CN109453000A - 一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法 - Google Patents
一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法 Download PDFInfo
- Publication number
- CN109453000A CN109453000A CN201811167387.4A CN201811167387A CN109453000A CN 109453000 A CN109453000 A CN 109453000A CN 201811167387 A CN201811167387 A CN 201811167387A CN 109453000 A CN109453000 A CN 109453000A
- Authority
- CN
- China
- Prior art keywords
- magnetic therapy
- humidity
- moisture absorption
- layer
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种利于伤口愈合的控湿型磁疗环保敷料，包括吸湿顶层、磁疗吸湿层、传感器监测层与载层，其中，传感器监测层内的湿敏传感器包括上部电极、下部电极、感湿膜与绝缘基材，感湿膜的顶面与载层的底面相接触，上、下部电极通过信号线与位于环保敷料外部的湿度监测系统相连接，所述吸湿顶层由壳聚糖纳米纤维膜裁剪而成，壳聚糖纳米纤维膜由乙酸、壳聚糖、聚氧化乙烯经静电纺丝而得，所述磁疗吸湿层包括成一体结构的磁性物质、吸湿物质，其中，磁性物质包括钕铁硼稀土磁粉，吸湿物质包括丝素蛋白、海藻酸钠、甘油。本设计不仅具备控湿与磁疗功能，利于伤口愈合，而且绿色环保性较好，成本低、效率高。
Description
技术领域
本发明涉及一种敷料，属于医用敷料领域，尤其涉及一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法，具体适用于增强吸湿效果与增设磁疗作用，且绿色环保性较强。
背景技术
创面愈合是一个复杂的过程，多重外界因素会直接或间接影响着愈合的情况，这些因素包括伤口的温度、湿度、PH值、含氧量以及微生物的存活量等，因而，促进伤口愈合就必须多重考虑，不仅需要注意到常规的影响因素，如湿度，还得关注到一些能够促进伤口愈合的额外因素，如磁场，此外，还得考虑敷料的制造成本与废物处理成本，尽可能的采取绿色环保材料与技术，如此，才能获得高质量的医用敷料。
公开该背景技术部分的信息仅仅旨在增加对本专利申请的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
发明内容
本发明的目的是克服现有技术中存在的吸湿效果较弱、绿色环保性较差的缺陷与问题，提供一种吸湿效果较强、绿色环保性较好的利于伤口愈合的控湿型磁疗环保敷料及其制造方法。
为实现以上目的，本发明的技术解决方案是：一种利于伤口愈合的控湿型磁疗环保敷料，包括吸湿顶层与载层，且吸湿顶层、载层上下布置；
所述环保敷料还包括磁疗吸湿层与传感器监测层，所述吸湿顶层的底面与磁疗吸湿层的顶面相连接，磁疗吸湿层的底面与载层的顶面相连接；
所述传感器监测层包括湿敏传感器，该湿敏传感器包括上部电极、下部电极、感湿膜与绝缘基材，所述上部电极、下部电极的宽度均小于感湿膜的宽度，上部电极的底面与感湿膜的顶面相连接，感湿膜的顶面上围绕上部电极、感湿膜交接处的部位与载层的底面相接触，感湿膜的底面与绝缘基材的顶面相连接，感湿膜上近感湿膜、绝缘基材交接处的部位开设有内凹槽，该内凹槽内设置有下部电极，上部电极、下部电极各通过一根外导线与信号线的一端相连接，信号线的另一端与位于环保敷料外部的湿度监测系统相连接。
