CN109403010A - Terylene four sides elasticity cloth dyeing technique - Google Patents
Terylene four sides elasticity cloth dyeing technique Download PDFInfo
- Publication number
- CN109403010A CN109403010A CN201811064138.2A CN201811064138A CN109403010A CN 109403010 A CN109403010 A CN 109403010A CN 201811064138 A CN201811064138 A CN 201811064138A CN 109403010 A CN109403010 A CN 109403010A
- Authority
- CN
- China
- Prior art keywords
- terylene
- elasticity cloth
- sides elasticity
- dyeing
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses terylene four sides elasticity cloth dyeing technique, the terylene four sides elasticity cloth after dyeing can be obtained in pre-treatment, pre-setting, dyeing, dehydration, drying, open-width and sizing.The present invention under conditions of short liquor ratio, is dyed using disperse dyes by two stage heat preservations, then is cleaned by slowly cooling discharge sewage and with clear water.Terylene four sides elasticity cloth is dyed in the invention, has dyestuff dye-uptake height, good color fastness, it is possible to reduce the characteristics of folding line shortens working hour, energy saving, reduces cost.
Description
Technical field
The present invention relates to the whole dyeing technique fields of fabric, in particular to terylene four sides elasticity cloth dyeing technique.
Background technique
The main component of terylene four sides elasticity fabric is exactly terylene and spandex, and terylene spandex fabric is one in synthetic fibers
Important species, it is material through esterification or transesterification and contracting that it, which is using p-phthalic acid or dimethyl terephthalate (DMT) and ethylene glycol,
Fiber-forming polymer --- polyethylene terephthalate prepared by poly- reaction through spinning and post-processes manufactured fiber.It washs
The characteristics of synthetic fibre four-side elasticity fabric: intensity is high, elasticity is good, heat-resist, terylene appearance lubricates, wearability is good.Wearability is only second to
The optimal polyamide fibre of wearability, it is all better than other natural fibers and synthetic fibers, light resistance is good, corrosion-resistant, market development potential compared with
Greatly.
Due to the design feature of terylene, disperse dyes are easy upper dye spandex, while being also easy parsing, so color jail can be reduced
Degree.Solubility to dispersion of the disperse dyes in certain bath raio is limited, with the increase of disperse dyes, under the dye-uptake of disperse dyes
Drop, the utilization rates of disperse dyes reduce, how to improve the utilization rate of dyestuff, the fastness of dyeing, stability, reproducibility, reduction at
This, becomes dyeing industry and primarily solves the problems, such as.
Summary of the invention
It is high in view of the deficiencies of the prior art, the present invention intends to provide a kind of utilization rate of dyestuff, in dyeing
Dye rate is high, the terylene four sides elasticity cloth dyeing technique of good color fastness.
Above-mentioned technical purpose of the invention has the technical scheme that terylene four sides elasticity cloth dyeing work
Skill, comprising the following steps:
Terylene four sides elasticity cloth is put into the clear water of desizing rinsing machine by a) pre-treatment, in a water bath plus soda ash 7-12g/L, double
Oxygen water 4-8g/L, desizing agent 1.4-2g/L handle 10-15min in 45 DEG C of water-baths, and waste water discharge, injected clear water is at room temperature
Rinse 10 min;
Terylene four sides elasticity is arranged in pre-setting machine by b) pre-setting, and pre-setting temperature is 180-210 DEG C, speed 17-25m/
min;
C) it dyes, at room temperature, the terylene four sides elasticity cloth after pre-setting is put into the clear water of high temperature and pressure overflow dyeing machine,
High temperature levelling agent 1-1.5g/L, bleeding agent 1.5-2.5g/L are added in a water bath, glacial acetic acid is added by pH value and is adjusted to 4-6.5
When, then high temperature and pressure overflow dyeing machine heats up, and heating rate is 2 DEG C/min, and when temperature rises to 80-90 DEG C, dispersion dye is added
Expect 1.5-2% owf, heat preservation dyeing 20-30min, then high temperature and pressure overflow dyeing machine continues to heat up, heating rate be 2 DEG C/
Min when temperature rises to 120-130 DEG C, stops heating, and heat preservation dyeing 30-50min, then high temperature and pressure overflow dyeing machine cools down,
Cooling rate is 2.5 DEG C/min, when temperature is down to 40-60 DEG C, sewage is discharged, injected clear water carries out 5~10min of cleaning;
D dehydration, by the terylene four sides elasticity cloth dewaterer dehydration after dyeing;
E) open-width carries out open-width through scutcher to dewatered fabric;
F) it dries, the terylene four sides elasticity cloth drying machine after open-width is subjected to drying and processing, drying temperature is 80-130 °C;
G) it is formed, using needle plate type forming machine, controlled at 120-130 °C, rate 35-50m/min;The processing time is 100-
120s。
Above-mentioned terylene four sides elasticity cloth dyeing technique, wherein the bath raio of desizing rinsing machine is 1:15 in the step a.
