CN109537829A - A kind of compound Malaysia paint and its construction technology - Google Patents
A kind of compound Malaysia paint and its construction technology Download PDFInfo
- Publication number
- CN109537829A CN109537829A CN201811279935.2A CN201811279935A CN109537829A CN 109537829 A CN109537829 A CN 109537829A CN 201811279935 A CN201811279935 A CN 201811279935A CN 109537829 A CN109537829 A CN 109537829A
- Authority
- CN
- China
- Prior art keywords
- paint
- malaysia
- compound
- priming paint
- finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to chemistry painting industry construction method technical fields, specifically disclose a kind of compound Malaysia paint and its construction technology.The compound Malaysia is painted, including UV priming paint, and the Malaysia paint coated on UV priming paint, the finish of coating is painted in Malaysia；Wherein at least 4 layers of UV priming paint.Construction technology is the following steps are included: base material treatment；First of UV priming paint is brushed, carries out semi-solid preparation with ultraviolet light；Brushing second UV priming paint, carries out all solidstate with ultraviolet light；Grinding process；The UV priming paint of brushing rest layers, with ultraviolet light alternately semi-solid preparation and all solidstate；Grinding process；Malaysia paint construction；Spray finish.Malaysia paint provided by the invention and its construction technology, method is simple, the perfect collocation of Malaysia paint and UV photocuring system, embodies the abundant and whole painting effect stereovision of color, while improving the hardness of paint film.
Description
Technical field
The present invention relates to chemistry painting industry construction method technical field more particularly to a kind of compound Malaysia paint and its construction works
Skill.
Background technique
The splendid Malaysia paint coating of decorative effect necessarily plays an increasingly important role in decorations field.Malaysia paint
Tool batch scraping operation on metope is scraped by batch, generates silk plastering, glaze modelled after an antique plastering, the cool, Vinnie of parian paint, silk painting
All kinds of textures such as this plastering, the color jade in Europe, lacquer painting is bright and clean stone matter effect, and artistic effect is obvious, quality and slippery feel.For
The waterproofness and compactness of Malaysia paint paint film are taken into account, paint lotion used in Malaysia is the higher lotion of caking property mostly, is compared
It is easy dust stratification dirt, causes the stain resistance of paint film poor.Simultaneously because Malaysia paint attachment force is poor, hardness is inadequate, shadow significantly
The popularization of Malaysia paint is rung.
Summary of the invention
Aiming at the problem that poor paint film stain resistance, difference of hardness are painted in existing Malaysia, the present invention provides a kind of compound Malaysia paint.
And the present invention also provides the construction technologies of compound Malaysia paint.
To achieve the above object of the invention, the embodiment of the present invention uses the following technical solution:
A kind of compound Malaysia paint, paints painting including the Malaysia paint coated on UV priming paint, the UV priming paint and the Malaysia
The finish covered；Wherein at least 4 layers of UV priming paint.
Compared with prior art, compound Malaysia paint provided by the invention has the advantage that
(1) repeating construction using multilayer UV priming paint keeps paint film more evenly careful, increases the adhesive force between each layer of UV priming paint,
To improve the adhesive force of entire compound Malaysia paint；
(2) the perfect collocation of Malaysia paint and UV photocuring system, not only has the level of color abundant and whole coating
Sense, and multilayer UV priming paint is as basic paint film, substantially increased after UV photocuring between basic paint film and Malaysia paint with
And the cohesive force between Malaysia paint and finish, to greatly improve the hardness and adhesive force of compound Malaysia paint；
(3) paint film outermost layer coating paint cover, greatly strengthens the stain resistance of paint film.
(4) UV priming paint, finish and the Malaysia paint that the present invention uses are water-based material, use water as diluent, lower
It is carbon, more environmentally friendly, more energy efficient
And specifically, it is preferable to ground, the finish is fluorine carbon finish, and coating weight 15-25g/m2。
Using fluorine carbon finish cover, fluororine-carbon coating has extremely low surface energy, surface dirt can be self-cleaning by rainwater, fabulous
Hydrophobicity, will not non-dust absorption and non-fouling, greatly strengthen the stain resistance of paint film.
