CN103372532B - The construction technology of a kind of UV light finishing varnish on stone coating surface - Google Patents
The construction technology of a kind of UV light finishing varnish on stone coating surface Download PDFInfo
- Publication number
- CN103372532B CN103372532B CN201210128882.0A CN201210128882A CN103372532B CN 103372532 B CN103372532 B CN 103372532B CN 201210128882 A CN201210128882 A CN 201210128882A CN 103372532 B CN103372532 B CN 103372532B
- Authority
- CN
- China
- Prior art keywords
- coating
- brush
- irradiation
- light
- ray intensity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses UV light finishing varnish at the coating construction process on stone coating surface, it is characterized in that, comprise the following steps: material process; Brush head degree priming paint; Semi-solid preparation; Brush UV priming paint; All solidstate; Polishing; Brush UV priming paint; Semi-solid preparation; Brush UV priming paint; All solidstate; Sanding; Spraying stone coating coating; Roller coat light top coat top coat.Construction method of the present invention, can meet that hardness is good, transparency is high, feature that environmental protection, easy construction, rate of drying are fast, in turn enhance adhesive force between coating, all do not ftracture at low or elevated temperatures, embody the abundant of color and overall painting effect stereovision, enhance the stain resistance of paint film simultaneously.And be applicable to the woodwork having moulding.
Description
Technical field
The present invention relates to a kind of construction technology of painting effect, be specifically related to the coating process of UV light finishing varnish on stone coating surface.
Background technology
Use the furniture enterprise of UV paint to get more and more in recent years, and will be following development trend.The features such as to have hardness good for UV paint, and transparency is high, environmental protection, easy construction, rate of drying are fast.Its shortcoming is: equipment investment is large, coating surface levelling effect is poor, rolling wheel stamp is large, particularly mill base, the excessive negative effect added paint film adhesion and photocuring of look essence, hinder the reasonable demand of client to color, highlight a large deficiency of UV paint: color representation power is more dull, and painting effect stereovision is not strong.Along with improving constantly of living standard, people are to the design of personalization and require will get more and more, so traditional coating process can not meet modern Man's Demands far away.The splendid stone coating coating of decorative effect is inevitable play an increasingly important role in decorations field.Stone coating is a kind of high-grade aqueous architectural paint with the natural stone such as marble, granite decorative effect.The natural stone-powder of main employing shades of colour and different-grain diameter and macromolecule emulsion and various auxiliary agent process.With stone coating decoration, there is stronger third dimension, and the natural colour of tool natural real stone, give elegance, harmony, serious aesthetic feeling.Effect that is vivid, back to nature can be received.The advantages such as stone coating coating has fire prevention, waterproof, alkaline-resisting, anti-pollution, nonpoisonous and tasteless, bonding force is strong, will never fade, can effectively stop adverse circumstances to the erosion of facing, the service life extending ornament, be high-quality of new generation, high performance coating.But in order to the compactness of taking into account stone coating paint film and intensity, stone coating emulsion used is the emulsion that caking property is higher mostly, than being easier to dust stratification dirt, causes the stain resistance of paint film poor.
Summary of the invention
The object of the present invention is to provide the construction technology of a kind of UV light finishing varnish on stone coating surface, to meet the demand of big-and-middle furniture enterprise.The present invention designs the construction technology of a kind of UV light finishing varnish on stone coating surface, it is characterized in that comprising the following steps:
(1) material process: remove lagging surface blot and burr with sand paper;
(2) head degree priming paint is brushed; Water-bath is warmed to 40 ~ 60 DEG C, singly brushes once head degree priming paint, and coating weight is 20-25g/m
2;
(3) semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 150 ~ 180mj/m
2, UV-irradiation time 3-4 second;
(4) brush at the bottom of UV: use ultraviolet light UV brushing primer brush once, coating weight is 30-40g/m
2;
(5) all solidstate: UV-irradiation, ultraviolet ray intensity is 250 ~ 280mj/m
2, UV-irradiation time 3-4 second;
(6) polish: smooth with sand papering;
(7) brush at the bottom of UV: use ultraviolet light UV brushing primer brush once, coating weight is 30-40g/m
2;
(8) semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 150 ~ 180mj/m
2, UV-irradiation time 3-4 second;
(9) brush at the bottom of UV: use ultraviolet light UV brushing primer brush once, coating weight is 30-40g/m
2;
(10) all solidstate: UV-irradiation, ultraviolet ray intensity is 250 ~ 280mj/m
2, UV-irradiation time 3-4 second;
(11) polish: smooth without bright spot with sand papering;
(12) spray stone coating coating: according to the decorative pattern size of designing requirement, fluctuating sensing strong or weak adjustment spray gun gas output, spraying number of times also adjusts according to color, spraying 1-2 time;
(13) UV light finishing varnish is done: ultraviolet light roller coat light top coat top coat, coating weight 20-25g \ m
2;
(14) all solidstate: UV-irradiation, ultraviolet ray intensity is 350 ± 50mj/cm2, UV-irradiation time 3-4 second;
(15) packaging is detected.
Construction method of the present invention, hardness of paint film can be met good, the feature that transparency is high, environmental protection, easy construction, rate of drying are fast, in turn enhance adhesive force between coating, all do not ftracture at low or elevated temperatures, embody the abundant of color and overall painting effect stereovision, enhance the stain resistance of paint film simultaneously.