Above-mentioned terylene four sides elasticity cloth dyeing technique, wherein the bath raio of step c high temperature high pressure kicks overflow dyeing machine is 1:
6。
Above-mentioned terylene four sides elasticity cloth dyeing technique, wherein the high temperature levelling agent in the step c is styrene phenol
Polyoxyethylene ether ammonium sulfate salt.
Above-mentioned terylene four sides elasticity cloth dyeing technique, wherein the bleeding agent in the step c is penetrating agent JFC.
In conclusion the invention has the following advantages: the even dyeing of terylene four sides elasticity cloth, stabilization, fabric are soft
It is soft, color fastness is high.
For the present invention under conditions of short liquor ratio, the dye-uptake of dyestuff is high, it is possible to reduce and folding line shortens working hour, energy saving,
Reduce cost.
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
Below in conjunction with attached drawing, invention is further described in detail.The wherein identical appended drawing reference of identical components
It indicates.It should be noted that word "front", "rear" used in the following description, "left", "right", "up" and "down" refer to it is attached
Direction in figure, word " bottom surface " and " top surface ", "inner" and "outside" are referred respectively to towards or away from geometric center of specific component
Direction.
Embodiment one:
Terylene four sides elasticity cloth dyeing technique, comprising the following steps:
Terylene four sides elasticity cloth is put into the clear water of desizing rinsing machine by a) pre-treatment, in a water bath plus soda ash 7g/L, hydrogen peroxide
4g/L, desizing agent 1.4g/L, bath raio 1:15 handle 10min in 45 DEG C of water-baths, and waste water discharge, injected clear water is at room temperature
Rinse 10 min;
Terylene four sides elasticity is arranged in pre-setting machine by b) pre-setting, and pre-setting temperature is 180 DEG C, speed 17m/min;
C) it dyes, at room temperature, the terylene four sides elasticity cloth after pre-setting is put into the clear water of high temperature and pressure overflow dyeing machine,
High temperature levelling agent styrene phenol polyoxyethylene ether ammonium sulfate salt 1g/L, penetrating agent JFC 1.5g/L are added in a water bath, ice is added
When pH value is adjusted to 4 by acetic acid, bath raio 1:6, then high temperature and pressure overflow dyeing machine heats up, and heating rate is 2 DEG C/min, temperature
When degree rises to 80 DEG C, 1.5% owf of disperse dyes is added, heat preservation dyeing 20min, then high temperature and pressure overflow dyeing machine is after of continuing rising
Temperature, heating rate is 2 DEG C/min, when temperature rises to 120 DEG C, stops heating, heat preservation dyeing 30min, then high temperature and pressure overflow
Overflow dyeing machine cooling, cooling rate be 2.5 DEG C/min, when temperature is down to 40 DEG C, be discharged sewage, injected clear water, carry out cleaning 5~
10min;
D) it is dehydrated, by the terylene four sides elasticity cloth dewaterer dehydration after dyeing;
E) open-width carries out open-width through scutcher to dewatered fabric;
F) it dries, the terylene four sides elasticity cloth drying machine after open-width is subjected to drying and processing, drying temperature is 80 °C;
G) it is formed, using needle plate type forming machine, controlled at 120 °C, rate 35m/min;The processing time is 100s.