The fluororine-carbon coating in fluorine carbon finish contains a large amount of F-C key simultaneously, and Malaysia paint takes water as a solvent, F-C key and horse
Carry out surface of the paint film and form a large amount of hydrogen bonds, increase the cohesive force of paint film, increases the hardness, stability and weather resistance of paint film.
Preferably, the coating weight of the Malaysia paint is 80-120g/m2。
If coating weight is too high, not only increase the drying time of paint film, increases cost, and the excessive coating of coating weight is in paint film
Upper to flow naturally, coating quality not can guarantee, if coating weight is too small, then it cannot be guaranteed that the adhesive force of paint film, hardness and horse
To paint the color and decorative pattern of formation.Therefore selection 80-120g/m2Coating weight, not only guarantee paint film color and stereovision, also
It can guarantee the hardness and adhesive force of paint film.
Preferably, the coating weight of first layer UV priming paint is 15-25g/m2, the coating weight of remainder layer UV priming paint is 25-35g/
m2。
If coating weight is too high, not only increase the drying time of paint film, increases cost, and the excessive coating of coating weight is in paint film
Upper to flow naturally, coating quality not can guarantee, if coating weight is too small, then it cannot be guaranteed that the adhesive force of paint film, hardness.
The coating weight of first layer UV priming paint also needs to consider the flatness of paint film, prevents coating weight too big, causes paint film thin
Micro- is uneven, therefore selects 15-25g/m2Coating weight, not only guarantee the hardness and adhesive force of paint film, moreover it is possible to guarantee the
The flatness of coast of paint film.
The coating weight of remainder layer UV priming paint also needs to consider the hiding rare of coating, therefore selects 25-35g/m2Coating weight,
Not only guarantee the hardness and adhesive force of paint film, moreover it is possible to guarantee paint film to the hiding rare of substrate.
Further, it the present invention also provides the construction technology of above-mentioned compound Malaysia paint, at least includes the following steps:
Step a, base material treatment；
Step b, it brushes first of UV priming paint: UV priming paint being heated to 40-60 DEG C, is coated uniformly on substrate surface, then
Semi-solid preparation is carried out with ultraviolet light；
Step c, brushing second UV priming paint: UV priming paint is coated uniformly on first of paint film, and uses ultraviolet light
Carry out all solidstate；
Step d, grinding process is smooth to paint film；
Step e, the brushing rest layers UV priming paint on second paint film, and using ultraviolet light alternately semi-solid preparation and
All solidstate；
Step f, after UV prime, grinding process to the smooth no bright spot of paint film；
Step g, Malaysia paint construction is carried out on the paint film after step f grinding process；
Step h, finish finally is sprayed on the paint film of Malaysia.
Compared with prior art, the construction technology of compound Malaysia paint provided by the invention has the advantage that
(1) the perfect collocation of Malaysia paint and UV photocuring system, not only has the level of color abundant and whole coating
Feel, and greatly improve the hardness and cohesive force of paint film after UV photocuring, simplify construction technology, save the cost is conducive to
It widelys popularize in market.
(2) paint film outermost layer coating paint cover, greatly strengthens the stain resistance of paint film.
(3) UV priming paint, finish and the Malaysia paint that the present invention uses are water-based material, use water as diluent, lower
It is carbon, more environmentally friendly, more energy efficient.
Construction method provided by the invention, not only with the spy that hardness is high, cohesive force is high, easy for construction, rate of drying is fast
Point, moreover it is possible to enhance adhesive force between coating, not crack at low or elevated temperatures, embody the abundant and whole coating effect of color
Fruit stereovision, while paint cover is coated, enhance the stain resistance of paint film.
