CN109354933A - 一种竹木家具用耐磨涂料及其制备方法 - Google Patents

一种竹木家具用耐磨涂料及其制备方法 Download PDF

Info

Publication number
CN109354933A
CN109354933A CN201811202652.8A CN201811202652A CN109354933A CN 109354933 A CN109354933 A CN 109354933A CN 201811202652 A CN201811202652 A CN 201811202652A CN 109354933 A CN109354933 A CN 109354933A
Authority
CN
China
Prior art keywords
parts
nano
bamboo wood
wood furniture
resistant paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811202652.8A
Other languages
English (en)
Inventor
葛荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jixi Ma Dao Bamboo And Wood Products Co Ltd
Original Assignee
Jixi Ma Dao Bamboo And Wood Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jixi Ma Dao Bamboo And Wood Products Co Ltd filed Critical Jixi Ma Dao Bamboo And Wood Products Co Ltd
Priority to CN201811202652.8A priority Critical patent/CN109354933A/zh
Publication of CN109354933A publication Critical patent/CN109354933A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：苯丙乳液20‑30份、柠檬酸三丁酯15‑25份、伊利石功能粉4‑7份、纳米二氧化钛1‑3份、氧化石墨烯1‑2份、纳米海泡石1.2‑2.5份、耐磨助剂3‑5份、聚酰胺纤维3‑6份、纳米纤维素晶须3‑6份、空心玻璃微珠6‑10份、滑石粉6‑8份、植物胶2‑5份、抗湿剂1‑3份、偶联剂2‑6份、热稳定剂2‑4份、分散剂2‑4份、消泡剂1‑3份。本发明通过加入纳米海泡石、耐磨助剂、空心玻璃微珠、滑石粉、聚酰胺纤维和纳米纤维素晶须，可以提高涂料的耐磨性和耐腐蚀，能够对大多数化学药品和溶剂，表现出惰性、能耐强酸强碱、水和各种有机溶剂。

