CN109435560A - A kind of ceramic multilayer grouting process and ceramic - Google Patents
A kind of ceramic multilayer grouting process and ceramic Download PDFInfo
- Publication number
- CN109435560A CN109435560A CN201811608451.8A CN201811608451A CN109435560A CN 109435560 A CN109435560 A CN 109435560A CN 201811608451 A CN201811608451 A CN 201811608451A CN 109435560 A CN109435560 A CN 109435560A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- adobe
- pigment
- mud
- technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ceramic multilayer grouting process, is related to Ceramic Art Design manufacturing technology field, solves the technical issues of existing pottery preparation process existing in the prior art can not prepare the product with particular color hierarchy.Ceramic multilayer grouting process is by preparing the different pigment mud of two or more colors, and the pigment mud of different colours is successively poured into mold in batches, come formed two layers or more different colours adobe, again by scraping, cutting, digging, polishing and/or artistic carving, it is fired after so that adobe is manifested different colours level, the ceramic product with particular color hierarchy can be prepared by realizing, and increase the artistry and appreciation of ceramic.
Description
Technical field
The present invention relates to Ceramic Art Design manufacturing technology fields, more particularly, to a kind of ceramic multilayer grouting process and ceramics
Product.
Background technique
Ceramics development history be Chinese civilization history an important component part, China as four major acids ancient country it
One, brilliant contribution is made that for mankind's social progress and development, wherein the invention and development of ceramics have more unique meaning
Justice, each Chao Gedai has different artistic styles and different technical characteristics on Chinese history, with the development of modern science technology, closely
Occur many new ceramic kinds again over 100 years.
Ceramic all can describe upper paintings or font etc. in ceramic surface from ancient times to the present to achieve the effect that beauty
Decorated, thus make ceramics have ornamental value, this appreciative value be using ceramics be used as a kind of carrier, by describe with it is peculiar
The means such as firing other art forms are presented on ceramics.Due to the influence of firing temperature etc., existing pottery is being made
Even if colorant is added during standby can not also predict the determination pattern formed on finished product, it is even more impossible to prepare the rich of specific pattern
The ceramic of color hierarchy sense.
Applicants have discovered that at least there is following technical problem in the prior art:
Existing pottery preparation process can not prepare the product with particular color hierarchy.
Summary of the invention
The purpose of the present invention is to provide a kind of ceramic multilayer grouting process and ceramics, to solve in the prior art
The technical issues of existing existing pottery preparation process can not prepare the product with particular color hierarchy.
To achieve the above object, the present invention provides following technical schemes:
The present invention provides a kind of ceramic multilayer grouting process, comprising the following steps:
Step A: preparation at least two parts of ceramic muds, it is spare；
Step B: the pigment of different colours is added in each part ceramic mud and is stirred evenly, a variety of pigment mud are formed；
Step C: a kind of pigment mud is poured into mold, the pigment mud can adhere to die inside, pour out not
The pigment mud on mold is adhered to, adobe is formed；
Step D: another pigment mud is poured into mold, the pigment mud comes into full contact with the adobe
After pour out, formed multilayer different colours the adobe；
Step E: as needed, repetitive operation step D or F is entered step；
Step F: after the adobe is dry, taking out the adobe in mold, and the sun-dried mud brick layer surface into
Row processing, makes the adobe expose multilayered color-forming layer；
Step G: it by clear frit on the adobe after processing and is fired.
Optionally, pigment used by step B is refractory ceramics pigment.
Optionally, the mold used by step C is made of gypsum.
Optionally, the thickness of every layer of adobe can be stayed in mold by the pigment mud of this kind of color
Time controls.
Optionally, the processing method of step F includes scraping, cut, polish, dig and/or carving.
Optionally, it is fired described in step G, temperature range is 1100 DEG C to 1300 DEG C, and the time is 7 to 12 hours.
It optionally, further include portraying, depicting and the technique of printing type face on the adobe.
