CN109402836A - A kind of production method of the warming environment-protection fiber ultra-deep orchid denim of moisture absorbing and sweat releasing - Google Patents
A kind of production method of the warming environment-protection fiber ultra-deep orchid denim of moisture absorbing and sweat releasing Download PDFInfo
- Publication number
- CN109402836A CN109402836A CN201811387116.XA CN201811387116A CN109402836A CN 109402836 A CN109402836 A CN 109402836A CN 201811387116 A CN201811387116 A CN 201811387116A CN 109402836 A CN109402836 A CN 109402836A
- Authority
- CN
- China
- Prior art keywords
- fiber
- denim
- speed
- orchid
- moisture absorbing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production methods of the warming environment-protection fiber ultra-deep orchid denim of moisture absorbing and sweat releasing, the method use three kinds of Sorbtek365 fiber, cotton fiber, spandex fibers, it is matched by preferred raw material, improve blowing, cotton carding, rear spinning, dyeing, weaving step, it develops and keeps warm environment-protection fiber ultra-deep orchid denim with moisture absorbing and sweat releasing, the denim of this method production has that environmentally friendly concept, lines is clear, color is beautiful, good color fastness, soft, inherent physical index are stablized.It is tested through SGS inspection center, meets the center to moisture absorbing and sweat releasing and warming standard requirements, achieve good effect.
Description
Technical field
The present invention relates to a kind of production methods of denim, belong to field of textiles, in particular to a kind of moisture absorbing and sweat releasing is warming
The production method of environment-protection fiber ultra-deep orchid denim.
Background technique
As quality of life is continuously improved, consumer has the variation of matter to the functional requirement of garment material.Now, people
No longer using the durability of clothes as first choice, but using function, environmental protection and comfort as primary reference point.For
Cater to this demand of the majority of consumers at heart, denim manufacturing enterprise develops multiple performance difference, color, style one after another
The functional fabric of multiplicity.Variation due to choosing fiber content different, rear whole techniques when production fabric often arranges moisture absorption
The performances such as sweat, warming have larger impact, meanwhile, the problems such as flatness of cloth cover, color fastness, has also seriously perplexed manufacturing enterprise.
Summary of the invention
To solve the above problem, the present invention provides a kind of lifes of the warming environment-protection fiber ultra-deep orchid denim of moisture absorbing and sweat releasing
Production method uses new type functional environment-protection fiber -- Sorbtek365, preferred face liber content proportion, improvement is taken to dye,
The measures such as postfinishing process develop the warming environment-protection fiber ultra-deep orchid denim of moisture absorbing and sweat releasing.Fabric has environmentally friendly concept, line
Road is clear, color is beautiful, good color fastness, soft, inherent physical index is stable.It tests, meets through SGS inspection center
The center achieves good effect to moisture absorbing and sweat releasing and warming standard requirements.
