CN109535520A - 一种防静电、防腐蚀epe泡沫塑料 - Google Patents

一种防静电、防腐蚀epe泡沫塑料 Download PDF

Info

Publication number
CN109535520A
CN109535520A CN201811226595.7A CN201811226595A CN109535520A CN 109535520 A CN109535520 A CN 109535520A CN 201811226595 A CN201811226595 A CN 201811226595A CN 109535520 A CN109535520 A CN 109535520A
Authority
CN
China
Prior art keywords
parts
foamed plastics
agent
epe
anticorrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811226595.7A
Other languages
English (en)
Inventor
陈传湖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Rongmao Plastic Packaging Material Co Ltd
Original Assignee
Anhui Rongmao Plastic Packaging Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Rongmao Plastic Packaging Material Co Ltd filed Critical Anhui Rongmao Plastic Packaging Material Co Ltd
Priority to CN201811226595.7A priority Critical patent/CN109535520A/zh
Publication of CN109535520A publication Critical patent/CN109535520A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种防静电、防腐蚀EPE泡沫塑料，涉及塑料加工技术领域。所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯60‑80份、聚氯乙烯树脂12‑16份、石墨烯微片4‑6份、纳米二氧化硅5‑8份、柠檬酸4‑8份、磺酸钠1‑2份、庚二酸钙1‑3份、炭黑3‑4份、玻璃纤维2‑3份、发泡剂2‑3份、成核剂1‑2份、抗氧化剂2‑3份、抗紫外线剂1‑2份、分散剂1‑2份。本发明克服了现有技术的不足，在保证EPE材料原有的高强度、高回弹不易损坏的优良性质的同时，增强其耐腐蚀性和抗老化性，有效增加EPE塑料泡沫的使用寿命，并且本发明通过调节配方，有效增加产品的抗静电能力，加大材料的使用范围。