And specifically, it is preferable to ground, the finish is fluorine carbon finish, and coating weight is 15-25g/m2。
Preferably, it is 100-180mj/m that semi-solid preparation treatment conditions described in step b and step e, which are ultraviolet ray intensity,2, purple
Outer smooth irradiation time 2-4 seconds.
Preferably, it is 200-280mj/m that all solidstate treatment conditions described in step c and step e, which are ultraviolet ray intensity,2, purple
Outer smooth irradiation time 2-4 seconds.
Preferably, in step h, if environment temperature is higher than 35 DEG C, drying retardant is added in finish and is sprayed, wherein
The additional amount of drying retardant is the 5%-10% of finish quality.
Preferably, in step h, finish is completed, each spray strip by the way of spraying by both direction shunting in length and breadth
The edge of band should overlap in the strip edge that previous item has sprayed, and width is laminated in 30-40%.
Preferably, it in step a, is polished with the sand paper of 300-500 mesh, removes substrate lagging surface blot and burr.
Preferably, grinding process is carried out using the sand paper of 300-500 mesh in step d.
Preferably, in step f, it is smooth that paint film is polishing to using the sand paper of 300-500 mesh first, then with 800-1200 purpose
Sand paper is polishing to paint film without bright spot.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1
UV priming paint, Malaysia paint and the fluorine carbon finish that this implementation 1 uses are all from the limited public affairs of Hebei morning sun industry and trade group
Department.
The embodiment of the present invention provides a kind of compound Malaysia paint, including UV priming paint, the Malaysia paint coated on the UV priming paint, institute
State the finish that coating is painted in Malaysia；Wherein UV priming paint is 4 layers, and using ultraviolet light alternately semi-solid preparation and Quan Gu
Change.Finish is fluorine carbon finish.
The construction technology of above-mentioned compound Malaysia paint, comprising the following steps:
Step a, base material treatment: being polished with 320 mesh sand paper, removes substrate lagging surface blot and burr.
Step b, it brushes first of UV priming paint: by UV priming paint heating water bath to 40 DEG C, being coated uniformly on substrate surface, be coated with
Amount is 20g/m2, semi-solid preparation, semi-solid preparation condition then are carried out with ultraviolet light are as follows: ultraviolet ray intensity 150mj/m2, ultraviolet light
Irradiation time 3 seconds；
Step c, brushing second UV priming paint: UV priming paint is coated uniformly on first of paint film, coating weight 30g/m2,
And all solidstate is carried out with ultraviolet light, all solidstate treatment conditions are that ultraviolet ray intensity is 250mj/m2, the ultraviolet light time 3
Second；
Step d, to be polishing to paint film using the sand paper of 320 mesh smooth；
Step e, brushing third road UV priming paint: UV priming paint is coated uniformly on second paint film, coating weight 30g/m2,
Then semi-solid preparation, semi-solid preparation condition are carried out with ultraviolet light are as follows: ultraviolet ray intensity 150mj/m2, the ultraviolet light time 3
Second；
Step f, it brushes the 4th UV priming paint: UV priming paint being coated uniformly on third road paint film, coating weight 30g/m2,
And all solidstate is carried out with ultraviolet light, all solidstate treatment conditions are that ultraviolet ray intensity is 250mj/m2, the ultraviolet light time 3
Second；
Step g, be polishing to that paint film is smooth using the sand paper of 320 mesh first, then with the sand paper of 1000 mesh be polishing to paint film without
Bright spot grinding process is to the smooth no bright spot of paint film；
Step h, Malaysia paint construction is carried out on the paint film after grinding process, it is 100g/m that coating weight is painted in Malaysia2, use is dedicated
Malaysia paint batch knife, one knife of a knife is criticized on metope scrapes similar positive (length) rectangular pattern, is not overlapped as far as possible between each pattern, and
And each rectangular angle as far as possible towards it is different, be staggered, there are the gap of half of pattern magnitude between pattern and pattern,
Next it will implement most important Malaysia paint second operation work after finishing together, and equally go benefit first with Malaysia paint batch knife
The gap that road construction stays, twice batch have formed Malaysia paint pattern effect after scraping completion, have been adjusted with stainless steel knife
Angle batch scrapes polishing, until metope gloss, completion such as marble；
Step i, spraying fluorine carbon finish, coating weight 20g/m finally are painted in Malaysia2, by both direction in length and breadth when spraying
Shunting is completed, and when construction will select dedicated spray gun continuous spray, and the direction for spraying paint stream should be as far as possible perpendicular to body surface, behaviour
The edge of each spray strip band should overlap in the previous strip edge sprayed when making, and width overlapping 1/3 guarantees that spraying is equal
It is even consistent, it can not be sometimes fast and sometimes slow.