The present invention is achieved by the following technical solutions:
A kind of production method of the warming environment-protection fiber ultra-deep orchid denim of moisture absorbing and sweat releasing, step includes choosing raw material, blowing
Step, spins step, staining procedure, weaving step at cotton carding step afterwards, the specific steps are as follows:
(1) prepare raw material: it is fine to weigh Sorbtek365 fiber, cotton fiber, spandex respectively according to following mass percent
Dimension: Sorbtek365 fiber 18~30%, cotton fiber 70~80%, spandex fibre 1.5~2.5%；
(2) in blowing step, griping cotton machine hired roughneck stretch out rib distance be -2~+1mm, opener hired roughneck's revolving speed be 420~
450r/min, the comprehensive hired roughneck's revolving speed of single beater scutcher are 820~850r/min, and lap roller revolving speed is 10~13r/min；
(3) in cotton carding step, breast swift revolving speed is 320~360r/min, and licker-in revolving speed is 840~880r/min,
Doffing speed is 14~17r/min, and cover plate speed is 125~137mm/min；
(4) it spins in step afterwards, roving twist factor is 93~99, and spinning frame ingot speed is 9200~10000r/min, and back zone is led
Stretching multiple is 1.2~1.4；
(5) in staining procedure, liquid indigo content in bottom is 1.15~1.35g/L, and indigo bottom liquid alkaline content is 3.4~3.6 g/
L, Sodium Hydrosulfite Content are 1.98~2.09g/L, and indigo dye-uptake is 7~7.5%, and speed is 16~20m/min, staining bath padding machine
Pressure is 5~5.5kg, and kiering alkali content is 4~6g/L (90 DEG C), and citric acid content is 5~7g/L (60 DEG C), and descaling bath seeps
Saturating agent content is 3.5~6g/l, and soft agent content is 45~55g/L (60 DEG C)；
(6) in weaving step, opening time is 310~320 degree, and back beam height is 100~110mm, and the time of throwing a spear is 55
~65 degree, warp tension is 2.5~3.0N, and workshop relative humidity is 60~70%；
(7) in final finishing step, 35~45m/min of speed, anti-shrinkage 12%~14%, preshrinking rate -3~+3%, heating
80 DEG C~85 DEG C, setting time 40~20s, first group of cylinder 0.22~0.26MPa of steam pressure, rubber blanket cylinder vapour pressure
0.18~0.22MPa of power, 0.42~0.44MPa of blanket cylinder steam pressure；
Preferably, in step (1), Sorbtek365 fiber, cotton fiber, spandex fibre weigh percentage are as follows:
Sorbtek365 fiber 24%, cotton fiber 74%, spandex fibre 2%；
Preferably, in step (2), it is -1mm that griping cotton machine hired roughneck, which stretches out rib distance, and opener hired roughneck's revolving speed is 430r/
Min, the comprehensive hired roughneck's revolving speed of single beater scutcher are 830r/min, and lap roller revolving speed is 11r/min；
Preferably, in step (3), cylinder revolving speed is 330r/min, and licker-in revolving speed is 850r/min, and doffing speed is
15r/min, cover plate speed 129mm/min；
Preferably, in step (4), roving twist factor 97, ingot speed 9500r/min, back zone drafting multiple 1.25；
Preferably, in step (5), speed 18m/min, the indigo content of bottom liquid is 1.2g/l, and indigo bottom liquid alkaline content is
3.5g/l, Sodium Hydrosulfite Content 2.01g/l, indigo dye-uptake are 7.2%, and staining bath padding machine pressure is 5.2kg, kiering alkali content
For 5g/l (90 DEG C), citric acid content is 6g/l (60 DEG C), and it is 5g/l that descaling bath, which permeates agent content, and soft agent content is 50g/l
(60℃)；
Preferably, in step (6), opening time is 315 degree, back beam height 100mm；Throw a spear the time be 60 degree, upper machine
Tension is 2.9N, and workshop relative humidity is 69%；
Preferably, in step (7), speed 40m/min, anti-shrinkage is 13%, and preshrinking rate≤- 3% heats 82 DEG C, is determined
The type time is 30s, and first group of cylinder steam pressure is 0.24MPa, and rubber blanket cylinder steam pressure is 0.21MPa, blanket cylinder
Steam pressure is 0.43Mpa.
The present invention has used following three kinds of fibers when producing the denim fabric:
1) Sorbtek365 fiber is the novel function of high added value produced by Suzhou You Fu Fabritex S.r.l (UTSC)
Energy property environment-protection fiber, the special construction with odd-shaped cross section combination hollow gasbag.Sorbtek365 fiber surface forms groove,
Skin surface moisture and sweat are absorbed rapidly, and moment excretes, then sweat is spread by the fiber of cloth table and evaporated rapidly
Release, to achieve the purpose that moisture absorbing and sweat releasing, adjust body temperature, this is the permanent moisture absorption sweat discharging functions that fiber itself has.Together
When, in doughnut structure, and include a large amount of still air, there is preferable heat-preserving function, is brought for fabric refrigerant, dry
Refreshing, soft, warming, easy the features such as arranging；
2) cotton fiber (Cotton) is a natural fiber, and has soft, ventilative, good hygroscopicity, spy comfortable and easy to wear
Point；
3) spandex (Spandex) is a kind of elastomer, and scientific name polyurethane fiber, China's Mainland is known as " spandex ".Elasticity
It is excellent, 6~7 times can be elongated, but original state can be promptly restored to the disappearance of tension, and more resistant to chemical degradation.Spandex
Resistance to acid and alkali, sweat proof, dry cleaning resistance, wearability it is preferable.