Description

一种防静电、防腐蚀EPE泡沫塑料
技术领域
本发明涉及塑料加工技术领域，具体涉及一种防静电、防腐蚀EPE泡沫塑料。
背景技术
聚乙烯发泡棉是非交联闭孔结构 , 是一种新型环保的 包装材料。它由 低密度聚乙烯脂经物理发泡产生无数的独立气泡构成。克服了普通 发泡胶易碎、变形、回复性差的缺点。具有隔水防潮、防震、隔音、保温、可塑性能佳、韧性强、循环再造、环保、抗撞力强等诸多优点，亦具有很好的抗化学性能。是传统包装材料的理想替代品。广泛应用于 电子电器、 仪器仪表、 电脑、音响、 医疗器械、 工控机箱、 灯饰、工艺品、玻璃、陶瓷、家电、喷涂、家俱、酒类及 礼品包装、 五金制品、 玩具、 瓜果、 皮鞋的 内包装、日用品等多种产品的包装。
静电是一种客观的自然现象，产生的方式多种，如接触、摩擦等。静电防护技术，如电子工业、石油工业、兵器工业、纺织工业、橡胶工业以及兴航与军事领域的静电危害，寻求减少静电造成的损失。由于EPE泡沫运用范围广阔，于是对于其使用效果和使用寿命均有一定的要求，如何改善其性能达到抗静电防腐蚀为现在的一大研究方向。
发明内容
针对现有技术不足，本发明提供一种防静电、防腐蚀EPE泡沫塑料，在保证EPE材料原有的隔音、防震、保温的优良性质的同时，增强其耐腐蚀性和抗老化性，有效增加EPE塑料泡沫的使用寿命，并且本发明通过调节配方，有效增加产品的抗静电能力，加大材料的使用范围。
为实现以上目的，本发明的技术方案通过以下技术方案予以实现：
一种防静电、防腐蚀EPE泡沫塑料，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯60-80份、聚氯乙烯树脂12-16份、石墨烯微片4-6份、纳米二氧化硅5-8份、柠檬酸4-8份、磺酸钠1-2份、庚二酸钙1-3份、炭黑3-4份、玻璃纤维2-3份、发泡剂2-3份、成核剂1-2份、抗氧化剂2-3份、抗紫外线剂1-2份、分散剂1-2份。
优选的，一种防静电、防腐蚀EPE泡沫塑料，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯70份、聚氯乙烯树脂14份、石墨烯微片5份、纳米二氧化硅6份、柠檬酸6份、磺酸钠1.5份、庚二酸钙2份、炭黑3.5份、玻璃纤维2.5份、发泡剂2.5份、成核剂1.5份、抗氧化剂2.5份、抗紫外线剂1.5份、分散剂1.5份。
优选的，所述发泡剂为碳酸钙、正庚烷、十二烷基硫酸钠、脂肪醇聚氧乙烯醚硫酸钠和硅藻土质量比4∶2∶1∶1∶2的混合物。
优选的，所述成核剂为苯甲酸镉 、草酸钛、水杨酸铋质量比1∶2∶1的混合物。
优选的，所述抗氧化剂为二氢喹啉、2，6-三级丁基-4-甲基苯酚、硫代二丙酸双酯和三辛酯质量比2∶1∶2∶3的混合物。
优选的，所述抗紫外线剂为二苯甲酮和其衍生物中的任意一种。
优选的，所述分散剂为聚丙烯酰胺、乙烯基双硬脂酰胺和脂肪酸甲酯质量比16∶13∶9。
优选的，所述泡沫塑料在制作过程中先将聚氯乙烯树脂与庚二酸钙在高温下熔融搅拌改性后，再与其它物质混合制造。
本发明提供一种防静电、防腐蚀EPE泡沫塑料，与现有技术相比优点在于：
（1）本发明添加有庚二酸钙对聚氯乙烯树脂进行改性处理，能有效提升最终所得泡沫的强度和耐腐蚀性，增加泡沫的使用寿命，同时使泡沫的各类性能更佳稳定。
（2）本发明添加有石墨烯微片、纳米二氧化硅、柠檬酸和磺酸钠，能有效提升所得泡沫的耐磨性和抗静电能力，并且还添加有炭黑，在高效防静电的基础上能促进发泡，增强泡沫的稳定性，加快发泡速率，并且节约发泡成本。
（3）本发明发泡剂采用有机发泡和无机发泡的组合发泡方式，有效的增加发泡的速率，同时使所得泡沫孔隙率加大，增强泡沫抗压能力。
（4）本发明添加有抗氧化剂和抗紫外线剂，在有效减缓泡沫的老化速度的同时与泡沫中其它配方成分相互配合反应，增加泡沫的耐腐蚀性能。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面结合本发明实施例对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
一种防静电、防腐蚀EPE泡沫塑料，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯60份、聚氯乙烯树脂12份、石墨烯微片4份、纳米二氧化硅5份、柠檬酸4份、磺酸钠1份、庚二酸钙1份、炭黑3份、玻璃纤维2份、发泡剂2份、成核剂1份、抗氧化剂2份、抗紫外线剂1份、分散剂1份。
其中，所述发泡剂为碳酸钙、正庚烷、十二烷基硫酸钠、脂肪醇聚氧乙烯醚硫酸钠和硅藻土质量比4∶2∶1∶1∶2的混合物；所述成核剂为苯甲酸镉 、草酸钛、水杨酸铋质量比1∶2∶1的混合物；所述抗氧化剂为二氢喹啉、2，6-三级丁基-4-甲基苯酚、硫代二丙酸双酯和三辛酯质量比2∶1∶2∶3的混合物；所述抗紫外线剂为二苯甲酮和其衍生物中的任意一种；所述分散剂为聚丙烯酰胺、乙烯基双硬脂酰胺和脂肪酸甲酯质量比16∶13∶9；所述泡沫塑料在制作过程中先将聚氯乙烯树脂与庚二酸钙在高温下熔融搅拌改性后，再与其它物质混合制造。
实施例2：
一种防静电、防腐蚀EPE泡沫塑料，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯80份、聚氯乙烯树脂16份、石墨烯微片6份、纳米二氧化硅8份、柠檬酸8份、磺酸钠2份、庚二酸钙3份、炭黑4份、玻璃纤维3份、发泡剂3份、成核剂2份、抗氧化剂3份、抗紫外线剂2份、分散剂2份。
其中，所述发泡剂为碳酸钙、正庚烷、十二烷基硫酸钠、脂肪醇聚氧乙烯醚硫酸钠和硅藻土质量比4∶2∶1∶1∶2的混合物；所述成核剂为苯甲酸镉 、草酸钛、水杨酸铋质量比1∶2∶1的混合物；所述抗氧化剂为二氢喹啉、2，6-三级丁基-4-甲基苯酚、硫代二丙酸双酯和三辛酯质量比2∶1∶2∶3的混合物；所述抗紫外线剂为二苯甲酮和其衍生物中的任意一种；所述分散剂为聚丙烯酰胺、乙烯基双硬脂酰胺和脂肪酸甲酯质量比16∶13∶9；所述泡沫塑料在制作过程中先将聚氯乙烯树脂与庚二酸钙在高温下熔融搅拌改性后，再与其它物质混合制造。
实施例3：
一种防静电、防腐蚀EPE泡沫塑料，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯70份、聚氯乙烯树脂14份、石墨烯微片5份、纳米二氧化硅6份、柠檬酸6份、磺酸钠1.5份、庚二酸钙2份、炭黑3.5份、玻璃纤维2.5份、发泡剂2.5份、成核剂1.5份、抗氧化剂2.5份、抗紫外线剂1.5份、分散剂1.5份。
其中，所述发泡剂为碳酸钙、正庚烷、十二烷基硫酸钠、脂肪醇聚氧乙烯醚硫酸钠和硅藻土质量比4∶2∶1∶1∶2的混合物；所述成核剂为苯甲酸镉 、草酸钛、水杨酸铋质量比1∶2∶1的混合物；所述抗氧化剂为二氢喹啉、2，6-三级丁基-4-甲基苯酚、硫代二丙酸双酯和三辛酯质量比2∶1∶2∶3的混合物；所述抗紫外线剂为二苯甲酮和其衍生物中的任意一种；所述分散剂为聚丙烯酰胺、乙烯基双硬脂酰胺和脂肪酸甲酯质量比16∶13∶9；所述泡沫塑料在制作过程中先将聚氯乙烯树脂与庚二酸钙在高温下熔融搅拌改性后，再与其它物质混合制造。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个……”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。

