CN108424707A - A kind of anti-corrosion epoxy coating and preparation method thereof - Google Patents
A kind of anti-corrosion epoxy coating and preparation method thereof Download PDFInfo
- Publication number
- CN108424707A CN108424707A CN201810250627.0A CN201810250627A CN108424707A CN 108424707 A CN108424707 A CN 108424707A CN 201810250627 A CN201810250627 A CN 201810250627A CN 108424707 A CN108424707 A CN 108424707A
- Authority
- CN
- China
- Prior art keywords
- added
- dispersion liquid
- scolecite
- epoxy
- taken
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of anti-corrosion epoxy coatings, it is made of the raw material of following weight parts:Epoxy resin E51 100 130, nickel sulfamic acid 12, lauric acid amide of ethanol 0.7 1, trisnonyl phenyl phosphite 23, octylisothiazolinone 12, calcium propionate 23, scolecite 10 15, aluminum stearate 24, trimethylolpropane 0.8 1, the present invention is using scolecite as raw material, it is distributed in alcoholic solution, it is handled using trimethylolpropane, the effective surface-active for improving scolecite, reunite to effectively reduce, improves the uniform and stable property of finished product coating.
Description
Technical field
The invention belongs to paint fields, and in particular to a kind of anti-corrosion epoxy coating and preparation method thereof.
Background technology
Epoxy resin is used for coating maximum with liquid resin portion, but industrially using at present in anticorrosive coating
Major part is solvent based coating, and for conventional solution-type coating mostly using aromatic hydrocarbons, esters, alcohols, ketone etc. as solvent, these solvents are equal
With different degrees of toxicity, and volatile matter is directly discharged into air, and environmental pollution is heavier.With the increasing of people's environmental consciousness
By force, it is free of organic solvent or novel anticorrosion the coating such as powdery paints, solventless coatings and water paint etc. of low VOC is green
Coating is developed in succession.Powdery paints is because condition of cure is more harsh, to limit its development;Solventless epoxy coating exists
Solvent free paint field is that comparison is successful, only in recent years in the safe and reliable of the hypotoxicity of reactive diluent and curing agent
Property etc. is challenged, among improving;And waterborne epoxy coatings is other than the plurality of advantages for adhering to solvent based coating,
To improving performance, reducing pollution, expansion application etc. development, oneself covers locomotive, aviation, food, building etc. in field,
Therefore waterborne epoxy coatings is to develop a very rapid field in recent years;
For epoxy resin cured product because brittleness is big, impact resistance, resistance to acid and alkali, flexibility and temperature tolerance are poor, limit epoxy resin
The application of coating, therefore be always one of the emphasis studied anti-corrosive paint of epoxy resin to the modification of epoxy resin, and in order to
Its mechanical property is improved, is often added the inorganic fillers such as various bentonites, graphene wherein, but these inorganic fillers and ring
The compatibility of oxygen resin is poor, and the bin stability for be easy to causeing coating is poor, and is easy to form caking, reduces the product of coating
Matter.
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of anti-corrosion epoxy coating and its preparations
Method.
To achieve the above object, the present invention uses following technical scheme:
A kind of anti-corrosion epoxy coating, it is made of the raw material of following weight parts:
Epoxy resin E51 100-130, nickel sulfamic acid 1-2, lauric acid amide of ethanol 0.7-1, trisnonyl phenyl phosphite
2-3, octylisothiazolinone 1-2, calcium propionate 2-3, scolecite 10-15, aluminum stearate 2-4, trimethylolpropane 0.8-1.
A kind of preparation method of anti-corrosion epoxy coating, includes the following steps:
(1)Scolecite is taken, is calcined 1-2 hours at 650-700 DEG C, is cooled to room temperature, is mixed with calcium propionate, be added to mixture
In the deionized water of 1.7-2 times of weight, insulated and stirred is dry to water at 80-90 DEG C, wears into fine powder, obtains scolecite powder;
(2)Octylisothiazolinone is taken, is added in the absolute ethyl alcohol of 4-10 times of its weight, stirs evenly, raising temperature is 67-
80 DEG C, aluminum stearate is added, insulated and stirred 20-30 minutes obtains alcohol dispersion liquid;
(3)Above-mentioned scolecite powder is taken, is added in alcohol dispersion liquid, stirs evenly, trimethylolpropane is added, increasing temperature is
55-60 DEG C, insulated and stirred 1-2 hours obtains propane dispersion liquid;
(4)Lauric acid amide of ethanol is taken, is added in the deionized water of 120-130 times of its weight, stirs evenly, with above-mentioned third
Alkane dispersion liquid mixes, and epoxy resin E51 is added, 4-10 minutes ultrasonic, and ethyl alcohol is distilled off, obtains epoxy dispersion liquid;
(5)Take above-mentioned epoxy dispersion liquid, mix with remaining each raw material, 1000-1300 revs/min stir 1-2 hours to get.
Advantages of the present invention:
The present invention is distributed to using scolecite as raw material in alcoholic solution, is handled using trimethylolpropane, and calcium boiling is effectively improved
The surface-active of stone reunites to effectively reduce, improves the uniform and stable property of finished product coating, the present invention is also added into octyl
Isothiazolinone can effectively improve the antibacterial antiseptic property of coating, improve the quality of finished product.
