CN108424706A - A kind of polymer epoxy coating and preparation method thereof - Google Patents
A kind of polymer epoxy coating and preparation method thereof Download PDFInfo
- Publication number
- CN108424706A CN108424706A CN201810249027.2A CN201810249027A CN108424706A CN 108424706 A CN108424706 A CN 108424706A CN 201810249027 A CN201810249027 A CN 201810249027A CN 108424706 A CN108424706 A CN 108424706A
- Authority
- CN
- China
- Prior art keywords
- silicon powder
- taken
- stirred
- added
- mentioned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of polymer epoxy coatings, it is made of the raw material of following weight parts:Epoxy resin E51 100 120, ethylene thiourea 12, melamine 0.8 1, glyceryl tristearate 24, polyanhydride 35, polyacrylamide 12, ammonium molybdate 12, silicon powder 10 14, double decyl dimethyl ammonium bromides 0.6 1, N, N dimethylformamides 0.8 1, the present invention is first disperseed silicon powder using polyanhydride, then it is blended with melamine, it is reacted with sour by amine, improve the surface-active of silicon powder, to improve dispersion compatibility of the silicon powder between epoxy resin, the mechanical stability of finished product coating is improved.
Description
Technical field
The invention belongs to paint fields, and in particular to a kind of polymer epoxy coating and preparation method thereof.
Background technology
Epoxy resin is used for coating maximum with liquid resin portion, but industrially using at present in anticorrosive coating
Major part is solvent based coating, and for conventional solution-type coating mostly using aromatic hydrocarbons, esters, alcohols, ketone etc. as solvent, these solvents are equal
With different degrees of toxicity, and volatile matter is directly discharged into air, and environmental pollution is heavier.With the increasing of people's environmental consciousness
By force, it is free of organic solvent or novel anticorrosion the coating such as powdery paints, solventless coatings and water paint etc. of low VOC is green
Coating is developed in succession.Powdery paints is because condition of cure is more harsh, to limit its development;Solventless epoxy coating exists
Solvent free paint field is that comparison is successful, only in recent years in the safe and reliable of the hypotoxicity of reactive diluent and curing agent
Property etc. is challenged, among improving;And waterborne epoxy coatings is other than the plurality of advantages for adhering to solvent based coating,
To improving performance, reducing pollution, expansion application etc. development, oneself covers locomotive, aviation, food, building etc. in field,
Therefore waterborne epoxy coatings is to develop a very rapid field in recent years;
For epoxy resin cured product because brittleness is big, impact resistance, resistance to acid and alkali, flexibility and temperature tolerance are poor, limit epoxy resin
The application of coating, therefore be always one of the emphasis studied anti-corrosive paint of epoxy resin to the modification of epoxy resin, and in order to
Its mechanical property is improved, is often added the inorganic fillers such as various bentonites, graphene wherein, but these inorganic fillers and ring
The compatibility of oxygen resin is poor, and the bin stability for be easy to causeing coating is poor, and is easy to form caking, reduces the product of coating
Matter.
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of polymer epoxy coating and its systems
Preparation Method.
To achieve the above object, the present invention uses following technical scheme:
A kind of polymer epoxy coating, it is made of the raw material of following weight parts:
Epoxy resin E51 100-120, ethylene thiourea 1-2, melamine 0.8-1, glyceryl tristearate 2-4, polyanhydride 3-
5, polyacrylamide 1-2, ammonium molybdate 1-2, silicon powder 10-14, double decyl dimethyl ammonium bromide 0.6-1, N, N- dimethyl formyls
Amine 0.8-1.
A kind of preparation method of polymer epoxy coating, includes the following steps:
(1)Silicon powder, polyanhydride mixing are taken, is added in the deionized water of 25-30 times of mixture weight, stirs evenly, increase
Temperature is 60-65 DEG C, and insulated and stirred 1-2 hours obtains silicon powder solution;
(2)Polyacrylamide is taken, is added in the deionized water of 10-17 times of its weight, stirs evenly, raising temperature is 50-55
DEG C, obtain amide solution;
(3)Above-mentioned silicon powder solution, amide solution mixing are taken, is stirred evenly, 3-10 minutes ultrasonic, filtering washes precipitation, often
Temperature is dry, obtains modified silicon powder;
(4)Melamine is taken, is mixed with above-mentioned modified silicon powder, it is 65-70 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains cyanogen
Amination micro mist;
(5)Above-mentioned glyceryl tristearate is taken, is added in the deionized water of 80-100 times of its weight, stirs evenly, obtains ester point
Dispersion liquid;
(6)Above-mentioned cyanamide micro mist, the mixing of ester dispersion liquid are taken, is stirred evenly, remaining each raw material is added, 1300-2000 revs/min is stirred
1-2 hours are mixed to get the polymer epoxy coating.
Advantages of the present invention:
The present invention is first disperseed silicon powder using polyanhydride, is then blended with melamine, is reacted, is improved with sour by amine
The surface-active of silicon powder to improve dispersion compatibility of the silicon powder between epoxy resin improves finished product coating
Mechanical stability.
