CN109440210A - A kind of color fine toning process of weaving - Google Patents
A kind of color fine toning process of weaving Download PDFInfo
- Publication number
- CN109440210A CN109440210A CN201811191585.4A CN201811191585A CN109440210A CN 109440210 A CN109440210 A CN 109440210A CN 201811191585 A CN201811191585 A CN 201811191585A CN 109440210 A CN109440210 A CN 109440210A
- Authority
- CN
- China
- Prior art keywords
- color
- parts
- fiber
- mixing machine
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of color fine toning process of weaving, the following steps are included: S1: weighing the mill base raw material including following parts by weight；S2: weighing raw material by proportion described in S1, and fiber mill base be added in the first mixing machine, and subsequent addition color particle, the then mixing of addition filler；S3: polyurethane elastomeric fiber is added in the second mixing machine, softening agent is then added in mixing machine, is mixed；S4: by the raw material in mixed S3, it is added in the first mixing machine, make mixed polyurethane elastomeric fiber and softening agent, it is sufficiently mixed with mixed fiber mill base, color particle and filler, then synthetic thickening agent is added into the first mixing machine again, mix synthetic thickening agent adequately in the first mixing machine, the mill base for completing fiber is prepared；S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completes to process color fine toning.
Description
Technical field
The present invention relates to textile technology field more particularly to a kind of color fine toning process of weaving.
Background technique
It is existing color fine using " original liquid coloring " technology, during the spinning process by adding Masterbatch online under solution
The colored big chemical fibre of coloring production is mixed, main technical point is injected through drying, melted before polyester fondant enters spinning manifold
Modified feedstock after melting, filter, measuring, together with polyester fondant after the full and uniform mixing of high efficiency static mixer, jointly into
Enter spinning manifold and carries out spinning.It is carried out in process of manufacture to fiber mill base, when needing to make fiber mill base that there are various face
It when color, needs using color particle, carries out toning processing with condensating fiber mill base, it is existing that condensating fiber mill base is matched by color particle
The coloured silk recalled is fine, does not have good elasticity and pliability, is applied in textile industry, reduces the service performance of color fibre.
Therefore, we have proposed a kind of color fine toning process of weaving for solving the above problems.
Summary of the invention
The purpose of the present invention is to solve exist in the prior art it is existing by color particle with condensating fiber mill base tune
Coloured silk out is fine, does not have good elasticity and pliability, is applied in textile industry, reduces lacking for the service performance of color fibre
Point, and the color fine toning process of a kind of weaving proposed.
To achieve the goals above, present invention employs following technical solutions:
The color fine toning process of a kind of weaving proposed by the present invention, comprising the following steps:
S1: the mill base raw material including following parts by weight: 30~50 parts of fiber mill base, 25~35 parts of color particle, polyurethane is weighed
10~20 parts of elastomer, 5~15 parts of filler, 3~5 parts of synthetic thickening agent, 2~6 parts of softening agent；
S2: weighing raw material by proportion described in S1, and fiber mill base be added in the first mixing machine, and subsequent addition color is micro-
Then filler is added in grain, carry out being mixed into 10~15min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, softening agent is then added in mixing machine, is mixed into
8~10min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed with mixed fiber mill base, color particle and filler, and incorporation time is 15~20min, then
Synthetic thickening agent is added into the first mixing machine again, incorporation time is 10~20min, keeps synthetic thickening agent adequately mixed first
Mixing in conjunction machine, the mill base for completing fiber are prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
Preferably, described to weigh the mill base raw material including following parts by weight: 40 parts of fiber mill base, gathers 30 parts of color particle
15 parts of ammoniacum elastomer, 10 parts of filler, 4 parts of synthetic thickening agent, 5 parts of softening agent.
Preferably, the softening agent is selected as one in organic silicon, ester based quaternary ammonium salt or Gemini cationic softener
Kind.
Preferably, the thickener is selected as in fatty acid ester high-molecular compound, methacrylic acid or acrylate
One kind.
Preferably, the filler selection talcum powder, alumina powder, glass powder, flake asbestos, mica powder, silica flour or carbon
One of fiber.
Preferably, the color particle includes one or both of red, yellow, orange, blue, green, purple, black, goth black or white
Above mixture.
Preferably, the revolving speed of first mixing machine is 800~1000 revs/min, and the revolving speed of the second mixing machine is 500
~800 revs/min.
The beneficial effects of the present invention are:
1, of the invention, it is added to polyurethane fiber fiber in color fine toning raw material, increases the inoxidizability of color fine mill base and resistance to
It is hot, while it being added to softening agent in the feed, the surface-active of dyeing paste is improved, increases the stability of softening agent, more
Have both the function of sterilizing.