Embodiment 2
UV priming paint, Malaysia paint and the fluorine carbon finish that this implementation 2 uses are all from the limited public affairs of Hebei morning sun industry and trade group
Department.
The embodiment of the present invention provides a kind of compound Malaysia paint, including UV priming paint, the Malaysia paint coated on the UV priming paint, institute
State the finish that coating is painted in Malaysia；Wherein UV priming paint is 4 layers, and using ultraviolet light alternately semi-solid preparation and Quan Gu
Change.Finish is fluorine carbon finish.
The construction technology of above-mentioned compound Malaysia paint, comprising the following steps:
Step a, base material treatment: being polished with 500 mesh sand paper, removes substrate lagging surface blot and burr.
Step b, it brushes first of UV priming paint: by UV priming paint heating water bath to 60 DEG C, being coated uniformly on substrate surface, be coated with
Amount is 25g/m2, semi-solid preparation, semi-solid preparation condition then are carried out with ultraviolet light are as follows: ultraviolet ray intensity 180mj/m2, ultraviolet light
Irradiation time 2 seconds；
Step c, brushing second UV priming paint: UV priming paint is coated uniformly on first of paint film, coating weight 25g/m2,
And all solidstate is carried out with ultraviolet light, all solidstate treatment conditions are that ultraviolet ray intensity is 280mj/m2, the ultraviolet light time 2
Second；
Step d, to be polishing to paint film using the sand paper of 400 mesh smooth；
Step e, brushing third road UV priming paint: UV priming paint is coated uniformly on second paint film, coating weight 25g/m2,
Then semi-solid preparation, semi-solid preparation condition are carried out with ultraviolet light are as follows: ultraviolet ray intensity 180mj/m2, the ultraviolet light time 3
Second；
Step f, it brushes the 4th UV priming paint: UV priming paint being coated uniformly on third road paint film, coating weight 25g/m2,
And all solidstate is carried out with ultraviolet light, all solidstate treatment conditions are that ultraviolet ray intensity is 200mj/m2, the ultraviolet light time 3
Second；
Step g, be polishing to that paint film is smooth using the sand paper of 400 mesh first, then with the sand paper of 1200 mesh be polishing to paint film without
Bright spot grinding process is to the smooth no bright spot of paint film；
Step h, Malaysia paint construction is carried out on the paint film after grinding process, it is 120g/m that coating weight is painted in Malaysia2, use is dedicated
Malaysia paint batch knife, one knife of a knife is criticized on metope scrapes similar positive (length) rectangular pattern, is not overlapped as far as possible between each pattern, and
And each rectangular angle as far as possible towards it is different, be staggered, there are the gap of half of pattern magnitude between pattern and pattern,
Next it will implement most important Malaysia paint second operation work after finishing together, and equally go benefit first with Malaysia paint batch knife
The gap that road construction stays, twice batch have formed Malaysia paint pattern effect after scraping completion, have been adjusted with stainless steel knife
Angle batch scrapes polishing, until metope gloss, completion such as marble；
Step i, spraying fluorine carbon finish, coating weight 25g/m finally are painted in Malaysia2, by both direction in length and breadth when spraying
Shunting is completed, and when construction will select dedicated spray gun continuous spray, and the direction for spraying paint stream should be as far as possible perpendicular to body surface, behaviour
The edge of each spray strip band should overlap in the previous strip edge sprayed when making, and width overlapping 40% guarantees spraying
Uniformity, can not be sometimes fast and sometimes slow.
