CN109355789A - Bamboo charcoal fibre face fabric and preparation method thereof - Google Patents
Bamboo charcoal fibre face fabric and preparation method thereof Download PDFInfo
- Publication number
- CN109355789A CN109355789A CN201811339982.1A CN201811339982A CN109355789A CN 109355789 A CN109355789 A CN 109355789A CN 201811339982 A CN201811339982 A CN 201811339982A CN 109355789 A CN109355789 A CN 109355789A
- Authority
- CN
- China
- Prior art keywords
- fabric
- bamboo charcoal
- weight
- preparation
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of bamboo charcoal fibre face fabric, includes the following steps: that fabric is made to pad bacteria mildew-proof solution, obtain bamboo charcoal fibre face fabric；Fabric is formed by the raw material hybrid woven of following weight parts: 45~50 parts by weight of bamboo charcoal fiber；20~30 parts by weight of regenerated fiber；6~8 parts by weight of Fypro.For the present invention by carrying out compatibility to bacteria mildew-proof solution, fabric, which is made, has moisture absorbing and sweat releasing bacteria mildew-proof performance, and improves snugness of fit；Fabric of the present invention is added cotton fiber and is improved the hygroscopicity based on bamboo charcoal fiber；Casein fibre, chitin fiber and zein fiber is added, so that the moisture absorbing and sweat releasing and anti-microbial property of fabric reach best.
Description
Technical field
The present invention relates to a kind of knitting fabrics, more particularly to a kind of bamboo charcoal fibre face fabric and preparation method thereof.
Background technique
Bamboo charcoal is another completely new environment-friendly materials with excellent performance of bamboo timber resource exploitation.Bamboo is passed through 800
After spending the processing of high temperature drying charring process, bamboo charcoal is formed.Bamboo charcoal has very strong adsorption-decomposition function ability and radiation infrared
Function can keep room air pure and fresh and bed drying, and have and generate far infrared with adsorbed moisture, peculiar smell and pernicious gas
Line effect, can promote the blood circulation at the positions such as human body shoulder, neck, be conducive to help for sleep, recover from fatigue, to scapulohumeral pain
Bitterly, arthritis, chilly, insomnia etc. have good improvement.Can hygroscopic desiccation, smelly eliminating antibacterial and there is anion the property such as to penetrate
Energy.
Bamboo charcoal fiber is comprehensively and effectively utilized not yet at present, and application is not extensive, and fabric type is less, in fabric
Bamboo charcoal content is low, causes fabric moisture absorbing and sweat releasing, heat accumulation thermal, bacteria mildew-proof and anti-ultraviolet property that ideal shape can be not achieved
State.
Summary of the invention
In view of the above shortcomings, it is an object of the invention to develop a bamboo charcoal fibre face fabric, the fabric has simultaneously
There are moisture absorbing and sweat releasing, heat accumulation thermal, bacteria mildew-proof performance.
Technical solution of the present invention is summarized as follows:
A kind of preparation method of bamboo charcoal fibre face fabric, wherein include the following steps: that fabric is made to pad bacteria mildew-proof solution,
Obtain the bamboo charcoal fibre face fabric；The fabric is formed by the raw material hybrid woven of following weight parts:
45~50 parts by weight of bamboo charcoal fiber；
20~30 parts by weight of regenerated fiber；
6~8 parts by weight of Fypro.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein the regenerated fiber include 20~
25wt% casein fibre, 45~50wt% chitin fiber and 30~35wt% zein fiber.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein the fabric further includes 4~6 parts by weight
Cotton fiber.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein the bacteria mildew-proof solution is mainly by following
The group of parts by weight is grouped as:
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein further include the stearoyl benzene of 2~4 parts by weight
Formyl methane.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein further include the hexafluoro third of 1~3 parts by weight
Alkene-ethylene-vinyl acetate copolymer.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein the hexafluoropropene-ethene-vinyl acetate
In copolymer, hexafluoropropene content is 10~12%, and ethylene contents are 24~26%, remaining is vinylacetate.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein further include the thiophene benzene miaow of 1~3 parts by weight
Azoles.
Preferably, the preparation method of the bamboo charcoal fibre face fabric, wherein the concrete operations padded are as follows: will
The bacteria mildew-proof solution passes through the method padded and is applied on the fabric, obtains padding the fabric for having bacteria mildew-proof solution,
Then there is the fabric of bacteria mildew-proof solution to dry described pad, then baked, obtain the bamboo charcoal fibre face fabric.
A kind of preparation method for the bamboo charcoal fibre face fabric being prepared by the preparation method of bamboo charcoal fibre face fabric.
The beneficial effects of the present invention are:
(1) for the present invention by carrying out compatibility to bacteria mildew-proof solution, fabric, which is made, has moisture absorbing and sweat releasing bacteria mildew-proof performance,
And improve snugness of fit.
