CN109433548A - A kind of production method of colorful, imitative stone heat insulating decorative board - Google Patents
A kind of production method of colorful, imitative stone heat insulating decorative board Download PDFInfo
- Publication number
- CN109433548A CN109433548A CN201811284363.7A CN201811284363A CN109433548A CN 109433548 A CN109433548 A CN 109433548A CN 201811284363 A CN201811284363 A CN 201811284363A CN 109433548 A CN109433548 A CN 109433548A
- Authority
- CN
- China
- Prior art keywords
- colorful
- intermediate layer
- plate
- imitative stone
- layer paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production method of colorful, imitative stone heat insulating decorative board is related to heat preservation, the decoration technique field of external wall, including plate pretreatment, the colorful intermediate layer paint of coating or imitative stone intermediate layer paint, plate post-processing；Wherein, plate pretreatment includes including fixed thick sanding；The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies closing, infiltration priming paint, colorful intermediate layer paint or imitative stone intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；Plate post-processing successively includes overlay film, compound and cut；The present invention passes through above-mentioned tens of procedure elaborates, its production process is simple, step is easy, at low cost, colorful made of it, imitative stone heat insulating decorative board integrates heat preservation, fire prevention, waterproof, freeze proof, and color difference is consistent, it never fades, and effectively increases the durability and weatherability of heat insulating decorative board facing.
Description
Technical field
The present invention relates to the heat preservations of external wall, decoration technique field.
Background technique
Currently, one " residential standard, product batch production, construction assembling " green building industry transformation quietly into
In row.
1, external inorganic precoating plate development status and trend
Inorganic pre-coating decorative plaques have had 20 years or more development courses as wall body structure and finishing material in foreign countries, are being permitted
Multinational is largely used.Its good building material of good, functional, applicability in construction as a kind of feature of environmental protection, gradually by people
Approved.In particular with the continuous development of timber structure and steel house, the application amount of inorganic pre-coating decorative plaques will be more next
It is bigger.Such as in Japan, Japan is therefore the problems such as more earthquakes are national, and earthquake can cause wall cracks, and cement mortar falls off resists
The inorganic pre-coating decorative plaques for the features such as shock stability is strong, decorative high, the easy for installation and construction period is short are from 1970 in day
Originally rapid application has been obtained.
Inorganic pre-coating decorative plaques are promoted in Belgium and Japan primarily as a kind of top-grade building material, main to apply
In the application field of some top grades, such as Belgian " good show " plate is mainly used in medical system clean room and subterranean tunnel；Japan
NOZANA Products are mainly used in top-grade building interior wall and exterior wall, and mainly villa system.
2, domestic inorganic precoating plate Analysis on development
From domestic on July 1st, 2003, start to enforce the requirement of building energy conservation 50%, therefore all new buildings
Exterior wall and existing building exterior wall must all carry out building energy-saving renovation before 2020.And the thin-coat plaster generally used at present
Polystyrene outer heat preservation system and glue powder polyphenyl particle outer heat preservation system belong to situ wet operation mode.Although first investment at
This is lower, but situ wet operation influence factor is more, causes lifetime of system short, and cracking just generally occurred using 3-5 years, falls off
Etc. defect so as to cause heat insulation function decline, along with current external coating generallys use low-grade coating, decorative effect and service life
All have a greatly reduced quality.And inorganic pre-coating decorative plaques is used to glue formula External Thermal Insulation Technology for External system for the anchor of host element, make for scene is dry
Industry, the prefabricated completion in factory of all processing works, scene are only assembled.Therefore, system reliability greatly improves, and thoroughly solves
Determined because metope cracking, fall off due to cause heat insulating ability to decline the problem of.Automatically cleaning, long-life epoxy coating and the water on surface
Property coating, make service life of whole system and decorative up to many decades, to have reached the level with building life basic synchronization, be mesh
The external thermal insulation system of preceding most technological innovation.
