CN109337455A - A kind of production method of aqueous temperature-sensitive skin texture paint - Google Patents
A kind of production method of aqueous temperature-sensitive skin texture paint Download PDFInfo
- Publication number
- CN109337455A CN109337455A CN201810922289.0A CN201810922289A CN109337455A CN 109337455 A CN109337455 A CN 109337455A CN 201810922289 A CN201810922289 A CN 201810922289A CN 109337455 A CN109337455 A CN 109337455A
- Authority
- CN
- China
- Prior art keywords
- proportion
- parts
- ordor removing
- agent
- ordor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of aqueous temperature-sensitive skin texture paint, successively deionized water is added in dispersion cylinder under stirring and sequentially adds the antifreeze wetting agent of ordor removing under stirring, ordor removing dispersing agent, first part of composite anti-foaming agent, inorganic thickening agent, titanium dioxide, calcined kaolin, temperature-sensitive powder, negative ion powder, coarse whiting, higher boiling ordor removing film forming agent, ordor removing is without ammonia PH regulator, ordor removing pure-acrylic emulsion, inorganic setting agent, second part of composite anti-foaming agent, ordor removing environment-friendly composite Antisepticize and mildew preventive, the mould proof imitative algae agent of ordor removing；It is uniform with high-speed stirred on dispersion machine, to obtain 100 parts of aqueous temperature-sensitive skin texture paint.
Description
Technical field
The present invention relates to a kind of production methods of aqueous temperature-sensitive skin texture paint.
Background technique
Aqueous temperature-sensitive skin texture paint solidifiable forms the skin texture paint film with temperature effect, is wall decoration material emerging at present
Material, since its plasticity is strong, can make metope show unique stereoscopic effect, make the more aobvious fashion of metope, beautiful, to make
It receives the welcome of the majority of consumers.But the ordor removing effect and VOC content of skin texture paint film, which can not fully meet consumer, to be wanted
It asks.
Therefore, it is necessary to be further improved.
Summary of the invention
It is an object of the invention to overcome above-mentioned the shortcomings of the prior art, and provide a kind of aqueous temperature-sensitive skin texture paint
Production method can effectively reduce the penetrating odor and VOC content of skin texture wall film slurry.
The object of the present invention is achieved like this:
A kind of production method of aqueous temperature-sensitive skin texture paint, made of following steps；
Step 1: ingredient according to the weight ratio:
28-35 parts of ordor removing pure-acrylic emulsion,
15-20 parts of titanium dioxide,
2-5 parts of calcined kaolin,
15-25 parts of temperature-sensitive powder,
1-1.5 parts of negative ion powder,
4-8 parts of coarse whiting,
Ordor removing without 0.05-0.1 parts of ammonia PH regulator,
Antifreeze wetting agent 0.3-0.5 parts of ordor removing,
0.4-0.6 parts of ordor removing dispersing agent,
0.3-0.6 parts of composite anti-foaming agent,
0.2-0.3 parts of ordor removing environment-friendly composite Antisepticize and mildew preventive,
Mould proof 0.3-0.5 parts of the imitative algae agent of ordor removing,
1-1.5 parts of higher boiling ordor removing film forming agent,
Inorganic setting agent 0.3-0.6 parts,
0.2-0.5 parts of inorganic thickening agent,
15-20 parts of deionized water；
The antifreeze wetting agent of ordor removing is sequentially added under stirring Step 2: deionized water is added in dispersion cylinder, ordor removing dispersion
Agent, first part of composite anti-foaming agent, inorganic thickening agent, titanium dioxide, calcined kaolin, temperature-sensitive powder, negative ion powder, coarse whiting, higher boiling
Ordor removing film forming agent, ordor removing is without ammonia PH regulator, ordor removing pure-acrylic emulsion, inorganic setting agent, second part of composite anti-foaming agent, ordor removing environmental protection
Composite anti-corrosion mould inhibitor, the mould proof imitative algae agent of ordor removing；
Step 3: it is uniform with high-speed stirred on dispersion machine, to obtain 100 parts of aqueous temperature-sensitive skin texture paint.
