CN103602221A - Functional isolation wall paint and preparation method thereof - Google Patents
Functional isolation wall paint and preparation method thereof Download PDFInfo
- Publication number
- CN103602221A CN103602221A CN201310643220.1A CN201310643220A CN103602221A CN 103602221 A CN103602221 A CN 103602221A CN 201310643220 A CN201310643220 A CN 201310643220A CN 103602221 A CN103602221 A CN 103602221A
- Authority
- CN
- China
- Prior art keywords
- component
- mass parts
- mass
- divider wall
- finish paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a functional isolation wall paint and a preparation method thereof, and aims to provide the paint which not only has decorative effect, but also can isolate harmful substances of a building wall body and completely eradicate pathogenic bacteria propagation, and the preparation method thereof. The technical scheme is that the paint comprises an A component and a B component according to the mass ratio of 1:1; the A component is composed of a pulping stage A1 component and a paint mixing stage A2 component; the pulping stage A1 component is composed of 10-17 parts by mass of deionized water, 14-27 parts by mass of a filler, and 1.8-3 parts by mass of a NO.1 auxiliary agent; the paint mixing stage A2 component is composed of 38-60 parts by mass of waterborne epoxy resin, 10-13 parts by mass of a pure acrylic emulsion, 3 parts by mass of a reactive diluent, and 0.3-0.4 part by mass of a defoaming agent; the B component is composed of 21-33 parts by mass of a waterborne curing agent, 44-51 parts by mass of a pigment filler, 20.6-26.1 parts by mass of deionized water, and 1.9-2.7 parts by mass of a NO.2 auxiliary agent. The functional isolation wall paint and the preparation method thereof belong to the field of coating technology.
Description
Technical field
The present invention discloses a kind of coating, specifically, is a kind of functional divider wall finish paint, and the present invention also discloses the preparation method of this wall paint, belongs to technical field of coatings.
Background technology
People spend indoor average nearly more than 80% time of every day.Modernization more along with production and mode of life, more work and sports entertainment all can carry out indoor, shopping also needn't be gone into the street every day, suitable indoor microclimate makes people needn't often to open air, go to regulate heat effect, like this, people's the indoor activity time is just more, even up to more than 93%.Therefore, IAQ (indoor air quality) just seems more closely more important to the relation of HUMAN HEALTH.
Although the concentration of indoor pollutant is often lower, because duration of contact is very long, therefore its accumulation Exposure is very high.The weak crowd such as especially old, young, sick, Abwehrkraft des Koepers are lower, outdoors chance still less, therefore, the quality of IAQ (indoor air quality) and their relation are particularly important.
Room air pollution refers to that in the room air causing due to a variety of causes, objectionable impurities exceeds standard, and then affects the indoor environmental pollution behavior of HUMAN HEALTH.Nuisance comprises formaldehyde, benzene, ammonia, radioactive radon etc.These nuisance overwhelming majority are in the middle of material of construction, cement brick wall, wall surface putty, ceramic tile etc., this invention provides a kind of functional divider wall finish paint, utilize its fine and close paint film effectively to isolate body of wall pollutent, and to germ, do not provide the environment that can grow, thereby improve the miniclimate of our living environment.
Summary of the invention
For the problems referred to above, the object of the present invention is to provide a kind ofly both there is decorative effect, objectionable impurities that again can separating building thing body of wall, stops functional divider wall finish paint of growing of germ and preparation method thereof.
Last technical scheme of the present invention is such: this functional divider wall finish paint, it is characterized in that, and A component and the B component of mass ratio 1:1, consist of, described A component is comprised of slurrying stage A 1 component and paint stage A 2;
Wherein:
Slurrying stage A 1 component is by 10-17 mass parts deionized water, 14-27 mass parts filler, and No. 1 auxiliary agent of 1.8-3 mass parts forms; No. 1 described auxiliary agent 0.3-1 mass parts emulsifying agent, 1.4-2 mass parts thickening material, 0.1 mass parts defoamer forms;
Paint stage A 2 components are by 38-60 mass parts aqueous epoxy resins; 10-13 mass parts pure-acrylic emulsion; 3 mass parts reactive thinners; 0.3-0.4 mass parts defoamer forms;
B component is by 21-33 mass parts waterborne curing agent; 44-51 mass parts color stuffing; 20.6-26.1 mass parts deionized water; No. 2 auxiliary agents of 1.9-2.7 mass parts; No. 2 described auxiliary agents are by 0.5-1 mass parts emulsifying agent, 0.3 mass parts wetting agent, and 0.1 mass parts dispersion agent, 0.5-1.8 mass parts defoamer forms.
Further, above-mentioned a kind of functional divider wall finish paint, described aqueous epoxy resins is bisphenol A-type aqueous epoxy resins; The 3520-WY-55 bisphenol A-type aqueous epoxy resins that described bisphenol A-type aqueous epoxy resins is Henkel Corp.; Described pure-acrylic emulsion is the RS-2806 pure-acrylic emulsion of the rich company of Ahmedabad; Described reactive thinner is the E10P reactive thinner of Henkel Corp.; Described color stuffing is Rutile type Titanium Dioxide; Described Rutile type Titanium Dioxide is the R-706 Rutile type Titanium Dioxide of E.I.Du Pont Company; Described filler is particle diameter in 800～1500 object calcium carbonate, calcined kaolin, talcous one of them or arbitrary combination; Described waterborne curing agent is the Auquamine721 waterborne curing agent of US Air gasification work.