Detailed description of the invention
Embodiment 1:
Material process: remove lagging surface blot and burr with 320# sand paper;
Brush head degree priming paint; Water-bath is warmed to 40 DEG C, singly brushes once head degree priming paint, and coating weight is 20g/m
2; (brushing the model ZW43014 of the rich minister Chemical Manufacture in the optional Shanghai of head degree)
Semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 150mj/m
2, 3 seconds UV-irradiation time;
At the bottom of brush UV: use ultraviolet light UV brushing primer brush once, coating weight is 30g/m
2; (brushing the model 2020L of the rich minister Chemical Manufacture in optional Shanghai at the bottom of UV)
All solidstate: UV-irradiation, ultraviolet ray intensity is 250mj/m
2, 3 seconds UV-irradiation time;
Polishing: smooth with No. 320 sand paperings;
At the bottom of brush UV: use ultraviolet light UV brushing primer brush once, coating weight is 30g/m
2; Brush the model ZW43012 of the rich minister Chemical Manufacture in optional Shanghai at the bottom of UV),
Semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 150mj/m
2, 3 seconds UV-irradiation time;
At the bottom of brush UV: use ultraviolet light UV brushing primer brush once, coating weight is 30g/m
2; (brushing the model ZW43012 of the rich minister Chemical Manufacture in optional Shanghai at the bottom of UV)
All solidstate: UV-irradiation, ultraviolet ray intensity is 250mj/m
2, 3 seconds UV-irradiation time;
Polishing: use 1000# sand papering smooth without bright spot again with first 320#;
Detect packaging.
Embodiment 2:
Material process: remove lagging surface blot and burr with 320# sand paper;
Brush head degree priming paint; Water-bath is warmed to 60 DEG C, singly brushes once head degree priming paint, and coating weight is 25g/m
2; (brushing the model ZW43014 of the rich minister Chemical Manufacture in the optional Shanghai of head degree)
Semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 180mj/m
2, 4 seconds UV-irradiation time;
At the bottom of brush UV: use ultraviolet light UV brushing primer brush once, coating weight is 40g/m
2; (brushing the model 2020L of the rich minister Chemical Manufacture in optional Shanghai at the bottom of UV)
All solidstate: UV-irradiation, ultraviolet ray intensity is 280mj/m
2, 4 seconds UV-irradiation time;
Polishing: smooth with No. 320 sand paperings;
At the bottom of brush UV: use ultraviolet light UV brushing primer brush once, coating weight is 40g/m
2; Brush the model ZW43012 of the rich minister Chemical Manufacture in optional Shanghai at the bottom of UV),
Semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 180mj/m
2, 4 seconds UV-irradiation time;
At the bottom of brush UV: use ultraviolet light UV brushing primer brush once, coating weight is 40g/m
2; (brushing the model ZW43012 of the rich minister Chemical Manufacture in optional Shanghai at the bottom of UV)
All solidstate: UV-irradiation, ultraviolet ray intensity is 280mj/m
2, 4 seconds UV-irradiation time;
Polishing: with first using 1000# sand papering smooth without bright spot again with 320#, detects packaging.
Commercially available product is at the bottom of the priming paint of the rich minister Chemical Manufacture in described Shanghai, UV, can commercially maybe can with similar products substitution.
The present invention should the requirement of a lot of big-and-middle furniture enterprise, the coating construction process of a kind of UV light finishing varnish of special research and development on stone coating surface, can meet that hardness of paint film is good, transparency is high, feature that environmental protection, easy construction, rate of drying are fast, in turn enhance adhesive force between coating and coating, all do not ftracture at low or elevated temperatures, embody the abundant of color and overall painting effect stereovision, enhance the stain resistance of paint film simultaneously.Practicality and aesthetic property are all greatly improved, and this technique is favored by client deeply, wide market.
Claims (1)
1. UV light finishing varnish is in the construction technology on stone coating surface, it is characterized in that comprising the following steps:
(1) material process: remove lagging surface blot and burr with sand paper;
(2) head degree priming paint is brushed; Water-bath is warmed to 40 ~ 60 DEG C, singly brushes once head degree priming paint, and coating weight is 20-25g/m
2;
(3) semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 150 ~ 180mj/m
2, UV-irradiation time 3-4 second;
(4) brush at the bottom of UV: use ultraviolet light UV brushing primer brush once, coating weight is 30-40g/m
2;
(5) all solidstate: UV-irradiation, ultraviolet ray intensity is 250 ~ 280mj/m
2, UV-irradiation time 3-4 second;
(6) polish: smooth with sand papering;
(7) brush at the bottom of UV: use ultraviolet light UV brushing primer brush once, coating weight is 30-40g/m
2;
(8) semi-solid preparation: UV-irradiation, ultraviolet ray intensity is 150 ~ 180mj/m
2, UV-irradiation time 3-4 second;
(9) brush at the bottom of UV: use ultraviolet light UV brushing primer brush once, coating weight is 30-40g/m
2;
(10) all solidstate: UV-irradiation, ultraviolet ray intensity is 250 ~ 280mj/m
2, UV-irradiation time 3-4 second;
(11) polish: smooth without bright spot with sand papering;
(12) spray stone coating coating: according to the decorative pattern size of designing requirement, fluctuating sensing strong or weak adjustment spray gun gas output, spraying number of times also adjusts according to color, spraying 1-2 time;
(13) UV light finishing varnish is done: ultraviolet light roller coat light top coat top coat, coating weight 20-25g/m
2;
(14) all solidstate: UV-irradiation, ultraviolet ray intensity is 350 ± 50mj/cm
2, UV-irradiation time 3-4 second;
(15) packaging is detected.