CN109338758A - A kind of dyeing of full Terylene chiffon cloth - Google Patents
A kind of dyeing of full Terylene chiffon cloth Download PDFInfo
- Publication number
- CN109338758A CN109338758A CN201811095471.XA CN201811095471A CN109338758A CN 109338758 A CN109338758 A CN 109338758A CN 201811095471 A CN201811095471 A CN 201811095471A CN 109338758 A CN109338758 A CN 109338758A
- Authority
- CN
- China
- Prior art keywords
- fabric
- dyeing
- carried out
- cloth according
- full terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dyeings of full Terylene chiffon cloth, are related to mull-chiffon staining technique field, and drip irrigation device is the following steps are included: (1), open width refining；(2), preshrunk；(3), it dries；(4), pre-setting；(5), Alkali reduction；(6), it washes；(7), it dyes；(8), finishing agent is coated；(9) cylinder cleaning is returned in pickling and (10), and the present invention has the effect of that the blackness for effectively improving mull-chiffon can be reached by increase dye uptake and improvement visual sense.
Description
Technical field
The present invention relates to mull-chiffon staining technique fields, and more specifically it is related to a kind of dyer of full Terylene chiffon cloth
Skill.
Background technique
Mull-chiffon is that a kind of latitude and longitude all use terylene or silk for raw material, the cloth being process through left and right,
The quality of mull-chiffon, color effect are good, and fabric is ultra-thin.Due to Shelley cloth fabric longitude and latitude Shu Lang, it is especially susceptible to breathe freely, adds
Decrement treatment in dyeing is sufficient and makes fabric hand feel especially soft, therefore is widely loved by the people, wherein China's production
Chiffon, which is furnished with, greatly to be sold toward Middle East, but is influenced by local religion humanity, and China sells the snow toward middle east
Woven fabric can generally dye black in advance, and blackness is higher, more be liked by local people.
But in the prior art, the mull-chiffon of black be usually using 10%(o.w.f) the black S-2BL of dispersion as coloring agent,
Then by fabric pass sequentially through preshrunk, washing, pre-setting, Alkali reduction, dyeing, rinsing, dehydration, open-width and sizing and etc. with complete
At the dyeing work of mull-chiffon, but the mull-chiffon that comes out of dyeing in this way be because must improve feel by caustic reduction processing,
But the fabric surface through alkali decrement treatment will form pit, so that visual sense color is deteriorated, lead to the finished product coloured light of dyeing
Apparent inclined feux rouges is the obvious inadequate performance of blackness, therefore hardly consistent with the demand of middle east client, and the prior art is still
There is not the visual sense solved the problems, such as under caustic reduction processing residual, the blackness of mull-chiffon is caused to be unable to get raising always.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of dyer of full Terylene chiffon cloth
Skill the advantage is that the blackness that can effectively improve mull-chiffon.
To achieve the above object, the present invention provides following technical solutions, including step 1: putting fabric into conche and does
Open width refinery activities；
Step 2: preshrunk processing will be carried out through the processed fabric of step 1；
Step 3: drying and processing will be carried out through the processed fabric of step 2 using dryer；
Step 4: pre-setting processing will be carried out through the processed fabric of step 3 using forming machine；
Step 5: alkali decrement treatment will be carried out through the processed fabric of step 4 using Alkali reduction machine；
Step 6: will be through remaining finish, terylene clast and polyester oligomer on the processed fabric of step 5 using clear water
Etc. cleaning up；
Step 7: coloring agent is sprayed at through the processed fabric of step 6 to dye to fabric using overflow dyeing machine；
Step 8: the finishing agent of upper one layer of low-refraction substance is covered on through the processed fabric surface of step 7 with after the completion
Housekeeping；
Step 9: pickling processes are carried out to through the processed fabric of step 8 using acid detergent, the fabric after the completion of pickling
It should be carried out dehydrating；
Step 10: the fabric through step 9 pickling and after the completion of being dehydrated being put into and does back cylinder cleaning in dye vat, clear through returning cylinder
Fabric after the completion of washing should be carried out dehydrating.