After provided by the invention, a technical scheme is such: prepare the preparation method of this functional divider wall finish paint, comprise the steps: successively
1) raw material described in A component slurrying stage A 1 is stirred to 60～120min in 1000～1200rpm, so that slurry fineness is less than 30um, and then add raw material described in the paint stage, with 600～800rpm, stir 30～60min, filter, obtain component A;
2) starting material described in B component are stirred to 60～90min in 1000～1200rpm and mix, filter, obtain B component;
3) before application, component A and B component are mixed with 1:1, obtain functional divider wall finish paint.
Compared with prior art, technical scheme tool provided by the invention has the following advantages:
1) select the aqueous epoxy resins of stable, environmental protection as the main filmogen of coating, epoxy resin and solidifying agent form fine and close paint film, can isolate body of wall nuisance.
2) select again collocation part pure-acrylic emulsion, as functional emulsion, be better coated the color stuffing in coating, and then make paint film finer and close.
3) by adding reactive thinner, wherein contain on the one hand oxygen groups alive, participate in film forming, make paint film finer and close, it has very strong hydrophobicity and makes paint film have better water tolerance and scrub resistance on the other hand, the paint film density that adds wall paint that experimental results show that reactive thinner has very large lifting, shows as gloss raising and resistance to soiling and strengthens.
4) technical scheme provided by the invention, environmental protection, high resistant, decorative effect is excellent, isolation nuisance, scrubbing resistance, fungus-resistant, can meet home decoration requirement.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, but do not form any limitation of the invention, and the change of the unsubstantiality content that anyone makes in the claims in the present invention protection domain, still in the claims in the present invention protection domain.
Embodiment 1
A kind of functional divider wall finish paint provided by the invention and preparation method thereof:
A component
Slurrying stage A 1 component
Described raw material is dropped in Scattered Kettle, with 1200rpm, carries out dispersed with stirring, be less than 30um to slurry fineness, normal dispersion 60min, wherein the aqueous solution of emulsifying agent be at Scattered Kettle in whipped state, continually slowly add.
Paint stage A 2 components
Above-mentioned paint stage A 2 components are dropped into aforementioned slurrying stage A 1 component, and reduce stirring velocity to 600rpm, dispersed with stirring 60min, filtration, packing get final product to obtain the functional divider wall finish paint of 100kg A component.
B component
Above-mentioned starting material are dropped into Scattered Kettle, with 1200rpm, carry out dispersed with stirring, be less than 30um to slurry fineness, normal dispersion 60, to 90min, filters and packages and gets final product to obtain the functional divider wall finish paint of 100kg B component.Wherein the aqueous solution of emulsifying agent be at Scattered Kettle in whipped state, continually slowly add.
Before brushing, by the mass ratio of 1:1, evenly mix A, B component, then add A, B and measure approximately 10% water, more than effectively disperseing 2min, get final product to such an extent that tool resistant, decorative effect are excellent, the functional divider wall finish paint (dumb light) of scrubbing resistance, fungus-resistant.
Embodiment 2
Functional divider wall finish paint of another kind provided by the invention and preparation method thereof:
A component
A1 slurrying stage component
Described raw material is dropped in Scattered Kettle, with 1200rpm, carry out dispersed with stirring, be less than 30um to slurry fineness, normal dispersion 90min can produce a desired effect.Wherein the aqueous solution of emulsifying agent be at Scattered Kettle in whipped state, continually slowly add.
A2 paint stage component
Above-mentioned raw materials is dropped in aforementioned slurry, and reduce stirring velocity to 600rpm, dispersed with stirring 60min, filtration, packing get final product to obtain the functional divider wall finish paint of 100kg A component.
B component
Above-mentioned starting material are dropped into Scattered Kettle, with 1200rpm, carry out dispersed with stirring, be less than 30um to slurry fineness, normal dispersion 90min can produce a desired effect.Filter and package and get final product to obtain the functional divider wall finish paint of 100kg B component.Wherein the aqueous solution of emulsifying agent be at Scattered Kettle in whipped state, continually slowly add.
Before brushing, by the mass ratio of 1:1, evenly mix A, B component, then add A, B and measure approximately 10% water, more than effectively disperseing 2min, get final product to such an extent that tool resistant, decorative effect are excellent, the functional divider wall finish paint (mercerising) of scrubbing resistance, fungus-resistant.
Embodiment 3
A kind of functional divider wall finish paint that the present invention also provides and preparation method thereof:
A component
A1 slurrying stage component
Described raw material is dropped in Scattered Kettle, with 1200rpm, carry out dispersed with stirring, be less than 30um to slurry fineness, normal dispersion 90min can produce a desired effect.Wherein the aqueous solution of emulsifying agent be at Scattered Kettle in whipped state, continually slowly add.
