CN108517170A - A kind of flame retardant epoxy coating and preparation method thereof - Google Patents
A kind of flame retardant epoxy coating and preparation method thereof Download PDFInfo
- Publication number
- CN108517170A CN108517170A CN201810292922.2A CN201810292922A CN108517170A CN 108517170 A CN108517170 A CN 108517170A CN 201810292922 A CN201810292922 A CN 201810292922A CN 108517170 A CN108517170 A CN 108517170A
- Authority
- CN
- China
- Prior art keywords
- added
- dispersion liquid
- taken
- epoxy
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of flame retardant epoxy coating, it is made of the raw material of following weight parts:Sodium stannate 46, zinc oxide 57, dimethylethanolamine 12, epoxy resin E44 100 120, abienol 35, diisocyanate 23, calcium aluminate 14, tetrabutylammonium bromide 23, butyl polyacrylate 10 15, barium naphthanate 0.1 0.3, ammonium polyphosphate 24, the present invention uses ammonium polyphosphate for raw material first, it distributes it in dimethylethanolamine, its dispersion compatibility with each raw material is improved, the surface strength and flame retardant property of finished product coating are enhanced.
Description
Technical field
The invention belongs to paint fields, and in particular to a kind of flame retardant epoxy coating and preparation method thereof.
Background technology
Epoxy resin is used for coating maximum with liquid resin portion, but industrially using at present in anticorrosive coating
Major part is solvent based coating, and for conventional solution-type coating mostly using aromatic hydrocarbons, esters, alcohols, ketone etc. as solvent, these solvents are equal
With different degrees of toxicity, and volatile matter is directly discharged into air, and environmental pollution is heavier.With the increasing of people's environmental consciousness
By force, it is free of organic solvent or novel anticorrosion the coating such as powdery paints, solventless coatings and water paint etc. of low VOC is green
Coating is developed in succession.Powdery paints is because condition of cure is more harsh, to limit its development;Solventless epoxy coating exists
Solvent free paint field is that comparison is successful, only in recent years in the safe and reliable of the hypotoxicity of reactive diluent and curing agent
Property etc. is challenged, among improving;And waterborne epoxy coatings is other than the plurality of advantages for adhering to solvent based coating,
To improving performance, reducing pollution, expansion application etc. development, oneself covers locomotive, aviation, food, building etc. in field,
Therefore waterborne epoxy coatings is to develop a very rapid field in recent years;
For epoxy resin cured product because brittleness is big, impact resistance, resistance to acid and alkali, flexibility and temperature tolerance are poor, limit epoxy resin
The application of coating, therefore be always one of the emphasis studied anti-corrosive paint of epoxy resin to the modification of epoxy resin, and in order to
Its mechanical property is improved, is often added the inorganic fillers such as various bentonites, graphene wherein, but these inorganic fillers and ring
The compatibility of oxygen resin is poor, and the bin stability for be easy to causeing coating is poor, and is easy to form caking, reduces the product of coating
Matter.
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of flame retardant epoxy coating and its preparations
Method.
To achieve the above object, the present invention uses following technical scheme:
A kind of flame retardant epoxy coating, it is made of the raw material of following weight parts:
Sodium stannate 4-6, zinc oxide 5-7, dimethylethanolamine 1-2, epoxy resin E44 100-120, abienol 3-5, two isocyanides
Acid esters 2-3, calcium aluminate 1-4, tetrabutylammonium bromide 2-3, butyl polyacrylate 10-15, barium naphthanate 0.1-0.3, ammonium polyphosphate
2-4。
A kind of preparation method of flame retardant epoxy coating, includes the following steps:
(1)Ammonium polyphosphate is taken, is added in the deionized water of 20-30 times of its weight, stirs evenly, it is 60-65 DEG C to increase temperature,
Dimethylethanolamine is added in insulated and stirred 10-14 minutes, stirs to room temperature, obtains hydramine dispersion liquid;
(2)Sodium stannate is taken, is added in the deionized water of 100-150 times of its weight, stirs evenly, abienol is added, stirring is equal
It is even, obtain sodium stannate solution;
(3)Zinc oxide is taken, is added in above-mentioned hydramine dispersion liquid, stirs evenly, mixed with above-mentioned sodium stannate solution, increases temperature
It it is 70-75 DEG C, insulated and stirred 1-2 hours obtains fire-retardant dispersion liquid;
(4)Diisocyanate is taken, is added in the absolute ethyl alcohol of 6-9 times of its weight, stirs evenly, it is mixed with above-mentioned fire-retardant dispersion liquid
It closes, it is 70-75 DEG C to increase temperature, and epoxy resin E44 is added, and insulated and stirred 3-4 hours obtains epoxy dispersion liquid;
(5)Above-mentioned epoxy dispersion liquid is taken, remaining each raw material is added, 1000-1300 revs/min is stirred 1-2 hours to get described fire-retardant
Epoxy coating.
Advantages of the present invention:
The present invention uses ammonium polyphosphate for raw material first, distributes it in dimethylethanolamine, improves itself and each raw material
Disperse compatibility, is then reacted by sodium stannate, zinc oxide, the fire-retardant dispersion liquid and epoxy blend that will be obtained, using two
Isocyanate-crosslinked modification enhances the surface strength and flame retardant property of finished product coating.