2, of the invention, it is added to thickener in color fine toning raw material, increases the viscosity of toning after stain mill base, and use
When tinctorial yield it is high, soft, fastness is also relatively good, while overcoming the colour brightness of synthetic thickening agent, while thickener
Easy to use, adaptability is good, and chemical compatibility is preferable, not will cause degradation or condensation, not easy to foaming, improves and utilizes dyeing
Stamp uniformity when machine uses.
3, of the invention, the weaving colored fiber mill base after the completion of mixing colours has stable structure, excellent patience, color fresh
Gorgeous, strong coloring force, durability are good, partial size is small and narrowly distributing, environmental-protecting performance height, good spinnability, non-discolouring in spinning process and not
The characteristics of migration, and chromatography is complete, has good aqueous, environmental protective.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment one
The color fine toning process of a kind of weaving proposed by the present invention, comprising the following steps:
S1: the mill base raw material including following parts by weight: 45 parts of fiber mill base, 20 parts of color particle, polyurethane elastomer fiber is weighed
13 parts, 8 parts of filler, 3 parts of synthetic thickening agent, 5 parts of softening agent；
S2: color fibre weighs raw material by proportion described in S1, and fiber mill base is added in the first mixing machine, the first mixing machine
Revolving speed is 800 revs/min, and subsequent addition color particle, then addition filler, carries out being mixed into 13min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, and the revolving speed of the second mixing machine is 500 revs/min then mixed
Softening agent is added in conjunction machine, carries out being mixed into 8~10min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed, incorporation time 15min with mixed fiber mill base, color particle and filler, then again to
Synthetic thickening agent is added in first mixing machine, incorporation time 18min mixes synthetic thickening agent adequately in the first mixing machine
It closes, the mill base for completing fiber is prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
Embodiment two
The color fine toning process of a kind of weaving proposed by the present invention, comprising the following steps:
S1: the mill base raw material including following parts by weight: 30 parts of fiber mill base, 25 parts of color particle, polyurethane elastomer fiber is weighed
20 parts, 12 parts of filler, 4 parts of synthetic thickening agent, 6 parts of softening agent；
S2: color fibre weighs raw material by proportion described in S1, and fiber mill base is added in the first mixing machine, the first mixing machine
Revolving speed is 800 revs/min, and subsequent addition color particle, then addition filler, carries out being mixed into 15min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, and the revolving speed of the second mixing machine is 800 revs/min then mixed
Softening agent is added in conjunction machine, carries out being mixed into 10min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed, incorporation time 18min with mixed fiber mill base, color particle and filler, then again to
Synthetic thickening agent is added in first mixing machine, incorporation time 15min mixes synthetic thickening agent adequately in the first mixing machine
It closes, the mill base for completing fiber is prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
Embodiment three
The color fine toning process of a kind of weaving proposed by the present invention, comprising the following steps:
S1: the mill base raw material including following parts by weight: 40 parts of fiber mill base, 30 parts of color particle, polyurethane elastomer fiber is weighed
15 parts, 10 parts of filler, 4 parts of synthetic thickening agent, 5 parts of softening agent；
S2: color fibre weighs raw material by proportion described in S1, and fiber mill base is added in the first mixing machine, the first mixing machine
Revolving speed is 800 revs/min, and subsequent addition color particle, then addition filler, carries out being mixed into 15min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, and the revolving speed of the second mixing machine is 500 revs/min then mixed
Softening agent is added in conjunction machine, carries out being mixed into 10min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed, incorporation time 20min with mixed fiber mill base, color particle and filler, then again to
Synthetic thickening agent is added in first mixing machine, incorporation time 20min mixes synthetic thickening agent adequately in the first mixing machine
It closes, the mill base for completing fiber is prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
Example IV
The color fine toning process of a kind of weaving proposed by the present invention, comprising the following steps:
S1: the mill base raw material including following parts by weight: 50 parts of fiber mill base, 25 parts of color particle, polyurethane elastomer fiber is weighed
10 parts, 5 parts of filler, 3 parts of synthetic thickening agent, 2 parts of softening agent；
S2: color fibre weighs raw material by proportion described in S1, and fiber mill base is added in the first mixing machine, the first mixing machine
Revolving speed is 1000 revs/min, and subsequent addition color particle, then addition filler, carries out being mixed into 10min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, and the revolving speed of the second mixing machine is 500 revs/min then mixed
