CN109531761A - 一种阻燃纤维板及其制作方法 - Google Patents

一种阻燃纤维板及其制作方法 Download PDF

Info

Publication number
CN109531761A
CN109531761A CN201710864209.6A CN201710864209A CN109531761A CN 109531761 A CN109531761 A CN 109531761A CN 201710864209 A CN201710864209 A CN 201710864209A CN 109531761 A CN109531761 A CN 109531761A
Authority
CN
China
Prior art keywords
parts
flame retardant
timber
sio
fibre board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710864209.6A
Other languages
English (en)
Inventor
刘智阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou Qiao Bang Furniture Manufacturing Co Ltd
Original Assignee
Guizhou Qiao Bang Furniture Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Qiao Bang Furniture Manufacturing Co Ltd filed Critical Guizhou Qiao Bang Furniture Manufacturing Co Ltd
Priority to CN201710864209.6A priority Critical patent/CN109531761A/zh
Publication of CN109531761A publication Critical patent/CN109531761A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃纤维板及其制作方法，该阻燃纤维板是由木料板层、喷涂在木料板层上的阻燃涂料层以及设在木料板层之间的阻燃材料层构成；阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2制成；阻燃材料层是由磷酸三甲苯酯、β‑三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2制成。本发明的阻燃纤维板具有板材较厚，不易破损，隔热效果较好，阻燃效果好的优点。