Embodiment 3
UV priming paint, Malaysia paint and the fluorine carbon finish that this implementation 3 uses are all from the limited public affairs of Hebei morning sun industry and trade group
Department, drying retardant are BASF FE302X.
The embodiment of the present invention provides a kind of compound Malaysia paint, including UV priming paint, the Malaysia paint coated on the UV priming paint, institute
State the finish that coating is painted in Malaysia；Wherein UV priming paint is 4 layers, and using ultraviolet light alternately semi-solid preparation and Quan Gu
Change.Finish is fluorine carbon finish.
Above-mentioned compound Malaysia coating construction process, comprising the following steps:
Step a, base material treatment: being polished with 400 mesh sand paper, removes substrate lagging surface blot and burr.
Step b, it brushes first of UV priming paint: by UV priming paint heating water bath to 50 DEG C, being coated uniformly on substrate surface, be coated with
Amount is 15g/m2, semi-solid preparation, semi-solid preparation condition then are carried out with ultraviolet light are as follows: ultraviolet ray intensity 100mj/m2, ultraviolet light
Irradiation time 4 seconds；
Step c, brushing second UV priming paint: UV priming paint is coated uniformly on first of paint film, coating weight 35g/m2,
And all solidstate is carried out with ultraviolet light, all solidstate treatment conditions are that ultraviolet ray intensity is 280mj/m2, the ultraviolet light time 4
Second；
Step d, to be polishing to paint film using the sand paper of 500 mesh smooth；
Step e, brushing third road UV priming paint: UV priming paint is coated uniformly on second paint film, coating weight 35g/m2,
Then semi-solid preparation, semi-solid preparation condition are carried out with ultraviolet light are as follows: ultraviolet ray intensity 100mj/m2, the ultraviolet light time 4
Second；
Step f, it brushes the 4th UV priming paint: UV priming paint being coated uniformly on third road paint film, coating weight 35g/m2,
And all solidstate is carried out with ultraviolet light, all solidstate treatment conditions are that ultraviolet ray intensity is 280mj/m2, the ultraviolet light time 2
Second；
Step g, be polishing to that paint film is smooth using the sand paper of 320 mesh first, then with the sand paper of 1200 mesh be polishing to paint film without
Bright spot grinding process is to the smooth no bright spot of paint film；
Step h, Malaysia paint construction is carried out on the paint film after grinding process, it is 80g/m that coating weight is painted in Malaysia2, use is dedicated
Malaysia paint batch knife, one knife of a knife is criticized on metope scrapes similar positive (length) rectangular pattern, is not overlapped as far as possible between each pattern, and
And each rectangular angle as far as possible towards it is different, be staggered, there are the gap of half of pattern magnitude between pattern and pattern,
Next it will implement most important Malaysia paint second operation work after finishing together, and equally go benefit first with Malaysia paint batch knife
The gap that road construction stays, twice batch have formed Malaysia paint pattern effect after scraping completion, have been adjusted with stainless steel knife
Angle batch scrapes polishing, until metope gloss, completion such as marble；
Step i, fluorine carbon finish, coating weight 15g/m are finally sprayed on the paint film of Malaysia2, since environment temperature is up to 40
DEG C, drying retardant is added in fluorine carbon finish, the additional amount of drying retardant is the 10% of fluorine carbon finish quality, in spraying by vertical
Horizontal both direction shunting is completed, and when construction will select dedicated spray gun continuous spray, spray paint stream direction should as far as possible perpendicular to
Body surface, when operation the edge of each spray strip band should overlap in the previous strip edge sprayed, width overlapping
30%, guarantee spraying uniformity, it can not be sometimes fast and sometimes slow.
The advantage for the construction method that embodiment provides in order to better illustrate the present invention, below constructs embodiment 1,2,3
Obtained paint film carries out performance detection, and testing result is as shown in the table.