所述传感器监测层还包括绝缘皮与聚氨酯透明贴膜，所述绝缘基材的底面与聚氨酯透明贴膜的中部相连接，聚氨酯透明贴膜的四周围与载层的底面相连接，湿敏传感器夹于载层、聚氨酯透明贴膜之间；所述上部电极上高于上部电极、感湿膜交接处的部位都外包裹有绝缘皮，感湿膜的顶面上围绕绝缘皮、感湿膜交接处的部位与载层的底面相接触。
所述感湿膜的制造原料为聚乙二醇、聚酰亚胺或醋酸纤维素。
所述吸湿顶层由壳聚糖纳米纤维膜裁剪而成，所述壳聚糖纳米纤维膜的制造工艺为静电纺丝，所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸93.4―97.7，壳聚糖2―5，聚氧化乙烯0.7―1.7。
所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸95.5，壳聚糖3.5，聚氧化乙烯1。
所述磁疗吸湿层包括成一体结构的磁性物质、吸湿物质，其中，所述磁性物质包括钕铁硼稀土磁粉，所述吸湿物质包括丝素蛋白、海藻酸钠、甘油。
所述磁疗吸湿层的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
所述磁疗吸湿层的制作原料及重量份比为：丝素蛋白溶液55，甘油0.9，海藻酸钠0.75，钕铁硼稀土磁粉2.5。
一种上述利于伤口愈合的控湿型磁疗环保敷料的制造方法，所述制造方法中所包括的磁疗吸湿层的制取工艺包括以下步骤：先通过蚕丝制取丝素蛋白溶液，再在丝素蛋白溶液中加入甘油作为增塑剂以获取一次处理溶液，然后在一次处理溶液中加入海藻酸钠作为增稠剂以获取二次处理溶液，再在搅拌的状态下向二次处理溶液中加入钕铁硼稀土磁粉，然后搅拌至混合均匀后铺膜以得到一次膜，再将一次膜放入外源磁场中进行充磁处理以使其具备磁性，从而得到二次膜，最后对二次膜进行裁剪以得到最终的磁疗吸湿层；所述磁疗吸湿层的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
所述丝素蛋白溶液是经蚕丝脱胶透析而成，其制作过程为：先将蚕丝放入碳酸钠溶液中脱胶，再用常温水冲洗，脱胶温度高于常温，如此脱胶、冲洗操作重复三次之后，再对所得物进行真空干燥烘干以获得丝素纤维，然后将丝素纤维混合于溴化锂溶液中透析三天以获得丝素蛋白溶液，透析过程中的换水频率为1h/一次。
与现有技术相比，本发明的有益效果为：
1、本发明一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法中，在载层的下方设置有湿敏传感器，该湿敏传感器包括上部电极、下部电极、感湿膜与绝缘基材，感湿膜的顶面上围绕上部电极、感湿膜交接处的部位与载层的底面相接触，上部电极、下部电极各通过一根外导线与信号线的一端相连接，信号线的另一端与位于环保敷料外部的湿度监测系统相连接，应用时，湿敏传感器的电容数值会随湿度变化，从而反映伤口附近的湿度变化，如此，湿敏传感器能对伤口的湿度进行监测，并将监测信息通过信号线发给湿度监测系统，以便于医护人员实时掌控情况并采取合理措施，从而使伤口湿度处于一个最佳促愈范围，不仅利于伤口的愈合，而且能够减少资源浪费，提高工作效率。因此，本发明不仅具备控湿功能，利于伤口的愈合，而且能节省资源，提高医疗效率。
2、本发明一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法中，包括层层设置的吸湿顶层、磁疗吸湿层、载层，具备三层吸湿结构，可实现三阶段吸湿，确保较强的吸湿效果，利于伤口的愈合，此外，吸湿顶层由壳聚糖纳米纤维膜裁剪而成，而壳聚糖纳米纤维膜的制造工艺为静电纺丝，制造原料为乙酸、壳聚糖、聚氧化乙烯，其中，静电纺丝所得的膜具备较大的比表面积和密集的孔隙，具备较好的吸液性，能够从整体上进一步提高敷料的吸湿性，同时，壳聚糖对常见菌落有一定的抑制能力，对红血细胞有凝结作用，可吸收乙酸释放出的质子来止痛，壳聚糖的生物活性便于疮口的自主愈合，聚氧化乙烯可改善壳聚糖的纺丝性能，毒性极低，壳聚糖、聚氧化乙烯都为绿色环保材料，静电纺丝技术也无污染产生，环保性较强。因此，本发明不仅吸湿效果较强、利于伤口愈合，而且绿色环保性较好、杀菌效果较佳。