The proportion of deionized water in the step 2 is 16.1 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.3, ordor removing point
The proportion of powder is 0.4 part, and the proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of inorganic thickening agent is 0.48 part, titanium
The proportion of white powder is 17 parts, and the proportion of calcined kaolin is 4 parts, and the proportion of temperature-sensitive powder is 20 parts, and the proportion of negative ion powder is 1.5
Part, the proportion of coarse whiting is 6.3 parts, and the proportion of higher boiling ordor removing film forming agent is 1.2 parts, and proportion of the ordor removing without ammonia PH regulator is
0.1 part, the proportion of ordor removing pure-acrylic emulsion is 31 parts, and the proportion of inorganic setting agent is 0.42 part, and second part of composite anti-foaming agent is matched
Than being 0.25 part, the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.25 part, and the proportion of the mould proof imitative algae agent of ordor removing is 0.45
Part.
The proportion of deionized water in the step 2 is 19.29 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.3, ordor removing
The proportion of dispersing agent is 0.5 part, and the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of inorganic thickening agent is 0.4, titanium white
The proportion of powder is 18 parts, and the proportion of calcined kaolin is 2.5 parts, and the proportion of temperature-sensitive powder is 16 parts, and the proportion of negative ion powder is 1.2
Part, the proportion of coarse whiting is 6.75 parts, and the proportion of higher boiling ordor removing film forming agent is 1.3 parts, and proportion of the ordor removing without ammonia PH regulator is
0.06 part, the proportion of ordor removing pure-acrylic emulsion is 32 parts, and the proportion of inorganic setting agent is 0.5 part, and second part of composite anti-foaming agent is matched
Than being 0.3 part, the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.2 part, and the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part.
The proportion of deionized water in the step 2 is 18.4 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.4, ordor removing point
The proportion of powder is 0.6 part, and the proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of inorganic thickening agent is 0.3 part, titanium white
The proportion of powder is 20 parts, and the proportion of calcined kaolin is 3.5 parts, and the proportion of temperature-sensitive powder is 18 parts, and the proportion of negative ion powder is 1
Part, the proportion of coarse whiting is 5 parts, and the proportion of higher boiling ordor removing film forming agent is 1.2 parts, and proportion of the ordor removing without ammonia PH regulator is 0.05
Part, the proportion of ordor removing pure-acrylic emulsion is 29.95 parts, and the proportion of inorganic setting agent is 0.4 part, the proportion of second part of composite anti-foaming agent
It is 0.3 part, the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.25 part, and the proportion of the mould proof imitative algae agent of ordor removing is 0.4 part.
The proportion of deionized water in the step 2 is 16.22 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.5, ordor removing
The proportion of dispersing agent is 0.5 part, and the proportion of first part of composite anti-foaming agent is 0.3 part, and the proportion of inorganic thickening agent is 0.4 part, titanium
The proportion of white powder is 18 parts, and the proportion of calcined kaolin is 2.3 parts, and the proportion of temperature-sensitive powder is 22 parts, and the proportion of negative ion powder is
1.2 parts, the proportion of coarse whiting is 5.5 parts, and the proportion of higher boiling ordor removing film forming agent is 1.5 parts, proportion of the ordor removing without ammonia PH regulator
It is 0.08 part, the proportion of ordor removing pure-acrylic emulsion is 30.05 parts, and the proportion of inorganic setting agent is 0.35 part, second part of compound defoaming
The proportion of agent is 0.3 part, and the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.3 part, and the proportion of the mould proof imitative algae agent of ordor removing is
0.5 part.
