CN109370317A - A kind of engraving ashtray colouring dyestuff of resistance to sintering and preparation method thereof - Google Patents
A kind of engraving ashtray colouring dyestuff of resistance to sintering and preparation method thereof Download PDFInfo
- Publication number
- CN109370317A CN109370317A CN201811244388.4A CN201811244388A CN109370317A CN 109370317 A CN109370317 A CN 109370317A CN 201811244388 A CN201811244388 A CN 201811244388A CN 109370317 A CN109370317 A CN 109370317A
- Authority
- CN
- China
- Prior art keywords
- parts
- ashtray
- engraving
- dyestuff
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the engraving ashtray of a kind of resistance to sintering colouring dyestuffs and preparation method thereof, including following raw material by weight: 22 parts of alumina silicate, 34 parts of soil, 23 parts of bagasse, 43 parts of pigment, 58 parts of hydrotropy solution.Bagasse is handled, supernatant is taken；Alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by stirring 2-4h with the mixing speed of 500-700r/min；It is concentrated at a temperature of being placed into 60-90 DEG C again after stirring, colouring dyestuff is obtained after concentration.The engraving ashtray of the resistance to sintering of the present invention is painted dyestuff, increases the ingredient of alumina silicate, soil in dyestuff of painting, after brushing paint, the surface of closing engraving ashtray is when by high temperature sintering, agglomeration makes its densification, and heat is stopped to enter, and then can achieve high temperature resistant sintering；Increase bagasse, the wear-resisting scratch resistance of colouring dyestuff can be improved；Low manufacture cost, simple process.
Description
Technical field
The present invention relates to a kind of colouring dyestuff and preparation method thereof, the engraving ashtray of specifically a kind of resistance to sintering, which is painted, to be contaminated
Material and preparation method thereof.
Background technique
Ashtray is the tool for containing cigarette ash and cigarette butts, is resulted from the end of the 19th century.After the advent of cigarette, cigarette ash and cigarette butts everywhere throw away by bullet
Hinder health, ashtray also just generates therewith.Initially, someone's ashtray is referred to as cigarette dish, with pottery, porcelain be it is common, also have with glass
What glass, plastics, jade or metal material made.Its shape, size all bear obvious signs without fixation, that is, cigarette ash
The slot of the road cylinder Shang Junyouji cigarette thickness aims at and places cigarette and design.Sintering, refers to and granular material is changed into densification
Body is a traditional technical process.People are produced ceramics using this technique very early, powder metallurgy, refractory material, surpassed
High-temperature material etc..In general, powder is a kind of polycrystalline material by being sintered obtained dense body after overmolding, micro-
Structure is made of crystal, vitreum and stomata.
It is special due to ashtray currently in order to beautiful and product diversity, often can all give engraving ashtray colouring
Purposes, needing can be with high temperature resistant, and existing engraving ashtray does not have sintering heat-resisting quantity.
Summary of the invention
The purpose of the present invention is to provide the engraving ashtray of a kind of resistance to sintering colouring dyestuffs and preparation method thereof, to solve
The problems mentioned above in the background art.
To achieve the above object, the invention provides the following technical scheme:
A kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight: 18-30 parts of alumina silicate,
25-40 parts of soil, 20-28 parts of bagasse, 35-55 parts of pigment, 45-60 parts of hydrotropy solution.
As a further solution of the present invention: the engraving ashtray of the resistance to sintering is painted dyestuff, including it is following by weight
The raw material of part: 20-25 parts of alumina silicate, 30-38 parts of soil, 22-25 parts of bagasse, 40-45 parts of pigment, 50-59 parts of hydrotropy solution.
As further scheme of the invention: the engraving ashtray colouring dyestuff of the resistance to sintering, including below by weight
Measure the raw material of part: 22 parts of alumina silicate, 34 parts of soil, 23 parts of bagasse, 43 parts of pigment, 58 parts of hydrotropy solution.
As the present invention further scheme: the hydrotropy solution by by weight for 1-6:1-3:1-4 compatilizer,
Activating agent and antioxidant composition.
As further scheme of the invention: the hydrotropy solution is by by weight compatilizer, the activating agent for being 3:2:2
It is formed with antioxidant.
As further scheme of the invention: the compatilizer is EVA non-reactive compatilizer.
As it is a further object to provide a kind of resistance to sintering engraving ashtray colouring dyestuff preparation method,
The following steps are included:
1) bagasse, is handled
Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；
Second step smashes the bagasse after drying；
Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；
2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with 500-700r/min's
Mixing speed stirs 2-4h；
3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
As further scheme of the invention: the mixing speed in the step 2) is 680r/min.
As further scheme of the invention: the mixing time in the step 2) is 3h.