3、本发明一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法中，磁疗吸湿层包括成一体结构的磁性物质、吸湿物质，其中，所述磁性物质包括钕铁硼稀土磁粉，所述吸湿物质包括丝素蛋白、海藻酸钠、甘油，应用时，蚕丝蛋白具有良好的吸湿性能，海藻酸钠具有良好的生物相容性、可降解特性、优异的吸水性与透氧性，吸湿物质能对透过吸湿顶层的残留伤口分泌液进行二次吸收，扩大了吸液量，而磁性物质产生的磁场效应能够加快伤口愈合的速度。因此，本发明不仅吸湿效果较强，而且具备磁疗功能，利于伤口愈合。
4、本发明一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法中，在制取磁疗吸湿层时，在丝素蛋白溶液中依次加入甘油、海藻酸钠、钕铁硼稀土磁粉后混合均匀，再铺膜、充磁、裁剪以得到产品，整个流程衔接顺畅，操作难度较低，且取材方便，成本少，污染低。因此，本发明不仅制作效率较高，而且成本低、环保性强。
5、本发明一种利于伤口愈合的控湿型磁疗环保敷料及其制造方法中，吸湿顶层采用乙酸、壳聚糖、聚氧化乙烯制作，磁疗吸湿层采用丝素蛋白、海藻酸钠、钕铁硼稀土磁粉制作，载层优选采用海藻酸钠水刺材料或季铵盐壳聚糖水凝胶材料制作，由此可见，绝大部分原材料都是绿色环保无污染的材料，非常利于推广应用，迎合可持续发展战略。因此，本发明的绿色环保性较强。
附图说明
图1是本发明的爆炸视图。
图2是图1中湿敏传感器的结构示意图。
图3是图1中湿敏传感器所监测信息的传输流程图。
图4是本发明中增设有雾化补水器的结构示意图。
图中：吸湿顶层1、磁疗吸湿层2、载层3、传感器监测层4、湿敏传感器41、上部电极411、下部电极412、感湿膜413、绝缘基材414、内凹槽415、绝缘皮42、信号线43、聚氨酯透明贴膜44、外导线45、湿度监测系统5、信号转换器51、存储器52、输出显示器53、蓝牙装置54、雾化补水器6。
具体实施方式
以下结合附图说明和具体实施方式对本发明作进一步详细的说明。
参见图1至图4，一种利于伤口愈合的控湿型磁疗环保敷料，包括吸湿顶层1与载层3，且吸湿顶层1、载层3上下布置；
所述环保敷料还包括磁疗吸湿层2与传感器监测层4，所述吸湿顶层1的底面与磁疗吸湿层2的顶面相连接，磁疗吸湿层2的底面与载层3的顶面相连接；
所述传感器监测层4包括湿敏传感器41，该湿敏传感器41包括上部电极411、下部电极412、感湿膜413与绝缘基材414，所述上部电极411、下部电极412的宽度均小于感湿膜413的宽度，上部电极411的底面与感湿膜413的顶面相连接，感湿膜413的顶面上围绕上部电极411、感湿膜413交接处的部位与载层3的底面相接触，感湿膜413的底面与绝缘基材414的顶面相连接，感湿膜413上近感湿膜413、绝缘基材414交接处的部位开设有内凹槽415，该内凹槽415内设置有下部电极412，上部电极411、下部电极412各通过一根外导线45与信号线43的一端相连接，信号线43的另一端与位于环保敷料外部的湿度监测系统5相连接。
所述传感器监测层4还包括绝缘皮42与聚氨酯透明贴膜44，所述绝缘基材414的底面与聚氨酯透明贴膜44的中部相连接，聚氨酯透明贴膜44的四周围与载层3的底面相连接，湿敏传感器41夹于载层3、聚氨酯透明贴膜44之间；所述上部电极411上高于上部电极411、感湿膜413交接处的部位都外包裹有绝缘皮42，感湿膜413的顶面上围绕绝缘皮42、感湿膜413交接处的部位与载层3的底面相接触。
所述感湿膜413的制造原料为聚乙二醇、聚酰亚胺或醋酸纤维素。
所述吸湿顶层1由壳聚糖纳米纤维膜裁剪而成，所述壳聚糖纳米纤维膜的制造工艺为静电纺丝，所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸93.4―97.7，壳聚糖2―5，聚氧化乙烯0.7―1.7。
