CN101632982B - Method for producing wood floors of blue and white porcelain technology - Google Patents
Method for producing wood floors of blue and white porcelain technology Download PDFInfo
- Publication number
- CN101632982B CN101632982B CN2009103021329A CN200910302132A CN101632982B CN 101632982 B CN101632982 B CN 101632982B CN 2009103021329 A CN2009103021329 A CN 2009103021329A CN 200910302132 A CN200910302132 A CN 200910302132A CN 101632982 B CN101632982 B CN 101632982B
- Authority
- CN
- China
- Prior art keywords
- semi
- solid preparation
- primer
- consumption
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for producing wood floors of blue and white porcelain technology, which comprises the following production steps: (a) brushing an aqueous adhesive, drying with infrared rays, coating a sealing primer, and scraping elastic hardening putty; (b) coating the sealing primer, brushing the elastic hardening primer, and sanding; (c) spraying the primer, leveling, collecting plates and tenoning; (d) brushing the first line of wear-resistant primer, and then, brushing the second line of the wear-resistant primer after UV semi-solid preparation; (e) brushing the elastic hardening primer, and sanding; (f) spraying the primer, and leveling; and (g) coating the first line of elastic hardening finish, and then, coating the second line of the elastic hardening finish after UV semi-solid preparation. The floor produced by adopting the method of the invention forms a layer of hard and clear enamel on the paint surface, shows natural three-dimension effect and tactile sensation similar to the blue and white porcelain, has clear, bright and beautiful texture on the surface, has high hardness, good wear resistance and good scraping resistance of the paint film, has harmonious light colors which achieve perfect integral paving effect, can resist ultraviolet rays and can not fade easily.
Description
Technical field
The present invention relates to a kind of production method of timber floor, especially a kind of production method of wood floors of blue and white porcelain technology.
Background technology
The paint face on normal wood floor is more single, and superficial makings is clear inadequately, beautiful, lacks stereovision; And its lacquer painting poor adhesive force, hardness of paint film is not high yet, and wearability is generally lower; The scraping and wiping resistance performance of floor surface is also relatively poor, is easy to be scratched, and the service life on floor is not ideal enough, is difficult to satisfy market and consumer's higher demand.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of production method with higher hardness of paint film and stronger wearability, wood floors of blue and white porcelain technology that scraping and wiping resistance performance is good, thereby overcomes the deficiencies in the prior art.
For solving the problems of the technologies described above, technical scheme of the present invention is as follows: the production method of wood floors of blue and white porcelain technology.Comprise following production stage:
A, swabbing adhesive agent, seal coat is gone up in deburring behind the infrared drying then, and the UV semi-solid preparation is scraped elastic hardening putty, then the UV surface cure;
B, last seal coat, the UV semi-solid preparation is brushed elastic hardening primer then, UV surface cure, sanding;
C, usefulness flow coating machine showering priming paint, levelling, the UV semi-solid preparation is received the plate mortise then;
D, the brush first road wear-resistant primer, the UV semi-solid preparation, and then brush the second road wear-resistant primer, UV semi-solid preparation;
E, brush elastic hardening primer, UV surface cure, sanding then;
F, usefulness flow coating machine showering priming paint, levelling, UV semi-solid preparation then;
G, the last first road elastic hardening finish paint, the UV semi-solid preparation is gone up the second road elastic hardening finish paint then, and UV solidifies entirely.