Description

一种竹木家具用耐磨涂料及其制备方法
技术领域
本发明涉及竹木家具领域，具体是一种竹木家具用耐磨涂料及其制备方法。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。
近几年环保一直都是人们关注的焦点，因此很多人在房屋装修时也会选择使用环保的家具，于是中国传统的竹木家具就越来越受到人们的青睐。竹木家具就是采用天然的竹材作为家具板材制作而成，然而竹木家具的不具备耐磨性。
发明内容
本发明的目的在于提供一种竹木家具用耐磨涂料及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液20-30份、柠檬酸三丁酯15-25份、伊利石功能粉4-7份、纳米二氧化钛1-3份、氧化石墨烯1-2份、纳米海泡石1.2-2.5份、耐磨助剂3-5份、聚酰胺纤维3-6份、纳米纤维素晶须3-6份、空心玻璃微珠6-10份、滑石粉6-8份、植物胶2-5份、抗湿剂1-3份、偶联剂2-6份、热稳定剂2-4份、分散剂2-4份、消泡剂1-3份。
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液20份、柠檬酸三丁酯15份、伊利石功能粉4份、纳米二氧化钛1份、氧化石墨烯1份、纳米海泡石1.2份、耐磨助剂3份、聚酰胺纤维3份、纳米纤维素晶须3份、空心玻璃微珠6份、滑石粉6份、植物胶2份、抗湿剂1份、偶联剂2份、热稳定剂2份、分散剂2份、消泡剂1份。
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液30份、柠檬酸三丁酯25份、伊利石功能粉7份、纳米二氧化钛3份、氧化石墨烯2份、纳米海泡石2.5份、耐磨助剂5份、聚酰胺纤维6份、纳米纤维素晶须6份、空心玻璃微珠10份、滑石粉8份、植物胶5份、抗湿剂3份、偶联剂6份、热稳定剂4份、分散剂4份、消泡剂3份。
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液26份、柠檬酸三丁酯20份、伊利石功能粉6份、纳米二氧化钛2份、氧化石墨烯1.5份、纳米海泡石1.8份、耐磨助剂4份、聚酰胺纤维4.5份、纳米纤维素晶须5份、空心玻璃微珠8份、滑石粉7份、植物胶3.5份、抗湿剂2份、偶联剂4份、热稳定剂3份、分散剂3份、消泡剂2份。
所述伊利石功能粉中掺杂有质量百分比0.06％以上的功能元素，所述功能元素为Au、Ag、Nd、Pt和Pd中的一种或多种。
所述耐磨助剂，由如下重量份数的原料制成：SBA-15分子筛4-8份、纳米纤维素晶须3-5份、硅溶胶/微晶纤维素2-3份、聚乙烯醇树脂1-2份、阴离子表面活性剂1-2份、纳米碳化硅2-4份、活性重质碳酸钙2-5份、乙二醇4-8份。
所述植物胶为从石花菜中提取的石花胶。
所述聚酰胺纤维和纳米纤维素晶须的长度为0.5-3mm。
一种竹木家具用耐磨涂料的制备方法，包括如下步骤：
(1)按所述重量配比计量各原料，在球磨机中加入去离子水、苯丙乳液、柠檬酸三丁酯、伊利石功能粉，以200r/min速度，进行第一次球磨，制得浆料；
(2)加入纳米二氧化钛、氧化石墨烯、纳米海泡石、耐磨助剂、聚酰胺纤维、纳米纤维素晶须、空心玻璃微珠、滑石粉、抗湿剂、偶联剂、热稳定剂、分散剂、消泡剂，以400r/min高速球磨12小时并充分分散，使其混合均匀；
(3)加入植物胶，以50r/min低速搅拌4小时，过筛并稠化制得。
与现有技术相比，本发明的有益效果是：
本发明通过加入纳米海泡石、耐磨助剂、空心玻璃微珠、滑石粉、聚酰胺纤维和纳米纤维素晶须，可以提高涂料的耐磨性和耐腐蚀，能够对大多数化学药品和溶剂，表现出惰性、能耐强酸强碱、水和各种有机溶剂；通过加入伊利石功能粉，使得涂料具有释放负离子、吸收甲醛等功能，能够有效净化空气；本发明在各原料的科学配伍下，防腐性能好，粘结性好，成本低，强度大，光泽好，流平效果好，具有防水、防潮、防腐的功能，有效期时间较长，耐高温，耐低温，还具备防白蚁的功能，值得大力推广使用。
具体实施方式
实施例1