The proportion of deionized water in the step 2 is 17.95 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.4, ordor removing
The proportion of dispersing agent is 0.5 part, and the proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of inorganic thickening agent is 0.45 part,
The proportion of titanium dioxide is 15 parts, and the proportion of calcined kaolin is 5 parts, and the proportion of temperature-sensitive powder is 25 parts, and the proportion of negative ion powder is
1.1 parts, the proportion of coarse whiting is 4 parts, and the proportion of higher boiling ordor removing film forming agent is 1 part, and proportion of the ordor removing without ammonia PH regulator is
0.07 part, the proportion of ordor removing pure-acrylic emulsion is 28 parts, and the proportion of inorganic setting agent is 0.3 part, and second part of composite anti-foaming agent is matched
Than being 0.3 part, the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.2 part, and the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part.
The beneficial effects of the present invention are:
The penetrating odor that skin texture paint can be effectively reduced by the aqueous temperature-sensitive skin texture paint that this manufacturing method manufactures, reaches ordor removing
Effect, while VOC content is further decreased, reach to become zero releasing effect, skin texture paint also has antimildew and antibacterial effect.
Specific embodiment
The present invention will be further described below with reference to examples.
First embodiment
The production method of this aqueous temperature-sensitive skin texture paint, made of following steps；
Step 1: ingredient according to the weight ratio:
28-35 parts of ordor removing pure-acrylic emulsion,
15-20 parts of titanium dioxide,
2-5 parts of calcined kaolin,
15-25 parts of temperature-sensitive powder,
1-1.5 parts of negative ion powder,
4-8 parts of coarse whiting,
Ordor removing without 0.05-0.1 parts of ammonia PH regulator,
Antifreeze wetting agent 0.3-0.5 parts of ordor removing,
0.4-0.6 parts of ordor removing dispersing agent,
0.3-0.6 parts of composite anti-foaming agent,
0.2-0.3 parts of ordor removing environment-friendly composite Antisepticize and mildew preventive,
Mould proof 0.3-0.5 parts of the imitative algae agent of ordor removing,
1-1.5 parts of higher boiling ordor removing film forming agent,
Inorganic setting agent 0.3-0.6 parts,
0.2-0.5 parts of inorganic thickening agent,
15-20 parts of deionized water；
The antifreeze wetting agent of ordor removing is sequentially added under stirring Step 2: deionized water is added in dispersion cylinder, ordor removing dispersion
Agent, first part of composite anti-foaming agent, inorganic thickening agent, titanium dioxide, calcined kaolin, temperature-sensitive powder, negative ion powder, coarse whiting, higher boiling
Ordor removing film forming agent, ordor removing is without ammonia PH regulator, ordor removing pure-acrylic emulsion, inorganic setting agent, second part of composite anti-foaming agent, ordor removing environmental protection
Composite anti-corrosion mould inhibitor, the mould proof imitative algae agent of ordor removing；
Step 3: it is uniform with high-speed stirred on dispersion machine, to obtain 100 parts of aqueous temperature-sensitive skin texture paint；
Ordor removing pure-acrylic emulsion makes this skin texture paint paint film generated have preferable weatherability and water resistance, simultaneously as lotion is added
It is big that amount compares the prior art, to ensure that paint film has better elasticity；
Ordor removing does not distribute organic amine taste without ammonia PH regulator, and has dispersion moistening, while increasing the scrub resistance of paint film；
The antifreeze wetting agent of ordor removing both guarantees dispersion moistening, while using this aqueous temperature-sensitive skin texture paint when can reduce solvent such as second
Glycol, the addition of propandiols；
Higher boiling ordor removing film forming agent can reduce VOC content；
Ordor removing environment-friendly composite Antisepticize and mildew preventive fundamentally reduces the content of formaldehyde, while guaranteeing the mildew resistance of paint film；
The mould proof imitative algae agent of ordor removing makes dry paint will not the long algae of mildew under rugged environment；
Powder titanium dioxide therein, calcined kaolin, temperature-sensitive powder and negative ion powder are free of heavy metal, wherein titanium dioxide and calcining
Kaolin had both guaranteed the covering power of paint film, the richness of guaranteed paint film, while calcining the suspension that high territory also guarantees coating,
Temperature-sensitive powder is being node with 18 DEG C -31 DEG C, the color variation with temperature of paint film and change, face when relative temperature is lower
Color is deeper, and color is simple more and elegant when relative temperature is higher, while playing the role of filling, toning, and anion is in medical field
It is known as " air vitamin ", the addition of negative ion powder can make paint film long-term negative ion release, people is allowed more to have good health and a long life；
The addition of coarse whiting further increases the hardness and weatherability of paint film in addition to increasing fillibility；
Inorganic setting agent had both guaranteed the feature of environmental protection of coating, in turn ensured the formative nature of paint film texture.