By using above-mentioned technical proposal, refining half bleaching processing can be carried out to fabric by step 1, can be cleaned
The impurity such as the dust on to fabric effectively increase the dye uptake of fabric, and can increase ironing fastness and the friction jail of mull-chiffon
Degree, the residuals being at after the completion of fabric half bleaching by step 2 and step 3 can reduce base by step 6
Influence of the terylene clast, polyester oligomer on cloth surface to dyeing quality, while ensuring the dyeing effect of step 7, pass through step
Eight adhere to the finishing agent of upper one layer low refraction substance on fabric, by the arrangement for covering upper low refraction substance on fabric surface
Agent can reduce the ray refractive index on fabric surface, to improve visual sense, people obviously be experienced when watching fabric
Color burn effectively improves the blackness of fabric, and the arrangement for remaining in fabric surface can be cleaned up by step 9 and step 10
Agent and impurity, so that not only blackness significantly improves the mull-chiffon dyed, but also soft, feel is also effectively changed
It is kind.
The present invention is further arranged to: the step 1 carries out in conche, and the operating temperature of conche is no more than 40
DEG C, fabric is in the speed of service in conche between 30 ~ 40m/min.
By using above-mentioned technical proposal, the operating temperature control of conche be can be avoided into mull-chiffon within 40 DEG C and existed
Fine wrinkle is generated under humid tropical condition, the speed of service of fabric is controlled by the spiral spreading roll being set in conche, by the fortune of fabric
Row speed control can be avoided spiral spreading roll excessive velocities between 30 ~ 40m/min and leave obvious scratch on fabric surface,
Ensure that adverse effect will not be generated after fabric increases open width refinery activities.
The present invention is further arranged to: the step 2 carries out in preshrunk equipment, added with degreaser in preshrunk equipment.
By using above-mentioned technical proposal, a large amount of finish can be added in mull-chiffon in spinning and fabrication processes, by removing
Finish can remove remaining finish on mull-chiffon.
The present invention is further arranged to: the drying equipment that the step 3 uses is guide belt loose-drying machine.
By using above-mentioned technical proposal, when being dried with conventional roller dryer to fabric, fabric be easy by
It is hot uneven and generate winding, cause fabric that can generate biggish warp direction stretching phenomenon, using guide belt loose-drying machine because
Homogeneous heating, keeps the fluffy degree and resilience of fabric, to keep the good feel of mull-chiffon, while can be maximum
Roller dryer is reduced to fabric bring aurora print and folding line.
The present invention is further arranged to: the reduction device that the step 5 uses is continuous deweighing machine.
By using above-mentioned technical proposal, carrying out Alkali reduction work using continuous deweighing machine, can to reduce feel cylinder poor, from
And the flexibility of fabric is effectively provided,
The present invention is further arranged to: being added with antistatic agent using lye is interior in the step 5.
By using above-mentioned technical proposal, fabric surface affinity moisture can be made by antistatic agent, and antistatic agent belongs to
One kind of surface ion surfactant, therefore also there is electric action, the electrostatic that fabric surface can be made to adhere to leaks in time.
The present invention is further arranged to: fabric should be cooled to 60 DEG C once after the completion of the step 7, after the completion of cooling
It should once be washed.
By using above-mentioned technical proposal, the extra coloring agent on fabric surface can be gone out by washing, so that base
Cloth causes fabric crimping and cooling can be avoided and directly rinse when fabric overheats convenient for covering upper finishing agent, by carrying out to fabric
The case where occur.
The present invention is further arranged to: the step 8 detailed process are as follows: loose-drying --- padding finishing agent --- is red
Outside line central drying short --- sizing.