所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸95.5，壳聚糖3.5，聚氧化乙烯1。
所述磁疗吸湿层2包括成一体结构的磁性物质、吸湿物质，其中，所述磁性物质包括钕铁硼稀土磁粉，所述吸湿物质包括丝素蛋白、海藻酸钠、甘油。
所述磁疗吸湿层2的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
所述磁疗吸湿层2的制作原料及重量份比为：丝素蛋白溶液55，甘油0.9，海藻酸钠0.75，钕铁硼稀土磁粉2.5。
一种上述利于伤口愈合的控湿型磁疗环保敷料的制造方法，所述制造方法中所包括的磁疗吸湿层2的制取工艺包括以下步骤：先通过蚕丝制取丝素蛋白溶液，再在丝素蛋白溶液中加入甘油作为增塑剂以获取一次处理溶液，然后在一次处理溶液中加入海藻酸钠作为增稠剂以获取二次处理溶液，再在搅拌的状态下向二次处理溶液中加入钕铁硼稀土磁粉，然后搅拌至混合均匀后铺膜以得到一次膜，再将一次膜放入外源磁场中进行充磁处理以使其具备磁性，从而得到二次膜，最后对二次膜进行裁剪以得到最终的磁疗吸湿层2；所述磁疗吸湿层2的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
所述丝素蛋白溶液是经蚕丝脱胶透析而成，其制作过程为：先将蚕丝放入碳酸钠溶液中脱胶，再用常温水冲洗，脱胶温度高于常温，如此脱胶、冲洗操作重复三次之后，再对所得物进行真空干燥烘干以获得丝素纤维，然后将丝素纤维混合于溴化锂溶液中透析三天以获得丝素蛋白溶液，透析过程中的换水频率为1h/一次。
本发明的原理说明如下：
本发明旨在应对一般伤口出现的问题，提供一种新型智能敷料，以利于伤口的愈合。其中，吸湿顶层优选为壳聚糖纳米纤维膜材料，即壳聚糖、聚氧化乙烯混合后再经静电纺丝获得(壳聚糖的性质为高脱乙酰度≥95％，中粘度≥200mpas，所述聚氧化乙烯的性质为中分子量)，该技术具备高吸液率、半渗透性、止血效果好、功能性、环保的优点，吸湿顶层作为基底，直接贴附于伤口表面，具有更好的贴附性、吸液性、抗菌性，可止血止痛，同时壳聚糖的生物活性便于疮口的自主愈合在医疗卫生领域，壳聚糖对常见菌落有一定的抑制能力，对红血细胞有凝结作用，可吸收乙酸释放出的质子来止痛，而聚氧化乙烯可改善壳聚糖的纺丝性能，毒性极低。磁疗吸湿层内设置有磁性物质(优选为钕铁硼稀土磁粉)与吸湿物质(优选为丝素蛋白与海藻酸钠)，其中，蚕丝质地柔软、透气性良好、悬垂感优良，与人体具有良好的组织相容性，其加工成的蚕丝蛋白具有良好的吸湿性能，海藻酸钠具有良好的生物相容性、可降解特性、优异的吸水性与透氧性，吸湿物质能对透过吸湿顶层的残留伤口分泌液进行二次吸收，扩大了吸液量，而磁性物质产生的磁场效应能够加快伤口愈合的速度。传感器监测层能使得本发明相对于单纯抗菌的纤维状敷料具有智能感湿、控湿功能，方便实时感应患者伤口周围的湿度，若湿度低，则补水以提高湿度，若湿度高，则报警，并更换敷料，使更换时间次数合理化，减少伤痛。载层则能进一步优化敷料整体的机械强度、粘附固定性及吸液性。
综上所述，本发明所公开的敷料集抗菌、透气、三阶段吸湿于一体，一定程度上增加了其使用时间，减少了资源浪费，同时智能感应传递伤口实时湿度以及补水操作以维持最佳愈合环境更接近现代化医疗。
载层的制造材料优选为汉麻/海藻酸钠水刺材料或季铵盐壳聚糖水凝胶材料的原因在于：汉麻纤维含有四氢大麻酚等酚类物质，对金黄色葡萄球菌等菌落有抑制抑菌杀菌作用，且汉麻纤维表面分布着许多微孔和缝隙，可阻止厌氧细菌的生理活动，有效杀菌。同时，季铵盐壳聚糖是带正电荷的碱性多糖，细菌与其接触后，表面阳离子基团与组成微生物细胞壁的唾液酸磷脂等阴离子彼此吸引，拘束了微生物的自由度，阻截其代谢，有效杀菌。