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液20份、柠檬酸三丁酯15份、伊利石功能粉4份、纳米二氧化钛1份、氧化石墨烯1份、纳米海泡石1.2份、耐磨助剂3份、聚酰胺纤维3份、纳米纤维素晶须3份、空心玻璃微珠6份、滑石粉6份、植物胶2份、抗湿剂1份、偶联剂2份、热稳定剂2份、分散剂2份、消泡剂1份。
所述伊利石功能粉中掺杂有质量百分比0.06％以上的功能元素，所述功能元素为Au、Ag、Nd、Pt和Pd中的一种或多种。
所述耐磨助剂，由如下重量份数的原料制成：SBA-15分子筛4-8份、纳米纤维素晶须3-5份、硅溶胶/微晶纤维素2-3份、聚乙烯醇树脂1-2份、阴离子表面活性剂1-2份、纳米碳化硅2-4份、活性重质碳酸钙2-5份、乙二醇4-8份。
所述植物胶为从石花菜中提取的石花胶。
所述聚酰胺纤维和纳米纤维素晶须的长度为0.5-3mm。
一种竹木家具用耐磨涂料的制备方法，包括如下步骤：
(1)按所述重量配比计量各原料，在球磨机中加入去离子水、苯丙乳液、柠檬酸三丁酯、伊利石功能粉，以200r/min速度，进行第一次球磨，制得浆料；
(2)加入纳米二氧化钛、氧化石墨烯、纳米海泡石、耐磨助剂、聚酰胺纤维、纳米纤维素晶须、空心玻璃微珠、滑石粉、抗湿剂、偶联剂、热稳定剂、分散剂、消泡剂，以400r/min高速球磨12小时并充分分散，使其混合均匀；
(3)加入植物胶，以50r/min低速搅拌4小时，过筛并稠化制得。
实施例2
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液30份、柠檬酸三丁酯25份、伊利石功能粉7份、纳米二氧化钛3份、氧化石墨烯2份、纳米海泡石2.5份、耐磨助剂5份、聚酰胺纤维6份、纳米纤维素晶须6份、空心玻璃微珠10份、滑石粉8份、植物胶5份、抗湿剂3份、偶联剂6份、热稳定剂4份、分散剂4份、消泡剂3份。
所述伊利石功能粉中掺杂有质量百分比0.06％以上的功能元素，所述功能元素为Au、Ag、Nd、Pt和Pd中的一种或多种。
所述耐磨助剂，由如下重量份数的原料制成：SBA-15分子筛4-8份、纳米纤维素晶须3-5份、硅溶胶/微晶纤维素2-3份、聚乙烯醇树脂1-2份、阴离子表面活性剂1-2份、纳米碳化硅2-4份、活性重质碳酸钙2-5份、乙二醇4-8份。
所述植物胶为从石花菜中提取的石花胶。
所述聚酰胺纤维和纳米纤维素晶须的长度为0.5-3mm。
一种竹木家具用耐磨涂料的制备方法，包括如下步骤：
(1)按所述重量配比计量各原料，在球磨机中加入去离子水、苯丙乳液、柠檬酸三丁酯、伊利石功能粉，以200r/min速度，进行第一次球磨，制得浆料；
(2)加入纳米二氧化钛、氧化石墨烯、纳米海泡石、耐磨助剂、聚酰胺纤维、纳米纤维素晶须、空心玻璃微珠、滑石粉、抗湿剂、偶联剂、热稳定剂、分散剂、消泡剂，以400r/min高速球磨12小时并充分分散，使其混合均匀；
(3)加入植物胶，以50r/min低速搅拌4小时，过筛并稠化制得。
实施例3
一种竹木家具用耐磨涂料，其由以下重量份数的原料制成：
苯丙乳液26份、柠檬酸三丁酯20份、伊利石功能粉6份、纳米二氧化钛2份、氧化石墨烯1.5份、纳米海泡石1.8份、耐磨助剂4份、聚酰胺纤维4.5份、纳米纤维素晶须5份、空心玻璃微珠8份、滑石粉7份、植物胶3.5份、抗湿剂2份、偶联剂4份、热稳定剂3份、分散剂3份、消泡剂2份。
所述伊利石功能粉中掺杂有质量百分比0.06％以上的功能元素，所述功能元素为Au、Ag、Nd、Pt和Pd中的一种或多种。
所述耐磨助剂，由如下重量份数的原料制成：SBA-15分子筛4-8份、纳米纤维素晶须3-5份、硅溶胶/微晶纤维素2-3份、聚乙烯醇树脂1-2份、阴离子表面活性剂1-2份、纳米碳化硅2-4份、活性重质碳酸钙2-5份、乙二醇4-8份。
所述植物胶为从石花菜中提取的石花胶。
所述聚酰胺纤维和纳米纤维素晶须的长度为0.5-3mm。
一种竹木家具用耐磨涂料的制备方法，包括如下步骤：
(1)按所述重量配比计量各原料，在球磨机中加入去离子水、苯丙乳液、柠檬酸三丁酯、伊利石功能粉，以200r/min速度，进行第一次球磨，制得浆料；
(2)加入纳米二氧化钛、氧化石墨烯、纳米海泡石、耐磨助剂、聚酰胺纤维、纳米纤维素晶须、空心玻璃微珠、滑石粉、抗湿剂、偶联剂、热稳定剂、分散剂、消泡剂，以400r/min高速球磨12小时并充分分散，使其混合均匀；
(3)加入植物胶，以50r/min低速搅拌4小时，过筛并稠化制得。