(2) fabric of the present invention is added cotton fiber and is improved the hygroscopicity based on bamboo charcoal fiber；Casein fibre, crust is added
Cellulose fiber and zein fiber, so that the moisture absorbing and sweat releasing and anti-microbial property of fabric reach best.
(3) chitin, lithium carbonate and dimercaptodimethyl ammonium chloride collaboration are used as antibacterial in bacteria mildew-proof solution of the present invention
Agent is mentioned so that having killing effect to pathogenic microorganism or growth being inhibited to reach best by the way that stearoyl benzoyl methane is added
Heat-resisting sublimability, washing fastness, thermo-oxidative stability and the anti-ultraviolet property of high fabric；By the way that hexafluoropropene-ethylene-vinegar is added
Sour ethylene copolymer improves bacteria mildew-proof solution in the firmness of fabric, and its bacteria mildew-proof performance can be improved.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments, to enable those skilled in the art referring to specification
Text can be implemented accordingly.
This case proposes a kind of preparation method of bamboo charcoal fibre face fabric, includes the following steps: fabric is made to pad bacteria mildew-proof molten
Liquid obtains bamboo charcoal fibre face fabric；Fabric is formed by the raw material hybrid woven of following weight parts:
45~50 parts by weight of bamboo charcoal fiber；
20~30 parts by weight of regenerated fiber；
6~8 parts by weight of Fypro.
Bamboo charcoal fiber have soft, toughness and wearability are strong, drapability is good, moisture absorption is ventilative and bacteriostasis antibiosis it is excellent
Point；Fypro has that light, wrinkle resistance is excellent, good permeability and good durability, dyeability and thermal finalization.
As the another embodiment of this case, wherein regenerated fiber includes 20~25wt% casein fibre, 45~50wt% crust
Cellulose fiber and 30~35wt% zein fiber.
The snugness of fit of casein fibre improvement bamboo charcoal fibre face fabric；Exist on its macromolecular chain of chitin fiber a large amount of
The hydrophilic radicals such as hydroxyl (- OH) and amino (- NH2), therefore fiber has good hydrophily and very high hygroscopicity.Chitin is fine
The equilibrium moisture regain of dimension is generally between 12%~16%, under different molding conditions, water retention value 130% or so,
Also have the function of soft warm, non-stimulated, bacteriostasis, and deodorization, has good maintenance action to skin；It is fine by the way that corn is added
Dimension improves drapability, slipping, sucting wet air permeability, natural bacteriostatic and the faintly acid for enabling skin trust, good heat-resisting of fabric
Property and anti-ultraviolet function and rich in gloss and elasticity；Casein fibre, chitin fiber and zein fiber are made by reasonable compatibility
The moisture absorbing and sweat releasing and anti-microbial property for obtaining fabric reach best.
As the another embodiment of this case, wherein fabric further includes the cotton fiber of 4~6 parts by weight.
Cotton fiber is porous material, and there are many hydrophilic radicals (- OH) on its cellulose macromolecule, so its
Hygroscopicity is preferable, further improves the moisture absorbing and sweat releasing performance of fabric by the way that cotton fiber is added.
As the another embodiment of this case, wherein bacteria mildew-proof solution is mainly made of following components in parts by weight:
Chitin, lithium carbonate and dimercaptodimethyl ammonium chloride collaboration are used as antibacterial agent, so that killing to pathogenic microorganism
Dead effect inhibits growth to reach best；The stability of antimicrobial treatment solution can be improved as compatilizer in ethyl alcohol.
As the another embodiment of this case, wherein further include the stearoyl benzoyl methane of 2~4 parts by weight.Stearoyl benzene first
Acyl methane can absorbing wavelength be strongly the ultraviolet light of 270~380nm, and chemical stability is good, and compatible lover, passes through with polyurethane
Heat-resisting sublimability, washing fastness, thermo-oxidative stability and anti-ultraviolet property that stearoyl benzoyl methane improves fabric is added.
As the another embodiment of this case, wherein further include hexafluoropropene-ethene-vinyl acetate copolymerization of 1~3 parts by weight
Object.Bacteria mildew-proof solution is improved in the firmness of fabric by the way that hexafluoropropene-ethylene-vinyl acetate copolymer is added, and can be mentioned
Its high bacteria mildew-proof performance.
As the another embodiment of this case, wherein in hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is
10~12%, ethylene contents are 24~26%, remaining is vinylacetate.
As the another embodiment of this case, wherein further include the thiabendazole of 1~3 parts by weight.By be added thiabendazole into
One step, which is improved to pathogenic microorganism, to be had killing effect or inhibits growth.