Description

一种阻燃纤维板及其制作方法
技术领域
本发明涉及一种纤维板，特别是一种阻燃纤维板及其制作方法。
背景技术
纤维板是由木质纤维素纤维交织成型并利用其固有胶粘性能制成的人造板。制造过程中可以施加胶粘剂和（或）添加剂。
纤维板又名密度板，是以木质纤维或其他植物素纤维为原料，施加脲醛树脂或其他适用的胶粘剂制成的人造板。制造过程中可以施加胶粘剂和（或）添加剂。纤维板具有材质均匀、纵横强度差小、不易开裂等优点，用途广泛。制造 1立方米纤维板约需2.5～3立方米的木材，可代替3立方米锯材或5立方米原木。发展纤维板生产是木材资源综合利用的有效途径。但纤维板中含木料元素较多，极易燃烧，当起火时会迅速燃烧，扩大火势。
阻燃板，作为一种防火建材被广大建筑企业所应用，尤其是应用在现代住宅建筑中比较多，其主要应用于住宅外墙体的防火及保温。但阻燃板一般较薄，极易破损；并且由于现有阻燃板通常只是喷涂阻燃涂料，并且阻燃板较薄，隔热效果有限，当温度较高时仍会使阻燃板燃烧，阻燃效果较差。因此，现有的阻燃纤维板存在板材较薄，极易破损，隔热效果较差，阻燃效果不理想的缺点。
发明内容
本发明的目的在于，提供一种阻燃纤维板及其制作方法。本发明的阻燃纤维板具有板材较厚，不易破损，隔热效果较好，阻燃效果好的优点。
本发明的技术方案：一种阻燃纤维板，该阻燃纤维板是由木料板层、喷涂在木料板层上的阻燃涂料层以及设在木料板层之间的阻燃材料层构成。
前述的一种阻燃纤维板中，所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂80~100份，偏二氯乙烯共聚物乳液30~60份，聚磷酸铵20~40份，有机卤代磷酸酯20~40份，钛白粉10~20份，锑白粉10~20份，SiO210~20份。
前述的一种阻燃纤维板中，所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯5~10份，β-三氯乙烯磷酸酯5~10份，氢氧化镁10~20份，氢氧化铝10~20份，十溴联苯酸5~10份，四溴双酚A5~10份，氯化石蜡1~4份，SiO220~40份。
前述的一种阻燃纤维板中，所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂90份，偏二氯乙烯共聚物乳液45，聚磷酸铵30份，有机卤代磷酸酯30份，钛白粉15份，锑白粉15份，SiO215份。
前述的一种阻燃纤维板中，所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯8份，β-三氯乙烯磷酸酯7份，氢氧化镁15份、氢氧化铝15份，十溴联苯酸6份，四溴双酚A6份，氯化石蜡3份，SiO215份。
前述的一种阻燃纤维板的制作方法，该方法包括以下步骤；
A：将磷酸三甲苯酯、β-三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2混合均匀，制成阻燃材料；
B：根据生产需求，将木料制成相对应规格的木料板；
C：将阻燃材料和胶粘剂混合均匀，向两块木料板之间填充厚度为0.3~0.5cm的阻燃材料层，并将木料板粘接；
D：将填充了阻燃材料和粘接完成的木料板放置24~36h，使木料板粘接稳定；
E：取树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2混合搅拌均匀，制成阻燃涂料；
F：待木板板粘接稳定后，在木板表面均匀喷涂阻燃涂料，待阻燃涂料风干，制得阻燃纤维板。
本发明的优点是：通过设置双层式木料板结构，增加阻燃纤维板厚度，增加隔热能力；通过在木料板层之间设置阻燃材料层，提高阻燃纤维板的阻燃能力；选用树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2制作阻燃涂料，形成的阻燃涂料防护层具有阻燃隔热效果好，不易破损的优点；选用磷酸三甲苯酯、β-三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2制作阻燃材料层，阻燃效果较好，即使一侧木料板起火，阻燃材料层仍可避免另一侧的木料板燃烧。综上所述，本发明的阻燃纤维板具有板材较厚，不易破损，隔热效果较好，阻燃效果好的优点。
具体实施方式
下面结合实施例对本发明作进一步的说明，但并不作为对本发明限制的依据。
实施例1。一种阻燃纤维板，该阻燃纤维板是由木料板层、喷涂在木料板层上的阻燃涂料层以及设在木料板层之间的阻燃材料层构成。
所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂80份，偏二氯乙烯共聚物乳液30份，聚磷酸铵20份，有机卤代磷酸酯20份，钛白粉10份，锑白粉10份，SiO210份。
所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯5份，β-三氯乙烯磷酸酯5份，氢氧化镁10份，氢氧化铝10份，十溴联苯酸5份，四溴双酚A5份，氯化石蜡1份，SiO220份。
上述阻燃纤维板的制作方法，该方法包括以下步骤；
A：将磷酸三甲苯酯、β-三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2混合均匀，制成阻燃材料；
B：根据生产需求，将木料制成相对应规格的木料板；
C：将阻燃材料和胶粘剂混合均匀，向两块木料板之间填充厚度为0.3cm的阻燃材料层，并将木料板粘接；
D：将填充了阻燃材料和粘接完成的木料板放置24h，使木料板粘接稳定；
E：取树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2混合搅拌均匀，制成阻燃涂料；
F：待木板板粘接稳定后，在木板表面均匀喷涂阻燃涂料，待阻燃涂料风干，制得阻燃纤维板。
实施例2。一种阻燃纤维板，该阻燃纤维板是由木料板层、喷涂在木料板层上的阻燃涂料层以及设在木料板层之间的阻燃材料层构成。
所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂90份，偏二氯乙烯共聚物乳液45，聚磷酸铵30份，有机卤代磷酸酯30份，钛白粉15份，锑白粉15份，SiO215份。
所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯8份，β-三氯乙烯磷酸酯7份，氢氧化镁15份，氢氧化铝15份，十溴联苯酸6份，四溴双酚A6份，氯化石蜡3份，SiO215份。
上述阻燃纤维板的制作方法，该方法包括以下步骤；
A：将磷酸三甲苯酯、β-三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2混合均匀，制成阻燃材料；
B：根据生产需求，将木料制成相对应规格的木料板；
C：将阻燃材料和胶粘剂混合均匀，向两块木料板之间填充厚度为0.4cm的阻燃材料层，并将木料板粘接；
D：将填充了阻燃材料和粘接完成的木料板放置30h，使木料板粘接稳定；
E：取树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2混合搅拌均匀，制成阻燃涂料；
F：待木板板粘接稳定后，在木板表面均匀喷涂阻燃涂料，待阻燃涂料风干，制得阻燃纤维板。
实施例3。一种阻燃纤维板，该阻燃纤维板是由木料板层、喷涂在木料板层上的阻燃涂料层以及设在木料板层之间的阻燃材料层构成。
所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂100份，偏二氯乙烯共聚物乳液60份，聚磷酸铵40份，有机卤代磷酸酯40份，钛白粉20份，锑白粉20份，SiO220份。
所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯10份，β-三氯乙烯磷酸酯10份，氢氧化镁20份，氢氧化铝20份，十溴联苯酸10份，四溴双酚A10份，氯化石蜡4份，SiO240份。
上述阻燃纤维板的制作方法，该方法包括以下步骤；
A：将磷酸三甲苯酯、β-三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2混合均匀，制成阻燃材料；
B：根据生产需求，将木料制成相对应规格的木料板；
C：将阻燃材料和胶粘剂混合均匀，向两块木料板之间填充厚度为0.5cm的阻燃材料层，并将木料板粘接；
D：将填充了阻燃材料和粘接完成的木料板放置36h，使木料板粘接稳定；
E：取树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2混合搅拌均匀，制成阻燃涂料；
F：待木板板粘接稳定后，在木板表面均匀喷涂阻燃涂料，待阻燃涂料风干，制得阻燃纤维板。