Claims (8)

1.一种防静电、防腐蚀EPE泡沫塑料，其特征在于，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯60-80份、聚氯乙烯树脂12-16份、石墨烯微片4-6份、纳米二氧化硅5-8份、柠檬酸4-8份、磺酸钠1-2份、庚二酸钙1-3份、炭黑3-4份、玻璃纤维2-3份、发泡剂2-3份、成核剂1-2份、抗氧化剂2-3份、抗紫外线剂1-2份、分散剂1-2份。
2.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于，所述EPE泡沫塑料由以下重量份的原料制成：低密度聚乙烯70份、聚氯乙烯树脂14份、石墨烯微片5份、纳米二氧化硅6份、柠檬酸6份、磺酸钠1.5份、庚二酸钙2份、炭黑3.5份、玻璃纤维2.5份、发泡剂2.5份、成核剂1.5份、抗氧化剂2.5份、抗紫外线剂1.5份、分散剂1.5份。
3.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于：所述发泡剂为碳酸钙、正庚烷、十二烷基硫酸钠、脂肪醇聚氧乙烯醚硫酸钠和硅藻土质量比4∶2∶1∶1∶2的混合物。
4.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于：所述成核剂为苯甲酸镉 、草酸钛、水杨酸铋质量比1∶2∶1的混合物。
5.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于：所述抗氧化剂为二氢喹啉、2，6-三级丁基-4-甲基苯酚、硫代二丙酸双酯和三辛酯质量比2∶1∶2∶3的混合物。
6.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于：所述抗紫外线剂为二苯甲酮和其衍生物中的任意一种。
7.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于：所述分散剂为聚丙烯酰胺、乙烯基双硬脂酰胺和脂肪酸甲酯质量比16∶13∶9。
8.根据权利要求1所述的一种防静电、防腐蚀EPE泡沫塑料，其特征在于：所述泡沫塑料在制作过程中先将聚氯乙烯树脂与庚二酸钙在高温下熔融搅拌改性后，再与其它物质混合制造。
CN201811226595.7A 2018-10-22 2018-10-22 一种防静电、防腐蚀epe泡沫塑料 Pending CN109535520A (zh)