Further, the proportion of the deionized water in step 2 is 16.1 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.3,
The proportion of ordor removing dispersing agent is 0.4 part, and the proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of inorganic thickening agent is 0.48
Part, the proportion of titanium dioxide is 17 parts, and the proportion of calcined kaolin is 4 parts, and the proportion of temperature-sensitive powder is 20 parts, the proportion of negative ion powder
It is 1.5 parts, the proportion of coarse whiting is 6.3 parts, and the proportion of higher boiling ordor removing film forming agent is 1.2 parts, and ordor removing is matched without ammonia PH regulator
Than being 0.1 part, the proportion of ordor removing pure-acrylic emulsion is 31 parts, and the proportion of inorganic setting agent is 0.42 part, second part of composite anti-foaming agent
Proportion be 0.25 part, the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.25 part, and the proportion of the mould proof imitative algae agent of ordor removing is
0.45 part, obtained skin texture wall film can achieve 5000 circulation color changeable effects.
Second embodiment
The present embodiment and first embodiment the difference is that: in two the step of the production method of this aqueous temperature-sensitive skin texture paint
The proportion of deionized water is 19.29 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.3, and the proportion of ordor removing dispersing agent is 0.5 part, the
The proportion of a composite anti-foaming agent is 0.2 part, and the proportion of inorganic thickening agent is 0.4, and the proportion of titanium dioxide is 18 parts, calcines kaolinite
The proportion of soil is 2.5 parts, and the proportion of temperature-sensitive powder is 16 parts, and the proportion of negative ion powder is 1.2 parts, and the proportion of coarse whiting is 6.75 parts,
The proportion of higher boiling ordor removing film forming agent is 1.3 parts, and proportion of the ordor removing without ammonia PH regulator is 0.06 part, and ordor removing pure-acrylic emulsion is matched
Than being 32 parts, the proportion of inorganic setting agent is 0.5 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, ordor removing environment-friendly composite
The proportion of Antisepticize and mildew preventive is 0.2 part, and the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part, and obtained skin texture wall film can achieve
3500 circulation color changeable effects.
Remaining does not describe the same first embodiment in part, is not repeated herein.
3rd embodiment
The present embodiment and first embodiment the difference is that: in two the step of the production method of this aqueous temperature-sensitive skin texture paint
The proportion of deionized water is 18.4 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.4, and the proportion of ordor removing dispersing agent is 0.6 part, first
The proportion of part composite anti-foaming agent is 0.25 part, and the proportion of inorganic thickening agent is 0.3 part, and the proportion of titanium dioxide is 20 parts, calcining height
The proportion of ridge soil is 3.5 parts, and the proportion of temperature-sensitive powder is 18 parts, and the proportion of negative ion powder is 1 part, and the proportion of coarse whiting is 5 parts, high boiling
The proportion of point ordor removing film forming agent is 1.2 parts, and proportion of the ordor removing without ammonia PH regulator is 0.05 part, and the proportion of ordor removing pure-acrylic emulsion is
29.95 parts, the proportion of inorganic setting agent is 0.4 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, ordor removing environment-friendly composite
The proportion of Antisepticize and mildew preventive is 0.25 part, and the proportion of the mould proof imitative algae agent of ordor removing is 0.4 part, and obtained skin texture wall film can achieve
4000 circulation color changeable effects.
Remaining does not describe the same first embodiment in part, is not repeated herein.
