CN105238273A - Nanometer composite wall coating - Google Patents
Nanometer composite wall coating Download PDFInfo
- Publication number
- CN105238273A CN105238273A CN201510610527.0A CN201510610527A CN105238273A CN 105238273 A CN105238273 A CN 105238273A CN 201510610527 A CN201510610527 A CN 201510610527A CN 105238273 A CN105238273 A CN 105238273A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- nano
- defoamer
- wallcovering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a nanometer composite wall coating. The coating is composed of the following materials by mass: 100 to 150 parts of calcined kaolin, 250 to 300 parts of nanometer calcium carbonate, 20 to 80 parts of active shell powder, 10 to 20 parts of a nanometer additive, 150 to 250 parts of emulsion, 300 to 340 parts of pure water, 1 to 10 parts of a dispersing agent, 1 to 10 parts of a wetting agent, 2 to 3 parts of special cellulose, 2 to 6 parts of a nanometer suspended thickening agent, 0.2 to 0.8 part of a defoaming agent, 2 to 8 parts of propylene glycol, 40 to 60 parts of titanium dioxide, 10 to 20 parts of a film forming additive, 0.2 to 0.4 part of a defoaming agent, 1 to 2 parts of an anticorrosion and bactericidal agent, 1 to 3 parts of a multifunctional additive AMP-95, 1 to 2 parts of a fluorescent whitening agent and 1 to 3 parts of a thickening agent. The coating provided by the invention improves water resistance, alkali resistance, washing and scrubbing resistance, stain resistance and weather resistance of an emulsion coating layer, effectively prevents concrete from carbonation and protects wall of a building while improving decorative features.
Description
Technical field
The present invention relates to a kind of nano combined wallcovering, belong to technical field of coatings.
Background technology
Wallcovering refers to and plays decoration and protection for building wall, makes building wall beautiful and clean, simultaneously also can play architecture protection metope, extend the effect in its work-ing life.Wallcovering comprises interior wall coating and exterior coating two parts by building wall classification.Interior wall coating focuses on decoration and environmental protection; Exterior coating focus on protection and durable.
Summary of the invention
The object of the present invention is to provide a kind of nano combined wallcovering, to improve the result of use of wallcovering better, conveniently use coating as required.
To achieve these goals, technical scheme of the present invention is as follows.
A kind of nano combined wallcovering, be made up of the material of following mass fraction: calcined kaolin 100 ~ 150 parts, nano-calcium carbonate 250 ~ 300 parts, active oyster shell whiting 20 ~ 80 parts, nano assistant 10 ~ 20 parts, emulsion 150 ~ 250 parts, pure water 300 ~ 340 parts, dispersion agent 1 ~ 10 part, wetting agent 1 ~ 10 part, special cellulose 2 ~ 3 parts, nanoparticle suspension thickening material 2 ~ 6 parts, defoamer 0.2 ~ 0.8 part, propylene glycol 2 ~ 8 parts, titanium dioxide 40 ~ 60 parts, film coalescence aid 10 ~ 20 parts, defoamer 0.2 ~ 0.4 part, anticorrosion and bactericidal agent 1 ~ 2 part, AMP-95 multifunctional assistant 1 ~ 3 part, white dyes 1 ~ 2 part, thickening material 1 ~ 3 part.
Further, above-mentioned nano combined wallcovering, is made up of the material of following mass fraction: calcined kaolin 100 parts, nano-calcium carbonate 250 parts, active oyster shell whiting 20 parts, nano assistant 10 parts, emulsion 150 parts, pure water 300 parts, dispersion agent 1 part, wetting agent 1 part, special cellulose 2 parts, nanoparticle suspension thickening material 2 parts, defoamer 0.2 part, propylene glycol 2 parts, titanium dioxide 40 parts, film coalescence aid 10 parts, defoamer 0.2 part, anticorrosion and bactericidal agent 1 part, AMP-95 multifunctional assistant 1 part, white dyes 1 part; Thickening material 1 part.
Further, above-mentioned nano combined wallcovering, is made up of the material of following mass fraction: calcined kaolin 150 parts, nano-calcium carbonate 300 parts, active oyster shell whiting 80 parts, nano assistant 20 parts, emulsion 250 parts, pure water 340 parts, dispersion agent 10 parts, wetting agent 10 parts, special cellulose 3 parts, nanoparticle suspension thickening material 6 parts, defoamer 0.8 part, propylene glycol 8 parts, titanium dioxide 60 parts, film coalescence aid 20 parts, defoamer 0.4 part, anticorrosion and bactericidal agent 2 parts, AMP-95 multifunctional assistant 3 parts, white dyes 2 parts; Thickening material 3 parts.
Further, above-mentioned nano combined wallcovering, is made up of the material of following mass fraction: calcined kaolin 125 parts, nano-calcium carbonate 275 parts, active oyster shell whiting 50 parts, nano assistant 15 parts, emulsion 175 parts, pure water 320 parts, dispersion agent 5 parts, wetting agent 5 parts, special cellulose 2.5 parts, nanoparticle suspension thickening material 4 parts, defoamer 0.5 part, propylene glycol 5 parts, titanium dioxide 50 parts, film coalescence aid 15 parts, defoamer 0.3 part, anticorrosion and bactericidal agent 1.5, AMP-95 multifunctional assistant 2 parts, white dyes 1.5 parts; Thickening material 2 parts.
Further, above-mentioned nano combined wallcovering, its preparation method is, is fully mixed by above-mentioned material, stirs.