By using above-mentioned technical proposal, the extra moisture of fabric can be evaporated by loose-drying, while make base
Cloth surface can more adsorb finishing agent in padding finishing agent, base when utilizing central drying short can be rapidly after padding
Moisture evaporation on cloth surface, it is as much as possible that finishing agent is stayed on fabric surface.
The present invention is further arranged to: coloring agent used in the step 7 includes 100% powdery disperse dark blue
HGL7.2%(o.w.f), 100% powdery disperse orange S-4RL2.5%(o.w.f) and 100% powdery Disperse Rubine S-2GFL 7.2%
(o.w.f).
By using above-mentioned technical proposal, disperse dark blue, disperse orange and dispersed ruby mixing will become ater, and dispersion is deep
Blue HGL is since relative molecular mass is larger, even if thermophoresis amount is larger, mixed coloring agent can also show preferably to rise
Magnificent fastness.
The present invention is further arranged to: softening agent and fluorine-containing water repellent are added in the finishing agent.
By using above-mentioned technical proposal, it can be improved the smooth degree of fabric by softening agent, friction can also be reduced
Power can effectively improve the dry fastness of fabric, and fluorine-containing splashproof machine, which is added, can be improved the fastness to wet rubbing of fabric.
In conclusion the invention has the following advantages that
1, visual sense compromises of the mull-chiffon after alkali decrement treatment are solved, the blackness of mull-chiffon is effectively improved；
2, by can be improved the smooth degree of fabric added with softening agent and fluorine-containing water repellent in finishing agent, while making base
The dry fastness and fastness to wet rubbing of cloth also get a promotion；
3, it can be improved the dye uptake of fabric by increasing open width refining procedure, further increase the blackness of mull-chiffon.
Detailed description of the invention
Fig. 1 is the step schematic diagram of the present embodiment.
Specific embodiment
Below in conjunction with attached drawing, invention is further described in detail.
A kind of dyeing of full Terylene chiffon cloth, as shown in Figure 1, including the following steps:
Step 1: it puts fabric into conche and does open width refinery activities；
Step 2: preshrunk processing will be carried out through the processed fabric of step 1；
Step 3: drying and processing will be carried out through the processed fabric of step 2 using dryer；
Step 4: pre-setting processing will be carried out through the processed fabric of step 3 using forming machine；
Step 5: alkali decrement treatment will be carried out through the processed fabric of step 4 using Alkali reduction machine；
Step 6: will be through remaining finish, terylene clast and polyester oligomer on the processed fabric of step 5 using clear water
Etc. cleaning up；
Step 7: coloring agent is sprayed at through the processed fabric of step 6 to dye to fabric using overflow dyeing machine；
Step 8: the finishing agent of upper one layer of low-refraction substance is covered on through the processed fabric surface of step 7 with after the completion
Housekeeping；
Step 9: pickling processes are carried out to through the processed fabric of step 8 using acid detergent, the fabric after the completion of pickling
It should be carried out dehydrating；
Step 10: the fabric through step 9 pickling and after the completion of being dehydrated being put into and does back cylinder cleaning in dye vat, clear through returning cylinder
Fabric after the completion of washing should be carried out dehydrating.
Wherein, for being added with antistatic agent, the coloring agent that step 7 uses in the lye of alkali decrement treatment in step 5
By 100% powdery disperse dark blue HGL7.2%(o.w.f), 100% powdery disperse orange S-4RL2.5%(o.w.f) and 100% powdery dispersion
Carbuncle S-2GFL7.2%(o.w.f) it mixes, added with softening agent in the finishing agent in step 8 for covering fabric surface
And fluorine-containing water repellent.
Specifically, filling water-soluble refining liquid in the conche used in step 1, while controlling the work of conche
Make temperature no more than 40 DEG C, fabric between 30 ~ 40m/min, can be set in the speed of service in conche in existing conche
Be equipped with for transmit fabric and to fabric carry out expanding work spiral spreading roll, using conche to fabric play refining and
The effect of half bleaching to effectively remove remaining impurity on fabric, and can make inside fabric in step 2 and step 3
Residual stress generates certain deflection, therefore the necessary wall product sizing of pre-setting width of spiral spreading roll is big by 7~10%.
