CN105131739A - Environment-friendly humidifying diatom ooze coating - Google Patents
Environment-friendly humidifying diatom ooze coating Download PDFInfo
- Publication number
- CN105131739A CN105131739A CN201510551883.XA CN201510551883A CN105131739A CN 105131739 A CN105131739 A CN 105131739A CN 201510551883 A CN201510551883 A CN 201510551883A CN 105131739 A CN105131739 A CN 105131739A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- agent
- powder
- environmental protection
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly humidifying diatom ooze coating. The coating is prepared from silica sol/benzene-acrylic compound emulsion, pure acrylic emulsion, modified diatom ooze, light calcium carbonate, lithopone, anion powder, sodium alginate, dispersing agents SN-5040, ethylene glycol, wetting agents AP-680, alcohol ester-12, propylene glycol monomethyl ether acetate, thickening agents, flatting agents, defoaming agents, sterilization and mildew prevention agents and deionized water. The environment-friendly humidifying diatom ooze coating has the effects of absorbing moisture, releasing moisture, cleaning air and releasing anions, harmful ingredients in indoor air can be absorbed, and the environment protection and healthy effects are achieved.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of environmental protection moisture adjustable diatom ooze coating.
Background technology
Along with people produce and the modernization more of mode of life, more work and sports entertainment all can carry out in indoor, and shopping also need not be gone into the street every day, and suitable kryptoclimate makes people often need not arrive outdoors, like this, most of activity time of people is all spent in indoor.Add up according to investigations, people every day on average nearly more than 80% time spend in indoor, have even up to more than 93%.Therefore, the relation of IAQ (indoor air quality) and HUMAN HEALTH is just more tight, and people also just pay attention to IAQ (indoor air quality) more.Because existing indoor paint is more weak to objectionable constituent adsorption in the air of indoor, some product even also discharges the volatile organic matter such as formaldehyde, benzene,toluene,xylene, serious harm HUMAN HEALTH.And along with the development of society and growth in the living standard, people to the comfort level of living environment and security requirement more and more higher.Indoor air relative humidity is also the important environmental parameters of residence comfort, Application and Development humidity adjusting material to save energy, environmental protect comfortableness, promote ecotope significant.And when indoor relative humidity be that 50-60%, VOC content are low, anion concentration height time, human body sensory is comfortable, good for health.
The diatom ooze applied in current coating, general all have purify air, the performance such as sound insulation, but damping DeGrain usually, and it is limited in one's ability to purify air, therefore, developing the multi-functional diatom ooze coatings such as a kind of humidity absorption and release, anion releasing, removal obnoxious flavour, ecological, environmental protective, is the vital task that current in the art urgent need is researched and solved.
Summary of the invention
The present invention proposes a kind of environmental protection moisture adjustable diatom ooze coating, it can not only have humidity absorption and release, fresh air, anion releasing, and can adsorb the objectionable constituent in room air, environment protection health.
The present invention proposes a kind of environmental protection moisture adjustable diatom ooze coating, its raw material comprises by weight: silicon sol/phenylpropyl alcohol compound emulsion 40-56 part, pure-acrylic emulsion 10-20 part, modification diatom ooze 35-45 part, light calcium carbonate 8-15 part, zinc sulfide white 3-6 part, negative ion powder 5-10 part, sodium alginate 0.1-0.3 part, dispersion agent SN-50400.1-0.3 part, ethylene glycol 3-5 part, wetting agent AP-6800.3-0.5 part, alcohol ester 12 0.4-0.6 part, 1-Methoxy-2-propyl acetate 0.1-0.3 part, thickening material 0.5-1 part, flow agent 0.2-0.4 part, defoamer 0.2-0.4 part, biocide mildewcide 0.01-0.1 part, deionized water 65-80 part.
In a particular embodiment, the weight part of silicon sol/phenylpropyl alcohol compound emulsion can 42, 43, 44, 45, 46, 47, 48, 49, 51, 52, 53, 54, 55, the weight part of pure-acrylic emulsion can be 12, 13, 14.4, 15, 15.3, 16, 16.8, 17, 18, 19, the weight part of modification diatom ooze can be 36, 36.8, 37, 38, 39, 40, 41.7, 42, 43.5, 44, the weight part of light calcium carbonate can be 8.6, 9.1, 9.7, 11, 12.4, 13, 13.5, 14.3, the weight part of zinc sulfide white can be 3.2, 3.5, 3.7, 4.2, 4.8, 5.2, 5.6, 5.8, the weight part of negative ion powder can be 5.4, 6, 6.3, 7, 7.8, 8, 8.5, 9, 9.8 part.