Fourth embodiment
The present embodiment and first embodiment the difference is that: the proportion of the deionized water in this step 2 be 16.22 parts, only
The proportion of the antifreeze wetting agent of taste is 0.5, and the proportion of ordor removing dispersing agent is 0.5 part, and the proportion of first part of composite anti-foaming agent is 0.3
Part, the proportion of inorganic thickening agent is 0.4 part, and the proportion of titanium dioxide is 18 parts, and the proportion of calcined kaolin is 2.3 parts, temperature-sensitive powder
Proportion be 22 parts, the proportion of negative ion powder is 1.2 parts, and the proportion of coarse whiting is 5.5 parts, and the proportion of higher boiling ordor removing film forming agent is
1.5 parts, proportion of the ordor removing without ammonia PH regulator is 0.08 part, and the proportion of ordor removing pure-acrylic emulsion is 30.05 parts, inorganic setting agent
Proportion is 0.35 part, and the proportion of second part of composite anti-foaming agent is 0.3 part, and the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is
0.3 part, the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part, and obtained skin texture wall film can achieve 5300 circulation color changeable effects.
Remaining does not describe the same first embodiment in part, is not repeated herein.
5th embodiment
The present embodiment and first embodiment the difference is that: the proportion of the deionized water in this step 2 be 17.95 parts, only
The proportion of the antifreeze wetting agent of taste is 0.4, and the proportion of ordor removing dispersing agent is 0.5 part, and the proportion of first part of composite anti-foaming agent is 0.25
Part, the proportion of inorganic thickening agent is 0.45 part, and the proportion of titanium dioxide is 15 parts, and the proportion of calcined kaolin is 5 parts, temperature-sensitive powder
Proportion is 25 parts, and the proportion of negative ion powder is 1.1 parts, and the proportion of coarse whiting is 4 parts, and the proportion of higher boiling ordor removing film forming agent is 1 part,
Proportion of the ordor removing without ammonia PH regulator is 0.07 part, and the proportion of ordor removing pure-acrylic emulsion is 28 parts, and the proportion of inorganic setting agent is 0.3
Part, the proportion of second part of composite anti-foaming agent is 0.3 part, and the proportion of ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.2 part, and ordor removing is anti-
The proportion of mould imitative algae agent is 0.5 part, and obtained skin texture wall film can achieve 6000 circulation color changeable effects.
Remaining does not describe the same first embodiment in part, is not repeated herein.
The present invention aqueous temperature-sensitive skin texture paint produced is constructed from can opening to upper wall, then accomplishes real ordor removing to moving in；
Pure C is wherein selected to guarantee the weatherability and water resistance of paint film, simultaneously as lotion additive amount is bigger, to ensure that paint film
There is certain elasticity；The ordor removing wherein selected does not distribute organic amine taste without ammonia PH regulator, and has dispersion moistening, simultaneously
Increase the scrub resistance of film；The antifreeze wetting agent of the ordor removing of selection both guarantees dispersion moistening, while reducing solvent such as ethylene glycol,
The addition of propandiols；Select higher boiling ordor removing film forming agent that can reduce VOC content；Select ordor removing environment-friendly composite anticorrosive mildewproof
Agent, fundamentally reduces the content of formaldehyde, while guaranteeing the mildew resistance of paint film；The mould proof imitative algae agent of ordor removing is selected, so that dry paint
Under rugged environment will not the long algae of mildew, selected powder is free of heavy metal, and wherein titanium dioxide and calcined kaolin be both
Guarantee the covering power of paint film, the richness of guaranteed paint film, while calcining the suspension that high territory also guarantees coating；Temperature-sensitive powder exists
Be node with 18 DEG C -31 DEG C, the color variation with temperature of paint film and change, it is darker when relative temperature is lower
Thickness, color is simple more and elegant when relative temperature is higher, while playing the role of filling, toning；Anion is referred to as in medical field
It is " air vitamin " that the addition of negative ion powder can make paint film long-term negative ion release, achieve the purpose that fresh air；Allow people
It more has good health and a long life, the addition of coarse whiting further increases the hardness and weatherability of paint film in addition to increasing fillibility, and it is inorganic fixed to select
Type agent had both guaranteed the feature of environmental protection of coating, in turn ensured the formative nature of paint film texture.