Specific implementation mode
Embodiment 1
A kind of anti-corrosion epoxy coating, it is made of the raw material of following weight parts:
Epoxy resin E51 100, nickel sulfamic acid 1, lauric acid amide of ethanol 0.7, trisnonyl phenyl phosphite 2, octyl are different
Thiazolinone 1, calcium propionate 2, scolecite 10, aluminum stearate 2, trimethylolpropane 0.8.
A kind of preparation method of anti-corrosion epoxy coating, includes the following steps:
(1)Scolecite is taken, is calcined 1 hour at 650 DEG C, is cooled to room temperature, is mixed with calcium propionate, be added to mixture weight
In 1.7 times of deionized water, insulated and stirred is dry to water at 80 DEG C, wears into fine powder, obtains scolecite powder;
(2)Octylisothiazolinone is taken, is added in the absolute ethyl alcohol of 4 times of its weight, stirs evenly, it is 67 DEG C to increase temperature,
Aluminum stearate is added, insulated and stirred 20 minutes obtains alcohol dispersion liquid;
(3)Above-mentioned scolecite powder is taken, is added in alcohol dispersion liquid, stirs evenly, trimethylolpropane is added, it is 55 to increase temperature
DEG C, insulated and stirred 1 hour obtains propane dispersion liquid;
(4)Lauric acid amide of ethanol is taken, is added in the deionized water of 120 times of its weight, stirs evenly, with above-mentioned propane point
Dispersion liquid mixes, and epoxy resin E51 is added, and ultrasound 4 minutes is distilled off ethyl alcohol, obtains epoxy dispersion liquid;
(5)Take above-mentioned epoxy dispersion liquid, mix with remaining each raw material, 1000 revs/min stir 1-2 hours to get.
Embodiment 2
A kind of anti-corrosion epoxy coating, it is made of the raw material of following weight parts:
Epoxy resin E51 130, nickel sulfamic acid 2, lauric acid amide of ethanol 1, trisnonyl phenyl phosphite 3, the different thiophene of octyl
Oxazoline ketone 2, calcium propionate 3, scolecite 15, aluminum stearate 4, trimethylolpropane 1.
A kind of preparation method of anti-corrosion epoxy coating, includes the following steps:
(1)Scolecite is taken, is calcined 2 hours at 700 DEG C, is cooled to room temperature, is mixed with calcium propionate, be added to mixture weight 2
In deionized water again, insulated and stirred is dry to water at 90 DEG C, wears into fine powder, obtains scolecite powder;
(2)Octylisothiazolinone is taken, is added in the absolute ethyl alcohol of 10 times of its weight, stirs evenly, it is 80 DEG C to increase temperature,
Aluminum stearate is added, insulated and stirred 30 minutes obtains alcohol dispersion liquid;
(3)Above-mentioned scolecite powder is taken, is added in alcohol dispersion liquid, stirs evenly, trimethylolpropane is added, it is 60 to increase temperature
DEG C, insulated and stirred 2 hours obtains propane dispersion liquid;
(4)Lauric acid amide of ethanol is taken, is added in the deionized water of 130 times of its weight, stirs evenly, with above-mentioned propane point
Dispersion liquid mixes, and epoxy resin E51 is added, and ultrasound 10 minutes is distilled off ethyl alcohol, obtains epoxy dispersion liquid;
(5)Take above-mentioned epoxy dispersion liquid, mix with remaining each raw material, 1300 revs/min stir 2 hours to get.
Claims (2)
1. a kind of anti-corrosion epoxy coating, which is characterized in that it is made of the raw material of following weight parts:
Epoxy resin E51 100-130, nickel sulfamic acid 1-2, lauric acid amide of ethanol 0.7-1, trisnonyl phenyl phosphite
2-3, octylisothiazolinone 1-2, calcium propionate 2-3, scolecite 10-15, aluminum stearate 2-4, trimethylolpropane 0.8-1.
2. a kind of preparation method of anti-corrosion epoxy coating as described in claim 1, which is characterized in that include the following steps:
(1)Scolecite is taken, is calcined 1-2 hours at 650-700 DEG C, is cooled to room temperature, is mixed with calcium propionate, be added to mixture
In the deionized water of 1.7-2 times of weight, insulated and stirred is dry to water at 80-90 DEG C, wears into fine powder, obtains scolecite powder;
(2)Octylisothiazolinone is taken, is added in the absolute ethyl alcohol of 4-10 times of its weight, stirs evenly, raising temperature is 67-
80 DEG C, aluminum stearate is added, insulated and stirred 20-30 minutes obtains alcohol dispersion liquid;
(3)Above-mentioned scolecite powder is taken, is added in alcohol dispersion liquid, stirs evenly, trimethylolpropane is added, increasing temperature is
55-60 DEG C, insulated and stirred 1-2 hours obtains propane dispersion liquid;
(4)Lauric acid amide of ethanol is taken, is added in the deionized water of 120-130 times of its weight, stirs evenly, with above-mentioned third
Alkane dispersion liquid mixes, and epoxy resin E51 is added, 4-10 minutes ultrasonic, and ethyl alcohol is distilled off, obtains epoxy dispersion liquid;
(5)Take above-mentioned epoxy dispersion liquid, mix with remaining each raw material, 1000-1300 revs/min stir 1-2 hours to get.