Preferably, the preparation technology of described silicon sol/phenylpropyl alcohol compound emulsion comprises: by weight by after silicon sol 10-20 part, sodium laurylsulfonate 0.1-0.2 part, wetting agent X-4050.1-0.2 part and silane coupling agent KH-5600.5-1 part stirring and evenly mixing, leave standstill 10-12h, add benzene emulsion 20-30 part under stirring to mix, adjust ph is 9-10, obtains described silicon sol/phenylpropyl alcohol compound emulsion.
Due to benzene emulsion and silicon sol consistency poor, the two directly mixes and compositely easily occurs being separated and rear thickening behavior, therefore must carry out modification respectively to the two.By benzene emulsion tensio-active agent and silane coupling agent are carried out coated process to the fine particle of silicon sol, make hydroxyl SiO in inorganic coupling group (RO) m-in silane coupling agent and silicon sol
2micelle surface produces crosslinked or absorption, makes coupling agent and tensio-active agent with the form of unimolecular layer or polymolecular layer at SiO
2particle surface forms protective membrane, thus has slackened Nano-meter SiO_2
2the surface energy of particle and adsorptive power, the mixed consistency of both improvement, affinity and stability.
Preferably, the preparation method of described modification diatom ooze comprises: by weight diatomite 30-45 part of particle diameter < 60um is formed thick slurry with water-dispersion, add nano titanium oxide 10-15 part to stir, 10-20min is dehydrated at 80-100 DEG C, add terra alba 10-15 part, wilkinite 3-5 part, the mixing of redispersable latex powder 2-4 part again, obtain described modification diatom ooze; Preferably, in described diatomite, the content of amorphous silicon di-oxide is more than 80%.
Preferably, described redispersable latex powder is one or more in polyacrylic ester rubber powder, ethylene-vinyl acetate copolymer rubber powder, poly-sbr powder.
Preferably, described negative ion powder is that the rare earth element powder of 3-4:1 and tourmaline powder form by quality proportioning.
Preferably, described thickening material is one or more in aerosil, modified polyacrylate sodium, hydrophobic polyether compound, Modified polyacryloamid, ethoxyquin urethane polymer, non-ionic polyurethane compound, Natvosol; Described flow agent be polyurethanes flow agent, polyacrylic flow agent, GSK-588 series flow agent in one or more; Described defoamer is mineral oil antifoam agent or organic-silicon-modified defoamer; Described biocide mildewcide is one or more in nitrogenous organic heterocyclic molecule, termil, CMIT, Kathon.
Preferably, the weight proportion of wetting agent AP-680 and sodium alginate is 3-4:1.
A kind of preparation method of described environmental protection moisture adjustable diatom ooze coating, comprise: by dispersion agent SN-5040, after wetting agent AP-680 and deionized water mix, 3-5min is disperseed under 300-400r/min rotating speed, add modification diatom ooze, light calcium carbonate, zinc sulfide white and negative ion powder, 35-40min is disperseed under 1800-2200r/min rotating speed, be ground to fineness < 60 μm, add silicon sol/phenylpropyl alcohol compound emulsion again, pure-acrylic emulsion, sodium alginate, alcohol ester 12, 1-Methoxy-2-propyl acetate, ethylene glycol, thickening material, flow agent, defoamer and biocide mildewcide disperse 15-20min even to mixing liquid under 1000-1200r/min rotating speed.
