannic acid of poplar, solves the problems such as common solid wood is swollen and fiberboard is swollen, and therefore not be used in brushing seal coat on timber, has saved a procedure.
Conventionally the filler that priming paint is used has powdered whiting, talcum powder, barium sulfate etc. Talcum powder oil absorption is larger, but can increase grinability. Coarse whiting hardness is moderate, and grinability is good. But calcium carbonate granule is thick, covering power is poor, and compatibility general and high polymer is poor, easily cause in high polymer base-material, disperse inhomogeneous. The grinability of barium sulfate is poor. The covering power of titanium dioxide is good, and spherical titanium dioxide is more even in the dispersion of high polymer, but on the high side, therefore in the present embodiment, adopts above-mentioned. In guaranteed performance, reduce white primer price by powdered whiting, talcum powder, supporting the use of titanium dioxide.
To sum up, white primer of the present invention has excellent grinability and fillibility, has the advantages such as hardness is high, closure is good simultaneously, can effectively seal the tannic acid in timber, and solve the problem that solid wood is swollen and fiberboard is swollen, and can simplify working procedure, save painting cost. In addition, the cost of this white primer is also low more than other priming paint.
Below be only the preferred embodiment of the present invention, protection scope of the present invention is also not only confined to above-described embodiment, and all technical schemes belonging under thinking of the present invention all belong to protection scope of the present invention. It should be pointed out that for those skilled in the art, some improvements and modifications without departing from the principles of the present invention, should be considered as protection scope of the present invention.
Claims (7)
1. for the white primer of wood furniture, it is characterized in that, by weight percentage, comprise following component: aqueous acrylic emulsion 38-41%, filler 53-56%, auxiliary agent 1.7%, coalescents 4%, thickener 0.3%, described filler is made up of titanium dioxide, coarse whiting, talcum powder, and the percentage by weight that three accounts for white primer raw material is respectively: titanium dioxide 4.5-5.5%, coarse whiting 38.5-40%, talcum powder 9-10.5%.
2. the white primer for wood furniture according to claim 1, is characterized in that, described auxiliary agent is one or more combination in defoamer, dispersant, wetting agent, antimildew disinfectant.
3. the white primer for wood furniture according to claim 1, is characterized in that, described aqueous acrylic emulsion is selected the metal corsslinking type emulsion with acrylic compounds nucleocapsid structure, predetermined vitrification point.
4. the white primer for wood furniture according to claim 1, is characterized in that, described titanium dioxide, coarse whiting, talcum powder are all selected 1200 object powders.
5. according to the arbitrary described white primer for wood furniture of claim 1 to 4, it is characterized in that, by weight percentage, comprise following component: aqueous acrylic emulsion 39%, titanium dioxide 5%, coarse whiting 40%, talcum powder 10%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1.2%, wetting agent 0.2%, antimildew disinfectant 0.1%.
6. the white primer for wood furniture according to claim 1 and 2, it is characterized in that, by weight percentage, comprise following component: aqueous acrylic emulsion 40%, titanium dioxide 5%, coarse whiting 39%, talcum powder 10%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, antimildew disinfectant 0.3%.
7. the white primer for wood furniture according to claim 1 and 2, it is characterized in that, by weight percentage, comprise following component: aqueous acrylic emulsion 40%, titanium dioxide 5%, coarse whiting 39.5%, talcum powder 9.5%, coalescents 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, antimildew disinfectant 0.3%.