CN109454502A - 一种抗菌耐指纹的磨砂不锈钢制作方法 - Google Patents
一种抗菌耐指纹的磨砂不锈钢制作方法 Download PDFInfo
- Publication number
- CN109454502A CN109454502A CN201811285321.5A CN201811285321A CN109454502A CN 109454502 A CN109454502 A CN 109454502A CN 201811285321 A CN201811285321 A CN 201811285321A CN 109454502 A CN109454502 A CN 109454502A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- stainless steel
- production method
- fingerprint
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种抗菌耐指纹的磨砂不锈钢制作方法,其特征在于所述该制作方法包括如下步骤:(1)对原料(半成品钢卷)进行压平和磨边处理:(2)对磨边压平后的钢板进行表面的活化处理:(3)将活化处理后的钢板进行长度定测和剪切:(4)将上述剪切后的钢板进行宽度定测和剪切;它具有制作工艺简单,效果好,产品使用耐久度稳定持久,制作的过程中用的都是纯天然的材料,不会制造污染,并且制作出来的抗指纹效果好,永久抗指纹和抗菌,比一般的环保钢材效果更好。
Description
技术领域
本发明涉及抗菌耐指纹的磨砂不锈钢制作方法,属于不锈钢领域。
背景技术
不锈钢在生活中运用的非常多,生活中好多材料都是由不锈钢制作的,不锈钢其不锈的特性,深受大家的喜欢,但是不锈钢仅仅只是不生锈,但是还是会在使用中产生大量的细菌的,久而久之细菌会大量的堆积在不锈钢的表面,比如常用的刀具,或者炒菜用的锅子,都会堆积在钢材的表面。
发明内容
本发明的目的在于克服现有技术存在的不足,而提供一种制作方法简单,制作步骤简化,制造的产品更稳定,使用寿命长,能够抗菌的不锈钢材料。
本发明的目的是通过如下技术方案来完成的,所述的一种抗菌耐指纹的磨砂不锈钢制作方法,所述该制作方法包括如下步骤:
(1)对原料(半成品钢卷)进行压平和磨边处理:
(2)对磨边压平后的钢板进行表面的活化处理:
(3)将活化处理后的钢板进行长度定测和剪切:
(4)将上述剪切后的钢板进行宽度定测和剪切:
(5)将定测和剪切后的钢板放入燃烧炉中进行加热处理:
(6)对处理后的钢板拿出后进行冷处理:
(7)处理后的钢板进行冷却放置2-4小时:
(8)将预处理好的钢板放入磨砂机进行表面磨砂处理:
(9)磨砂处理后的钢板进入激光机中进行抗指纹处理,使一侧表面均匀收到激光扫射:
(10)将处理好的不锈钢板浸入抗菌化学池中浸泡2-6小时;
(11)浸泡后的不锈钢板直接进入贴膜机进行贴膜。
(12)贴膜后的不锈钢板进入烘干箱进行烘干
(12)烘干后的不锈钢板进行包装入库。
作为优选:所述步骤(2)活化处理为将钢板接阳极,在将铅板放入阴极,连接好后放入酸池中进行电解活化处理。
作为优选:所述步骤(3)和步骤(4)是将钢板放入大型切割机中进行剪切,所述剪切后的钢板用打磨机进行边缘打磨光滑。
作为优选:所述步骤(5)燃烧炉中的温度为300°。
作为优选:所述步骤(6)中冷处理的温度为常温。
作为优选:所述步骤(7)中放置时间为4小时。
作为优选:所述步骤(9)中使用的抗指纹处理用的激光机为光滑激光喷水机。
作为优选:所述步骤(10)中将处理好的不锈钢板浸入抗菌化学池中浸泡6小时