In the present invention, silicon sol/phenylpropyl alcohol compound emulsion is added in described environmental protection moisture adjustable diatom ooze coating, phenylpropyl alcohol solution itself has good water tolerance, sticking power and flexibility, but the humidity due to simple emulsion paint is not very desirable, by adding inorganic filming substance silicon sol in benzene emulsion, sticking power and the moisture uptake of film are all greatly improved, appropriate silicon sol, further improve the water-permeable and air permeable of film, anticorrosion, water tolerance; Simultaneously by silicon sol/phenylpropyl alcohol compound emulsion and pure-acrylic emulsion composite, while improving the water tolerance of film, sticking power, water absorbability and flexibility, can also the inorganic color stuffing such as coated diatom ooze, light calcium carbonate, zinc sulfide white better, be conducive to being formed the paint film of densification continuously; By at diatomaceous hollow microporous structural load titanium dioxide, coordinate the modification diatom ooze that other composition is prepared from, not only significantly can improve purifying formaldehyde performance and the purifying formaldehyde persistence of diatom ooze, and due to the multi-cellular structure of diatomite itself, it has the performances such as excellent wet swelling, moisture releasing reduction and water migration; The anionic particle of the negative ion powder release of the specific proportioning objectionable impurities by effectively dissociating in absorbed air after the reaction of the various ways such as coated sedimentation, reaction, field current decomposition, and by its oxygenolysis, produce the effect purified the air of a room thus; Light calcium carbonate and the composite opacifying power that can improve coating of zinc sulfide white, prevent the problems such as a point water, caking, poor fluidity; The stable storing performance of the sodium alginate of specified proportion and the composite raising coating of wetting agent AP-680, and film is stable, good weatherability; The film coalescence aid such as alcohol ester 12,1-Methoxy-2-propyl acetate, due to superior solubility, are conducive to film stable, even.
In the present invention, the humidity of described environmental protection moisture adjustable diatom ooze coating is excellent, and anion releasing, while fresh air, also harmful species adsorbs or reduction activity, thus the Air quality environment of safe occupancy life is provided, and described coating also has excellent weathering resistance, water tolerance, contamination resistance and tack, long-term exposure does not ftracture under air, do not peel off, not shedding, nondiscoloration, durable in use, safety non-toxic, pollution-free, be applicable to indoor wall decorations.
Embodiment
Embodiment 1
In the present embodiment, a kind of environmental protection moisture adjustable diatom ooze coating, its raw material comprises by weight: silicon sol/phenylpropyl alcohol compound emulsion 40 parts, pure-acrylic emulsion 20 parts, modification diatom ooze 35 parts, light calcium carbonate 15 parts, 3 parts, zinc sulfide white, negative ion powder 10 parts, sodium alginate 0.1 part, dispersion agent SN-50400.3 part, ethylene glycol 3 parts, wetting agent AP-6800.5 part, alcohol ester 12 parts, 1-Methoxy-2-propyl acetate 0.3 part, thickening material 0.5 part, flow agent 0.4 part, defoamer 0.2 part, biocide mildewcide 0.1 part, deionized water 65 parts;
The preparation technology of described silicon sol/phenylpropyl alcohol compound emulsion comprises: by weight by after silicon sol 10 parts, sodium laurylsulfonate 0.2 part, wetting agent X-4050.1 part and silane coupling agent KH-5601 part stirring and evenly mixing, leave standstill 10h, add benzene emulsion 30 parts under stirring to mix, adjust ph is 9-10, obtains described silicon sol/phenylpropyl alcohol compound emulsion;
The preparation method of described modification diatom ooze comprises: by weight 30 parts, the diatomite of particle diameter < 60um is formed thick slurry with water-dispersion, add nano titanium oxide 15 parts to stir, 20min is dehydrated at 80 DEG C, add terra alba 10 parts, wilkinite 5 parts, polyacrylic ester rubber powder 2 parts mixing again, obtain described modification diatom ooze, in wherein said diatomite, the content of amorphous silicon di-oxide is more than 80%;
Described negative ion powder is that the rare earth element powder of 3:1 and tourmaline powder form by quality proportioning; Described thickening material is aerosil; Described flow agent is polyurethanes flow agent; Described defoamer is mineral oil antifoam agent; Described biocide mildewcide is nitrogenous organic heterocyclic molecule.