本发明中“上部电极411上高于上部电极411、感湿膜413交接处的部位都外包裹有绝缘皮42，感湿膜413的顶面上围绕绝缘皮42、感湿膜413交接处的部位与载层3的底面相接触”是指：上部电极411的底面已经与感湿膜413的顶面相连接，不再暴露于外部，因而不需要绝缘，本设计只需将上部电极411剩下的其余暴露于外部的部位裹上绝缘皮42即可。同时，由于上部电极411的宽度小于感湿膜413，因而，感湿膜413的顶面上还有剩余空间与载层3的底面相接触，从而监测伤口附近的湿度。
本发明中湿敏传感器41的相关物理量关系为：根据含弱极性官能团的感湿膜的感湿机理，水分子在膜上近似独立存在，主要是水分子影响介电常数的变化，关系式可近似表示为ε1≈KIPRH-εH2O，进一步可得电容与相对湿度的关系C＝ε1·S/K2D＝KIPRHεH2O-S/K2D(其中K1，2为比例系数，P为聚乙二醇膜的气孔率，RH为相对湿度)。
本发明中的吸湿顶层优选为采用壳聚糖纳米纤维膜制作，而壳聚糖纳米纤维膜采用静电纺丝工艺制作，其静电纺丝的工艺参数优选为：纺丝电压为17kv，纺丝距离为18cm，纺丝液流速为0.6ml/h。具体制作时，先进行预纺，观察纺丝过程的间隙微调工艺参数，待情况稳定后，开始正式进行纺丝，最后选取电镜测试下纤维最均匀地备用。由于电纺膜较大的比表面积和较高的孔隙率使得膜材料拥有良好的延展性、吸液性和透气性。此外，电纺层可以根据病情需要，加入杀菌剂、消炎药物、生长因子甚至活细胞等负载药物，对症下药，方便合理地缩短患病周期。
本发明中的磁疗吸湿层2优选结构为分成多个小块，而不是一个整块，且所有小块的整体面积比吸湿顶层、载层都小，此时，分成小块不仅利于均匀布置，增强磁场作用，而且不会完全覆盖吸湿顶层，利于透气。
实施例1：
参见图1至图4，一种利于伤口愈合的控湿型磁疗环保敷料，包括吸湿顶层1、磁疗吸湿层2、载层3与传感器监测层4，所述吸湿顶层1的底面与磁疗吸湿层2的顶面相连接，磁疗吸湿层2的底面与载层3的顶面相连接；所述传感器监测层4包括湿敏传感器41，该湿敏传感器41包括上部电极411、下部电极412、感湿膜413与绝缘基材414，所述上部电极411、下部电极412的宽度均小于感湿膜413的宽度，上部电极411的底面与感湿膜413的顶面相连接，感湿膜413的顶面上围绕上部电极411、感湿膜413交接处的部位与载层3的底面相接触，感湿膜413的底面与绝缘基材414的顶面相连接，感湿膜413上近感湿膜413、绝缘基材414交接处的部位开设有内凹槽415，该内凹槽415内设置有下部电极412，上部电极411、下部电极412各通过一根外导线45与信号线43的一端相连接，信号线43的另一端与位于环保敷料外部的湿度监测系统5相连接。
应用时，先由湿敏传感器41检测病患伤口的湿度，再将反映湿度的初始信息经信号线43传送到位于敷料之外的湿度监测系统5中，并由湿度监测系统5对监测的湿度信息进行显示，然后根据显示的湿度信息对敷料进行操作。
实施例2：
基本内容同实施例1，不同之处在于：
所述传感器监测层4还包括绝缘皮42与聚氨酯透明贴膜44，所述绝缘基材414的底面与聚氨酯透明贴膜44的中部相连接，聚氨酯透明贴膜44的四周围与载层3的底面相连接，湿敏传感器41夹于载层3、聚氨酯透明贴膜44之间；所述上部电极411上高于上部电极411、感湿膜413交接处的部位都外包裹有绝缘皮42，感湿膜413的顶面上围绕绝缘皮42、感湿膜413交接处的部位与载层3的底面相接触。
实施例3：
基本内容同实施例1，不同之处在于：
所述吸湿顶层1由壳聚糖纳米纤维膜裁剪而成，所述壳聚糖纳米纤维膜的制造工艺为静电纺丝，所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸93.4―97.7，壳聚糖2―5，聚氧化乙烯0.7―1.7。优选壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸95.5，壳聚糖3.5，聚氧化乙烯1。
实施例4：
基本内容同实施例1，不同之处在于：