本发明具有制作工艺简单,效果好,产品使用耐久度稳定持久,制作的过程中用的都是纯天然的材料,不会制造污染,并且制作出来的抗指纹效果好,永久抗指纹,比一般的环保钢材效果更好。
具体实施方式
下面将对本发明作详细的介绍:本发明所述的一种环保型彩色不锈钢板的制作方法,所述该制作方法包括如下步骤:
一种抗菌耐指纹的磨砂不锈钢制作方法,所述该制作方法包括如下步骤:
(1)对原料(半成品钢卷)进行压平和磨边处理:
(2)对磨边压平后的钢板进行表面的活化处理:
(3)将活化处理后的钢板进行长度定测和剪切:
(4)将上述剪切后的钢板进行宽度定测和剪切:
(5)将定测和剪切后的钢板放入燃烧炉中进行加热处理:
(6)对处理后的钢板拿出后进行冷处理:
(7)处理后的钢板进行冷却放置2-4小时:
(8)将预处理好的钢板放入磨砂机进行表面磨砂处理:
(9)磨砂处理后的钢板进入激光机中进行抗指纹处理,使一侧表面均匀收到激光扫射:
(10)将处理好的不锈钢板浸入抗菌化学池中浸泡2-6小时;
(11)浸泡后的不锈钢板直接进入贴膜机进行贴膜。
(12)贴膜后的不锈钢板进入烘干箱进行烘干
(12)烘干后的不锈钢板进行包装入库。
作为优选实施例:所述步骤(2)活化处理为将钢板接阳极,在将铅板放入阴极,连接好后放入酸池中进行电解活化处理,所述步骤(3)和步骤(4)是将钢板放入大型切割机中进行剪切,所述剪切后的钢板用打磨机进行边缘打磨光滑,所述步骤(5)燃烧炉中的温度为300°,所述步骤(6)中冷处理的温度为常温,所述步骤(7)中放置时间为4小时,所述步骤(9)中使用的抗指纹处理用的激光机为光滑激光喷水机,所述步骤(10)中将处理好的不锈钢板浸入抗菌化学池中浸泡6小时。
Claims (8)
1.一种抗菌耐指纹的磨砂不锈钢制作方法,其特征在于所述该制作方法包括如下步骤:
(1)对原料(半成品钢卷)进行压平和磨边处理:
(2)对磨边压平后的钢板进行表面的活化处理:
(3)将活化处理后的钢板进行长度定测和剪切:
(4)将上述剪切后的钢板进行宽度定测和剪切:
(5)将定测和剪切后的钢板放入燃烧炉中进行加热处理:
(6)对处理后的钢板拿出后进行冷处理:
(7)处理后的钢板进行冷却放置2-4小时:
(8)将预处理好的钢板放入磨砂机进行表面磨砂处理:
(9)磨砂处理后的钢板进入激光机中进行抗指纹处理,使一侧表面均匀收到激光扫射:
(10)将处理好的不锈钢板浸入抗菌化学池中浸泡2-6小时;
(11)浸泡后的不锈钢板直接进入贴膜机进行贴膜;
(12)贴膜后的不锈钢板进入烘干箱进行烘干
(12)烘干后的不锈钢板进行包装入库。
2.根据权利要求1所述的抗菌耐指纹的磨砂不锈钢的制作方法,其特征在于所述步骤(2)活化处理为将钢板接阳极,在将铅板放入阴极,连接好后放入酸池中进行电解活化处理。
3.根据权利要求1所述的环保型彩色不锈钢板的制作方法,其特征在于所述步骤(3)和步骤(4)是将钢板放入大型切割机中进行剪切,所述剪切后的钢板用打磨机进行边缘打磨光滑。
4.根据权利要求1所述的环保型彩色不锈钢板的制作方法,其特征在于所述步骤(5)燃烧炉中的温度为300°。
5.根据权利要求1所述的环保型彩色不锈钢板的制作方法,其特征在于所述步骤(6)中冷处理的温度为常温。
6.根据权利要求1所述的环保型彩色不锈钢板的制作方法,其特征在于所述步骤(7)中放置时间为4小时。
7.根据权利要求1所述的环保型彩色不锈钢板的制作方法,其特征在于所述步骤(9)中使用的抗指纹处理用的激光机为光滑激光喷水机。
8.根据权利要求1所述的环保型彩色不锈钢板的制作方法,其特征在于所述步骤(10)中将处理好的不锈钢板浸入抗菌化学池中浸泡6小时。