It is had the following characteristics that complete each process parameter of Sorbtek365 environment-protection fiber ultra-deep orchid denim
1) three kinds of fiber blends such as Sorbtek365, cotton, spandex have been used to be interwoven in fabric, science chooses each group
Point fiber shared weight percent in fabric meets SGS inspection center to moisture absorbing and sweat releasing and warming with lower cost
It is required that reaching design effect；
2) in cotton cleaning process, the characteristics of according to fiber, take " fine crawl, it is caducous it is few it is broken, beaten with comb generation, few wound fibre
The technological principle of dimension ".Griping cotton machine is frequently grabbed every time, is grabbed less, acts on inspiration raw material by wind-force, in favor of being uniformly mixed；It reduces each
Beater Speed, to reduce fibre damage；
3) principle of " sufficiently combing, reinforcement transfer " in carding step, is grasped.Reinforce carding efficacy, down control sliver knot
It is miscellaneous, improve the carded sliver uniformity；
4) it spins in process afterwards, takes and properly increase roving twist, increase reeling roving density, it is smooth, fluffy to make up fiber
Defect caused by pine.The relatively low grasp of spinning process speed, back zone drafting multiple suitably put small, reduction hair dry to reach improvement item
The purpose of plumage；
5) in dyeing process, to improve dye-uptake and dyeing color fastness, using the dyeing of " low dense, low speed, multiple-grooved "
Principle.Staining bath padding machine pressure is adjusted simultaneously, to ensure that yarn thoroughly permeates, the oxidation-reduction process of dyeing is abundant, preferably solves
Dye stability is bad and the problem of dyefastness difference；
6) in weaving process, to ensure that cloth machine is weaved with low consumption, efficient optimum state, beam of a loom is adopted after placing for 24 hours
With the knitting technology principle of " early opening, the low back rest, middle tension ", cloth cover is smooth, and lines is clear, wefting insertion is smooth, substantially without disconnected
Head, weaving efficiency are high；
7) in postfinishing process, according to the characteristic of 365 fiber of sorbtek in fabric, take fabric appropriate before entering machine
Dewing (10%-15%) and heating, drying cylinder are dried, and so that fiber is become softer and is had biggish plasticity, to add
Strong preshrunk control and raising preshrunk effect.The selection of heating temperature is that we pass through the data that test of many times obtains, both guaranteed
When not damaging fibre property, and can make fabric through rubber blanket pre-shrinking, first effective preliminary drying removes partial moisture, passes through again after machine out
Tension-free felt rug drying machine is dried and is plated, smooth to obtain because shrinking the wrinkle excessively generated when eliminating compression
Cloth cover and excellent elasticity.
Compared with prior art, the beneficial effects of the present invention are:
Moisture absorbing and sweat releasing keeps warm environment-protection fiber ultra-deep orchid denim, is that new type functional environment-protection fiber is passed through new process, new
Technology is dissolved among denim fabric, makes that product is fine quality, comfortable feel is soft, color is beautiful, has environmentally friendly concept, deep
Liked, economic benefits, while also having pulled the development of cowboy's cotton ready made clothings and its relevant industries have good by customers
Good social benefit.
Specific embodiment
Here is that the present invention is further described in conjunction with the embodiments.