As the another embodiment of this case, wherein the concrete operations padded are as follows: bacteria mildew-proof solution is passed through to the side padded
Method is applied on fabric, obtains padding the fabric for having bacteria mildew-proof solution, will then be padded the fabric for having bacteria mildew-proof solution and is dried
It is dry, then baked, obtain bamboo charcoal fibre face fabric.
The present invention also protects a kind of bamboo charcoal fibre face fabric being prepared by bamboo charcoal fibre face fabric preparation method.
Some specific embodiments and comparative example is listed below:
Embodiment 1:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:6, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is 10%, ethylene contents 24%, remaining
For vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Embodiment 2:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:8, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is 11%, ethylene contents 25%, remaining
For vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Embodiment 3:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:8, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content be 10~12%, ethylene contents be 24~
26%, remaining is vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Comparative example 1:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:6, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is 10%, ethylene contents 24%, remaining
For vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Comparative example 2:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:6, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is 10%, ethylene contents 24%, remaining
For vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Comparative example 3:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:6, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is 10%, ethylene contents 24%, remaining
For vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Comparative example 4:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:6, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content is 10%, ethylene contents 24%, remaining
For vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
Comparative example 5:
A kind of bamboo charcoal fibre face fabric preparation method, includes the following steps:
(1) fabric is blended at scribbled by bamboo charcoal fiber and regenerated celulose fibre using common process, then with blended
Yarn and Fypro, cotton fiber obtain fabric using Weft knitting large circle machine progress knitting and weaving.Fabric is by following weight
The raw material hybrid woven of part forms:
(2) fabric pads bacteria mildew-proof solution and obtains bamboo charcoal fibre face fabric；The mass ratio of fabric and bacteria mildew-proof solution is
100:8, bacteria mildew-proof solution are made of following components in parts by weight:
In hexafluoropropene-ethylene-vinyl acetate copolymer, hexafluoropropene content be 10~12%, ethylene contents be 24~
26%, remaining is vinylacetate.
The concrete operations padded are as follows: bacteria mildew-proof solution being passed through the method padded and is applied on fabric, is padded
There is the fabric of bacteria mildew-proof solution, will then pad the fabric for having bacteria mildew-proof solution and dry, then baked, obtain bamboo charcoal fibre
Tie up fabric.The temperature of drying is 110 DEG C, and the time is 1 minute；The temperature baked is 120 DEG C, and the time is 3 minutes.
The performance test results of embodiment and comparative example are listed below:
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited
In specific details.
Claims (10)
1. a kind of preparation method of bamboo charcoal fibre face fabric, which is characterized in that include the following steps: fabric is made to pad bacteria mildew-proof molten
Liquid obtains the bamboo charcoal fibre face fabric；The fabric is formed by the raw material hybrid woven of following weight parts:
45~50 parts by weight of bamboo charcoal fiber；
20~30 parts by weight of regenerated fiber；
6~8 parts by weight of Fypro.
2. the preparation method of bamboo charcoal fibre face fabric according to claim 1, which is characterized in that the regenerated fiber includes
20~25wt% casein fibre, 45~50wt% chitin fiber and 30~35wt% zein fiber.
3. the preparation method of bamboo charcoal fibre face fabric according to claim 1, which is characterized in that the fabric further includes 4~6
The cotton fiber of parts by weight.
4. the preparation method of bamboo charcoal fibre face fabric according to claim 1, which is characterized in that the bacteria mildew-proof solution master
It to be made of following components in parts by weight:
5. the preparation method of bamboo charcoal fibre face fabric according to claim 4, which is characterized in that further include 2~4 parts by weight
Stearoyl benzoyl methane.
6. the preparation method of bamboo charcoal fibre face fabric according to claim 4, which is characterized in that further include 1~3 parts by weight
Hexafluoropropene-ethylene-vinyl acetate copolymer.
7. the preparation method of bamboo charcoal fibre face fabric according to claim 6, which is characterized in that the hexafluoropropene-ethylene-
In acetate ethylene copolymer, hexafluoropropene content is 10~12%, and ethylene contents are 24~26%, remaining is vinylacetate.
8. the preparation method of bamboo charcoal fibre face fabric according to claim 4, which is characterized in that further include 1~3 parts by weight
Thiabendazole.
9. the preparation method of bamboo charcoal fibre face fabric according to claim 1, it is characterised in that: the concrete operations padded
It is as follows: the bacteria mildew-proof solution being passed through into the method padded and is applied on the fabric, obtaining padding has bacteria mildew-proof solution
Fabric, then there is the fabric of bacteria mildew-proof solution to dry described pad, then baked, obtain the bamboo charcoal fiber face
Material.
10. a kind of preparation method for the bamboo charcoal fibre face fabric being prepared by any one of claim 1-9 the method.