This beneficial effect of the invention is: coating of the present invention improves water tolerance, alkali resistance, scrub resistance, contamination resistance, the weathering resistance of emulsion paint coating, effectively prevent concrete carbonization, improving ornamental while, and the body of wall of architecture protection thing.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
embodiment 1
Nano combined wallcovering in the present embodiment, is made up of the material of following mass fraction: calcined kaolin 100 parts, nano-calcium carbonate 250 parts, active oyster shell whiting 20 parts, nano assistant 10 parts, emulsion 150 parts, pure water 300 parts, dispersion agent 1 part, wetting agent 1 part, special cellulose 2 parts, nanoparticle suspension thickening material 2 parts, defoamer 0.2 part, propylene glycol 2 parts, titanium dioxide 40 parts, film coalescence aid 10 parts, defoamer 0.2 part, anticorrosion and bactericidal agent 1 part, AMP-95 multifunctional assistant 1 part, white dyes 1 part; Thickening material 1 part.Above-mentioned nano combined wallcovering, its preparation method is, is fully mixed by above-mentioned material, stirs.
embodiment 2
Nano combined wallcovering in the present embodiment, is made up of the material of following mass fraction: calcined kaolin 150 parts, nano-calcium carbonate 300 parts, active oyster shell whiting 80 parts, nano assistant 20 parts, emulsion 250 parts, pure water 340 parts, dispersion agent 10 parts, wetting agent 10 parts, special cellulose 3 parts, nanoparticle suspension thickening material 6 parts, defoamer 0.8 part, propylene glycol 8 parts, titanium dioxide 60 parts, film coalescence aid 20 parts, defoamer 0.4 part, anticorrosion and bactericidal agent 2 parts, AMP-95 multifunctional assistant 3 parts, white dyes 2 parts; Thickening material 3 parts.Above-mentioned nano combined wallcovering, its preparation method is, is fully mixed by above-mentioned material, stirs.
embodiment 3
Nano combined wallcovering in the present embodiment, be made up of the material of following mass fraction: calcined kaolin 125 parts, nano-calcium carbonate 275 parts, active oyster shell whiting 50 parts, nano assistant 15 parts, emulsion 175 parts, pure water 320 parts, dispersion agent 5 parts, wetting agent 5 parts, special cellulose 2.5 parts, nanoparticle suspension thickening material 4 parts, defoamer 0.5 part, propylene glycol 5 parts, titanium dioxide 50 parts, film coalescence aid 15 parts, defoamer 0.3 part, anticorrosion and bactericidal agent 1.5, AMP-95 multifunctional assistant 2 parts, white dyes 1.5 parts; Thickening material 2 parts.Above-mentioned nano combined wallcovering, its preparation method is, is fully mixed by above-mentioned material, stirs.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (4)
1. a nano combined wallcovering, it is characterized in that: be made up of the material of following mass fraction: calcined kaolin 100 ~ 150 parts, nano-calcium carbonate 250 ~ 300 parts, active oyster shell whiting 20 ~ 80 parts, nano assistant 10 ~ 20 parts, emulsion 150 ~ 250 parts, pure water 300 ~ 340 parts, dispersion agent 1 ~ 10 part, wetting agent 1 ~ 10 part, special cellulose 2 ~ 3 parts, nanoparticle suspension thickening material 2 ~ 6 parts, defoamer 0.2 ~ 0.8 part, propylene glycol 2 ~ 8 parts, titanium dioxide 40 ~ 60 parts, film coalescence aid 10 ~ 20 parts, defoamer 0.2 ~ 0.4 part, anticorrosion and bactericidal agent 1 ~ 2 part, AMP-95 multifunctional assistant 1 ~ 3 part, white dyes 1 ~ 2 part, thickening material 1 ~ 3 part.
2. nano combined wallcovering according to claim 1, it is characterized in that: described nano combined wallcovering, be made up of the material of following mass fraction: calcined kaolin 100 parts, nano-calcium carbonate 250 parts, active oyster shell whiting 20 parts, nano assistant 10 parts, emulsion 150 parts, pure water 300 parts, dispersion agent 1 part, wetting agent 1 part, special cellulose 2 parts, nanoparticle suspension thickening material 2 parts, defoamer 0.2 part, propylene glycol 2 parts, titanium dioxide 40 parts, film coalescence aid 10 parts, defoamer 0.2 part, anticorrosion and bactericidal agent 1 part, AMP-95 multifunctional assistant 1 part, white dyes 1 part, thickening material 1 part.
3. nano combined wallcovering according to claim 1, it is characterized in that: described nano combined wallcovering, be made up of the material of following mass fraction: calcined kaolin 150 parts, nano-calcium carbonate 300 parts, active oyster shell whiting 80 parts, nano assistant 20 parts, emulsion 250 parts, pure water 340 parts, dispersion agent 10 parts, wetting agent 10 parts, special cellulose 3 parts, nanoparticle suspension thickening material 6 parts, defoamer 0.8 part, propylene glycol 8 parts, titanium dioxide 60 parts, film coalescence aid 20 parts, defoamer 0.4 part, anticorrosion and bactericidal agent 2 parts, AMP-95 multifunctional assistant 3 parts, white dyes 2 parts, thickening material 3 parts.
4. nano combined wallcovering according to claim 1, it is characterized in that: described nano combined wallcovering, be made up of the material of following mass fraction: calcined kaolin 125 parts, nano-calcium carbonate 275 parts, active oyster shell whiting 50 parts, nano assistant 15 parts, emulsion 175 parts, pure water 320 parts, dispersion agent 5 parts, wetting agent 5 parts, special cellulose 2.5 parts, nanoparticle suspension thickening material 4 parts, defoamer 0.5 part, propylene glycol 5 parts, titanium dioxide 50 parts, film coalescence aid 15 parts, defoamer 0.3 part, anticorrosion and bactericidal agent 1.5, AMP-95 multifunctional assistant 2 parts, white dyes 1.5 parts, thickening material 2 parts.