CN109534714A - 高性能减水剂 - Google Patents
高性能减水剂 Download PDFInfo
- Publication number
- CN109534714A CN109534714A CN201811626720.3A CN201811626720A CN109534714A CN 109534714 A CN109534714 A CN 109534714A CN 201811626720 A CN201811626720 A CN 201811626720A CN 109534714 A CN109534714 A CN 109534714A
- Authority
- CN
- China
- Prior art keywords
- mother liquor
- reducing agent
- agent
- water reducing
- performance water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高性能减水剂,包括以下质量百分比原料:保坍母液20‑22%、减水母液24‑26%、糊精0.9‑1.1%、白砂糖0.9‑1.1%、葡萄糖酸钠1.9‑2.1%、引气剂0.07‑0.09%、消泡剂0.05‑0.07%、水48.86‑50.86%;保坍母液为丙烯酸羟乙酯和甲基烯丙基聚氧乙烯醚共聚生产物;减水母液为异丁烯醇聚氧乙烯醚和丙烯酸羟乙酯的合成物;消泡剂为聚醚型消泡剂;引气剂为十二烷基硫酸钠。解决常规减水剂在混凝土在使用过程中减水率较低、保坍能差、适用面窄等问题。
Description
技术领域
本发明及高分子材料的新型加工和应用技术,具体涉及高性能减水剂。
背景技术
减水剂是一种在维持混凝土坍落度不变的条件下,能减少拌合用水量的混凝土外加剂。大多属于阴离子表面活性剂,有木质素磺酸盐、萘磺酸盐甲醛聚合物等。加入混凝土拌合物后对水泥颗粒有分散作用,能改善其工作性,减少单位用水量,改善混凝土拌合物的流动性;或减少单位水泥用量,节约水泥。外观形态分为水剂和粉剂。水剂含固量一般有20%,40%,60%(又称母液),粉剂含固量一般为98%。根据减水剂减水及增强能力,分为普通减水剂(又称塑化剂,减水率不小于8%)、高效减水剂(又称超塑化剂,减水率不小于14%)和高性能减水剂(减水率不小于25%),并又分别分为早强型、标准型和缓凝型。按组成材料分为:(1)木质素磺酸盐类;(2)多环芳香族盐类;(3)水溶性树脂磺酸盐类。普通减水剂宜用于日最低气温5℃以上施工的混凝土。高性能减水剂宜用于日最低气温0℃以上施工的混凝土,并适用于制备大流动性混凝土、高强混凝土以及蒸养混凝土。
发明内容
本发明的目的在于提供一种高性能减水剂,解决常规减水剂在混凝土在使用过程中减水率较低、保坍能差、适用面窄等问题。
为解决上述的技术问题,本发明采用以下技术方案:
一种高性能减水剂,包括以下质量百分比原料:保坍母液20-22%、减水母液24-26%、糊精0.9-1.1%、白砂糖0.9-1.1%、葡萄糖酸钠1.9-2.1%、引气剂0.07-0.09%、消泡剂0.05-0.07%、水48.86-50.86%。
进一步的;所述保坍母液为丙烯酸羟乙酯和甲基烯丙基聚氧乙烯醚共聚生产物。
进一步的;所述减水母液为异丁烯醇聚氧乙烯醚和丙烯酸羟乙酯的合成物。
进一步的;所述消泡剂为聚醚型消泡剂。
进一步的;所述引气剂为十二烷基硫酸钠。
进一步的;搅拌机中加水搅拌,设置转速为50r/min,先加入糊精搅拌5min,再加入葡萄糖酸钠搅拌2min,再加入白砂糖搅拌5min,再加入保坍母液搅拌2min后,再加入减水母液搅拌5min,再加入引气剂搅拌2min后,最后加入消泡剂搅拌19min,取样检验后,即为成品。
与现有技术相比,本发明的至少具有以下有益效果之一:
1、原料按照比例添加,适量糊精使得混凝土不扒底,提高和易性,流动性好;适量的葡萄糖酸钠、白砂糖可缓凝保障混凝土的保坍效果;产品减水率提高,使混凝土流动后和易性好,适应性强,便于施工,保证混凝土的强度,保证强度的前提下,减少水泥用量,保证工程质量。
2、减水母液在产品生产中的添加,使得混凝土高减水,提高后期强度。
3、保坍母液在产品生产中的添加,使得混凝土提高坍密度,保证施工,适用天热施工和复杂工序施工。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