所述磁疗吸湿层2包括成一体结构的磁性物质、吸湿物质，其中，所述磁性物质包括钕铁硼稀土磁粉，所述吸湿物质包括丝素蛋白、海藻酸钠、甘油。所述磁疗吸湿层2的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。优选丝素蛋白溶液的浓度为4％―5％wt，所述甘油的浓度为8％―10％w/v。
一种上述利于伤口愈合的控湿型磁疗环保敷料的制造方法，所述制造方法中所包括的磁疗吸湿层2的制取工艺包括以下步骤：先通过蚕丝制取丝素蛋白溶液，再在丝素蛋白溶液中加入甘油作为增塑剂以获取一次处理溶液，然后在一次处理溶液中加入海藻酸钠作为增稠剂以获取二次处理溶液，再在搅拌的状态下向二次处理溶液中加入钕铁硼稀土磁粉(在搅拌状态下加入钕铁硼稀土磁粉时，优选操作为：将二次处理溶液放置电动搅拌器内，调制温度为50℃，再在搅拌的过程中分批缓慢加入钕铁硼稀土磁粉)，然后搅拌至混合均匀后铺膜以得到一次膜，再将一次膜放入外源磁场中进行充磁处理以使其具备磁性，从而得到二次膜，最后对二次膜进行裁剪以得到最终的磁疗吸湿层2；所述磁疗吸湿层2的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
实施例5：
基本内容同实施例4，不同之处在于：
所述丝素蛋白溶液是经蚕丝脱胶透析而成，其制作过程为：先将蚕丝放入碳酸钠溶液中脱胶，再用常温水冲洗，脱胶温度高于常温，如此脱胶、冲洗操作重复三次之后，再对所得物进行真空干燥烘干以获得丝素纤维，然后将丝素纤维混合于溴化锂溶液中透析三天以获得丝素蛋白溶液，透析过程中的换水频率为1h/一次。
实施例6：
基本内容同实施例1，不同之处在于：
所述湿度监测系统5包括信号转换器51、存储器52、输出显示器53与蓝牙装置54，所述信号转换器51的输入端经信号线43与湿敏传感器41相连接，信号转换器51的输出端依次经存储器52、蓝牙装置54后与输出显示器53相连接，且信号转换器51、存储器52、蓝牙装置54集成在同一块电路板上。所述敷料还包括雾化补水器6，该雾化补水器6的出气口与载层3的底面相通。
反映湿度的初始信息先经信号线43传送到位于敷料之外的信号转换器51中，再由信号转换器51对初始信息进行转换，然后将转换后的信息发至存储器52进行存储，再由存储器52将存储的信息经蓝牙装置54发至输出显示器53上进行显示。所述根据显示的湿度信息对敷料进行操作是指：当湿敏传感器41检测的湿度高于设定湿度范围，且湿度信息已在湿度监测系统5上进行显示时，湿度监测系统5进行报警，以提醒更换敷料；当湿敏传感器41检测的湿度低于设定湿度范围，且湿度信息已在湿度监测系统5上进行显示时，对敷料进行补水以提高伤口周围的湿度；当湿敏传感器41检测的湿度位于设定湿度范围之内，且湿度信息已在湿度监测系统5上进行显示时，不操作。上述设定湿度范围优选为40％―60％。
实施例7：
基本内容同实施例1，不同之处在于：
载层的制造材料为汉麻/海藻酸钠水刺材料或季铵盐壳聚糖水凝胶材料，其中，伤口出血期采用汉麻/海藻酸钠水刺材料，肉芽形成期采用季铵盐壳聚糖水凝胶材料。
Claims (10)
1.一种利于伤口愈合的控湿型磁疗环保敷料，包括吸湿顶层(1)与载层(3)，且吸湿顶层(1)、载层(3)上下布置，其特征在于：
所述环保敷料还包括磁疗吸湿层(2)与传感器监测层(4)，所述吸湿顶层(1)的底面与磁疗吸湿层(2)的顶面相连接，磁疗吸湿层(2)的底面与载层(3)的顶面相连接；
所述传感器监测层(4)包括湿敏传感器(41)，该湿敏传感器(41)包括上部电极(411)、下部电极(412)、感湿膜(413)与绝缘基材(414)，所述上部电极(411)、下部电极(412)的宽度均小于感湿膜(413)的宽度，上部电极(411)的底面与感湿膜(413)的顶面相连接，感湿膜(413)的顶面上围绕上部电极(411)、感湿膜(413)交接处的部位与载层(3)的底面相接触，感湿膜(413)的底面与绝缘基材(414)的顶面相连接，感湿膜(413)上近感湿膜(413)、绝缘基材(414)交接处的部位开设有内凹槽(415)，该内凹槽(415)内设置有下部电极(412)，上部电极(411)、下部电极(412)各通过一根外导线(45)与信号线(43)的一端相连接，信号线(43)的另一端与位于环保敷料外部的湿度监测系统(5)相连接。