Wherein, overseas market.Annual new completion construction area external at present is more than 5,000,000,000 square metres, decorative panel market year
Demand is more than 5 Yi ㎡, and overseas market is mainly based on the country such as America and Europe, Southeast Asia, the Middle East, Russia.In developed country,
Novel wall plate usage amount accounts for the ratio of wallboard demand as Japan 64%, the U.S. 48%, Europe 47%.It is expected that following several
Year, global decorative panel annual requirement will be increased with 20% or more speed, and the international market prospect of dalle is very wide.
Domestic market.Currently, the annual newly constructed house area in China is up to 20 Yi ㎡, according to the need of new building area 60%
Dosage calculates, and newly constructed house will be up to 12 Yi ㎡ or more to the annual requirement of decorative panel；China's existing building area about 40,000,000,000
㎡ need to build existing highly energy-consuming and carry out reducing energy consumption for the target for being accomplished to " 2020,65% or more building energy-saving ",
Renovation finishing is carried out to it in annual 5% ratio, decorative panel annual requirement is up to 20 Yi ㎡.It new building and existing builds
Building aspect is that heat insulation decoration integrated plate brings the huge market space.
In addition, for example, the existing Chinese invention patent document application No. is 201610460584 .x discloses a kind of building
The preparation method of colorful titanium pressed sheet is decorated, but above-mentioned production process is complicated, cumbersome, inconvenient, higher cost, and is made
Production board color difference it is inconsistent, cannot get a desired effect.
Summary of the invention
Thoroughly to solve problems of the prior art, present invention aims at proposing that a kind of process is simple, step is simple
Just, at low cost, manufactured production board corrosion resistant performance and weather resistance are strong, and good effect of heat insulation, color difference is consistent, and never moves back
Color, construction and installation are convenient, and the producer of energy conservation and environmental protection, colorful, imitative stone heat insulating decorative board safe and reliable, with long service life
Method.
The production method of colorful, imitative stone heat insulating decorative board of the present invention successively includes during plate pre-processes, coating is colorful
Layer paint or imitative stone intermediate layer paint, plate post-processing；
The plate pretreatment includes carrying out washed ore light to plate using contact calibrating machine, and to washed ore light including fixed thick sanding
Treated plate is purged processing by dust of the dust removing machine to its surface；
The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies closing, infiltration priming paint, colorful intermediate layer paint or imitative stone
Intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；
Plate post-processing successively includes overlay film, compound and cut.
The present invention successively includes plate pretreatment, the colorful intermediate layer paint of coating or imitative stone intermediate layer paint, plate post-processing；Wherein,
Plate pretreatment includes including fixed thick sanding；The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies closing, seeps
It reveals the exact details paint, colorful intermediate layer paint or imitative stone intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；It successively includes overlay film that plate, which post-processes, multiple
It closes and cuts；For the present invention by above-mentioned tens of procedure elaborates, production process is simple, and step is easy, at low cost, system
At colorful, imitative stone heat insulating decorative board integrate heat preservation, fire prevention, waterproof, freeze proof, and color difference is consistent, never fades, and effectively
Improve the durability and weatherability of heat insulating decorative board facing.
Further, the colorful intermediate layer paint of the coating or imitative stone intermediate layer paint specific steps are as follows:
1) back applies closing, carries out UV seal coat to pretreated plate, UV curing time is 3-5 seconds；
2) priming paint is permeated, epoxy infiltration paint coating is carried out to above-mentioned plate using roll coater above and below double roller, paint temperature when coating
At 30~50 DEG C, and natural drying 24 hours solidify；
3) colorful intermediate layer paint or imitative stone intermediate layer paint, using roll coater above and below double roller to above-mentioned plate carry out the colorful intermediate layer paint of roller coating or
Imitative stone intermediate layer paint, 70~80 DEG C of temperature, baking time is 8-10 minutes；
4) colorful lacquer or imitation stone lacquer carries out roller coating colorful lacquer or imitation stone lacquer, temperature to above-mentioned plate using roll coater above and below double roller
30~40 DEG C, natural drying 24 hours；
5) finishing varnish carries out roller coating finishing varnish to above-mentioned plate using double roller roll coater, and 70~80 DEG C of temperature, baking time is
2-3 hours.