As further scheme of the invention: the thickening temperature in the step 3) is 80 DEG C.
Compared with prior art, the beneficial effects of the present invention are:
1, it paints and increases the ingredient of alumina silicate, soil in dyestuff, after brushing paint, the surface of closing engraving ashtray exists
When by high temperature sintering, agglomeration makes its densification, and heat is stopped to enter, and then can achieve high temperature resistant sintering；
2, increase bagasse, the wear-resisting scratch resistance of colouring dyestuff can be improved；
3, low manufacture cost, simple process.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight:
18 parts of alumina silicate, 25 parts of soil, 20 parts of bagasse, 35 parts of pigment, 45 parts of hydrotropy solution.
Wherein, the hydrotropy solution is described by forming by weight for compatilizer, activating agent and the antioxidant of 1:1:1
Compatilizer is EVA non-reactive compatilizer.
A kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering: the following steps are included:
1) bagasse, is handled
Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；
Second step smashes the bagasse after drying；
Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；
2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with 500-700r/min's
Mixing speed stirs 2-4h；
3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
Wherein, the mixing speed in the step 2) is 680r/min, and the mixing time in the step 2) is 3h, described
Thickening temperature in step 3) is 80 DEG C.
Embodiment 2
In the embodiment of the present invention, a kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight:
30 parts of alumina silicate, 40 parts of soil, 28 parts of bagasse, 55 parts of pigment, 60 parts of hydrotropy solution.
Wherein, the hydrotropy solution is described by forming by weight for compatilizer, activating agent and the antioxidant of 6:3:4
Compatilizer is EVA non-reactive compatilizer.
A kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering, comprising the following steps:
1) bagasse, is handled
Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；
Second step smashes the bagasse after drying；
Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；
2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with 500-700r/min's
Mixing speed stirs 2-4h；
3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
Wherein, the mixing speed in the step 2) is 680r/min, and the mixing time in the step 2) is 3h, described
Thickening temperature in step 3) is 80 DEG C.
Embodiment 3
In the embodiment of the present invention, a kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight:
25 parts of alumina silicate, 38 parts of soil, 25 parts of bagasse, 45 parts of pigment, 59 parts of hydrotropy solution
Wherein, the hydrotropy solution is described by forming by weight for compatilizer, activating agent and the antioxidant of 3:2:2
Compatilizer is EVA non-reactive compatilizer.
A kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering, comprising the following steps:
1) bagasse, is handled
Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；
Second step smashes the bagasse after drying；
Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；
2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with 500-700r/min's
Mixing speed stirs 2-4h；
3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
Wherein, the mixing speed in the step 2) is 680r/min, and the mixing time in the step 2) is 3h, described
Thickening temperature in step 3) is 80 DEG C.
Embodiment 4
In the embodiment of the present invention, a kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight:
20 parts of alumina silicate, 30 parts of soil, 22 parts of bagasse, 40 parts of pigment, 50 parts of hydrotropy solution
Wherein, the hydrotropy solution is described by forming by weight for compatilizer, activating agent and the antioxidant of 3:2:2
Compatilizer is EVA non-reactive compatilizer.
A kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering, comprising the following steps:
1) bagasse, is handled
Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；
Second step smashes the bagasse after drying；
Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；
2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with 500-700r/min's
Mixing speed stirs 2-4h；
3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
Wherein, the mixing speed in the step 2) is 680r/min, and the mixing time in the step 2) is 3h, described
Thickening temperature in step 3) is 80 DEG C.
Embodiment 5
In the embodiment of the present invention, a kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight:
22 parts of alumina silicate, 34 parts of soil, 23 parts of bagasse, 43 parts of pigment, 58 parts of hydrotropy solution.
Wherein, the hydrotropy solution is described by forming by weight for compatilizer, activating agent and the antioxidant of 3:2:2
Compatilizer is EVA non-reactive compatilizer.
A kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering, comprising the following steps:
1) bagasse, is handled
Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；
Second step smashes the bagasse after drying；
Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；
2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with 500-700r/min's
Mixing speed stirs 2-4h；
3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
Wherein, the mixing speed in the step 2) is 680r/min, and the mixing time in the step 2) is 3h, described
Thickening temperature in step 3) is 80 DEG C.
Comparative example 1
A kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight: 34 parts of soil, bagasse
23 parts, 43 parts of pigment, 58 parts of hydrotropy solution.
Comparative example 2
A kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight: 22 parts of alumina silicate, sugarcane
23 parts of slag, 43 parts of pigment, 58 parts of hydrotropy solution.
Comparative example 3
A kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight: 23 parts of bagasse, pigment
43 parts, 58 parts of hydrotropy solution.