In the production method of above-mentioned wood floors of blue and white porcelain technology, the consumption of the adhesive agent of water-based described in the step a is 10-20g/m
2, the consumption of elastic hardening putty is 10-30g/m
2, the consumption of seal coat is 20-40g/m
2The temperature of infrared drying is the 65-90 degree, and the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2, the amount of radiation of UV surface cure is 40-60mj/cm
2
In the production method of aforementioned wood floors of blue and white porcelain technology, the consumption of seal coat described in the step b is 10-30g/m
2, the consumption of elastic hardening primer is 10-30g/m
2The amount of radiation of UV semi-solid preparation is 40-60mj/cm
2, the amount of radiation of UV surface cure is 80-100mj/cm
2The used sand paper of sanding is 3M sand paper, and the sanding amount is 4-6g/m
2
In the production method of aforementioned wood floors of blue and white porcelain technology, the consumption of the priming paint of showering described in the step c is 80-100g/m
2, the temperature of levelling is the 65-90 degree, the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2
In the production method of aforementioned wood floors of blue and white porcelain technology, the consumption of the first road wear-resistant primer described in the steps d is 20-25g/m
2, the consumption of the second road wear-resistant primer is 15-20g/m
2The amount of radiation of UV semi-solid preparation is 40-60mj/cm
2
In the production method of aforementioned wood floors of blue and white porcelain technology, the consumption of elastic hardening primer described in the step e is 10-30g/m
2, the amount of radiation of UV surface cure is 80-100mj/cm
2The used sand paper of sanding is 3M sand paper, and the sanding amount is 6-9g/m
2
In the production method of aforementioned wood floors of blue and white porcelain technology, the consumption of the priming paint of showering described in the step f is 80-100g/m
2, the levelling temperature is the 65-90 degree, the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2
In the production method of aforementioned wood floors of blue and white porcelain technology, the consumption of the first road elastic hardening finish paint is 5-9g/m described in the step g
2, the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2The consumption of the second road elastic hardening finish paint is 4-8g/m
2, UV is complete, and the amount of radiation of solidifying is 200-280mj/cm
2
Beneficial effect of the present invention: compared with prior art, the present invention makes paint film successively go deep into wood-fibred inside by unique production process, and through the high temperature ultraviolet light polymerization, lacquer painting strong adhesion, hardness of paint film height, have stronger wearability and scraping and wiping resistance performance, its hardness of paint film, floor wearability and scraping and wiping resistance performance are considerably beyond the normal wood floor.The timber floor that adopts method of the present invention to produce has following characteristics: 1, incomparable wearability, its wearability can reach 1500-4000 changes, considerably beyond the anti-wear performance on normal wood floor.2, incomparable paint film adhesion, the present invention adopts the water-based adhesive agent, has guaranteed wooden the adhesive force superpower with lacquer painting in floor.3, incomparable hardness of paint film, its hardness can reach more than the 6H.4, incomparable scratch resistance, finish paint of the present invention adopts the elastic hardening finish paint, and the powerful hardness of paint film that promotes strengthens floor wearability and scratch resistance, and service life is considerably beyond the normal wood floor.5, incomparable porcelain texture, the present invention forms the clear enamel lacquer painting of the hard look of one deck matter at painted surface, its paint film is full, smooth, and light sensation is pure, presents natural innervation and texture as the blue and white porcelain, porcelain texture is strong, three-dimensional color is obvious, and stereovision is abundant, the integral body on the floor photochromic harmony of effect of mating formation, and uvioresistant is difficult for fading.6, incomparable transparency, high transparent priming materials of the present invention are thin, and (consumption is at 5~20g/m
2Between), lacquer painting is successively penetrating comprehensively, transparency height, the limpid exquisiteness of lacquer painting, floor surface clean mark, beautiful, gorgeous.
The present invention is further illustrated below in conjunction with the specific embodiment.
The specific embodiment
Embodiment.The production method of wood floors of blue and white porcelain technology, produce according to following step: a, remove the floor surface dust with dust-removing machine, use twin-roll machine swabbing adhesive agent then, the consumption of water-based adhesive agent is 15g/m
2Carry out drying with infrared drier then, baking temperature is the 65-90 degree, removes burr with the flash removed machine, and then with seal coat on the twin-roll machine, the consumption of seal coat is 30g/m
2, with UV drying machine semi-solid preparation (about half lamp), its amount of radiation is 40-60mj/cm
2, scrape elastic hardening putty with the putty machine again, with UV drying machine surface cure (about two and half lamps), its amount of radiation is 40-60mj/cm
2
B, with seal coat on the twin-roll machine, the seal coat consumption is 20g/m
2, with UV drying machine semi-solid preparation (about half lamp), amount of radiation is 40-60mj/cm
2Brush elastic hardening primer then, the consumption of elastic hardening primer is 20g/m