Above-described embodiment is preferred embodiment of the invention, and the present invention can also have other embodiments.The technology of this field
Personnel can also make equivalent deformation or replacement on the premise of without prejudice to spirit of the invention, these equivalent variation or replacement are wrapped
It is contained in range set by the claim of this application.
Claims (6)
1. a kind of production method of aqueous temperature-sensitive skin texture paint, which is characterized in that made of following steps；
Step 1: ingredient according to the weight ratio:
28-35 parts of ordor removing pure-acrylic emulsion,
15-20 parts of titanium dioxide,
2-5 parts of calcined kaolin,
15-25 parts of temperature-sensitive powder,
1-1.5 parts of negative ion powder,
4-8 parts of coarse whiting,
Ordor removing without 0.05-0.1 parts of ammonia PH regulator,
Antifreeze wetting agent 0.3-0.5 parts of ordor removing,
0.4-0.6 parts of ordor removing dispersing agent,
0.3-0.6 parts of composite anti-foaming agent,
0.2-0.3 parts of ordor removing environment-friendly composite Antisepticize and mildew preventive,
Mould proof 0.3-0.5 parts of the imitative algae agent of ordor removing,
1-1.5 parts of higher boiling ordor removing film forming agent,
Inorganic setting agent 0.3-0.6 parts,
0.2-0.5 parts of inorganic thickening agent,
15-20 parts of deionized water；
The antifreeze wetting agent of ordor removing is sequentially added under stirring Step 2: deionized water is added in dispersion cylinder, ordor removing dispersion
Agent, first part of composite anti-foaming agent, inorganic thickening agent, titanium dioxide, calcined kaolin, temperature-sensitive powder, negative ion powder, coarse whiting, higher boiling
Ordor removing film forming agent, ordor removing is without ammonia PH regulator, ordor removing pure-acrylic emulsion, inorganic setting agent, second part of composite anti-foaming agent, ordor removing environmental protection
Composite anti-corrosion mould inhibitor, the mould proof imitative algae agent of ordor removing；
Step 3: it is uniform with high-speed stirred on dispersion machine, to obtain 100 parts of aqueous temperature-sensitive skin texture paint.
2. the production method of aqueous temperature-sensitive skin texture paint according to claim 1, it is characterised in that: in the step 2 go from
The proportion of sub- water is 16.1 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.3, and the proportion of the ordor removing dispersing agent is 0.4 part,
The proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of the inorganic thickening agent is 0.48 part, the titanium dioxide
Proportion is 17 parts, and the proportion of the calcined kaolin is 4 parts, and the proportion of the temperature-sensitive powder is 20 parts, and the negative ion powder is matched
Than being 1.5 parts, the proportion of the coarse whiting is 6.3 parts, and the proportion of the higher boiling ordor removing film forming agent is 1.2 parts, the ordor removing without
The proportion of ammonia PH regulator is 0.1 part, and the proportion of the ordor removing pure-acrylic emulsion is 31 parts, and the proportion of the inorganic setting agent is
0.42 part, the proportion of second part of composite anti-foaming agent is 0.25 part, the proportion of the ordor removing environment-friendly composite Antisepticize and mildew preventive
It is 0.25 part, the proportion of the mould proof imitative algae agent of ordor removing is 0.45 part.
3. the production method of aqueous temperature-sensitive skin texture paint according to claim 1, it is characterised in that: in the step 2 go from
The proportion of sub- water is 19.29 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.3, and the proportion of the ordor removing dispersing agent is 0.5
Part, the proportion of first part of composite anti-foaming agent is 0.2 part, and the proportion of the inorganic thickening agent is 0.4, and the titanium dioxide is matched
Than being 18 parts, the proportion of the calcined kaolin is 2.5 parts, and the proportion of the temperature-sensitive powder is 16 parts, and the negative ion powder is matched
Than being 1.2 parts, the proportion of the coarse whiting is 6.75 parts, and the proportion of the higher boiling ordor removing film forming agent is 1.3 parts, the ordor removing without
The proportion of ammonia PH regulator is 0.06 part, and the proportion of the ordor removing pure-acrylic emulsion is 32 parts, and the proportion of the inorganic setting agent is
0.5 part, the proportion of second part of composite anti-foaming agent is 0.3 part, and the proportion of the ordor removing environment-friendly composite Antisepticize and mildew preventive is
0.2 part, the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part.