Comparative example 4
A kind of engraving ashtray colouring dyestuff of resistance to sintering, including following raw material by weight: 22 parts of alumina silicate, soil
34 parts, 43 parts of pigment, 58 parts of hydrotropy solution.
Recipe ingredient such as the following table 1 of the engraving ashtray colouring dyestuff of resistance to sintering in above-described embodiment 1-5:
Table 1
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | |
| Alumina silicate | 18 | 30 | 25 | 20 | 22 |
| Soil | 25 | 40 | 38 | 30 | 34 |
| Bagasse | 20 | 28 | 25 | 22 | 23 |
| Pigment | 35 | 55 | 45 | 40 | 43 |
| Hydrotropy solution | 45 | 60 | 59 | 50 | 58 |
Recipe ingredient such as the following table 2 of the engraving ashtray colouring dyestuff of resistance to sintering in above-mentioned comparative example 1-3:
Table 2
| Comparative example 1 | Comparative example 2 | Comparative example 3 | Comparative example 4 | |
| Alumina silicate | 0 | 22 | 0 | 22 |
| Soil | 34 | 0 | 0 | 34 |
| Bagasse | 23 | 23 | 23 | 0 |
| Pigment | 43 | 43 | 43 | 43 |
| Hydrotropy solution | 58 | 58 | 58 | 58 |
Test experience is carried out to product obtained in embodiment 1-5 and comparative example 1-4 respectively, testing result such as the following table 3:
Table 3
| The Wear track depth (mm) of experiment 7 days | Sintering ratio (%) | |
| Embodiment 1 | 0.06 | 2 |
| Embodiment 2 | 0.05 | 3 |
| Embodiment 3 | 0.06 | 2 |
| Embodiment 4 | 0.06 | 2 |
| Embodiment 5 | 0.04 | 1 |
| Comparative example 1 | 1 | 30 |
| Comparative example 2 | 1 | 35 |
| Comparative example 3 | 1.8 | 58 |
| Comparative example 4 | 0.06 | 5 |
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (9)
- The dyestuff 1. a kind of engraving ashtray of resistance to sintering is painted, which is characterized in that including following raw material by weight: alumina silicate 18-30 parts, 25-40 parts of soil, 20-28 parts of bagasse, 35-55 parts of pigment, 45-60 parts of hydrotropy solution.
- The dyestuff 2. a kind of engraving ashtray of resistance to sintering according to claim 1 is painted, which is characterized in that the resistance to sintering Engraving ashtray paint dyestuff, including following raw material by weight: 20-25 parts of alumina silicate, 30-38 parts of soil, bagasse 22-25 parts, 40-45 parts of pigment, 50-59 parts of hydrotropy solution.
- The dyestuff 3. a kind of engraving ashtray of resistance to sintering according to claim 1 is painted, which is characterized in that the resistance to sintering Engraving ashtray paint dyestuff, including following raw material by weight: 22 parts of alumina silicate, 34 parts of soil, 23 parts of bagasse, water 43 parts of powder, 58 parts of hydrotropy solution.
- The dyestuff 4. a kind of engraving ashtray of resistance to sintering according to claim 1 to 3 is painted, which is characterized in that the hydrotropy Solution by weight for compatilizer, activating agent and the antioxidant of 1-6:1-3:1-4 by forming.
- The dyestuff 5. a kind of engraving ashtray of resistance to sintering according to claim 1 to 3 is painted, which is characterized in that the hydrotropy Solution by weight for compatilizer, activating agent and the antioxidant of 3:2:2 by forming.
- 6. a kind of preparation method of the engraving ashtray colouring dyestuff of -5 any resistance to sintering according to claim 1, special Sign is, comprising the following steps:1) bagasse, is handled:Bagasse is put into clear water and is cleaned by the first step, and 50 DEG C of drying is placed on after cleaning；Second step smashes the bagasse after drying；Bagasse after smashing is added in ethanol solution, first stirs and be centrifuged afterwards, takes supernatant by third step；2), alumina silicate, soil, pigment, hydrotropy solution are once added in supernatant, by with the stirring of 500-700r/min Speed stirs 2-4h；3) it is concentrated at a temperature of being placed into 60-90 DEG C again after, stirring, colouring dyestuff is obtained after concentration.
- 7. a kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering according to claim 6, which is characterized in that Mixing speed in the step 2 is 680r/min.
- 8. a kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering according to claim 6, which is characterized in that Mixing time in the step 2 is 3h.
- 9. a kind of preparation method of the engraving ashtray colouring dyestuff of resistance to sintering according to claim 6, which is characterized in that Thickening temperature in the step 3) is 80 DEG C.