Specifically, being needed before dyeing since mull-chiffon joined a large amount of finish in spinning and fabrication processes
Finish remaining on mull-chiffon is removed, therefore, when carrying out step 2, assistant before degreaser etc. should be added in preshrunk equipment
Agent；Wherein, should be using existing dye vat in factory for the preshrunk equipment of preshrunk work, doing preshrunk equipment using dye vat can prevent
Upper other colors are only infected on fabric, fabric should carry out cooling processing to dye vat before taking out dye vat, when staff being avoided to operate
Scald, can increase the cooling rate of dye vat by being gradually added into cold water in dye vat, if the operating temperature in dye vat is greater than
Cold water is added at 60 DEG C to easily lead to fabric surface and fine wrinkle occur.
Specifically, the drying equipment that step 3 uses utilizes guide belt loose-drying function for guide belt loose-drying machine
Enough ensure the upper and lower surface homogeneous heating to fabric, and fabric will not be made to be rolled into one as roller dryer, can effectively protect
The fluffy degree and resilience of fabric are held, so that the good feel of mull-chiffon is kept, for conventional roller dryer,
Guide belt loose-drying machine will not be to fabric bring aurora print and folding line, so that the feel of fabric is more secure, wherein lead
The drying rate of belt loose-drying machine is subject to fabric dry tack free.
Specifically, the equipment that step 4 uses is pre-setting machine, wherein the heat setting temperature of pre-setting machine is 185~195
DEG C, the speed of pre-setting machine is 40~60m/min, and it is big by 5 that pre-setting breadth of the fabric in pre-setting machine than finished product fixs breadth
~10%.
Specifically, the reduction device that step 5 uses carries out Alkali reduction work for continuous deweighing machine, using continuous deweighing machine
It can reduce that feel cylinder is poor, to effectively provide the flexibility of fabric, wherein poor in order to control decrement cylinder, it should be ensured that every cylinder cloth is equal
There are be reduced later feel sample.
Specifically, using common washing work in step 6, washing times are subject to last limpid free from admixture of cylinder water.
Specifically, the operating temperature for the overflow dyeing machine that step 7 uses is 130 DEG C, working time 60min, the liter of overflow dyeing machine
Cooling rate and consistent with the requirement that preshrunk works into the temperature of cold water, wherein coloring agent height of water level in overflow dyeing machine with
Based on complete dipped fabric, levelling agent is not added in dyeing course, wherein the operating temperature of coloring agent should be dropped after the completion of dyeing
To 60 DEG C, then the fabric after the completion of dyeing is taken out and washes out fabric coloring agent remained on surface.
Specifically, the detailed process of step 8 are as follows: loose-drying, --- padding finishing agent --- infrared ray becate dries
It is dry --- sizing, finishing agent are selected as low refraction substance.
Specifically, pickling detergent is sprayed on fabric upper surface in common washing room using spray head by step 9,
The pickling detergent contained in fabric should be deviate from using drum-type dewaterer after having sprayed pickling detergent.
Specifically, step 10 needs repeatedly to immerse fabric progress clear water immersion in dye vat, again by base after the completion of impregnating
Cloth is put into drum-type dewaterer and is carried out dehydrating, this work is multiple repeatedly, until the water of dewaterer discharge is limpid.
The dye uptake that fabric can be increased by step 1 and step 6, the blackness for improving mull-chiffon have direct side
It helps；The ray refractive index that can reduce fabric surface by step 8, effectively improves visual sense, so that the finished product coloured light of mull-chiffon is bright
Inclined green light is shown, this is the phenomenon that fabric blackness effectively improves；It can be cleaned up by step 9 and step 10 and remain in base
The finishing agent and impurity on cloth surface, so that increasing the mull-chiffon not only blackness of open width refining procedure and finishing agent coating process
It significantly improves, and soft, feel is also effectively improved.