Embodiment 2
In the present embodiment, a kind of environmental protection moisture adjustable diatom ooze coating, its raw material comprises by weight: silicon sol/phenylpropyl alcohol compound emulsion 56 parts, pure-acrylic emulsion 10 parts, modification diatom ooze 45 parts, light calcium carbonate 8 parts, 6 parts, zinc sulfide white, negative ion powder 5 parts, sodium alginate 0.3 part, dispersion agent SN-50400.1 part, ethylene glycol 5 parts, wetting agent AP-6800.3 part, alcohol ester 12 parts, 1-Methoxy-2-propyl acetate 0.1 part, thickening material 1 part, flow agent 0.2 part, defoamer 0.4 part, biocide mildewcide 0.01 part, deionized water 80 parts;
The preparation technology of described silicon sol/phenylpropyl alcohol compound emulsion comprises: by weight by after silicon sol 20 parts, sodium laurylsulfonate 0.1 part, wetting agent X-4050.2 part and silane coupling agent KH-5600.5 part stirring and evenly mixing, leave standstill 12h, add benzene emulsion 20 parts under stirring to mix, adjust ph is 9-10, obtains described silicon sol/phenylpropyl alcohol compound emulsion;
The preparation method of described modification diatom ooze comprises: by weight 45 parts, the diatomite of particle diameter < 60um is formed thick slurry with water-dispersion, add nano titanium oxide 10 parts to stir, 10min is dehydrated at 100 DEG C, add terra alba 15 parts, wilkinite 3 parts, ethylene-vinyl acetate copolymer rubber powder 4 parts mixing again, obtain described modification diatom ooze, in wherein said diatomite, the content of amorphous silicon di-oxide is more than 80%;
Described negative ion powder is that the rare earth element powder of 4:1 and tourmaline powder form by quality proportioning; Described thickening material is modified polyacrylate sodium; Described flow agent is polyacrylic flow agent; Described defoamer is organic-silicon-modified defoamer; Described biocide mildewcide is termil.
Embodiment 3
In the present embodiment, a kind of environmental protection moisture adjustable diatom ooze coating, its raw material comprises by weight: silicon sol/phenylpropyl alcohol compound emulsion 48 parts, pure-acrylic emulsion 15 parts, modification diatom ooze 40 parts, light calcium carbonate 11 parts, 4 parts, zinc sulfide white, negative ion powder 7 parts, sodium alginate 0.2 part, dispersion agent SN-50400.2 part, ethylene glycol 4 parts, wetting agent AP-6800.4 part, alcohol ester 12 parts, 1-Methoxy-2-propyl acetate 0.2 part, thickening material 0.7 part, flow agent 0.3 part, defoamer 0.3 part, biocide mildewcide 0.05 part, deionized water 70 parts;
The preparation technology of described silicon sol/phenylpropyl alcohol compound emulsion comprises: by weight by after silicon sol 15 parts, sodium laurylsulfonate 0.15 part, wetting agent X-4050.15 part and silane coupling agent KH-5600.7 part stirring and evenly mixing, leave standstill 11h, add benzene emulsion 25 parts under stirring to mix, adjust ph is 9-10, obtains described silicon sol/phenylpropyl alcohol compound emulsion;
The preparation method of described modification diatom ooze comprises: by weight 37 parts, the diatomite of particle diameter < 60um is formed thick slurry with water-dispersion, add nano titanium oxide 12 parts to stir, 15min is dehydrated at 90 DEG C, add terra alba 12 parts, wilkinite 4 parts, poly-sbr powder 3 parts mixing again, obtain described modification diatom ooze, in wherein said diatomite, the content of amorphous silicon di-oxide is more than 80%;
Described negative ion powder is that the rare earth element powder of 3.5:1 and tourmaline powder form by quality proportioning; Described thickening material is hydrophobic polyether compound, Modified polyacryloamid two kinds of compositions; Described flow agent is GSK-588 series flow agent; Described defoamer is mineral oil antifoam agent; Described biocide mildewcide is CMIT.