2.根据权利要求1所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述传感器监测层(4)还包括绝缘皮(42)与聚氨酯透明贴膜(44)，所述绝缘基材(414)的底面与聚氨酯透明贴膜(44)的中部相连接，聚氨酯透明贴膜(44)的四周围与载层(3)的底面相连接，湿敏传感器(41)夹于载层(3)、聚氨酯透明贴膜(44)之间；所述上部电极(411)上高于上部电极(411)、感湿膜(413)交接处的部位都外包裹有绝缘皮(42)，感湿膜(413)的顶面上围绕绝缘皮(42)、感湿膜(413)交接处的部位与载层(3)的底面相接触。
3.根据权利要求1或2所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述感湿膜(413)的制造原料为聚乙二醇、聚酰亚胺或醋酸纤维素。
4.根据权利要求1或2所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述吸湿顶层(1)由壳聚糖纳米纤维膜裁剪而成，所述壳聚糖纳米纤维膜的制造工艺为静电纺丝，所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸93.4―97.7，壳聚糖2―5，聚氧化乙烯0.7―1.7。
5.根据权利要求4所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述壳聚糖纳米纤维膜的组成成分及重量份比为：乙酸95.5，壳聚糖3.5，聚氧化乙烯1。
6.根据权利要求1或2所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述磁疗吸湿层(2)包括成一体结构的磁性物质、吸湿物质，其中，所述磁性物质包括钕铁硼稀土磁粉，所述吸湿物质包括丝素蛋白、海藻酸钠、甘油。
7.根据权利要求6所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述磁疗吸湿层(2)的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
8.根据权利要求7所述的一种利于伤口愈合的控湿型磁疗环保敷料，其特征在于：所述磁疗吸湿层(2)的制作原料及重量份比为：丝素蛋白溶液55，甘油0.9，海藻酸钠0.75，钕铁硼稀土磁粉2.5。
9.一种权利要求1或2所述的利于伤口愈合的控湿型磁疗环保敷料的制造方法，其特征在于：所述制造方法中所包括的磁疗吸湿层(2)的制取工艺包括以下步骤：先通过蚕丝制取丝素蛋白溶液，再在丝素蛋白溶液中加入甘油作为增塑剂以获取一次处理溶液，然后在一次处理溶液中加入海藻酸钠作为增稠剂以获取二次处理溶液，再在搅拌的状态下向二次处理溶液中加入钕铁硼稀土磁粉，然后搅拌至混合均匀后铺膜以得到一次膜，再将一次膜放入外源磁场中进行充磁处理以使其具备磁性，从而得到二次膜，最后对二次膜进行裁剪以得到最终的磁疗吸湿层(2)；
所述磁疗吸湿层(2)的制作原料及重量份比为：丝素蛋白溶液50―60，甘油0.8―1，海藻酸钠0.5―1，钕铁硼稀土磁粉2―3。
10.根据权利要求9所述的一种利于伤口愈合的控湿型磁疗环保敷料的制造方法，其特征在于：所述丝素蛋白溶液是经蚕丝脱胶透析而成，其制作过程为：先将蚕丝放入碳酸钠溶液中脱胶，再用常温水冲洗，脱胶温度高于常温，如此脱胶、冲洗操作重复三次之后，再对所得物进行真空干燥烘干以获得丝素纤维，然后将丝素纤维混合于溴化锂溶液中透析三天以获得丝素蛋白溶液，透析过程中的换水频率为1h/一次。