Further, the plate post-processes specific steps are as follows:
1) overlay film carries out coating processing to above-mentioned finishing varnish treated plate, becomes multicolored ornamental veneer or imitative stone dress
Adorn veneer；
2) compound, above-mentioned multicolored ornamental veneer or imitative stone fancy veneer are subjected to pressing company with corresponding thermal insulation material by glue
It connects, the pressing time is 3-5 hours, pressure 0.35-0.5mpa to press machine at normal temperature, and it is multiple to become colorful insulation decoration
Plywood or imitative stone heat-insulating decorative composite board；
3) it cuts, above-mentioned colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board is cut according to customer demand,
Sizing plate is become, to meet the actual needs.
Further, glue is polyurethane glue in the step 2.
Further, the plate is calcium silicate board.
Detailed description of the invention
Fig. 1 is the flow sheet of invention.
Specific embodiment
As shown in Figure 1, embodiment one:
A kind of production method of colorful, imitative stone heat insulating decorative board, the production method of colorful, the imitative stone heat insulating decorative board are successively wrapped
The pretreatment of rubbing board material, the colorful intermediate layer paint of coating or imitative stone intermediate layer paint, plate post-processing；
The plate pretreatment includes carrying out washed ore light to plate using contact calibrating machine, and to washed ore light including fixed thick sanding
Treated plate is purged processing by dust of the dust removing machine to its surface；
The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies closing, infiltration priming paint, colorful intermediate layer paint or imitative stone
Intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；
Plate post-processing successively includes overlay film, compound and cut.
Wherein, the colorful intermediate layer paint of the coating or imitative stone intermediate layer paint specific steps are as follows:
1) back applies closing, carries out UV seal coat to pretreated plate, UV curing time is 3 seconds；
2) priming paint is permeated, epoxy infiltration paint coating is carried out to above-mentioned plate using double roller roll coater, paint temperature exists when coating
30 DEG C, and natural drying 24 hours solidify；
3) colorful intermediate layer paint or imitative stone intermediate layer paint carry out the colorful intermediate layer paint of roller coating or imitative stone to above-mentioned plate using double roller roll coater
Intermediate layer paint, temperature 70 C, baking time are 8 minutes；
4) colorful lacquer or imitation stone lacquer, using double roller roll coater to above-mentioned plate carry out roller coating colorful lacquer or imitation stone lacquer, 30 DEG C of temperature,
Natural drying 24 hours；
5) finishing varnish carries out roller coating finishing varnish, temperature 70 C to above-mentioned plate using double roller roll coater, and baking time is 2 hours.
Wherein, the plate post-processes specific steps are as follows:
1) overlay film carries out coating processing to above-mentioned finishing varnish treated plate, becomes multicolored ornamental veneer or imitative stone dress
Adorn veneer；
2) compound, above-mentioned multicolored ornamental veneer or imitative stone fancy veneer are subjected to pressing company with corresponding thermal insulation material by glue
Connect, press machine at normal temperature the pressing time be 3 hours, pressure 0.35mpa, become colorful insulation decoration composite plate or
Imitative stone heat-insulating decorative composite board；
3) it cuts, above-mentioned colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board is cut according to customer demand,
Sizing plate is become, to meet the actual needs.
Wherein, above-mentioned multi-color is that two or more aqueous colored particle is suspended in aqueous interlayer, by primary
Spraying generates the one-component coating for exterior walls of buildings of multicolour, it is using acrylic silicon resin lotion and fluorine carbon tree
Rouge cream is painted with base-material, in conjunction with high-quality inorganic pigment and high performance adjuvant, breaks through painting scientific principle, is process through special process
Water-based exterior wall multicolor finish.Meanwhile multi-color color polyisocyanate, aesthetic feeling is full, and simulation quality is strong, and the surface constructed has solid
Sense and multi-color decorative aesthetic feeling；And it is cheap, designs and varieties are more, construction is simple, anti-cracking waterproof is more excellent, service life is identical.