Embodiment 1
A kind of moisture absorbing and sweat releasing keeps warm the production method of environment-protection fiber ultra-deep orchid denim, and step includes choosing raw material, clear
Flower, cotton carding, rear spinning, dyeing, weaving, the specific steps are as follows:
(1) prepare raw material: it is fine to weigh Sorbtek365 fiber, cotton fiber, spandex respectively according to following mass percent
Dimension: Sorbtek365 fiber 16%, cotton fiber 82%, spandex fibre 2.0%；
(2) in blowing step, it is -1mm that griping cotton machine hired roughneck, which stretches out rib distance, and opener hired roughneck's revolving speed is 430r/min,
The comprehensive hired roughneck's revolving speed of single beater scutcher is 830r/min, and lap roller revolving speed is 11r/min；
(3) in cotton carding step, breast swift revolving speed is 330r/min, and licker-in revolving speed is 850r/min, and doffing speed is
15r/min, cover plate speed 129mm/min；
(4) it spins in step afterwards, roving twist factor 97, spinning frame ingot speed is 9500r/min, and back zone drafting multiple is
1.25；
(5) in staining procedure, speed 18m/min, the indigo content of bottom liquid is 1.2g/L, and indigo bottom liquid alkaline content is 3.5g/
L, Sodium Hydrosulfite Content 2.01g/L, indigo dye-uptake are 7.2%, and staining bath padding machine pressure is 5.2kg, and kiering alkali content is 5g/L
(90 DEG C), citric acid content are 6g/L (60 DEG C), and it is 5g/l that descaling bath, which permeates agent content, and soft agent content is 50g/L (60
℃)；
(6) in weaving step, opening time is 315 degree, back beam height 100mm, and humidity of throwing a spear is 60 degree, upper machine
Power is 2.9N, and workshop relative humidity is 69%；
(7) in final finishing step, speed 40m/min, anti-shrinkage 13%, preshrinking rate -3~+3%, 82 DEG C of heating, sizing
Time 30s, first group of cylinder steam pressure 0.24MPa, rubber blanket cylinder steam pressure 0.21MPa, blanket cylinder steam pressure
0.43Mpa。
Implementation result: fabric has reached general effect.Development cost is although lower, tests through SGS inspection center,
Moisture absorbing and sweat releasing and warming the test center is not achieved to the standard requirements of fabric.
Embodiment 2
A kind of moisture absorbing and sweat releasing keeps warm the production method of environment-protection fiber ultra-deep orchid denim, and step includes choosing raw material, clear
Flower, cotton carding, rear spinning, dyeing, weaving, the specific steps are as follows:
(1) prepare raw material: it is fine to weigh Sorbtek365 fiber, cotton fiber, spandex respectively according to following mass percent
Dimension: Sorbtek365 fiber 24%, cotton fiber 74%, spandex fibre 2.0%；
(2) in blowing step, it is -1mm that griping cotton machine hired roughneck, which stretches out rib distance, and opener hired roughneck's revolving speed is 430r/min,
The comprehensive hired roughneck's revolving speed of single beater scutcher is 890r/min, and lap roller revolving speed is 11r/min；
(3) in cotton carding step, breast swift revolving speed is 330r/min, and licker-in revolving speed is 850r/min, and doffing speed is
15r/min, cover plate speed 129mm/min；
(4) it spins in step afterwards, roving twist factor 97, spinning frame ingot speed is 9500r/min, and back zone drafting multiple is
1.25；
(5) in staining procedure, speed 15m/min, the indigo content of bottom liquid is 1.6g/L, and indigo bottom liquid alkaline content is 3.5g/
L, Sodium Hydrosulfite Content 2.01g/L, indigo dye-uptake are 7.8%, and staining bath padding machine pressure is 5.2kg, and kiering alkali content is 5g/L
(90 DEG C), citric acid content are 6g/L (60 DEG C), and it is 5g/l that descaling bath, which permeates agent content, and soft agent content is 50g/L (60
℃)；
(6) in weaving step, opening time is 315 degree, back beam height 100mm, and the time of throwing a spear is 60 degree, upper machine
Power is 2.9N, and workshop relative humidity is 67-70%；
(7) in final finishing step, speed 35m/min, anti-shrinkage 13%, preshrinking rate -3~+3%, 95 DEG C of heating, sizing
Time 40s, first group of cylinder steam pressure 0.24MPa, rubber blanket cylinder steam pressure 0.21MPa, blanket cylinder steam pressure
0.43MPa。
Implementation result: general effect has been reached.Fabric poor color fastness leads to fiber since final finishing heating temperature is excessively high
Functional, tested through SGS inspection center, moisture absorbing and sweat releasing and warming the test center be not achieved the standard of fabric is wanted
It asks.