4. the production method of aqueous temperature-sensitive skin texture paint according to claim 1, it is characterised in that: in the step 2 go from
The proportion of sub- water is 18.4 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.4, and the proportion of the ordor removing dispersing agent is 0.6 part,
The proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of the inorganic thickening agent is 0.3 part, and the titanium dioxide is matched
Than being 20 parts, the proportion of the calcined kaolin is 3.5 parts, and the proportion of the temperature-sensitive powder is 18 parts, and the negative ion powder is matched
Than being 1 part, the proportion of the coarse whiting is 5 parts, and the proportion of the higher boiling ordor removing film forming agent is 1.2 parts, and the ordor removing is without ammonia PH
The proportion of regulator is 0.05 part, and the proportion of the ordor removing pure-acrylic emulsion is 29.95 parts, and the proportion of the inorganic setting agent is
0.4 part, the proportion of second part of composite anti-foaming agent is 0.3 part, and the proportion of the ordor removing environment-friendly composite Antisepticize and mildew preventive is
0.25 part, the proportion of the mould proof imitative algae agent of ordor removing is 0.4 part.
5. the production method of aqueous temperature-sensitive skin texture paint according to claim 1, it is characterised in that: in the step 2 go from
The proportion of sub- water is 16.22 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.5, and the proportion of the ordor removing dispersing agent is 0.5
Part, the proportion of first part of composite anti-foaming agent is 0.3 part, and the proportion of the inorganic thickening agent is 0.4 part, the titanium dioxide
Proportion is 18 parts, and the proportion of the calcined kaolin is 2.3 parts, and the proportion of the temperature-sensitive powder is 22 parts, the negative ion powder
Proportion is 1.2 parts, and the proportion of the coarse whiting is 5.5 parts, and the proportion of the higher boiling ordor removing film forming agent is 1.5 parts, the ordor removing
The proportion of no ammonia PH regulator is 0.08 part, and the proportion of the ordor removing pure-acrylic emulsion is 30.05 parts, and the inorganic setting agent is matched
Than being 0.35 part, the proportion of second part of composite anti-foaming agent is 0.3 part, and the ordor removing environment-friendly composite Antisepticize and mildew preventive is matched
Than being 0.3 part, the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part.
6. the production method of aqueous temperature-sensitive skin texture paint according to claim 1, it is characterised in that: in the step 2 go from
The proportion of sub- water is 17.95 parts, and the proportion of the antifreeze wetting agent of ordor removing is 0.4, and the proportion of the ordor removing dispersing agent is 0.5
Part, the proportion of first part of composite anti-foaming agent is 0.25 part, and the proportion of the inorganic thickening agent is 0.45 part, the titanium dioxide
Proportion be 15 parts, the proportion of the calcined kaolin is 5 parts, and the proportion of the temperature-sensitive powder is 25 parts, the negative ion powder
Proportion is 1.1 parts, and the proportion of the coarse whiting is 4 parts, and the proportion of the higher boiling ordor removing film forming agent is 1 part, and the ordor removing is without ammonia
The proportion of PH regulator is 0.07 part, and the proportion of the ordor removing pure-acrylic emulsion is 28 parts, and the proportion of the inorganic setting agent is 0.3
Part, the proportion of second part of composite anti-foaming agent is 0.3 part, and the proportion of the ordor removing environment-friendly composite Antisepticize and mildew preventive is 0.2
Part, the proportion of the mould proof imitative algae agent of ordor removing is 0.5 part.