Wherein, above-mentioned imitation stone lacquer is that a kind of decorative effect exactly likes marble, granitic thick matter exterior wall decorating coating；Mainly
It is formulated using the natural stone-powder of various colors, is chiefly used in manufacturing the imitation stone effect of external wall, therefore also known as liquid stone.It is imitative
Mineral varnish has fire prevention, waterproof, acid and alkali-resistance, anti-pollution.It is nontoxic, tasteless, bonding force is strong, it is will never fade the features such as, can effective ground resistance
Only extraneous adverse circumstances corrode building, extend the service life of building, since imitation stone lacquer has good adhesive force and resistance to jelly
Melt performance, therefore is particularly suitable for using in cold district.Imitation stone lacquer easy construction, easily do it is time saving, it is easy for construction the advantages that.
Wherein, above-mentioned finishing varnish is the finishing varnish of a kind of transparent, not yellowing, UV resistant and chemical attack.Purposes: have
High glaze and high gloss retention, can be used for various wear surfaces, play decoration and protective effect.Advantage: 1. high gloss retentions, not yellowing；
2. high abrasion resistance, resistant to many chemicals corrodes smooth finish surface as 3. ceramic tiles, and effective dust is antifouling.
Wherein, glue is polyurethane glue in the step 2, in the present embodiment, can be incited somebody to action by the polyurethane glue
Multicolored ornamental veneer or imitative stone fancy veneer are reliably connected with corresponding thermal insulation material, and tensile strength is equivalent to every square metre
10-15 tons of pulling force can be born, so that colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board structural strength are high, is used
Service life is long.
Wherein, the plate is calcium silicate board, it should be noted that calcium silicate board is with inorganic mineral fiber or cellulose
The loose staple fiber such as fiber is reinforcing material, with siliceous-calcium materials as main part cementing material, through slurrying, molding, in high temperature height
Accelerate curing reaction in pressure saturated vapor, form calcium silicate gel and manufactured plate, has that bulk density is light, intensity is high, thermally conductive
Coefficient is small, high temperature resistant, corrosion-resistant, the features such as capable of cutting, capable of sawing, and thickness is usually in 30mm or more, and density is in 200-1000kg/
m3, in this way made of colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board good effect of heat insulation, corrosion resistance is strong,
Long service life.
Embodiment two:
A kind of production method of colorful, imitative stone heat insulating decorative board, the production method of colorful, the imitative stone heat insulating decorative board are successively wrapped
The pretreatment of rubbing board material, the colorful intermediate layer paint of coating or imitative stone intermediate layer paint, plate post-processing；
The plate pretreatment includes carrying out washed ore light to plate using contact calibrating machine, and to washed ore light including fixed thick sanding
Treated plate is purged processing by dust of the dust removing machine to its surface；
The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies closing, infiltration priming paint, colorful intermediate layer paint or imitative stone
Intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；
Plate post-processing successively includes overlay film, compound and cut.
Further, the colorful intermediate layer paint of the coating or imitative stone intermediate layer paint specific steps are as follows:
1) back applies closing, carries out UV seal coat to pretreated plate, UV curing time is 5 seconds；
2) priming paint is permeated, epoxy infiltration paint coating is carried out to above-mentioned plate using double roller roll coater, paint temperature is 50 when coating
DEG C, and natural drying 24 hours solidify；
3) colorful intermediate layer paint or imitative stone intermediate layer paint, using roll coater above and below double roller to above-mentioned plate carry out the colorful intermediate layer paint of roller coating or
Imitative stone intermediate layer paint, 80 DEG C of temperature, baking time is 10 minutes；
4) colorful lacquer or imitation stone lacquer carries out roller coating colorful lacquer or imitation stone lacquer to above-mentioned plate using roll coater, 40 DEG C of temperature, natural
Sunning 24 hours；
5) finishing varnish, using roll coater above and below double roller to above-mentioned plate carry out roller coating finishing varnish, 80 DEG C of temperature, baking time 3
Hour.