Embodiment 3 (optimised process embodiment)
A kind of moisture absorbing and sweat releasing keeps warm the production method of environment-protection fiber ultra-deep orchid denim, and step includes choosing raw material, clear
Flower, cotton carding, rear spinning, dyeing, weaving, the specific steps are as follows:
(1) prepare raw material: it is fine to weigh Sorbtek365 fiber, cotton fiber, spandex respectively according to following mass percent
Dimension: Sorbtek365 fiber 24%, cotton fiber 74%, spandex fibre 2.0%；
(2) in blowing step, it is -1mm that griping cotton machine hired roughneck, which stretches out rib distance, and opener hired roughneck's revolving speed is 430r/min,
The comprehensive hired roughneck's revolving speed of single beater scutcher is 890r/min, and lap roller revolving speed is 11r/min；
(3) in cotton carding step, breast swift revolving speed is 330r/min, and licker-in revolving speed is 850r/min, and doffing speed is
15r/min, cover plate speed 129mm/min；
(4) it spins in step afterwards, roving twist factor 97, spinning frame ingot speed is 9500r/min, and back zone drafting multiple is
1.25；
(5) in staining procedure, speed 18m/min, the indigo content of bottom liquid is 1.2g/L, and indigo bottom liquid alkaline content is 3.5g/
L, Sodium Hydrosulfite Content 2.01g/L, indigo dye-uptake are 7.2%, and staining bath padding machine pressure is 5.2kg, and kiering alkali content is 5g/L
(90 DEG C), citric acid content are 6g/L (60 DEG C), and it is 5g/l that descaling bath, which permeates agent content, and soft agent content is 50g/L (60
℃)；
(6) in weaving step, opening time is 315 degree, back beam height 100mm, and the time of throwing a spear is 60 degree, upper machine
Power is 2.9N, and workshop relative humidity is 69%；
(7) in final finishing step, speed 40m/min, anti-shrinkage -13%, preshrinking rate -3~+3%, 82 DEG C of heating, sizing
Time 30s, first group of cylinder steam pressure 0.24MPa, rubber blanket cylinder steam pressure 0.21MPa, blanket cylinder steam pressure
0.43Mpa。
Implementation result: fabric has reached design effect.Fabric lines is clear, color is beautiful, good color fastness, it is soft,
Physical index is stablized, and tests through SGS inspection center, meets the center to fabric moisture absorbing and sweat releasing and warming standard requirements.
Above preferred embodiment is only intended to the description and interpretation contents of the present invention, does not constitute to the content of present invention
Limitation.In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specific example "
Or the description of " some examples " etc. means to combine reality born of the same parents example or example particular features, structures, materials, or characteristics described packet
Contained at least one embodiment of the present invention or example.In the present specification, schematic expression of the above terms are necessarily
It is directed to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be at any one
Or it can be combined in any suitable manner in multiple embodiment or examples.In addition, without conflicting with each other, the technology of this field
Personnel can tie the feature of different embodiments or examples described in this specification and different embodiments or examples
It closes and combines.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, modifies, replacement and variant.