实施例1:
高性能减水剂,包括以下质量百分比原料:保坍母液21.32%、减水母液26%、糊精0.9%、白砂糖0.9%、葡萄糖酸钠1.9%、引气剂0.07%、消泡剂0.05%、水48.86%;原料按照比例添加,适量糊精使得混凝土不扒底,提高和易性,流动性好;适量的葡萄糖酸钠、白砂糖可保障混凝土的保坍效果;产品减水率提高,使混凝土流动后和易性好,适应性强,便于施工,保证混凝土的强度,保证工程质量。
实施例2:
在实施例1的基础上,高性能减水剂,包括以下质量百分比原料:保坍母液20.68%、减水母液24%、糊精1.1%、白砂糖1.1%、葡萄糖酸钠2.1%、引气剂0.08%、消泡剂0.06%、水50.86%;原料按照比例添加,适量糊精使得混凝土不扒底,提高和易性,流动性好;适量的葡萄糖酸钠、白砂糖可保障混凝土的保坍效果;产品减水率提高,使混凝土流动后和易性好,适应性强,便于施工,保证混凝土的强度,保证工程质量。
实施例3:
在实施例1-2的基础上,高性能减水剂,包括以下质量百分比原料:保坍母液21%、减水母液25%、糊精1%、白砂糖1%、葡萄糖酸钠2%、引气剂0.08%、消泡剂0.06%、水49.86%;原料按照比例添加,适量糊精使得混凝土不扒底,提高和易性,流动性好;适量的葡萄糖酸钠、白砂糖可保障混凝土的保坍效果;产品减水率提高,使混凝土流动后和易性好,适应性强,便于施工,保证混凝土的强度,保证工程质量。
实施例4:
在实施例1-3的基础上,保坍母液为丙烯酸羟乙酯和甲基烯丙基聚氧乙烯醚共聚生产物;保坍母液在原料中的添加,使得混凝土的保坍效果好。
实施例5:
在实施例1-4的基础上,减水母液为异丁烯醇聚氧乙烯醚和丙烯酸羟乙酯的合成物;减水母液在原料中的添加,使得混凝土提高减水效果。
实施例6:
在实施例1-5的基础上,消泡剂为聚醚型消泡剂;消泡剂的适量加入使得在制备过程产品中减少气泡产生,产品使得混凝土密实度提高,气孔少,提高混凝土强度。
实施例7:
在实施例1-6的基础上,引气剂为十二烷基硫酸钠;引气剂的适量加入产生减少混凝土泌水和离析,使得混凝土流动性好,便于泵送作业,提高混凝土的均质性。
实施例8:
在实施例1-7的基础上,搅拌机中加水搅拌,设置转速为50r/min,先加入糊精搅拌5min,再加入葡萄糖酸钠搅拌2min,再加入白砂糖搅拌5min,再加入保坍母液搅拌2min后,再加入减水母液搅拌5min,再加入引气剂搅拌2min后,最后加入消泡剂搅拌19min,取样检验后,即为成品;在搅拌机中按照原料的比例依次加入,控制搅拌速度和每种原料的搅拌时间,制备的减水剂效果好,制备的产品在取样检测,满足GB8076-2008以及施工相关标准,即可使用。
尽管这里参照本发明的多个解释性实施例对本发明进行了描述,但是,应该理解,本领域技术人员可以设计出很多其他的修改和实施方式,这些修改和实施方式将落在本申请公开的原则范围和精神之内。更具体地说,在本申请公开和权利要求的范围内,可以对主题组合布局的组成部件和/或布局进行多种变型和改进。除了对组成部件和/或布局进行的变形和改进外,对于本领域技术人员来说,其他的用途也将是明显的。
Claims (6)
1.一种高性能减水剂,其特征在于:包括以下质量百分比原料:保坍母液20-22%、减水母液24-26%、糊精0.9-1.1%、白砂糖0.9-1.1%、葡萄糖酸钠1.9-2.1%、引气剂0.07-0.09%、消泡剂0.05-0.07%、水48.86-50.86%。
2.根据权利要求1所述的高性能减水剂,其特征在于:所述保坍母液为丙烯酸羟乙酯和甲基烯丙基聚氧乙烯醚共聚生产物。
3.根据权利要求1所述的高性能减水剂,其特征在于:所述减水母液为异丁烯醇聚氧乙烯醚和丙烯酸羟乙酯的合成物。
4.根据权利要求1所述的高性能减水剂,其特征在于:所述消泡剂为聚醚型消泡剂。
5.根据权利要求1所述的高性能减水剂,其特征在于:所述引气剂为十二烷基硫酸钠。
6.根据权利要求1-5任意一条权利要求所述的高性能减水剂,其特征在于:搅拌机中加水搅拌,设置转速为50r/min,先加入糊精搅拌5min,再加入葡萄糖酸钠搅拌2min,再加入白砂糖搅拌5min,再加入保坍母液搅拌2min后,再加入减水母液搅拌5min,再加入引气剂搅拌2min后,最后加入消泡剂搅拌19min,取样检验后,即为成品。