CN109517489A - Water-base epoxy anti-corrosion floor material - Google Patents
Water-base epoxy anti-corrosion floor material Download PDFInfo
- Publication number
- CN109517489A CN109517489A CN201811378018.XA CN201811378018A CN109517489A CN 109517489 A CN109517489 A CN 109517489A CN 201811378018 A CN201811378018 A CN 201811378018A CN 109517489 A CN109517489 A CN 109517489A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- water
- byk
- floor material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-base epoxy anti-corrosion floor materials, including component A and B component, raw materials used component A includes: 8-10 parts of distilled water, 85-90 parts of E-20 epoxy resin, 1-3 parts of propylene glycol monomethyl ether, 12 1-3 parts of alcohol ester, 1-5 parts of mill base, 40-50 parts of talcum powder, 10-15 parts of silica flour, 10-15 parts of barium sulfate, 0.1-0.5 parts of BYK-348,0.1-0.3 parts of BYK-024,0.2-0.6 parts of BYK-191 by weight；Raw materials used B component includes: 40-50 parts of water-base epoxy fatty amine curing agent, 1-5 parts of isothiazolinone, 0.1-0.5 parts of polyether polyurethane by weight.The water-base epoxy anti-corrosion floor material is using water as decentralized medium, environmentally protective, Diamond Search, in moist environment construction and solidification, has wearability good, and soft glossy has good antiseptic property.
Description
Technical field
The invention belongs to floor material technical fields, and in particular to a kind of water-base epoxy anti-corrosion floor material.
Background technique
Aqueous epoxy floor is a kind of using epoxy resin as the floor material of raw material, and epoxy resin is with the shape of particle or drop
Formula be dispersed in using water as in the decentralized medium of continuous phase and with stable dispersion system.It is aqueous compared with existing anti-corrosion terrace
Epoxide terrace is environmentally protective using water as decentralized medium, Diamond Search, in moist environment construction and solidification, has wearability good,
Soft glossy has good antiseptic property.On the basis of industry ground slab is obtained and is widely applied, floor paint has become China's hair
Fastest one of industry is opened up, people is obtained and widely pays close attention to.Aqueous epoxy floor its as a kind of Novel terrace material,
It manufactures and is widely used in industry, be primarily adapted for use in electroplate factory, Battery Plant, chemical plant, electrolytic cell, pharmaceutical factory, acid-base neutralization pond
Ground, metope and the equipment surface in equal places.But often there is floor coatings material point in anti-corrosion terrace in the prior art
Minor structure defective tightness leads to not reach ideal anti-corrosion effect.Aqueous epoxy resins refer to epoxy resin with particle or liquid
The form of drop be dispersed in using water as in the decentralized medium of continuous phase and with stable dispersion system, particle surface in the system
Curative concentration is relatively mild, and surface cure speed is slower, and solidification agent molecule has time enough to be diffused into entire epoxy resin
Dispersed phase particles are allowed to completion of cure, thus can be formed uniformly, the film that is fully cured, with excellent corrosion-resistant
Performance.Water-base epoxy anti-corrosion floor material of the present invention is using water as decentralized medium simultaneously, environmentally protective, Diamond Search, and existing anti-
Rotten terrace generally contains volatile organic compounds, and smell is difficult to eliminate, dissolvent residual overlong time, and containing benzene has victimization
The substance of body health.As the improvement of people's living standards, the quality and environmental protection standard requirement to terrace are higher, therefore aqueous ring
Oxygen anti-corrosion terrace becomes the popular research direction of floor material.
Summary of the invention
The purpose of the present invention is to provide a kind of water-base epoxy anti-corrosion floor material, the property epoxy that the present invention is prepared is anti-
Rotten terrace is environmentally protective using water as decentralized medium, Diamond Search, in moist environment construction and solidification, has wearability good, light
Pool is soft, has good antiseptic property.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of water-base epoxy anti-corrosion floor material, including component A and B component, raw materials used component A includes: to steam by weight
8-10 parts of distilled water, 85-90 parts of E-20 epoxy resin, 1-3 parts of propylene glycol monomethyl ether, 12 1-3 parts of alcohol ester, 1-5 parts of mill base, talcum powder
40-50 parts, 10-15 parts of silica flour, 10-15 parts of barium sulfate, 0.1-0.5 parts of BYK-348,0.1-0.3 parts of BYK-024, BYK-
191 0.2-0.6 parts.
Raw materials used B component includes: 40-50 parts of water-base epoxy fatty amine curing agent, isothiazolinone 1-5 by weight
Part, 0.1-0.5 parts of polyether polyurethane.
The component A and the weight ratio of B component cooperation are 5:1.
A kind of water-base epoxy anti-corrosion floor material, preparation method the following steps are included:
(1) E-20 epoxy resin, propylene glycol monomethyl ether, alcohol ester 12, barium sulfate are uniformly mixed at normal temperature, at normal temperature 1500r/
Min is stirred 40 minutes；
(2) distilled water, mill base, talcum powder, silica flour, BYK-348, BYK-024, BYK- are added in the mixture of step (1)
191, it is uniformly mixed under room temperature, 1200r/min is stirred 30 minutes, obtains pretreated component A；
(3) pretreated component A is uniformly mixed to obtain water-base epoxy anti-corrosion floor material by weight 5:1 with B component.
The present invention has the advantages that
The present invention is mixed with to obtain water-base epoxy anti-corrosion floor material, using water as decentralized medium, green ring by two-component
It protects, is free of volatile organic compounds, in moist environment construction and solidification, have wearability good, soft glossy has good
Antiseptic property, meet the technical indicator of every aqueous epoxy floor.