Embodiment 4
In the present embodiment, a kind of environmental protection moisture adjustable diatom ooze coating, its raw material comprises by weight: silicon sol/phenylpropyl alcohol compound emulsion 49 parts, pure-acrylic emulsion 16 parts, modification diatom ooze 42 parts, light calcium carbonate 12 parts, 5 parts, zinc sulfide white, negative ion powder 8 parts, sodium alginate 0.2 part, dispersion agent SN-50400.25 part, ethylene glycol 4 parts, wetting agent AP-6800.45 part, alcohol ester 12 parts, 1-Methoxy-2-propyl acetate 0.15 part, thickening material 0.8 part, flow agent 0.3 part, defoamer 0.25 part, biocide mildewcide 0.06 part, deionized water 75 parts;
The preparation technology of described silicon sol/phenylpropyl alcohol compound emulsion comprises: by weight by after silicon sol 16 parts, sodium laurylsulfonate 0.16 part, wetting agent X-4050.16 part and silane coupling agent KH-5600.8 part stirring and evenly mixing, leave standstill 11h, add benzene emulsion 26 parts under stirring to mix, adjust ph is 9-10, obtains described silicon sol/phenylpropyl alcohol compound emulsion;
The preparation method of described modification diatom ooze comprises: by weight 38 parts, the diatomite of particle diameter < 60um is formed thick slurry with water-dispersion, add nano titanium oxide 13 parts to stir, 16min is dehydrated at 95 DEG C, add terra alba 13 parts, wilkinite 4 parts, redispersable latex powder 3 parts mixing again, obtain described modification diatom ooze, in wherein said diatomite, the content of amorphous silicon di-oxide is more than 80%; Described redispersable latex powder is polyacrylic ester rubber powder, ethylene-vinyl acetate copolymer rubber powder two kinds of compositions;
Described negative ion powder is that the rare earth element powder of 3.6:1 and tourmaline powder form by quality proportioning; Described thickening material is ethoxyquin urethane polymer, non-ionic polyurethane compound, Natvosol three kinds of compositions; Described flow agent is GSK-588 series flow agent; Described defoamer is organic-silicon-modified defoamer; Described biocide mildewcide is one or more in Kathon.
The preparation method of the environmental protection moisture adjustable diatom ooze coating described in above-described embodiment 1-4, comprise: by dispersion agent SN-5040, after wetting agent AP-680 and deionized water mix, 3-5min is disperseed under 300-400r/min rotating speed, add modification diatom ooze, light calcium carbonate, zinc sulfide white, negative ion powder, 35-40min is disperseed under 1800-2200r/min rotating speed, be ground to fineness < 60 μm, add silicon sol/phenylpropyl alcohol compound emulsion again, pure-acrylic emulsion, sodium alginate, alcohol ester 12, 1-Methoxy-2-propyl acetate, ethylene glycol, thickening material, flow agent, defoamer and biocide mildewcide disperse 15-20min even to mixing liquid under 1000-1200r/min rotating speed.
The performance test results of the environmental protection moisture adjustable diatom ooze coating that above-described embodiment 1-4 obtains is as shown in the table:
In the present invention, silicon sol/phenylpropyl alcohol compound emulsion is added in described environmental protection moisture adjustable diatom ooze coating, phenylpropyl alcohol solution itself has good water tolerance, sticking power and flexibility, but the humidity due to simple emulsion paint is not very desirable, by adding inorganic filming substance silicon sol in benzene emulsion, sticking power and the moisture uptake of film are all greatly improved, appropriate silicon sol, further improve the water-permeable and air permeable of film, anticorrosion, water tolerance; Simultaneously by silicon sol/phenylpropyl alcohol compound emulsion and pure-acrylic emulsion composite, while improving the water tolerance of film, sticking power, water absorbability and flexibility, can also the inorganic color stuffing such as coated diatom ooze, light calcium carbonate, zinc sulfide white better, be conducive to being formed the paint film of densification continuously; By at diatomaceous hollow microporous structural load titanium dioxide, coordinate the modification diatom ooze that other composition is prepared from, not only significantly can improve purifying formaldehyde performance and the purifying formaldehyde persistence of diatom ooze, and due to the multi-cellular structure of diatomite itself, it has the performances such as excellent wet swelling, moisture releasing reduction and water migration; The anionic particle of the negative ion powder release of the specific proportioning objectionable impurities by effectively dissociating in absorbed air after the reaction of the various ways such as coated sedimentation, reaction, field current decomposition, and by its oxygenolysis, produce the effect purified the air of a room thus; Light calcium carbonate and the composite opacifying power that can improve coating of zinc sulfide white, prevent the problems such as a point water, caking, poor fluidity; The stable storing performance of the sodium alginate of specified proportion and the composite raising coating of wetting agent AP-680, and film is stable, good weatherability; The film coalescence aid such as alcohol ester 12,1-Methoxy-2-propyl acetate, due to superior solubility, are conducive to film stable, even.