Specific implementation mode
Embodiment 1
A kind of polymer epoxy coating, it is made of the raw material of following weight parts:
Epoxy resin E51 100, ethylene thiourea 1, melamine 0.8, glyceryl tristearate 2, polyanhydride 3, polyacrylamide
1, ammonium molybdate 1, silicon powder 10, double decyl dimethyl ammonium bromides 0.6, N,N-dimethylformamide 0.8.
A kind of preparation method of polymer epoxy coating, includes the following steps:
(1)Silicon powder, polyanhydride mixing are taken, is added in the deionized water of 25 times of mixture weight, stirs evenly, increase temperature
It it is 60 DEG C, insulated and stirred 1 hour obtains silicon powder solution;
(2)Polyacrylamide is taken, is added in the deionized water of 10 times of its weight, stirs evenly, it is 50 DEG C to increase temperature, obtains acyl
Amine aqueous solution;
(3)Above-mentioned silicon powder solution, amide solution mixing are taken, is stirred evenly, ultrasound 3 minutes, filtering washes precipitation, room temperature
It is dry, obtain modified silicon powder;
(4)Melamine is taken, is mixed with above-mentioned modified silicon powder, it is 65 DEG C to increase temperature, and insulated and stirred 1 hour obtains cyanamide
Micro mist;
(5)Above-mentioned glyceryl tristearate is taken, is added in the deionized water of 80 times of its weight, stirs evenly, obtain ester dispersion liquid;
(6)Above-mentioned cyanamide micro mist, the mixing of ester dispersion liquid are taken, is stirred evenly, remaining each raw material is added, 1300 revs/min of stirrings 1 are small
When to get the polymer epoxy coating.
Embodiment 2
A kind of polymer epoxy coating, it is made of the raw material of following weight parts:
Epoxy resin E51 120, ethylene thiourea 2, melamine 1, glyceryl tristearate 4, polyanhydride 5, polyacrylamide 2,
Ammonium molybdate 2, silicon powder 14, double decyl dimethyl ammonium bromides 1, N,N-dimethylformamide 1.
A kind of preparation method of polymer epoxy coating, includes the following steps:
(1)Silicon powder, polyanhydride mixing are taken, is added in the deionized water of 30 times of mixture weight, stirs evenly, increase temperature
It it is 65 DEG C, insulated and stirred 2 hours obtains silicon powder solution;
(2)Polyacrylamide is taken, is added in the deionized water of 17 times of its weight, stirs evenly, it is 50-55 DEG C to increase temperature,
Obtain amide solution;
(3)Above-mentioned silicon powder solution, amide solution mixing are taken, is stirred evenly, ultrasound 10 minutes, filtering washes precipitation, room temperature
It is dry, obtain modified silicon powder;
(4)Melamine is taken, is mixed with above-mentioned modified silicon powder, it is 70 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains cyanamide
Change micro mist;
(5)Above-mentioned glyceryl tristearate is taken, is added in the deionized water of 100 times of its weight, stirs evenly, obtains ester dispersion
Liquid;
(6)Above-mentioned cyanamide micro mist, the mixing of ester dispersion liquid are taken, is stirred evenly, remaining each raw material, 2000 revs/min of stirrings 2 are added
Hour is to get the polymer epoxy coating.
Claims (2)
1. a kind of polymer epoxy coating, which is characterized in that it is made of the raw material of following weight parts:
Epoxy resin E51 100-120, ethylene thiourea 1-2, melamine 0.8-1, glyceryl tristearate 2-4, polyanhydride 3-
5, polyacrylamide 1-2, ammonium molybdate 1-2, silicon powder 10-14, double decyl dimethyl ammonium bromide 0.6-1, N, N- dimethyl formyls
Amine 0.8-1.
2. a kind of preparation method of polymer epoxy coating as described in claim 1, which is characterized in that include the following steps:
(1)Silicon powder, polyanhydride mixing are taken, is added in the deionized water of 25-30 times of mixture weight, stirs evenly, increase
Temperature is 60-65 DEG C, and insulated and stirred 1-2 hours obtains silicon powder solution;
(2)Polyacrylamide is taken, is added in the deionized water of 10-17 times of its weight, stirs evenly, raising temperature is 50-55
DEG C, obtain amide solution;
(3)Above-mentioned silicon powder solution, amide solution mixing are taken, is stirred evenly, 3-10 minutes ultrasonic, filtering washes precipitation, often
Temperature is dry, obtains modified silicon powder;
(4)Melamine is taken, is mixed with above-mentioned modified silicon powder, it is 65-70 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains cyanogen
Amination micro mist;
(5)Above-mentioned glyceryl tristearate is taken, is added in the deionized water of 80-100 times of its weight, stirs evenly, obtains ester point
Dispersion liquid;
(6)Above-mentioned cyanamide micro mist, the mixing of ester dispersion liquid are taken, is stirred evenly, remaining each raw material is added, 1300-2000 revs/min is stirred
1-2 hours are mixed to get the polymer epoxy coating.