2, with UV drying machine surface cure (about two and half lamps), amount of radiation is 80-100mj/cm
2, use abrasive finishing machine abrasive finishing then, the used sand paper of sanding is 3M sand paper, the sanding amount is 5g/m
2
C, usefulness flow coating machine showering priming paint, the priming paint consumption is 80-100g/m
2, use the leveling machine levelling then, the levelling temperature is the 65-90 degree, with UV drying machine semi-solid preparation (about half lamp), amount of radiation is 40-60mj/cm
2, receive the plate mortise;
D, brush the first road wear-resistant primer with accurate single roll mill, the consumption of the first road wear-resistant primer is 20-25g/m
2, use UV drying machine semi-solid preparation (about half lamp) then, amount of radiation is 40-60mj/cm
2Brush the second road wear-resistant primer with accurate single roll mill again, the consumption of the second road wear-resistant primer is 15-20g/m
2, with UV drying machine semi-solid preparation (about half lamp), amount of radiation is 40-60mj/cm
2
E, brush elastic hardening primer with twin-roll machine, the consumption of elastic hardening primer is 20g/m
2, with UV drying machine surface cure (about two and half lamps), amount of radiation is 80-100mj/cm
2, use abrasive finishing machine abrasive finishing then, used sand paper is 3M sand paper, the sanding amount is 8g/m
2
F, remove the floor surface dust with dust-removing machine, use flow coating machine showering priming paint then, the priming paint consumption is 80-100g/m
2, use the leveling machine levelling, the levelling temperature is the 65-90 degree, uses UV drying machine semi-solid preparation (about half lamp) again, amount of radiation is 40-60mj/cm
2
G, with the first road elastic hardening finish paint on the twin-roll machine, the consumption of the first road elastic hardening finish paint is 7g/m
2, with UV drying machine semi-solid preparation (about half lamp), amount of radiation is 40-60mj/cm
2Go up the second road elastic hardening finish paint then, the consumption of the second road elastic hardening finish paint is 6g/m
2, solidify (about two and half lamps add a full lamp) entirely with the UV drying machine, amount of radiation is 200-280mj/cm
2, receive at last plate, the packing get final product.Water-based adhesive agent in this example, elastic hardening putty, seal coat, elastic hardening primer, priming paint, wear-resistant primer and elastic hardening finish paint are the commercially available prod.
Embodiments of the present invention are not limited to the foregoing description, and the various variations of making under the prerequisite that does not break away from aim of the present invention all belong within protection scope of the present invention.
Claims (1)
1. the production method of a wood floors of blue and white porcelain technology is characterized in that, comprises following production stage:
A, swabbing adhesive agent, seal coat is gone up in deburring behind the infrared drying then, and the UV semi-solid preparation is scraped elastic hardening putty, then the UV surface cure;
B, last seal coat, the UV semi-solid preparation is brushed elastic hardening primer then, UV surface cure, sanding;
C, usefulness flow coating machine showering priming paint, levelling, the UV semi-solid preparation is received the plate mortise then;
D, the brush first road wear-resistant primer, the UV semi-solid preparation, and then brush the second road wear-resistant primer, UV semi-solid preparation;
E, brush elastic hardening primer, UV surface cure, sanding then;
F, usefulness flow coating machine showering priming paint, levelling, UV semi-solid preparation then;
G, the last first road elastic hardening finish paint, the UV semi-solid preparation is gone up the second road elastic hardening finish paint then, and UV solidifies entirely;
The consumption of the adhesive agent of water-based described in the step a is 10-20g/m
2, the consumption of elastic hardening putty is 10-30g/m
2, the consumption of seal coat is 20-40g/m
2The temperature of infrared drying is the 65-90 degree, and the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2, the amount of radiation of UV surface cure is 40-60mj/cm
2The consumption of seal coat described in the step b is 10-30g/m
2, the consumption of elastic hardening primer is 10-30g/m
2The amount of radiation of UV semi-solid preparation is 40-60mj/cm
2, the amount of radiation of UV surface cure is 80-100mj/cm
2The used sand paper of sanding is 3M sand paper, and the sanding amount is 4-6g/m
2The consumption of the priming paint of showering described in the step c is 80-100g/m
2, the temperature of levelling is the 65-90 degree, the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2The consumption of the first road wear-resistant primer described in the steps d is 20-25g/m
2, the consumption of the second road wear-resistant primer is 15-20g/m
2The amount of radiation of UV semi-solid preparation is 40-60mj/cm
2The consumption of elastic hardening primer described in the step e is 10-30g/m
2, the amount of radiation of UV surface cure is 80-100mj/cm
2The used sand paper of sanding is 3M sand paper, and the sanding amount is 6-9g/m
2The consumption of the priming paint of showering described in the step f is 80-100g/m
2, the levelling temperature is the 65-90 degree, the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2The consumption of the first road elastic hardening finish paint is 5-9g/m described in the step g
2, the amount of radiation of UV semi-solid preparation is 40-60mj/cm
2The consumption of the second road elastic hardening finish paint is 4-8g/m
2, UV is complete, and the amount of radiation of solidifying is 200-280mj/cm
2