Specific embodiment
Further to disclose rather than the present invention is limited, the present invention is described in further detail below in conjunction with example.
Embodiment 1
A kind of water-base epoxy anti-corrosion floor material, including component A and B component, it is characterised in that: component A is raw materials used by weight
Part meter includes: 8 parts of distilled water, 85 parts of E-20 epoxy resin, 1 part of propylene glycol monomethyl ether, 12 parts of alcohol ester, 1 part of mill base, talcum powder
40 parts, 10 parts of silica flour, 10 parts of barium sulfate, 0.1 part of BYK-348,0.1 part of BYK-024,0.2 part of BYK-191.
It includes: 40 parts of water-base epoxy fatty amine curing agent that B component is raw materials used by weight, 1 part of isothiazolinone, is gathered
0.1 part of ether-based polyurethane.
Component A and the weight ratio of B component cooperation are 5:1
Embodiment 2
A kind of water-base epoxy anti-corrosion floor material, including component A and B component, it is characterised in that: component A is raw materials used by weight
Part meter includes: 8 parts of distilled water, 88 parts of E-20 epoxy resin, 2 parts of propylene glycol monomethyl ether, 12 parts of alcohol ester, 3 parts of mill base, talcum powder
45 parts, 13 parts of silica flour, 13 parts of barium sulfate, 0.2 part of BYK-348,0.2 part of BYK-024,0.4 part of BYK-191.
It includes: 45 parts of water-base epoxy fatty amine curing agent that B component is raw materials used by weight, 3 parts of isothiazolinone, is gathered
0.3 part of ether-based polyurethane.
Component A and the weight ratio of B component cooperation are 5:1.
Embodiment 3
A kind of water-base epoxy anti-corrosion floor material, including component A and B component, it is characterised in that: component A is raw materials used by weight
Part meter includes: 10 parts of distilled water, 90 parts of E-20 epoxy resin, 3 parts of propylene glycol monomethyl ether, 12 parts of alcohol ester, 5 parts of mill base, talcum powder
50 parts, 15 parts of silica flour, 15 parts of barium sulfate, 0.5 part of BYK-348,0.3 part of BYK-024,0.6 part of BYK-191.
It includes: 50 parts of water-base epoxy fatty amine curing agent that B component is raw materials used by weight, 5 parts of isothiazolinone, is gathered
0.5 part of ether-based polyurethane.
Component A and the weight ratio of B component cooperation are 5:1.
Comparative example
A kind of water-base epoxy anti-corrosion floor material, including component A and B component, it is characterised in that: component A is raw materials used by weight
Part meter includes: 10 parts of distilled water, 90 parts of E-20 epoxy resin, 3 parts of propylene glycol monomethyl ether, 12 parts of alcohol ester, 5 parts of mill base, talcum powder
50 parts, 15 parts of silica flour, 15 parts of barium sulfate, 0.5 part of BYK-348,0.3 part of BYK-024,0.6 part of BYK-191.
Raw materials used B component includes: 50 parts of two diammonium hydrogen by weight.
Component A and the weight ratio of B component cooperation are 5:1.
Water-base epoxy anti-corrosion floor material in embodiment and comparative example, the preparation method is as follows:
(1) E-20 epoxy resin, propylene glycol monomethyl ether, alcohol ester 12, barium sulfate are uniformly mixed at normal temperature, at normal temperature 1500r/
Min is stirred 40 minutes；
(2) distilled water, mill base, talcum powder, silica flour, BYK-348, BYK-024, BYK- are added in the mixture of step (1)
191, it is uniformly mixed under room temperature, 1200r/min is stirred 30 minutes, obtains pretreated component A；
(3) pretreated component A is uniformly mixed to obtain water-base epoxy anti-corrosion floor material by weight 5:1 with B component.
The performance parameter for preparing obtained floor material is shown in Table 1:
The measured performance parameter of table 1 embodiment and comparative example terrace
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with repair
Decorations, are all covered by the present invention.
Claims (4)
1. a kind of water-base epoxy anti-corrosion floor material, including component A and B component, it is characterised in that: component A is raw materials used by weight
Measuring part meter includes: 8-10 parts of distilled water, 85-90 parts of E-20 epoxy resin, 1-3 parts of propylene glycol monomethyl ether, 12 1-3 parts of alcohol ester, color
Starch 1-5 parts, 40-50 parts of talcum powder, 10-15 parts of silica flour, 10-15 parts of barium sulfate, 0.1-0.5 parts of BYK-348, BYK-024
0.1-0.3 parts, 0.2-0.6 parts of BYK-191.
2. a kind of water-base epoxy anti-corrosion floor material according to claim 1, it is characterised in that: B component is raw materials used by weight
Measuring part meter includes: 40-50 parts of water-base epoxy fatty amine curing agent, 1-5 parts of isothiazolinone, 0.1-0.5 parts of polyether polyurethane.
3. water-base epoxy anti-corrosion floor material according to claim 1, it is characterised in that: the weight of component A and B component cooperation
Than for 5:1.
4. one kind as described in claim 1-3 is any water-base epoxy anti-corrosion floor material, which is characterized in that preparation method include with
Lower step:
(1) E-20 epoxy resin, propylene glycol monomethyl ether, alcohol ester 12, barium sulfate are uniformly mixed at normal temperature, at normal temperature 1500r/
Min is stirred 40 minutes；
(2) distilled water, mill base, talcum powder, silica flour, BYK-348, BYK-024, BYK- are added in the mixture of step (1)
191, it is uniformly mixed under room temperature, 1200r/min is stirred 30 minutes, obtains pretreated component A；
(3) pretreated component A is uniformly mixed to obtain water-base epoxy anti-corrosion floor material by weight 5:1 with B component.