A kind of ceramic is prepared using technique as claimed in claim 1 to 7.
Optionally, the ceramic surface layer has sunk structure.
Optionally, with the lines that color is different in the sunk structure.
The present invention provides a kind of ceramic multilayer grouting process, by preparing the different pigment mud of two or more colors, and
The pigment mud of different colours is successively poured into mold in batches, come formed two layers or more different colours adobe, then lead to
It crosses and scrapes, cuts, digging and/or artistic carving, be fired after so that adobe is manifested different colours level, realizing can prepare
The purpose of ceramic product with particular color hierarchy increases the artistry and appreciation of ceramic.
Detailed description of the invention
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technical description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments of invention for those of ordinary skill in the art without creative efforts, can be with
It obtains other drawings based on these drawings.
Fig. 1 is a kind of side partial sectional view of the ceramic prepared using the technique of ceramic multilayer slip casting of the present invention；
Fig. 2 is a kind of main view of the ceramic prepared using the technique of ceramic multilayer slip casting of the present invention.
1, adobe in figure；2, sunk structure.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, technical solution of the present invention will be carried out below
Detailed description.Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Base
Embodiment in the present invention, those of ordinary skill in the art are obtained all without making creative work
Other embodiment belongs to the range that the present invention is protected.
The present invention provides a kind of ceramic multilayer grouting process, comprising the following steps:
Step A: preparation at least two parts of ceramic muds, it is spare；
Step B: the pigment of different colours is added in each part ceramic mud and is stirred evenly, a variety of pigment mud are formed；
Step C: a kind of pigment mud is poured into mold, the pigment mud can adhere to die inside, pour out not
The pigment mud on mold is adhered to, adobe 1 is formed；
Step D: another pigment mud is poured into mold, after the pigment mud comes into full contact with adobe 1
It pours out, forms the adobe 1 of multilayer different colours；
Step E: as needed, repetitive operation step D or F is entered step；
Step F: after adobe 1 is dry, adobe 1 is taken out in mold, and processed on 1 surface of adobe, made
The adobe 1 exposes multilayered color-forming layer；
Step G: it by clear frit on the adobe 1 after processing and is fired.
The present invention, which realizes, can prepare the ceramic product with particular color hierarchy, beautify ceramic, increase
The ornamental value of ceramic is added.
Optionally embodiment, pigment used by step B are to refractory ceramics pigment.
Pigment used by step B of the present invention is refractory ceramics pigment, ensure that in sintering procedure, will not make outside pigment
Sight changes, and influences the overall beautiful degree of ceramic.
Optionally embodiment, the mold used by step C are made of gypsum.
The mold used by step C of the present invention is made of gypsum, and the adsorptivity of gypsum is larger, can be easy to face
Material mud is adsorbed on outer mold wall, adobe 1 easy to form, and the ability of gypsum adsorption moisture is strong, can be in the short time
Interior suction goes out the moisture in adobe 1, and acceleration forms adobe 1, improves processing and manufacturing efficiency.
The thickness of optionally embodiment, every layer of adobe 1 can be stopped by the pigment mud of this kind of color
Time in mold controls.
The thickness of every layer of adobe of the present invention 1 can stay in the time in mold by the pigment mud of this kind of color
Control, losing moisture due to mud is the rule followed from outside to inside, along with the mold for pouring into pigment mud absorb close to
The pigment slime water of mould inner wall point is hardened inside opposite pigment mud so the pigment mud dehydration close to outer mold wall is fast,
It is longer to shelve the time, and it is bigger to be formed by 1 thickness of adobe, and controls the thickness of adobe 1, then after can making machine-shaping
Product show different effects, keep product pattern more abundant.
Optionally embodiment, the processing method of step F include scraping, cut, polish, dig and/or carving.
As shown in Fig. 1 and Fig. 2 (wherein a, b, c, d, e respectively indicate different color layers), the described of step F of the present invention adds
Work method includes any processing that the different colours in adobe 1 can be made to show out such as scraping, cut, polish, dig and/or carving
The depth of method, processing is controllable, it can by the control of working depth, so that each processing unit is showed not of the same race
Color.