In the present invention, the humidity of described environmental protection moisture adjustable diatom ooze coating is excellent, and anion releasing, while fresh air, also harmful species adsorbs or reduction activity, thus the Air quality environment of safe occupancy life is provided, and described coating also has excellent weathering resistance, water tolerance, contamination resistance and tack, long-term exposure does not ftracture under air, do not peel off, not shedding, nondiscoloration, durable in use, safety non-toxic, pollution-free, be applicable to indoor wall decorations.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (8)
1. an environmental protection moisture adjustable diatom ooze coating, it is characterized in that, its raw material comprises by weight: silicon sol/phenylpropyl alcohol compound emulsion 40-56 part, pure-acrylic emulsion 10-20 part, modification diatom ooze 35-45 part, light calcium carbonate 8-15 part, zinc sulfide white 3-6 part, negative ion powder 5-10 part, sodium alginate 0.1-0.3 part, dispersion agent SN-50400.1-0.3 part, ethylene glycol 3-5 part, wetting agent AP-6800.3-0.5 part, alcohol ester 12 0.4-0.6 part, 1-Methoxy-2-propyl acetate 0.1-0.3 part, thickening material 0.5-1 part, flow agent 0.2-0.4 part, defoamer 0.2-0.4 part, biocide mildewcide 0.01-0.1 part, deionized water 65-80 part.
2. environmental protection moisture adjustable diatom ooze coating according to claim 1, it is characterized in that, the preparation technology of described silicon sol/phenylpropyl alcohol compound emulsion comprises: by weight by after silicon sol 10-20 part, sodium laurylsulfonate 0.1-0.2 part, wetting agent X-4050.1-0.2 part and silane coupling agent KH-5600.5-1 part stirring and evenly mixing, leave standstill 10-12h, add benzene emulsion 20-30 part under stirring to mix, adjust ph is 9-10, obtains described silicon sol/phenylpropyl alcohol compound emulsion.
3. environmental protection moisture adjustable diatom ooze coating according to claim 1 and 2, it is characterized in that, the preparation method of described modification diatom ooze comprises: by weight diatomite 30-45 part of particle diameter < 60um is formed thick slurry with water-dispersion, add nano titanium oxide 10-15 part to stir, 10-20min is dehydrated at 80-100 DEG C, add terra alba 10-15 part, wilkinite 3-5 part, the mixing of redispersable latex powder 2-4 part again, obtain described modification diatom ooze; Preferably, in described diatomite, the content of amorphous silicon di-oxide is more than 80%.
4. environmental protection moisture adjustable diatom ooze coating according to claim 3, is characterized in that, described redispersable latex powder is one or more in polyacrylic ester rubber powder, ethylene-vinyl acetate copolymer rubber powder, poly-sbr powder.
5. the environmental protection moisture adjustable diatom ooze coating according to any one of claim 1-4, is characterized in that, described negative ion powder is that the rare earth element powder of 3-4:1 and tourmaline powder form by quality proportioning.
6. the environmental protection moisture adjustable diatom ooze coating according to any one of claim 1-5, it is characterized in that, described thickening material is one or more in aerosil, modified polyacrylate sodium, hydrophobic polyether compound, Modified polyacryloamid, ethoxyquin urethane polymer, non-ionic polyurethane compound, Natvosol; Described flow agent be polyurethanes flow agent, polyacrylic flow agent, GSK-588 series flow agent in one or more; Described defoamer is mineral oil antifoam agent or organic-silicon-modified defoamer; Described biocide mildewcide is one or more in nitrogenous organic heterocyclic molecule, termil, CMIT, Kathon.
7. the environmental protection moisture adjustable diatom ooze coating according to any one of claim 1-6, is characterized in that, the weight proportion of wetting agent AP-680 and sodium alginate is 3-4:1.
8. the preparation method of the environmental protection moisture adjustable diatom ooze coating according to any one of claim 1-7, it is characterized in that, comprise: by dispersion agent SN-5040, after wetting agent AP-680 and deionized water mix, 3-5min is disperseed under 300-400r/min rotating speed, add modification diatom ooze, light calcium carbonate, zinc sulfide white, negative ion powder, 35-40min is disperseed under 1800-2200r/min rotating speed, be ground to fineness < 60 μm, add silicon sol/phenylpropyl alcohol compound emulsion again, pure-acrylic emulsion, sodium alginate, alcohol ester 12, 1-Methoxy-2-propyl acetate, ethylene glycol, thickening material, flow agent, defoamer and biocide mildewcide disperse 15-20min even to mixing liquid under 1000-1200r/min rotating speed.