Claims (8)
- The production method of environment-protection fiber ultra-deep orchid denim 1. a kind of moisture absorbing and sweat releasing keeps warm, step include choosing raw material, blowing step Suddenly, cotton carding step, afterwards spinning step, staining procedure, weaving step, which is characterized in that specific step is as follows:(1) prepare raw material: weighing Sorbtek365 fiber, cotton fiber, spandex fibre respectively according to following mass percent: Sorbtek365 fiber 18~30%, cotton fiber 70~80%, spandex fibre 1.5~2.5%；(2) in blowing step, it is -2~+1mm that griping cotton machine hired roughneck, which stretches out rib distance, and opener hired roughneck's revolving speed is 420~450r/ Min, the comprehensive hired roughneck's revolving speed of single beater scutcher are 820~850r/min, and lap roller revolving speed is 10~13r/min；(3) in cotton carding step, breast swift revolving speed is 320~360r/min, and licker-in revolving speed is 840~880r/min, doffer Revolving speed is 14~17r/min, and cover plate speed is 125~137mm/min；(4) it spins in step afterwards, roving twist factor is 93~99, and spinning frame ingot speed is 9200~10000r/min, back area draft times Number is 1.2~1.4；(5) in staining procedure, liquid indigo content in bottom is 1.15~1.35g/L, and indigo bottom liquid alkaline content is 3.4~3.6g/L, is protected Dangerous powder content is 1.98~2.09g/L, and indigo dye-uptake is 7~7.5%, and speed is 16~20m/min, and staining bath padding machine pressure is 5~5.5kg, kiering alkali content are 4~6g/L (90 DEG C), and citric acid content is 5~7g/L (60 DEG C), and descaling bath permeates agent content For 3.5~6g/l, soft agent content is 45~55g/L (60 DEG C)；(6) in weaving step, opening time is 310~320 degree, and back beam height is 100~110mm, and the time of throwing a spear is 55~65 Degree, warp tension are 2.5~3.0N, and workshop relative humidity is 60~70%；(7) in final finishing step, 35~45m/min of speed, anti-shrinkage 12%~14%, preshrinking rate -3~+3%, 80 DEG C of heating ~85 DEG C, setting time 40~20s, first group of cylinder 0.22~0.26MPa of steam pressure, rubber blanket cylinder steam pressure 0.18 ~0.22MPa, 0.42~0.44MPa of blanket cylinder steam pressure.
- 2. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature It is, in step (1), Sorbtek365 fiber, cotton fiber, spandex fibre weigh percentage are as follows: Sorbtek365 fiber 24%, cotton fiber 74%, spandex fibre 2%.
- 3. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature Be, in step (2), griping cotton machine hired roughneck stretch out rib distance be -1mm, opener hired roughneck's revolving speed be 430r/min, singles' hand at The comprehensive hired roughneck's revolving speed of volume machine is 830r/min, and lap roller revolving speed is 11r/min.
- 4. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature It is, in step (3), cylinder revolving speed is 330r/min, and licker-in revolving speed is 850r/min, doffing speed 15r/min, cover board speed Degree is 129mm/min.
- 5. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature It is, in step (4), roving twist factor 97, ingot speed 9500r/min, back zone drafting multiple 1.25.
- 6. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature It is, in step (5), speed 18m/min, the indigo content of bottom liquid is 1.2g/l, and indigo bottom liquid alkaline content is 3.5g/l, insurance Powder content is 2.01g/l, and indigo dye-uptake is 7.2%, and staining bath padding machine pressure is 5.2kg, and kiering alkali content is 5g/l (90 DEG C), Citric acid content is 6g/l (60 DEG C), and it is 5g/l that descaling bath, which permeates agent content, and soft agent content is 50g/l (60 DEG C).
- 7. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature It is, in step (6), opening time is 315 degree, back beam height 100mm；Throw a spear the time be 60 degree, warp tension 2.9N, Workshop relative humidity is 69%.
- 8. the production method of the warming environment-protection fiber ultra-deep orchid denim of a kind of moisture absorbing and sweat releasing according to claim 1, feature It is, in step (7), speed 40m/min, anti-shrinkage is 13%, and preshrinking rate≤- 3% heats 82 DEG C, and setting time is 30s, first group of cylinder steam pressure are 0.24MPa, and rubber blanket cylinder steam pressure is 0.21MPa, blanket cylinder steam pressure For 0.43MPa.