Optionally embodiment is fired described in step G, and temperature range is 1100 DEG C to 1300 DEG C, and the time arrives for 7
12 hours.
Baking temperature range of the present invention is 1100 DEG C to 1300 DEG C, and the time is 7 to 12 hours, and firing temperature is higher, porcelain
Degree is also higher, can satisfy the crowd of different demands.
Optionally embodiment further includes portraying, depicting and the technique of printing type face on the adobe 1.
The invention also includes portraying, depicting and the technique of printing type face on the adobe 1, there is the present invention not only
Color changeable in appearance, also other types of modification further improve the ceramic produced with this kind of technique
Ornamental value.
A kind of ceramic is prepared using any of the above ceramic multilayer grouting process.
The present invention provides a kind of ceramic, this ceramic is the ceramic product manufactured with process above, ornamental value
It is high.
Optionally embodiment, the ceramic surface layer have sunk structure 2.
Ceramic surface layer of the present invention has sunk structure 2, convenient for showing different color layers, and adds
The stereoscopic effect of this ceramic improves the aesthetic measure of this ceramic.
Optionally embodiment, the interior lines different with color of the sunk structure 2.
The lines different with color, makes this ceramic have ornamental value in sunk structure 2 of the present invention.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
Those familiar with the art in the technical scope disclosed by the present invention, can easily think of the change or the replacement, and should all contain
Lid is within protection scope of the present invention.Therefore, protection scope of the present invention should be based on the protection scope of the described claims.
Claims (10)
1. a kind of ceramic multilayer grouting process, which comprises the following steps:
Step A: preparation at least two parts of ceramic muds, it is spare；
Step B: the pigment of different colours is added in each part ceramic mud and is stirred evenly, a variety of pigment mud are formed；
Step C: a kind of pigment mud is poured into mold, the pigment mud can adhere to die inside, pour out nonadherent
The pigment mud on to mold is formed adobe (1)；
Step D: another pigment mud is poured into mold, the pigment mud comes into full contact with the adobe (1)
After pour out, formed multilayer different colours the adobe (1)；
Step E: as needed, repetitive operation step D or F is entered step；
Step F: it after the adobe (1) is dry, is taken out in mold the adobe (1), and in the adobe (1) table
Face is processed, and the adobe (1) is made to expose multilayered color-forming layer；
Step G: it by clear frit on the adobe (1) after processing and is fired.
2. the technique of ceramic multilayer slip casting described in accordance with the claim 1, it is characterised in that: pigment used by step B is resistance to
High temperature ceramic pigment.
3. the technique of ceramic multilayer slip casting described in accordance with the claim 1, it is characterised in that: the mold used by step C
It is made of gypsum.
4. the technique of ceramic multilayer slip casting described in accordance with the claim 1, it is characterised in that: the thickness of every layer of adobe (1)
Degree can be controlled by the time that the pigment mud of this kind of color stays in mold.
5. the technique of ceramic multilayer slip casting described in accordance with the claim 1, it is characterised in that: the processing method packet of step F
It includes and scrapes, cuts, polishes, digs and/or carve.
6. the technique of ceramic multilayer slip casting described in accordance with the claim 1, it is characterised in that: fired described in step G, temperature model
Enclosing is 1100 DEG C to 1300 DEG C, and the time is 7 to 12 hours.
7. according to the technique of any ceramic multilayer slip casting of claim 1-6, it is characterised in that: further include in the sun-dried mud brick
It portrays, depict and the technique of printing type face on layer (1).
8. a kind of ceramic, it is characterised in that: prepared using technique as claimed in claim 1 to 7.
9. ceramic according to claim 8, it is characterised in that: the ceramic surface layer has sunk structure (2).
10. ceramic according to claim 9, it is characterised in that: have color different in the sunk structure (2)
Lines.