Further, the plate post-processes specific steps are as follows:
1) overlay film carries out coating processing to above-mentioned finishing varnish treated plate, becomes multicolored ornamental veneer or imitative stone dress
Adorn veneer；
2) compound, above-mentioned multicolored ornamental veneer or imitative stone fancy veneer are subjected to pressing company with corresponding thermal insulation material by glue
It connects, the pressing time is 5 hours, pressure 0.5mpa to press machine at normal temperature, becomes colorful insulation decoration composite plate or imitative
Stone heat-insulating decorative composite board；
3) it cuts, above-mentioned colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board is cut according to customer demand,
Sizing plate is become, to meet the actual needs.
Further, glue is polyurethane glue in the step 2.
Further, the plate is calcium silicate board.
In the present embodiment, other are the same as example 1.
Embodiment three:
A kind of production method of colorful, imitative stone heat insulating decorative board, the production method of colorful, the imitative stone heat insulating decorative board are successively wrapped
The pretreatment of rubbing board material, the colorful intermediate layer paint of coating or imitative stone intermediate layer paint, plate post-processing；
The plate pretreatment includes carrying out washed ore light to plate using contact calibrating machine, and to washed ore light including fixed thick sanding
Treated plate is purged processing by dust of the dust removing machine to its surface；
The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies closing, infiltration priming paint, colorful intermediate layer paint or imitative stone
Intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；
Plate post-processing successively includes overlay film, compound and cut.
Wherein, the colorful intermediate layer paint of the coating or imitative stone intermediate layer paint specific steps are as follows:
1) back applies closing, carries out UV seal coat to pretreated plate, UV curing time is 4 seconds；
2) priming paint is permeated, epoxy infiltration paint coating is carried out to above-mentioned plate using roll coater above and below double roller, paint temperature when coating
At 40 DEG C, and natural drying 24 hours solidify；
3) colorful intermediate layer paint or imitative stone intermediate layer paint carry out the colorful intermediate layer paint of roller coating or imitative stone to above-mentioned plate using double roller roll coater
Intermediate layer paint, 75 DEG C of temperature, baking time is 9 minutes；
4) colorful lacquer or imitation stone lacquer carries out roller coating colorful lacquer or imitation stone lacquer to above-mentioned plate using roll coater, 35 DEG C of temperature, natural
Sunning 24 hours；
5) finishing varnish carries out roller coating finishing varnish to above-mentioned plate using double roller roll coater, and 75 DEG C of temperature, baking time is 2.5 small
When.
Wherein, the plate post-processes specific steps are as follows:
1) overlay film carries out coating processing to above-mentioned finishing varnish treated plate, becomes multicolored ornamental veneer or imitative stone dress
Adorn veneer；
2) compound, above-mentioned multicolored ornamental veneer or imitative stone fancy veneer are subjected to pressing company with corresponding thermal insulation material by glue
Connect, press machine at normal temperature the pressing time be 4 hours, pressure 0.45mpa, become colorful insulation decoration composite plate or
Imitative stone heat-insulating decorative composite board；
3) it cuts, above-mentioned colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board is cut according to customer demand,
Sizing plate is become, to meet the actual needs.
Wherein, glue is polyurethane glue in the step 2.
Wherein, the plate is calcium silicate board.
In the present embodiment, other are the same as example 1.