Embodiment two:
Terylene four sides elasticity cloth dyeing technique, comprising the following steps:
Terylene four sides elasticity cloth is put into the clear water of desizing rinsing machine by a) pre-treatment, in a water bath plus soda ash 10g/L, dioxygen
Water 6g/L, desizing agent 1.7g/L, bath raio 1:15 handle 10min in 45 DEG C of water-baths, and waste water discharge, injected clear water is in room temperature
10 min of lower flushing;
Terylene four sides elasticity is arranged in pre-setting machine by b) pre-setting, and pre-setting temperature is 200 DEG C, speed 21m/min;
C) it dyes, at room temperature, the terylene four sides elasticity cloth after pre-setting is put into the clear water of high temperature and pressure overflow dyeing machine,
High temperature levelling agent styrene phenol polyoxyethylene ether ammonium sulfate salt 1.3g/L, penetrating agent JFC 2g/L are added in a water bath, ice is added
When pH value is adjusted to 5 by acetic acid, bath raio 1:6, then high temperature and pressure overflow dyeing machine heats up, and heating rate is 2 DEG C/min, temperature
When degree rises to 85 DEG C, 1.8% owf of disperse dyes is added, heat preservation dyeing 25min, then high temperature and pressure overflow dyeing machine is after of continuing rising
Temperature, heating rate is 2 DEG C/min, when temperature rises to 125 DEG C, stops heating, heat preservation dyeing 40min, then high temperature and pressure overflow
Overflow dyeing machine cooling, cooling rate be 2.5 DEG C/min, when temperature is down to 50 DEG C, be discharged sewage, injected clear water, carry out cleaning 5~
10min;
D) it is dehydrated, by the terylene four sides elasticity cloth dewaterer dehydration after dyeing;
E) open-width carries out open-width through scutcher to dewatered fabric;
F) it dries, the terylene four sides elasticity cloth drying machine after open-width is subjected to drying and processing, drying temperature is 100 °C;
G) it is formed, using needle plate type forming machine, controlled at 125 °C, rate 40m/min;The processing time is 110s.
Embodiment three:
Terylene four sides elasticity cloth dyeing technique, comprising the following steps:
Terylene four sides elasticity cloth is put into the clear water of desizing rinsing machine by a) pre-treatment, in a water bath plus soda ash 12g/L, dioxygen
Water 8g/L, desizing agent 2g/L, bath raio 1:15 handle 15min in 45 DEG C of water-baths, and waste water discharge, injected clear water is at room temperature
Rinse 10 min;
Terylene four sides elasticity is arranged in pre-setting machine by b) pre-setting, and pre-setting temperature is 210 DEG C, speed 25m/min;
C) it dyes, at room temperature, the terylene four sides elasticity cloth after pre-setting is put into the clear water of high temperature and pressure overflow dyeing machine,
High temperature levelling agent styrene phenol polyoxyethylene ether ammonium sulfate salt 1.5g/L, penetrating agent JFC 2.5g/L are added in a water bath, is added
When pH value is adjusted to 6.5 by glacial acetic acid, bath raio 1:6, then high temperature and pressure overflow dyeing machine heat up, heating rate be 2 DEG C/
Min, when temperature rises to 90 DEG C, be added 2% owf of disperse dyes, heat preservation dyeing 30min, then high temperature and pressure overflow dyeing machine after
Temperature of continuing rising, heating rate is 2 DEG C/min, when temperature rises to 130 DEG C, stops heating, 50min is dyed in heat preservation, then high temperature and pressure
Overflow dyeing machine cooling, cooling rate is 2.5 DEG C/min, when temperature is down to 60 DEG C, sewage is discharged, injected clear water carries out clear
Wash 5~10min;
D) it is dehydrated, by the terylene four sides elasticity cloth dewaterer dehydration after dyeing;
E) open-width carries out open-width through scutcher to dewatered fabric;
F) it dries, the terylene four sides elasticity cloth drying machine after open-width is subjected to drying and processing, drying temperature is 130 °C;
G) it is formed, using needle plate type forming machine, controlled at 130 °C, rate 50m/min;The processing time is 120s.