Softening agent is added in conjunction machine, carries out being mixed into 8min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed, incorporation time 15min with mixed fiber mill base, color particle and filler, then again to
Synthetic thickening agent is added in first mixing machine, incorporation time 10min mixes synthetic thickening agent adequately in the first mixing machine
It closes, the mill base for completing fiber is prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
Embodiment five
The color fine toning process of a kind of weaving proposed by the present invention, comprising the following steps:
S1: the mill base raw material including following parts by weight: 40 parts of fiber mill base, 35 parts of color particle, polyurethane elastomer fiber is weighed
18 parts, 5 parts of filler, 5 parts of synthetic thickening agent, 6 parts of softening agent；
S2: color fibre weighs raw material by proportion described in S1, and fiber mill base is added in the first mixing machine, the first mixing machine
Revolving speed is 1000 revs/min, and subsequent addition color particle, then addition filler, carries out being mixed into 10min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, and the revolving speed of the second mixing machine is 500 revs/min then mixed
Softening agent is added in conjunction machine, carries out being mixed into 8min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed, incorporation time 15min with mixed fiber mill base, color particle and filler, then again to
Synthetic thickening agent is added in first mixing machine, incorporation time 10min mixes synthetic thickening agent adequately in the first mixing machine
It closes, the mill base for completing fiber is prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
It is as a result as follows to the fine dyeing paste of coloured silk that above-described embodiment one is obtained to the modulation of five shading process of embodiment:
| Embodiment one | Embodiment two | Embodiment three | Example IV | Embodiment five | |
| Saturation degree | It is lower | It is higher | It is high | It is higher | It is lower |
The mill base for according to embodiment one to the toning process of embodiment five, contrasting according to embodiment three, and being deployed according to needs
Color, weaving colored fiber mill base after the completion of mixing colours have stable structure, excellent patience, bright-colored, strong coloring force, resistance to
Long property is good, partial size is small and narrowly distributing, environmental-protecting performance height, good spinnability, non-discolouring and nonmigratory feature in spinning process, and color
Compose it is complete, have good aqueous, environmental protective.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of color fine toning process of weaving, which comprises the following steps:
S1: the mill base raw material including following parts by weight: 30~50 parts of fiber mill base, 25~35 parts of color particle, polyurethane is weighed
10~20 parts of elastomer, 5~15 parts of filler, 3~5 parts of synthetic thickening agent, 2~6 parts of softening agent；
S2: weighing raw material by proportion described in S1, and fiber mill base be added in the first mixing machine, and subsequent addition color is micro-
Then filler is added in grain, carry out being mixed into 10~15min；
S3: polyurethane elastomeric fiber is added in the second mixing machine, softening agent is then added in mixing machine, is mixed into
8~10min；
S4: the raw material in mixed S3 is added in the first mixing machine, makes mixed polyurethane elastomeric fiber and softness
Agent is adequately mixed with mixed fiber mill base, color particle and filler, and incorporation time is 15~20min, then
Synthetic thickening agent is added into the first mixing machine again, incorporation time is 10~20min, keeps synthetic thickening agent adequately mixed first
Mixing in conjunction machine, the mill base for completing fiber are prepared；
S5: when adding color particle in S2 step, the color configured as needed adds corresponding color particle, completion pair
Color fine toning processing.
2. the color fine toning process of a kind of weaving according to claim 1, which is characterized in that described to weigh including following heavy
Measure the mill base raw material of part: 40 parts of fiber mill base, 30 parts of color particle, 15 parts of polyurethane elastomer fiber, 10 parts of filler, synthesis increase
Thick dose 4 parts, 5 parts of softening agent.
3. the color fine toning process of a kind of weaving according to claim 1, which is characterized in that the softening agent has been selected as
One of machine silicon class, ester based quaternary ammonium salt or Gemini cationic softener.
4. the color fine toning process of a kind of weaving according to claim 1, which is characterized in that the thickener is selected as rouge
One of fat esters of gallic acid high-molecular compound, methacrylic acid or acrylate.
5. the color fine toning process of a kind of weaving according to claim 1, which is characterized in that the filler selects talcum
One of powder, alumina powder, glass powder, flake asbestos, mica powder, silica flour or carbon fiber.
6. a kind of color fine toning process of weaving according to claim 1, which is characterized in that the color particle includes
One or more of red, yellow, orange, blue, green, purple, black, goth black or white mixture.
7. the color fine toning process of a kind of weaving according to claim 1, which is characterized in that first mixing machine turns
Speed is 800~1000 revs/min, and the revolving speed of the second mixing machine is 500~800 revs/min.