A2 paint stage component
Above-mentioned raw materials is dropped in aforementioned slurry, and reduce stirring velocity to 600rpm, dispersed with stirring 60min, filtration, packing get final product to obtain the functional divider wall finish paint of 100kg A component.
B component
Above-mentioned starting material are dropped into Scattered Kettle, with 1200rpm, carry out dispersed with stirring, be less than 30um to slurry fineness, normal dispersion 90min can produce a desired effect.Filter and package and get final product to obtain the functional divider wall finish paint of 100kg B component.Wherein the aqueous solution of emulsifying agent be at Scattered Kettle in whipped state, continually slowly add.
Before brushing, by the mass ratio of 1:1, evenly mix A, B component, then add A, B and measure approximately 10% water, more than effectively disperseing 2min, get final product to such an extent that tool resistant, decorative effect are excellent, the functional divider wall finish paint (Gao Guang) of scrubbing resistance, fungus-resistant.
Effect embodiment 1
The functional divider wall finish paint (mercerising) of the embodiment of the present invention 2 is carried out to decoration construction to new body of wall, and the content of brushing radioactive radon gas between wall paint back room has obvious minimizing, in Table 1, has confirmed the effective buffer action of this wall paint to body of wall nuisance.
Table 1: indoor radon gas content data table
Effect embodiment 2
This functional divider wall finish paint is carried out to fungus-resistant detection, confirmed that this wall paint has good fungus-resistant effect.Detected result is as table 2:
Table 2: fungus-resistant experimental result
Above-described embodiment is preferably embodiment of the present invention; but embodiments of the present invention are not restricted to the described embodiments; other any do not deviate from change, the modification done under spirit of the present invention and principle, substitutes, combination, simplify; all should be equivalent substitute mode, within being included in protection scope of the present invention.
Claims (10)
1. a functional divider wall finish paint, is characterized in that, A component and the B component of mass ratio 1:1, consists of, and described A component is comprised of slurrying stage A 1 component and paint stage A 2;
Wherein:
Slurrying stage A 1 component is by 10-17 mass parts deionized water, 14-27 mass parts filler, and No. 1 auxiliary agent of 1.8-3 mass parts forms; No. 1 described auxiliary agent 0.3-1 mass parts emulsifying agent, 1.4-2 mass parts thickening material, 0.1 mass parts defoamer forms;
Paint stage A 2 components are by 38-60 mass parts aqueous epoxy resins; 10-13 mass parts pure-acrylic emulsion; 3 mass parts reactive thinners; 0.3-0.4 mass parts defoamer forms;
B component is by 21-33 mass parts waterborne curing agent; 44-51 mass parts color stuffing; 20.6-26.1 mass parts deionized water; No. 2 auxiliary agents of 1.9-2.7 mass parts; No. 2 described auxiliary agents are by 0.5-1 mass parts emulsifying agent, 0.3 mass parts wetting agent, and 0.1 mass parts dispersion agent, 0.5-1.8 mass parts defoamer forms.
2. a kind of functional divider wall finish paint according to claim 1, is characterized in that, described aqueous epoxy resins is bisphenol A-type aqueous epoxy resins.
3. a kind of functional divider wall finish paint according to claim 2, is characterized in that, the 3520-WY-55 bisphenol A-type aqueous epoxy resins that described bisphenol A-type aqueous epoxy resins is Henkel Corp..
4. a kind of functional divider wall finish paint according to claim 1, is characterized in that, described pure-acrylic emulsion is the RS-2806 pure-acrylic emulsion of the rich company of Ahmedabad.
5. a kind of functional divider wall finish paint according to claim 1, is characterized in that the E10P reactive thinner that described reactive thinner is Henkel Corp..
6. a kind of functional divider wall finish paint according to claim 1, is characterized in that, described color stuffing is Rutile type Titanium Dioxide.
7. a kind of functional divider wall finish paint according to claim 6, is characterized in that the R-706 Rutile type Titanium Dioxide that described Rutile type Titanium Dioxide is E.I.Du Pont Company.
8. a kind of functional divider wall finish paint according to claim 1, is characterized in that, described filler is particle diameter in 800～1500 object calcium carbonate, calcined kaolin, talcous one of them or arbitrary combination.
9. a kind of functional divider wall finish paint according to claim 1, is characterized in that, described waterborne curing agent is the Auquamine721 waterborne curing agent of US Air gasification work.
10. the preparation method of preparation functional divider wall finish paint claimed in claim 1, comprises the steps: successively
1) raw material described in A component slurrying stage A 1 is stirred to 60～120min in 1000～1200rpm, so that slurry fineness is less than 30um, and then add raw material described in the paint stage, with 600～800rpm, stir 30～60min, filter, obtain component A;
2) starting material described in B component are stirred to 60～90min in 1000～1200rpm and mix, filter, obtain B component;
3) before application, component A and B component are mixed with 1:1, obtain functional divider wall finish paint.