Specific implementation mode
Embodiment 1
A kind of flame retardant epoxy coating, it is made of the raw material of following weight parts:
Sodium stannate 4, zinc oxide 5, dimethylethanolamine 1, epoxy resin E44 100, abienol 3, diisocyanate 2, calcium aluminate
1, tetrabutylammonium bromide 2, butyl polyacrylate 10, barium naphthanate 0.1, ammonium polyphosphate 2.
A kind of preparation method of flame retardant epoxy coating, includes the following steps:
(1)Ammonium polyphosphate is taken, is added in the deionized water of 20 times of its weight, stirs evenly, it is 60 DEG C to increase temperature, and heat preservation is stirred
It mixes 10 minutes, dimethylethanolamine is added, stir to room temperature, obtain hydramine dispersion liquid;
(2)Sodium stannate is taken, is added in the deionized water of 100 times of its weight, stirs evenly, abienol is added, stirs evenly, obtains
Sodium stannate solution;
(3)Zinc oxide is taken, is added in above-mentioned hydramine dispersion liquid, stirs evenly, mixed with above-mentioned sodium stannate solution, increases temperature
It it is 70 DEG C, insulated and stirred 1 hour obtains fire-retardant dispersion liquid;
(4)Diisocyanate is taken, is added in the absolute ethyl alcohol of 6 times of its weight, stirs evenly, it is mixed with above-mentioned fire-retardant dispersion liquid
It closes, it is 70 DEG C to increase temperature, and epoxy resin E44 is added, and insulated and stirred 3 hours obtains epoxy dispersion liquid;
(5)Above-mentioned epoxy dispersion liquid is taken, remaining each raw material is added, 1000 revs/min of stirrings apply for 1 hour to get the flame retardant epoxy
Material.
Embodiment 2
A kind of flame retardant epoxy coating, it is made of the raw material of following weight parts:
Sodium stannate 6, zinc oxide 7, dimethylethanolamine 2, epoxy resin E44 120, abienol 5, diisocyanate 3, calcium aluminate
4, tetrabutylammonium bromide 3, butyl polyacrylate 15, barium naphthanate 0.3, ammonium polyphosphate 4.
A kind of preparation method of flame retardant epoxy coating, includes the following steps:
(1)Ammonium polyphosphate is taken, is added in the deionized water of 30 times of its weight, stirs evenly, it is 65 DEG C to increase temperature, and heat preservation is stirred
It mixes 14 minutes, dimethylethanolamine is added, stir to room temperature, obtain hydramine dispersion liquid;
(2)Sodium stannate is taken, is added in the deionized water of 150 times of its weight, stirs evenly, abienol is added, stirs evenly, obtains
Sodium stannate solution;
(3)Zinc oxide is taken, is added in above-mentioned hydramine dispersion liquid, stirs evenly, mixed with above-mentioned sodium stannate solution, increases temperature
It it is 75 DEG C, insulated and stirred 2 hours obtains fire-retardant dispersion liquid;
(4)Diisocyanate is taken, is added in the absolute ethyl alcohol of 9 times of its weight, stirs evenly, it is mixed with above-mentioned fire-retardant dispersion liquid
It closes, it is 75 DEG C to increase temperature, and epoxy resin E44 is added, and insulated and stirred 4 hours obtains epoxy dispersion liquid;
(5)Above-mentioned epoxy dispersion liquid is taken, remaining each raw material is added, 1300 revs/min of stirrings apply for 2 hours to get the flame retardant epoxy
Material.
Claims (2)
1. a kind of flame retardant epoxy coating, which is characterized in that it is made of the raw material of following weight parts:
Sodium stannate 4-6, zinc oxide 5-7, dimethylethanolamine 1-2, epoxy resin E44 100-120, abienol 3-5, two isocyanides
Acid esters 2-3, calcium aluminate 1-4, tetrabutylammonium bromide 2-3, butyl polyacrylate 10-15, barium naphthanate 0.1-0.3, ammonium polyphosphate
2-4。
2. a kind of preparation method of flame retardant epoxy coating as described in claim 1, which is characterized in that include the following steps:
(1)Ammonium polyphosphate is taken, is added in the deionized water of 20-30 times of its weight, stirs evenly, it is 60-65 DEG C to increase temperature,
Dimethylethanolamine is added in insulated and stirred 10-14 minutes, stirs to room temperature, obtains hydramine dispersion liquid;
(2)Sodium stannate is taken, is added in the deionized water of 100-150 times of its weight, stirs evenly, abienol is added, stirring is equal
It is even, obtain sodium stannate solution;
(3)Zinc oxide is taken, is added in above-mentioned hydramine dispersion liquid, stirs evenly, mixed with above-mentioned sodium stannate solution, increases temperature
It it is 70-75 DEG C, insulated and stirred 1-2 hours obtains fire-retardant dispersion liquid;
(4)Diisocyanate is taken, is added in the absolute ethyl alcohol of 6-9 times of its weight, stirs evenly, it is mixed with above-mentioned fire-retardant dispersion liquid
It closes, it is 70-75 DEG C to increase temperature, and epoxy resin E44 is added, and insulated and stirred 3-4 hours obtains epoxy dispersion liquid;
(5)Above-mentioned epoxy dispersion liquid is taken, remaining each raw material is added, 1000-1300 revs/min is stirred 1-2 hours to get described fire-retardant
Epoxy coating.