Pencil hardness examination criteria: GB/T6739-1996；
Spot-resistant examination criteria: HG/T4756-2014；
Weatherability examination criteria: GB/T 1865-2009；
Adhesive force examination criteria: GB/T 9286-98；
Rate of drying examination criteria: surface drying time: GB/T1728-89 (second method)；Do solid work the time: GB/T1728-89 (first
Method).
1 performance test results of table
As it can be seen from table 1 using construction method of the invention, obtained paint film has excellent stain resistance, weather-proof
Property, while greatly improving the hardness and adhesive force of paint film.
Adhesive force between each layer paint film of 1 preparation process of embodiment is subjected to performance detection, testing result is as follows.
2 adhesive force testing result of table
From table 2, it is apparent that using UV semi-solid preparation and all solidstate alternately mode, so that each layer paint film of UV priming paint
Between adhesive force it is stronger, to improve the adhesive force of compound Malaysia paint.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modification, equivalent replacement or improvement etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (8)
1. a kind of compound Malaysia paint, it is characterised in that: including the Malaysia paint coated on UV priming paint, the UV priming paint and the horse
To paint the finish of coating；Wherein at least 4 layers of UV priming paint.
2. compound Malaysia paint as described in claim 1, it is characterised in that: the finish is fluorine carbon finish, and coating weight
15-25g/m2；And/or
The coating weight of the Malaysia paint is 80-120g/m2；And/or
The coating weight of first layer UV priming paint is 15-25g/m2, the coating weight of remainder layer UV priming paint is 25-35g/m2。
3. the construction technology of compound Malaysia paint of any of claims 1 or 2, it is characterised in that: at least include the following steps:
Step a, base material treatment；
Step b, it brushes first of UV priming paint: UV priming paint being heated to 40-60 DEG C, is coated uniformly on substrate surface, then with purple
Outer illumination injects row semi-solid preparation；
Step c, brushing second UV priming paint: UV priming paint is coated uniformly on first of paint film, and is carried out with ultraviolet light
All solidstate；
Step d, grinding process is smooth to paint film；
Step e, the brushing rest layers UV priming paint on second paint film, and using ultraviolet light alternately semi-solid preparation and Quan Gu
Change；
Step f, after UV prime, grinding process to the smooth no bright spot of paint film；
Step g, Malaysia paint construction is carried out on the paint film after step f grinding process；
Step h, finish finally is sprayed on the paint film of Malaysia.
4. the construction technology of compound Malaysia paint as claimed in claim 3, it is characterised in that: half is solid described in step b and step e
It is 100-180mj/m that change treatment conditions, which are ultraviolet ray intensity,2, the ultraviolet light time 2-4 seconds.
5. the construction technology of compound Malaysia paint as claimed in claim 3, it is characterised in that: entirely solid described in step c and step e
It is 200-280mj/m that change treatment conditions, which are ultraviolet ray intensity,2, the ultraviolet light time 2-4 seconds.
6. the construction technology of compound Malaysia paint as claimed in claim 3, it is characterised in that: in step h, if environment temperature is higher than
At 35 DEG C, drying retardant is added in finish and is sprayed, wherein the additional amount of drying retardant is the 5%-10% of finish quality.
7. the construction technology of compound Malaysia paint as claimed in claim 3, it is characterised in that: in step h, finish is using spraying
Mode, by both direction shunting in length and breadth complete, the edge of each spray strip band should overlap the band that previous item has sprayed
On edge, width is laminated in 30-40%.
8. the construction technology of compound Malaysia paint as claimed in claim 3, it is characterised in that: in step a, with 300-500 purpose
Sand paper polishing, removes substrate lagging surface blot and burr；And/or
Grinding process is carried out using the sand paper of 300-500 mesh in step d；And/or
In step f, using the sand paper of 300-500 mesh to be polishing to first, paint film is smooth, then is polishing to the sand paper of 800-1200 mesh
Paint film is without bright spot.