Meanwhile using colorful insulation decoration composite plate made of the present invention or imitative stone heat-insulating decorative composite board, in construction
It is simple and convenient using " five step constructions ": " one, wall basal plane processing ", " two, cellular snap line ", " three, installation supporting part ",
" four, mounting finished product plate ", " five, plate stitch filling sealing "；The mounting means of " stickup+anchoring combination ", greatly enhances safety
Reliability；Construction period is only the 40-60% of stone material or metal curtain wall, greatly reduces construction cost.In addition, it is necessary to explanation
It is that the specific structure and application method and the prior art of the anchoring piece in the above-mentioned anchoring combination being related to are without essential distinction, therefore,
In the present embodiment, the specific structure of the anchoring piece in anchoring combination no longer discloses.
In addition, being demonstrate,proved using colorful insulation decoration composite plate made of the present invention or imitative stone heat-insulating decorative composite board through practice
It is bright, following technical performance index can be reached:
Claims (5)
1. a kind of production method of colorful, imitative stone heat insulating decorative board, it is characterised in that: colorful, the imitative stone heat insulating decorative board
Production method successively includes plate pretreatment, the colorful intermediate layer paint of coating or imitative stone intermediate layer paint, plate post-processing；The plate is located in advance
Reason includes fixed thick sanding, carries out washed ore light to plate using contact calibrating machine, and pass through dust to the plate after washed ore light processing
Removing machine is purged processing to the dust on its surface；The colorful intermediate layer paint of coating or imitative stone intermediate layer paint successively include that back applies envelope
It closes, permeate priming paint, colorful intermediate layer paint or imitative stone intermediate layer paint, colorful lacquer or imitation stone lacquer, finishing varnish；The plate post-processing is successively wrapped
Include overlay film, compound and cut.
2. the production method of colorful, the imitative stone heat insulating decorative board of one kind according to claim 1, it is characterised in that: the painting
Fill colorful intermediate layer paint or imitative stone intermediate layer paint specific steps are as follows:
1) back applies closing, carries out UV seal coat to pretreated plate, UV curing time is 3-5 seconds；
2) priming paint is permeated, epoxy infiltration paint coating is carried out to above-mentioned plate using double roller roll coater, paint temperature exists when coating
30~50 DEG C, and natural drying 24 hours solidify；
3) colorful intermediate layer paint or imitative stone intermediate layer paint, using roll coater above and below double roller to above-mentioned plate carry out the colorful intermediate layer paint of roller coating or
Imitative stone intermediate layer paint, 70~80 DEG C of temperature, baking time is 8-10 minutes.
4) colorful lacquer or imitation stone lacquer, using double roller roller coating to above-mentioned plate carry out roller coating colorful lacquer or imitation stone lacquer, temperature 30~
40 DEG C, baking time is 6-8 seconds, natural drying 24 hours；
5) finishing varnish, using double roller roll coater to above-mentioned plate carry out roller coating finishing varnish, 70~80 DEG C of temperature, baking time 2
~3 hours.
3. the production method of colorful, the imitative stone heat insulating decorative board of one kind according to claim 2, it is characterised in that: the plate
Material post-processes specific steps are as follows:
1) overlay film carries out coating processing to above-mentioned finishing varnish treated plate, becomes multicolored ornamental veneer or imitative stone dress
Adorn veneer；
2) compound, above-mentioned multicolored ornamental veneer or imitative stone fancy veneer are subjected to pressing company with corresponding thermal insulation material by glue
It connects, the pressing time is 3-5 hours, pressure 0.35-0.5mpa to press machine at normal temperature, and it is multiple to become colorful insulation decoration
Plywood or imitative stone heat-insulating decorative composite board；
3) it cuts, above-mentioned colorful insulation decoration composite plate or imitative stone heat-insulating decorative composite board is cut according to customer demand,
Sizing plate is become, to meet the actual needs.
4. the production method of colorful, the imitative stone heat insulating decorative board of one kind according to claim 3, it is characterised in that: the step
Glue is polyurethane glue in rapid 2.
5. the production method of colorful, the imitative stone heat insulating decorative board of one kind according to claim 3, it is characterised in that: the plate
Material is calcium silicate board.