Invention under conditions of short liquor ratio, is dyed, then by slow using disperse dyes by two stage heat preservations
Cooling discharge sewage and clean with clear water terylene four sides elasticity cloth is dyed, there is dyestuff dye-uptake height, good color fastness,
Folding line can be reduced, working hour is shortened, it is energy saving, reduce the effect of cost.
This specific embodiment is only explanation of the invention, is not limitation of the present invention, those skilled in the art
Member can according to need the modification that not creative contribution is made to the present embodiment after reading this specification, but as long as at this
All by the protection of Patent Law in the scope of the claims of invention.
Claims (5)
1. a kind of terylene four sides elasticity cloth dyeing technique, which comprises the following steps:
Terylene four sides elasticity cloth is put into the clear water of desizing rinsing machine by a) pre-treatment, in a water bath plus soda ash 7-12g/L, double
Oxygen water 4-8g/L, desizing agent 1.4-2g/L handle 10-15min in 45 DEG C of water-baths, and waste water discharge, injected clear water is at room temperature
Rinse 10 min;
Terylene four sides elasticity is arranged in pre-setting machine by b) pre-setting, and pre-setting temperature is 180-210 DEG C, speed 17-25m/
min;
C) it dyes, at room temperature, the terylene four sides elasticity cloth after pre-setting is put into the clear water of high temperature and pressure overflow dyeing machine,
High temperature levelling agent 1-1.5g/L, bleeding agent 1.5-2.5g/L are added in a water bath, glacial acetic acid is added by pH value and is adjusted to 4-6.5
When, then high temperature and pressure overflow dyeing machine heats up, and heating rate is 2 DEG C/min, and when temperature rises to 80-90 DEG C, dispersion dye is added
Expect 1.5-2% owf, heat preservation dyeing 20-30min, then high temperature and pressure overflow dyeing machine continues to heat up, heating rate be 2 DEG C/
Min when temperature rises to 120-130 DEG C, stops heating, and heat preservation dyeing 30-50min, then high temperature and pressure overflow dyeing machine cools down,
Cooling rate is 2.5 DEG C/min, when temperature is down to 40-60 DEG C, sewage is discharged, injected clear water carries out 5~10min of cleaning;
D) it is dehydrated, by the terylene four sides elasticity cloth dewaterer dehydration after dyeing;
E) open-width carries out open-width through scutcher to dewatered fabric;
F) it dries, the terylene four sides elasticity cloth drying machine after open-width is subjected to drying and processing, drying temperature is 80-130 DEG C;
G) it is formed, using needle plate type forming machine, controlled at 120-130 DEG C, rate 35-50m/min;The processing time is 100-
120s。
2. terylene four sides elasticity cloth dyeing technique as described in claim 1, which is characterized in that desizing is washed in the step a
The bath raio of machine is 1:15.
3. terylene four sides elasticity cloth dyeing technique as described in claim 1, which is characterized in that step c high temperature high pressure kicks
The bath raio of overflow dyeing machine is 1:6.
4. terylene four sides elasticity cloth dyeing technique as described in claim 1, which is characterized in that the high temperature in the step c is even
Stain is styrene phenol polyoxyethylene ether ammonium sulfate salt.
5. terylene four sides elasticity cloth dyeing technique as described in claim 1, which is characterized in that the bleeding agent in the step c
For penetrating agent JFC.