Claims (9)

1.一种竹木家具用耐磨涂料，其特征在于，其由以下重量份数的原料制成：
苯丙乳液20-30份、柠檬酸三丁酯15-25份、伊利石功能粉4-7份、纳米二氧化钛1-3份、氧化石墨烯1-2份、纳米海泡石1.2-2.5份、耐磨助剂3-5份、聚酰胺纤维3-6份、纳米纤维素晶须3-6份、空心玻璃微珠6-10份、滑石粉6-8份、植物胶2-5份、抗湿剂1-3份、偶联剂2-6份、热稳定剂2-4份、分散剂2-4份、消泡剂1-3份。
2.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，其由以下重量份数的原料制成：
苯丙乳液20份、柠檬酸三丁酯15份、伊利石功能粉4份、纳米二氧化钛1份、氧化石墨烯1份、纳米海泡石1.2份、耐磨助剂3份、聚酰胺纤维3份、纳米纤维素晶须3份、空心玻璃微珠6份、滑石粉6份、植物胶2份、抗湿剂1份、偶联剂2份、热稳定剂2份、分散剂2份、消泡剂1份。
3.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，其由以下重量份数的原料制成：
苯丙乳液30份、柠檬酸三丁酯25份、伊利石功能粉7份、纳米二氧化钛3份、氧化石墨烯2份、纳米海泡石2.5份、耐磨助剂5份、聚酰胺纤维6份、纳米纤维素晶须6份、空心玻璃微珠10份、滑石粉8份、植物胶5份、抗湿剂3份、偶联剂6份、热稳定剂4份、分散剂4份、消泡剂3份。
4.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，其由以下重量份数的原料制成：
苯丙乳液26份、柠檬酸三丁酯20份、伊利石功能粉6份、纳米二氧化钛2份、氧化石墨烯1.5份、纳米海泡石1.8份、耐磨助剂4份、聚酰胺纤维4.5份、纳米纤维素晶须5份、空心玻璃微珠8份、滑石粉7份、植物胶3.5份、抗湿剂2份、偶联剂4份、热稳定剂3份、分散剂3份、消泡剂2份。
5.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，所述伊利石功能粉中掺杂有质量百分比0.06％以上的功能元素，所述功能元素为Au、Ag、Nd、Pt和Pd中的一种或多种。
6.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，所述耐磨助剂，由如下重量份数的原料制成：SBA-15分子筛4-8份、纳米纤维素晶须3-5份、硅溶胶/微晶纤维素2-3份、聚乙烯醇树脂1-2份、阴离子表面活性剂1-2份、纳米碳化硅2-4份、活性重质碳酸钙2-5份、乙二醇4-8份。
7.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，所述植物胶为从石花菜中提取的石花胶。
8.根据权利要求1所述的竹木家具用耐磨涂料，其特征在于，所述聚酰胺纤维和纳米纤维素晶须的长度为0.5-3mm。
9.一种竹木家具用耐磨涂料的制备方法，其特征在于，包括如下步骤：
(1)按所述重量配比计量各原料，在球磨机中加入去离子水、苯丙乳液、柠檬酸三丁酯、伊利石功能粉，以200r/min速度，进行第一次球磨，制得浆料；
(2)加入纳米二氧化钛、氧化石墨烯、纳米海泡石、耐磨助剂、聚酰胺纤维、纳米纤维素晶须、空心玻璃微珠、滑石粉、抗湿剂、偶联剂、热稳定剂、分散剂、消泡剂，以400r/min高速球磨12小时并充分分散，使其混合均匀；
(3)加入植物胶，以50r/min低速搅拌4小时，过筛并稠化制得。
CN201811202652.8A 2018-10-16 2018-10-16 一种竹木家具用耐磨涂料及其制备方法 Pending CN109354933A (zh)