CN109456595A - 环保型铝型材加工工艺 - Google Patents
环保型铝型材加工工艺 Download PDFInfo
- Publication number
- CN109456595A CN109456595A CN201811047917.1A CN201811047917A CN109456595A CN 109456595 A CN109456595 A CN 109456595A CN 201811047917 A CN201811047917 A CN 201811047917A CN 109456595 A CN109456595 A CN 109456595A
- Authority
- CN
- China
- Prior art keywords
- aluminum profile
- environment
- processing technology
- friendly type
- type aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保型铝型材加工工艺,步骤如下:a、将铝制材料加工呈几何状铝型材;b、将步骤a中成型的铝型材的表面通过磨抛设备实施磨抛;c、对步骤b中完成磨抛的铝型材的表面镀上热塑性复合材料;e、步骤c中的热塑性复合材料为基料、碳纤维、超高分子氟乙烯、导电粒子、偶联剂及热稳定剂,其按照重量比为基料50%—60%、碳纤维15%—30%、超高分子氟乙烯1%—5%、导电粒子1%—3%、偶联剂5%—8%及余量热稳定剂。
Description
技术领域
本发明涉及一种铝型材,特别涉及一种环保型铝型材加工工艺。
背景技术
铝型材是一种采用铝制材料,通过轧制、挤出等工艺加工成型的呈几何形状的物体。其在建筑领域中运用广泛。
传统过的铝型材,铝型材的表面经过抗氧化处理后,不仅耐脏,而且表面光滑,易清洁。为了提高铝型材表面的光洁度以及耐酸耐腐性。通常在加工过程中会将铝型材加工材料或成型的铝型材投入防腐液中实施浸泡。然而,防腐液为化学材料,其内具有多种对环境具有严重危害性的成分。
因此,如何即能满足环保,又可提高其耐酸耐腐蚀性,一直是该领域技术人员无法克服的难题。
发明内容
针对现有技术存在的不足,本发明提供了一种对环境无污染、减少加工成本的环保型铝型材加工工艺。
为实现上述目的,本发明提供了如下技术方案:一种环保型铝型
材加工工艺,步骤如下:a、将铝制材料加工呈几何状铝型材;b、将步骤a中成型的铝型材的表面通过磨抛设备实施磨抛;c、对步骤b中完成磨抛的铝型材的表面镀上热塑性复合材料;e、步骤c中的热塑性复合材料为基料、碳纤维、超高分子氟乙烯、导电粒子、偶联剂及热稳定剂,其按重量比为基料50%—60%、碳纤维15%—30%、超高分子氟乙烯1%—5%、导电粒子1%—3%、偶联剂5%—8%及余量热稳定剂。
其中,步骤c中实施镀热塑性复合材料的温度为80℃—90℃,热塑性复合材料与铝型材表面之间涂设有粘合剂。
其中,偶联剂为硅烷偶联剂。基料为PA66。热稳定剂为有机锡类热稳定剂或有机化合物热稳定剂。导电粒子为碳纳米管和氧化石墨稀包覆纳米铝颗粒。
采用上述技术方案,通过在铝型材的表面镀上热塑性复合材料,不仅使铝型材的受力强度、抗冲击力及耐磨性更好,而且加工方便,无需对铝型材本身做更多的处理。节省了加工成本,而且热塑性复合材料对环境无污染。
具体实施方式
本发明为一种环保型铝型材加工工艺,步骤如下:a、将铝制材料
加工呈几何状铝型材;b、将步骤a中成型的铝型材的表面通过磨抛设备实施磨抛;c、对步骤b中完成磨抛的铝型材的表面镀上热塑性复合材料;e、步骤c中的热塑性复合材料为基料、碳纤维、超高分子氟乙烯、导电粒子、偶联剂及热稳定剂,其按重量比为基料50%—60%、碳纤维15%—30%、超高分子氟乙烯1%—5%、导电粒子1%—3%、偶联剂5%—8%及余量热稳定剂。采用上述技术方案,通过在铝型材的表面镀上热塑性复合材料,不仅使铝型材的受力强度、抗冲击力及耐磨性更好,而且加工方便,无需对铝型材本身做更多的处理。节省了加工成本,而且热塑性复合材料对环境无污染。
在本发明实施例中,步骤c中实施镀热塑性复合材料的温度为80℃—90℃,热塑性复合材料与铝型材表面之间涂设有粘合剂。其中,偶联剂为硅烷偶联剂。基料为PA66。热稳定剂为有机锡类热稳定剂或有机化合物热稳定剂。导电粒子为碳纳米管和氧化石墨稀包覆纳米铝颗粒。
在本发明实施例1中,热塑性复合材料按重量比为基料50%、碳纤维15%、超高分子氟乙烯1%、导电粒子1%、偶联剂5%及余量热稳定剂。
在本发明实施2中,其按重量比为基料55%、碳纤维20%、超高分子氟乙烯3%、导电粒子1.5%、偶联剂6%及余量热稳定剂。
在本发明实施例3中,其按重量比为基料60%、碳纤维30%、超高分子氟乙烯5%、导电粒子3%、偶联剂8%及余量热稳定剂。
下面结合下表对上述实施例的试验数据进行说明。
实施例一 | 实施例二 | 实施例三 | |
拉伸强度/MPa | 2130 | 1928 | 3032 |
0°压缩强度/MPa | 909 | 838 | 1070 |
0°弯曲模量/GPa | 121 | 107 | 138 |
弯曲强度/MPa | 1380 | 1197 | 1570 |
90°拉伸强度/MPa | 80 | 71 | 96 |
0°剪切强度/MPa | 105 | 99 | 117 |
层间断裂韧性/(kj/m2) | 1. 1-1.7 | 0. 8-1.0 | 1.1- 1.2 |
阻燃性能 | V0级 | V0级 | V2级 |
Claims (8)
1.一种环保型铝型材加工工艺,其特征在于,步骤如下:a、将
铝制材料加工呈几何状铝型材;
b、将步骤a中成型的铝型材的表面通过磨抛设备实施磨抛;
c、对步骤b中完成磨抛的铝型材的表面镀上热塑性复合材料;
e、步骤c中的热塑性复合材料为基料、碳纤维、超高分子氟乙烯、导电粒子、偶联剂及热稳定剂,其按照重量比为基料50%—60%、碳纤维15%—30%、超高分子氟乙烯1%—5%、导电粒子1%—3%、偶联剂5%—8%及余量热稳定剂。
2.根据权利要求1所述的环保型铝型材加工工艺,其特征在于:
所述的步骤c中实施镀热塑性复合材料的温度为80℃—90℃,热塑性复合材料与铝型材表面之间涂设有粘合剂。
3.根据权利要求1或2所述的环保型铝型材加工工艺,其特征在于:所述的偶联剂为硅烷偶联剂。
4.根据权利要求1或2所述的环保型铝型材加工工艺,其特征在于:所述的基料为PA66。
5.根据权利要求3所述的环保型铝型材加工工艺,其特征在于:所述的基料为PA66。
6.根据权利要求1或2所述的环保型铝型材加工工艺,其特征在于:所述的热稳定剂为有机锡类热稳定剂或有机化合物热稳定剂。
7.根据权利要求1或2或5所述的环保型铝型材加工工艺,其特征在于:所述的导电粒子为碳纳米管和氧化石墨稀包覆纳米铝颗粒。
8.根据权利要求3所述的环保型铝型材加工工艺,其特征在于:所述的导电粒子为碳纳米管和氧化石墨稀包覆纳米铝颗粒。