Wherein, it is noted that last bucket for last cylinder clear water and the step 10 discharge impregnated in step 6 is clear
Water can collect and be used for the flushing work of step 7, last cylinder clear water impregnated in step 6 and step 10 discharge
Last barrel of clear water it is more limpid, the impurity that contains of inside is less, is used directly for rinsing remaining coloring agent on fabric.
Wherein, it is noted that step 9 residual and the dirt of the pickling detergent of abjection and former barrels of step 10 abjections
Contain a large amount of acid detergent in water, the pickling detergent of this part can recycle, and be filtered, and filter out
More clean pickling detergent can be with direct reuse in step 9, and the remaining sewage containing pickling detergent can be with step
Five lye used neutralize, and the sediment isolated is filtered, and the sewage isolated can be back to equipment cleaning after processing.
Wherein, it is noted that Step 1: Step 2: Step 5: Step 6: Step 7: step 7 and step 10 generate
Waste water and tap water and rainwater-collecting after can by precipitation process, and by precipitation process complete mixing water inject Ro film
Conditioning tank, which carries out sewage treatment, can produce recycle-water, this part recycle-water is finally back to equipment flushing.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to restrict the invention, all in design structure of the invention
Within think of, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of dyeing of full Terylene chiffon cloth, which comprises the steps of:
Step 1: it puts fabric into conche and does open width refinery activities；
Step 2: preshrunk processing will be carried out through the processed fabric of step 1；
Step 3: drying and processing will be carried out through the processed fabric of step 2 using dryer；
Step 4: pre-setting processing will be carried out through the processed fabric of step 3 using forming machine；
Step 5: alkali decrement treatment will be carried out through the processed fabric of step 4 using Alkali reduction machine；
Step 6: will be through remaining finish, terylene clast and polyester oligomer on the processed fabric of step 5 using clear water
Etc. cleaning up；
Step 7: coloring agent is sprayed at through the processed fabric of step 6 to dye to fabric using overflow dyeing machine；
Step 8: the finishing agent of upper one layer of low-refraction substance is covered on through the processed fabric surface of step 7 with after the completion
Housekeeping；
Step 9: pickling processes are carried out to through the processed fabric of step 8 using acid detergent, the fabric after the completion of pickling
It should be carried out dehydrating；
Step 10: the fabric through step 9 pickling and after the completion of being dehydrated being put into and does back cylinder cleaning in dye vat, clear through returning cylinder
Fabric after the completion of washing should be carried out dehydrating.
2. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: the step 1 is in essence
Carry out in mill, the operating temperature of conche is no more than 40 DEG C, the speed of service of the fabric in conche 30 ~ 40m/min it
Between.
3. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: the step 2 is pre-
It is carried out in contracting equipment, added with degreaser in preshrunk equipment.
4. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: the step 3 uses
Drying equipment be guide belt loose-drying machine.
5. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: the step 5 uses
Reduction device be continuous deweighing machine.
6. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: make in the step 5
With in lye be added with antistatic agent.
7. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: the step 7 is completed
After fabric should be cooled to 60 DEG C once, should once be washed after the completion of cooling.
8. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: the step 8 is specific
--- padding finishing agent --- infrared ray central drying short --- sizing of process are as follows: loose-drying.
9. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: make in the step 7
Coloring agent includes 100% powdery disperse dark blue HGL7.2%(o.w.f), 100% powdery disperse orange S-4RL2.5%(o.w.f) and
100% powdery Disperse Rubine S-2GFL 7.2%(o.w.f).
10. a kind of dyeing of full Terylene chiffon cloth according to claim 1, it is characterised in that: in the finishing agent
Added with softening agent and fluorine-containing water repellent.