Claims (6)

1.一种阻燃纤维板，其特征在于：该阻燃纤维板是由木料板层、喷涂在木料板层上的阻燃涂料层以及设在木料板层之间的阻燃材料层构成。
2.根据权利要求1所述的一种阻燃纤维板，其特征在于：所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂80~100份，偏二氯乙烯共聚物乳液30~60份，聚磷酸铵20~40份，有机卤代磷酸酯20~40份，钛白粉10~20份，锑白粉10~20份，SiO210~20份。
3.根据权利要求1所述的一种阻燃纤维板，其特征在于：所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯5~10份，β-三氯乙烯磷酸酯5~10份，氢氧化镁10~20份，氢氧化铝10~20份，十溴联苯酸5~10份，四溴双酚A5~10份，氯化石蜡1~4份，SiO220~40份。
4.根据权利要求1或2所述的一种阻燃纤维板，其特征在于：所述阻燃涂料层是由阻燃涂料制成，该阻燃涂料是由以下重量份的原料制成：树脂90份，偏二氯乙烯共聚物乳液45，聚磷酸铵30份，有机卤代磷酸酯30份，钛白粉15份，锑白粉15份，SiO215份。
5.根据权利要求1或3所述的一种阻燃纤维板，其特征在于：所述阻燃材料层是由以下重量份的原料制成：磷酸三甲苯酯8份，β-三氯乙烯磷酸酯7份，氢氧化镁15份，氢氧化铝15份，十溴联苯酸6份，四溴双酚A6份，氯化石蜡3份，SiO215份。
6.按照如权利要求1-5任一权利要求所述的一种阻燃纤维板的制作方法，其特征在于：该方法包括以下步骤；
A：将磷酸三甲苯酯、β-三氯乙烯磷酸酯、氢氧化镁、氢氧化铝、十溴联苯酸、四溴双酚A、氯化石蜡和SiO2混合均匀，制成阻燃材料；
B：根据生产需求，将木料制成相对应规格的木料板；
C：将阻燃材料和胶粘剂混合均匀，向两块木料板之间填充厚度为0.3~0.5cm的阻燃材料层，并将木料板粘接；
D：将填充了阻燃材料和粘接完成的木料板放置24~36h，使木料板粘接稳定；
E：取树脂、偏二氯乙烯共聚物乳液、聚磷酸铵、有机卤代磷酸酯、钛白粉、锑白粉和SiO2混合搅拌均匀，制成阻燃涂料；
F：待木板板粘接稳定后，在木板表面均匀喷涂阻燃涂料，待阻燃涂料风干，制得阻燃纤维板。
CN201710864209.6A 2017-09-22 2017-09-22 一种阻燃纤维板及其制作方法 Pending CN109531761A (zh)